刚性聚合物改性PVC/CPE/CaCO_3共混体的研究

本文研究刚性聚合物(PS、PMMA)对CaCO_2填充的PVC/CPE共混体力学性能和流变性能的影响。结果表明,刚性聚合物的填入提高了共混体的冲击强度,其中,对PVC/CPE/CaCO_3=100/15/10体系的增韧效果较好。PMMA使共混体的拉伸强度有所提高而PS使共混体拉伸强度下降。流变性的测定显示,Ca-CO_2使共混体的表观粘度和粘流活化能增加,牛顿的流动性增强,而在PVC/CPE/CaCO_3共混体中加入4.5份PS能明显降低共混体的表观粘度和粘流活化能,牛顿的流动性降低,但仍有良好的挤出物外观和较低的挤出膨胀率。     

埃洛石纳米管对PVC/CPE复合材料性能的影响

制备了PVC/CPE/埃洛石纳米管（HNTs）复合材料,研究了HNTs对PVC/CPE复合材料力学性能、微观形貌及热性能的影响.结果显示,HNTs对PVC/CPE材料的增韧效果与基体的韧性及HNTs的添加量有关.当基体韧性较低时,添加少量的HNTs可显著提高PVC/CPE的冲击强度,同时,材料的拉伸强度、弯曲强度和热性能也得到一定的提高.当m（PVC）∶m（CPE）∶m（HNTs）=100∶ 3∶3时,复合材料的冲击强度可达22.17 J/m2,为纯PVC基体树脂的3.4倍,复合材料的冲击断面较粗糙,HNTs在基体中分散较均匀.     

PE/PVC共混物与PE界面黏结性能研究

为改善聚氯乙烯(PVC)和聚乙烯(PE)界面黏结性能,制备了一系列PE/PVC共混物及其与PE的黏结材料,探究了原料比例和成型温度对(PE/PVC)/PE界面黏结性能的影响。结果表明,PE/PVC共混物为不相容体系。共混物中随着PE含量升高,体系拉伸强度增大,断裂伸长率升高。(PE/PVC)/PE材料中,随着PE/PVC共混物中PVC含量升高,PE/PVC与PE的界面黏结强度先升高后降低。成型温度升高,界面黏结性能提高。在PE/PVC比例为60/40、黏结温度为100℃时,PE/PVC共混物与PE的界面黏结强度最大,可与共混物拉伸强度接近。     

PVC/ACS/CPE三元共混体系性能研究

采用机械共混制备了聚氯乙烯(PVC)/丙烯腈-氯化聚乙烯-苯乙烯共聚物(ACS)/氯化聚乙烯(CPE)三元共混合金,研究了共混体系的组成与合金力学性能及耐热性能的关系。结果表明,不同型号PVC对合金的性能影响不同,随着PVC摩尔质量的增加,共混合金的拉伸强度、冲击强度、热变形温度、硬度及氧指数逐渐增大,熔体质量流动速率(MFR)下降;随着共混合金中CPE用量的增加,PVC/ACS/CPE共混合金的冲击强度上升,氧指数增大,拉伸强度、弯曲强度、弯曲模量、热变形温度及MFR下降。     

无机粒子/弹性体协同增韧PVC的力学性能研究

采用乙烯-醋酸乙烯共聚物(EVA)、氯化聚乙烯(CPE)及碳酸钙(Ca CO3)对聚氯乙烯(PVC)进行协同增韧改性。研究表明,当CPE/EVA/PVC配比为6/4/100时,共混体系的拉伸强度达到最大。共混体系中Ca CO3用量控制10份左右,在增韧的同时还起到增强的作用。光老化条件下,Ca CO3/CPE/EVA/PVC共混体系的拉伸强度及冲击强度总体呈下降趋势,但强度保持率均在88%以上。     

EDA-GO/CPE/PS纳米复合材料的制备及性能研究

选取氯化聚乙烯(CPE)弹性体为增韧剂,乙二胺接枝氧化石墨烯(EDA-GO)为纳米填料,经熔融共混法制备了CPE/聚苯乙烯树脂(PS)和EDA-GO/CPE/PS纳米复合材料。采用红外光谱、拉伸测试、冲击测试和熔融指数测试方法研究了EDA-GO的表面结构,复合材料的拉伸性能、冲击性能和熔融流动性能。结果表明,乙二胺(EDA)已成功接枝于氧化石墨烯(GO)的表面上;在CPE/PS复合材料中,材料的拉伸强度和冲击强度的变化规律与一般弹性体增韧塑料的规律一致;在EDA-GO/CPE/PS纳米复合材料中,随着EDA-GO含量的增加其拉伸强度、冲击强度、断裂伸长率和弹性模量都有先上升后下降的趋势,当EDA-GO质量分数为0.5%时,拉伸强度达最大值,较CPE/PS复合材料提高了38%,较纯PS提高了61%;在EDA-GO质量分数为0.75%时,其冲击强度和弹性模量最大,比CPE/PS复合材料冲击强度和弹性模量分别提高了18%和41%。因此,当EDA-GO的质量分数在0.5%~0.75%之间时,复合材料的综合力学性能最好。随着EDA-GO的加入,纳米复合材料的熔融指数先下降后上升。     

