Features of the charge-transport mechanism in layered Bi<Subscript>2</Subscript>Te<Subscript>3</Subscript> single crystals doped with chlorine and terbium

The temperature dependences (T = 5−300 K) of the resistivity in the plane of layers and in the direction perpendicular to the layers, as well as the Hall effect and the magnetoresistance (H < 80 kOe, T = 0.5−4.2 K) in Bi₂Te₃ single crystals doped with chlorine and terbium, are investigated. It is shown that the doping of Bi₂Te₃ with terbium atoms results in p-type conductivity and in increasing hole concentration. The doping of Bi₂Te₃ with chlorine atoms modifies also the character of its conductivity instead of changing only the type from p to n. In the temperature dependence of the resistivity in the direction perpendicular to layers, a portion arises with the activation conductivity caused by the hopping between localized states. The charge-transport mechanism in Bi₂Te₃ single crystals doped with chlorine is proposed.     

Synthesis and electrical properties of Bi<Subscript>2</Subscript>Te<Subscript>3</Subscript>-based thermoelectric materials doped with Er,Tm, Yb,and Lu

Nanopowders of Bi₂Te₃ and R_0.1Bi_1.9Te₃ (where R = Er, Tm, Yb, Lu) are obtained by microwave solvothermal synthesis. The powder-like materials are compacted by cold isostatic compression followed by annealing in argon. The influence of the doping agent on the structure and characteristics of the derived materials are investigated. It is demonstrated that the introduction of rare-earth elements (2 at %) into the bismuth-telluride lattice leads to a decrease in the electrical resistivity and to an increase in the Seebeck coefficient. The best thermoelectric properties are obtained for the sample of bismuth telluride doped with thulium.     

Electrical and Thermal Conductivity and Conduction Mechanism of Ge<Subscript>2</Subscript>Sb<Subscript>2</Subscript>Te<Subscript>5</Subscript> Alloy

Ge₂Sb₂Te₅ alloy has drawn much attention due to its application in phase-change random-access memory and potential as a thermoelectric material. Electrical and thermal conductivity are important material properties in both applications. The aim of this work is to investigate the temperature dependence of the electrical and thermal conductivity of Ge₂Sb₂Te₅ alloy and discuss the thermal conduction mechanism. The electrical resistivity and thermal conductivity of Ge₂Sb₂Te₅ alloy were measured from room temperature to 823 K by four-terminal and hot-strip method, respectively. With increasing temperature, the electrical resistivity increased while the thermal conductivity first decreased up to about 600 K then increased. The electronic component of the thermal conductivity was calculated from the Wiedemann–Franz law using the resistivity results. At room temperature, Ge₂Sb₂Te₅ alloy has large electronic thermal conductivity and low lattice thermal conductivity. Bipolar diffusion contributes more to the thermal conductivity with increasing temperature. The special crystallographic structure of Ge₂Sb₂Te₅ alloy accounts for the thermal conduction mechanism.     

Effects of Cooling Rate on Thermoelectric Properties of <Emphasis Type="Italic">n</Emphasis>-Type Bi<Subscript>2</Subscript>(Se<Subscript>0.4</Subscript>Te<Subscript>0.6</Subscript>)<Subscript>3</Subscript> Compounds

A series of Bi₂(Se_0.4Te_0.6)₃ compounds were synthesized by a rapid route of melt spinning (MS) combined with a subsequent spark plasma sintering (SPS) process. Measurements of the Seebeck coefficient, electrical conductivity, and thermal conductivity were performed over the temperature range from 300 K to 520 K. The measurement results showed that the cooling rate of melt spinning had a significant impact on the transport properties of electrons and phonons, effectively enhancing the thermoelectric properties of the compounds. The maximum ZT value reached 0.93 at 460 K for the sample prepared with the highest cooling rate, and infrared spectrum measurement results showed that the compound with lower tellurium content, Bi₂(Se_0.4Te_0.6)₃, possesses a larger optical forbidden gap (E _g) compared with the traditional n-type zone-melted material with formula Bi₂(Se_0.07Te_0.93)₃. Our work provides a new approach to develop low-tellurium-bearing Bi₂Te₃-based compounds with good thermoelectric performance.     

Effect of Composition on Thermoelectric Properties in PbTe-Bi<Subscript>2</Subscript>Te<Subscript>3</Subscript> Composites

The solidification of alloys in the Bi₂Te₃-PbTe pseudobinary system at off- and near-eutectic compositions was investigated for their microstructure and thermoelectric properties. Dendritic and lamellar structures were clearly observed due to the phase separation and the existence of a metastable ternary phase. In this system, three phases with different compositions were observed: binary Bi₂Te₃, PbTe, and metastable PbBi₂Te₄. The Seebeck coefficient, electrical resistivity, and thermal conductivity of ternary alloys as well as binary compounds were measured. The phonon thermal conductivities of Pb-Bi-Te alloys were lower than those in binary PbTe and Bi₂Te₃, which could have resulted from the increased interfacial area between phases due to the existence of the metastable ternary phase and the resultant phase separation.     