氯化聚丙烯对PP/PVC共混物性能的影响

以氯化聚丙烯(CPP)为增容剂,探讨了CPP不同含量下PP/PVC体系的力学性能、相容性、流变性能以及对应的微观结构,并与氯化聚乙烯(CPE)增容剂进行了比较。发现添加5份CPP可明显改善PP和PVC两相界面相容性,与PP/PVC体系相比,拉伸强度提高了61%,无缺口冲击强度提高了100%。此时CPP还起到了一定的增塑作用,共混体系加工性能较好。与CPE相比,含有CPP的共混体系拉伸强度较高。     

PVC/CPE/GF复合材料制备及力学性能

采用玻璃纤维(GF)及氯化聚乙烯(CPE)对聚氯乙烯(PVC)协同增韧改性。研究表明,当共混体系中有一定量的GF时,CPE的加入不仅能够改善共混物的韧性,还能够促进GF在PVC基体中的分散,两者协同增韧。随着CPE加入量的增加,GF分散效果增强,PVC/CPE/GF共混物的硬度呈现先显著增强后缓慢增强的趋势、拉伸强度和断裂伸长率逐渐上升、拉伸弹性模量先升高后下降,增韧效果明显。当经过硅烷偶联剂KH–550处理过的GF的质量一定,CPE用量为配方总质量的15%~20%之间时,通过PVC/CPE/GF共混物样条冲击断面的扫描电子显微镜观察可见,GF在基体中分散均匀,与基体粘结紧密,断面产生了大量有规则的网丝结构,增韧效果最佳。     

用氯化聚乙烯改善聚氯乙烯的冲击强度

氯化聚乙烯(CPE)是聚氯乙烯(PVC)最常用的冲击改性剂之一,常用于PVC的增韧改性。本文从相容性、共混物形态与体系性能的关系,影响共混物形态及冲击强度的因素及共混体系的不可逆形变4个方面介绍了采用CPE改善PVC冲击性能,从而找出了提高PVC/CPE共混体系冲击强度的最佳途径。     

CPE对PVC／PP共混体系的增容作用

在单螺杆挤出机上用一次投料直接共混方法制样,通过差热分析(DSC),透射电镜(TEM),图象分析和力学性能试验等法研究表明,PVC 和 PP 不相容,CPE对 PVC/PP 共混体系具有较好的增容作用。5份 CPE 使得 PVC/PP 体系分散相(PP)粒径变小,粒径分布均匀性提高,并且使得 PVC 和 PP 两相界面变得比较模糊。在 PVC/PP 体系中加入 CPE 后,共混物的拉伸性能和冲击性能都有较大提高。     

PVC-C/PVC共混材料的性能研究

采用氯化聚乙烯（CPE）对氯化聚氯乙烯（PVC—C）进行抗冲改性，将改性后的PVC—C与PVC进行共混，研究了PVC-C／PVC配比对PVC-C／PVC共混物力学性能、耐热性能及流变形能的影响。结果表明，PVC—C／PVC共混物的维卡软化点随PVC—C的用量增加而上升，在50／50（质量比）处有一拐点，大于50／50时上升更快些。共混物的拉伸强度、弯曲强度和熔体黏度随PVC—C用量的增加而提高；混物中随PVC—C用量增加，塑化时间缩短，塑化能力增强，而冲击强度和断裂伸长率却随PVC—C用量增加而下降。共平衡转矩增加。     

Compatibilizers for recycling of the plastic mixture wastes. II. The effect of a compatibilizer for binary blends on the properties of ternary blends

In this article, we discuss the effect of a compatibilizer for binary blends on the properties of ternary blends composed of high‐density polyethylene (HDPE), polypropylene (PP), or polystyrene (PS) and poly(vinyl chloride) (PVC) virgin polymers with a simulated waste plastics fraction. Chlorinated polyethylene (CPE), ethylene–propylene rubber (EPR), and their 1/1 (w/w) mixture were tested as compatibilizers for the HDPE/PP/PVC ternary blend. CPE, styrene‐ethylene‐propylene block copolymer (SEP), or their 1/1 (w/w) mixture were tested as compatibilizers for the HDPE/PS/PVC ternary blend. The composition of the ternary blends were fixed at 8/1/1 by weight ratio. The amount of the compatibilizer was 3 phr. Rheological, mechanical, and thermal properties were measured. For the 8/1/1 HDPE/PP/PVC ternary blends, the tensile strength was slightly decreased, but the impact strength was significantly increased by adding EPR, CPE, or their mixture. EPR exhibited the most significant impact modification effect for the ternary blends. In a similar way, for 8/1/1 HDPE/PS/PVC ternary blends, on adding SEP, CPE, or their mixture, the tensile strength was slightly decreased, but the impact strength was noticeably increased. It was found that the SEP worked much better as an impact modifier for the ternary blends than CPE or the SEP/CPE mixture did. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 76: 1048–1053, 2000     