Specific thermoelectric properties of lightly doped Bi<Subscript>2</Subscript>(TeSe)<Subscript>3</Subscript> solid solutions

Electrical and thermoelectric properties of a lightly doped n-Bi₂Te_2.7Se_0.3 solid solution have been studied in the temperature range 77–300 K. The results are compared with data for the compound PbTe_0.9Se_0.1 with a similar magnitude of the Seebeck coefficient S at 84 K. Along with lower thermal conductivity, Bi₂Te_2.7Se_0.3 has a higher electrical conductivity σ and a much weaker temperature dependence. As a result, the power coefficient S ²σ in optimal samples begins to decrease only when the density of minority carriers becomes significant. In this case, |S| considerably exceeds the standard value of 200 μV/K. The reduction of the electron density reduces the thermoelectric figure of merit Z at its maximum and slightly lowers the temperature of the maximum; therefore, the expected effect on the average value of Z in the range 77–300 K is absent. Similar behavior is observed in Bi₂Te_2.88Se_0.12, although the effect is less pronounced. The experimental results are discussed taking into account possible changes in the dominant scattering mechanisms, carrier density, and electron energy spectrum. __________ Translated from Fizika i Tekhnika Poluprovodnikov, Vol. 38, No. 7, 2004, pp. 811–815. Original Russian Text Copyright ? 2004 by Konstantinov, Prokof’eva, Ravich, Fedorov, Kompaniets.     

Doping of the Bi<Subscript>1.9</Subscript>Sb<Subscript>0.1</Subscript>Te<Subscript>3</Subscript> solid solution with Sn impurity

In (Bi_1.9Sb_0.1)_{1 − x} Sn _x Te₃ solid solution with different contents of Sn, the electrical conductivity (σ₁₁) and the Hall (R ₁₂₃ and R ₃₂₁), Seebeck (S ₁₁ and S ₃₃), and Nernst-Ettingshausen (Q ₁₂₃ and Q ₃₂₁) coefficients have been measured. It is shown that doping with tin strongly modifies temperature dependences of the kinetic coefficients. The effect of tin on electrical homogeneity of the samples has been studied: with increasing number of Sn atoms embedded, crystals become more homogeneous. These features indicate the presence of the quasi-local states of Sn in the valence band of Bi_1.9Sb_0.1Te₃. Within a one-band model, we estimated the effective mass of the density of hole states (m _d ), the energy gap extrapolated to 0 K (E _g0 = 0.20–0.25 eV), the energy of impurity states (E _Sn ≈ 40–45 meV), and the scattering parameter (r ≈ 0.1–0.4). Numerical values of the scattering parameter indicate a mixed mechanism of scattering in the samples under investigation with dominant scattering at acoustic phonons. With increasing content of tin in the samples, the contribution of impurity scattering increases.     

Effects of SiC Nanodispersion on the Thermoelectric Properties of <Emphasis Type="Italic">p</Emphasis>-Type and <Emphasis Type="Italic">n</Emphasis>-Type Bi<Subscript>2</Subscript>Te<Subscript>3</Subscript>-Based Alloys

Polycrystalline p-type Bi_0.5Sb_1.5Te₃ and n-type Bi₂Te_2.7Se_0.3 thermoelectric (TE) alloys containing a small amount (vol.% ≤5) of SiC nanoparticles were fabricated by mechanical alloying and spark plasma sintering. It was revealed that the effects of SiC addition on TE properties can be different between p-type and n-type Bi₂Te₃-based alloys. SiC addition slightly increased the power factor of the p-type materials by decreasing both the electrical resistivity (ρ) and Seebeck coefficient (α), but decreased the power factor of n-type materials by increasing both ρ and α. Regardless of the conductivity type, the thermal conductivity was reduced by dispersing SiC nanoparticles in the Bi₂Te₃-based alloy matrix. As a result, a small amount (0.1 vol.%) of SiC addition increased the maximum dimensionless figure of merit (ZT _max) of the p-type Bi_0.5Sb_1.5Te₃ alloys from 0.88 for the SiC-free sample to 0.97 at 323 K, though no improvement in TE performance was obtained in the case of n-type Bi₂Te_2.7Se_0.3 alloys. Importantly, the SiC-dispersed alloys showed better mechanical properties, which can improve material machinability and device reliability.     

Influence of Nanoinclusions on Thermoelectric Properties of <Emphasis Type="Italic">n</Emphasis>-Type Bi<Subscript>2</Subscript>Te<Subscript>3</Subscript> Nanocomposites

n-Type Bi₂Te₃ nanocomposites with enhanced figure of merit, ZT, were fabricated by a simple, high-throughput method of mixing nanostructured Bi₂Te₃ particles obtained through melt spinning with micron-sized particles. Moderately high power factors were retained, while the thermal conductivity of the nanocomposites was found to decrease with increasing weight percent of nanoinclusions. The peak ZT values for all the nanocomposites were above 1.1, and the maximum shifted to higher temperature with increasing amount of nanoinclusions. A maximum ZT of 1.18 at 42°C was obtained for the 10 wt.% nanocomposite, which is a 43% increase over the bulk sample at the same temperature. This is the highest ZT reported for n-type Bi₂Te₃ binary material, and higher ZT values are expected if state-of-the-art Bi₂Te_3−x Se _x materials are used.