固相法氯磺化聚乙烯改性聚氯乙烯的研究

本文着重讨论了氯磺化聚乙烯（ＣＳＭ）的氯含量，硫含量以及ＣＳＭ的用量对聚氯乙烯（ＰＶＣ）增韧性能的影响。实验结果表明随ＣＳＭ中的氯含量、硫含量的增加．ＰＶＣ—ＣＳＭ共混体系的位伸强度增加，冲击强度下降；随ＣＳＭ加入量的增加，体系的拉伸强度下降，冲击强度上升。ＣＳＭ作为增韧剂改性ＰＶＣ可取得比ＰＶＣ─ＣＰＥ体系更好的效果。ＰＶＣ─ＣＳＭ体系可在其冲击强度满足工业生产要求的基础上最小限度的降低拉伸强度，使拉伸强度保持在９０％左右。     

PP三元填充共混体系力学性能的研究

研究了乙烯-醋酸乙烯共聚物(EVA)、HDPE、LLDPE、PS、氯化聚乙烯(CPE)和丙烯酸酯类共聚物(ACR)等6种聚合物分别组成的PP/滑石粉/聚合物三元填充共混体系的缺口冲击强度、拉伸强度、断裂伸长率、拉伸弹性模量、球压痕硬度、成型收缩率及熔体流动速率等性能。结果表明:EVA、CPE和PS对PP/滑石粉二元填充体系的改性效果明显。     

硬质高聚合度PVC的改性

以硬质高聚合度ＰＶＣ为对象,采用ＤＯＰ、ＣＰＥ或ＳＡＮ进行增韧改性,研究了液体丁腈、ＡＣＲ及内、外润滑剂对加工流变性能的影响,结果表明,ＣＰＥ是高聚合度ＰＶＣ的优良增韧改性剂,对拉伸强度影响很小,ＳＡＮ对ＰＶＣ／ＣＰＥ＝１００／１０体系起到既增韧又增强效果,用量在３份以下,ＬＮＢＲ可降低熔体的表观粘度、缩短塑化时间,降低能耗,改善流变性,ＡＣＲ－２可明显改善熔体强度,促进熔融塑化,在高速剪切下,表面平整光滑,从力学性能、混炼状态、熔体流动和挤出物外观,选择ＥＳＯ、丁二烯、ＴＲＯ１６为润滑剂。硬质料的挤出性能及外观接近进口料水平。     

A study on poly(vinyl chloride) blends with chlorinated polyethylene and polyethylene

By means of a twin-roll masticator and Brabender rheometer, the effect of chlorinated polyethylene (CPE) and polyethylene (PE) on the impact strength and processability of poly(vinyl chloride) (PVC) was studied. The experimental results show that CPE can promote the plasticity of PVC and the effect increases with the amount of CPE. Addition of a small amount of PE in PVC/CPE (100/12) makes an impressive improvement in the impact strength of the mixture. The impact strength of PVC/CPE/PE (100/ 12/2.5) at 20°C is 30.0 kJ/m² higher than that of PVC/CPE (100/12). The dynamic viscoelastic spectra, tensile strength, and elongation test reveal that CPE is incompatible with PVC but may act as a compatibilizer for PVC/PE. The disperse state of the polyblend was studied by differential scanning calorimetry (DSC); it was found that the mixing sequence has an influence on the impact strength of the blend.     

ABS/PVC/CPE共混体系的力学性能

研究了填充改性丙烯腈-丁二烯-苯乙烯(ABS)三元共聚物、聚氯乙烯(PVC)和CPE三元共混体系力学性能与结构的关系。结果表明，在ABS／PVC共混体系中加入增容剂氯化聚乙烯(CPE)后，提高了共混体系的相容性和机械力学性能；随着共混体系中CPE用量的增加，ABS／PVC／CPE共混体系的冲击强度、断裂伸长率上升，拉伸强度下降，而弹性模量则出现了极大值。     

NBR/PVC共混胶的结构与性能

采用机械共混法和乳液共沉法制备了NBR/PVC共混胶,通过差示扫描量热仪(DSC)和场发射扫描电子显微镜(FE-SEM)对共混胶的微观形貌、结构进行了表征,考察了共混方式和共混胶配比对其力学性能的影响,并比较了共混胶、CPE、P-83对硬质/软质PVC的改性效果。结果表明:①与机械共混胶相比,乳液共沉胶混合得更均匀,分散性更好,其分子级混合程度更好;②乳液共沉胶试样的力学性能在总体上优于机械共混胶;③对于硬质PVC,CPE的改性效果优于其他改性剂;④对于软质PVC,乳液共沉胶的改性效果最好,特别是对撕裂强度的提高非常明显。