退火工艺对YIG多晶薄膜铁磁共振线宽的影响

主要研究了退火工艺对钇铁石榴石(YIG)薄膜铁磁共振线宽的影响。实验中微米级的YIG薄膜通过磁控溅射法在Gd3Ga5O12(GGG)(111)衬底上制备,并通过750~950 ℃常压常规退火及750~850 ℃真空快速退火两种方式对薄膜进行退火晶化处理。最终系统地研究了薄膜的微观晶体结构、磁性能和铁磁共振线宽性能。研究发现,经过800 ℃,10 min的真空快速热处理的YIG薄膜磁性能优异,其铁磁共振线宽为2 626.1 A/m@9.3 GHz,阻尼系数α=2.077×10-3,薄膜表面粗糙度为1.9 nm。     

退火条件对射频磁控溅射法制备YIG薄膜性能的影响

本文采用射频磁控溅射法在硅基片上沉积YIG薄膜,主要研究了退火条件对YIG薄膜性能的影响。研究结果表明在750oC退火4小时制备的薄膜性能最好,其饱和磁化强度可达到185.9emu/cm3,远大于YIG块材的Ms(139emu/cm3)。此外,其磁性与Fe2+相关。     

快速热处理中退火温度对Sol-gel法制备PZT铁电薄膜性能的影响

利用Sol-Gel法在Pt/TiO2/SiO2/Si基底上用快速热处理(Rapid Thermal Processing,RTP)退火工艺制备出了致密的PZT铁电薄膜,主要研究了在退火时间为500s时退火温度对薄膜的结晶结构、表面形貌和铁电性能的影响。通过X射线衍射仪(XRD)、扫描电子显微镜(SEM)和铁电测试仪对制备的薄膜进行了性能表征。研究结果表明,当退火温度为6000C时,PZT薄膜具有(111)择优取向,表面致密无裂纹,且具有较好的铁电性能(其饱和极化值约为30 C/cm2,剩余极化约为20 C/cm2,矫顽场约为150KV/cm)。在100KV/cm电场下,电流密度J在10-1A/cm2数量级,表明所制的PZT纳米薄膜质量较好,能承受较高的场强以达到饱和极化状态而不被击穿。     

氧气压强对Si基片上沉积YIG薄膜微观结构和磁性的影响

本文研究了氧气压强对用脉冲激光沉积技术(PLD)在Si(100)基片上制备的YIG薄膜性能的影响。采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、震动样品磁强计(VSM)、铁磁共振仪(FMR)等检测了薄膜微观性能及磁性。研究发现:(1)在0.3Pa和1Pa下制备的YIG薄膜中没有杂相,而在4Pa和16Pa的薄膜中出现了YIP相;(2)薄膜的晶粒尺寸随氧压增大而减小;(3)在1Pa下制备得到的薄膜共振线宽最小,为91Oe;(4)薄膜饱和磁化强度(Ms)随氧压的增加而降低,1Pa下得到的薄膜的Ms为138Oe,最接近理论值。     

(Bi3.7Dy0.3)(Ti2.8V0.2)O12铁电薄膜的制备及退火影响

铁电材料在铁电存储器等领域具有良好的应用前景,受到极大的关注,其中铋层状铁电薄膜因为其良好的铁电性,得到了广泛的研究.采用溶胶-凝胶法在Pt(111)/Ti/SiO2/Si(100)基底成功沉积出(Bi3.7Dy0.3)(Ti2.8V0.2)O12(BDTV)的A、B位同时掺杂的铁电薄膜,发现这种双掺能够显著改善薄膜的铁电性.研究了650～800℃不同退火温度下,BDTV铁电薄膜的铁电性能、晶体结构及表面形貌变化.通过SEM分析发现,温度为750℃时,薄膜的颗粒生长较好,薄膜的铁电性能最佳.     

掺ZBS玻璃低温烧结YIG铁氧体及其磁性能研究

采用普通陶瓷工艺,分别制备了不同ZnO-B2O3-SiO2(ZBS)玻璃掺量的Y3Fe5O12(YIG)和Y1.05Bi0.75Ca1.2Fe4.4V0.6O12(YBiCaVIG)铁氧体样品。分析了样品的物相组成、显微结构及磁性能。结果表明,ZBS玻璃能有效地降低YIG和YBiCaVIG陶瓷的烧结温度,当w(ZBS)=10%时,其烧结温度可分别降低到1 280℃和950℃,但XRD显示烧结体中分别出现少量SiO2和YFeO3(YIP)杂相,SEM显示样品的晶粒大小约2～4μm,气孔率偏高。添加ZBS玻璃后材料的饱和磁化强度4πMs下降,铁磁共振线宽ΔH增大,但由于烧结体晶粒较细,自旋波线宽ΔHk较大,可作为YIG大功率材料使用。     

退火对非晶态碲镉汞薄膜微结构和光敏性的影响

对射频磁控溅射生长的非晶态碲镉汞(a-MCT)薄膜在真空状态下进行退火,并通过X射线衍射(XRD)技术指出原生及低于125℃退火后的MCT薄膜均为非晶态.采用双体相关函数g(r)和电学测试系统研究了退火对a-MCT薄膜微结构和光敏性的影响.结果表明:经110℃,115℃和120℃退火后的a-MCT薄膜短程有序畴Rs由退火前的13.9 分别增大至17.9 、20.8 和26.2 ;光敏性则由原来的1.17,分别增加至退火后的2.01、2.67和4.25.     

Au/PZT/p-Si结构铁电存储二极管的制备及其性能

采用准分子脉冲激光沉积 (PL D)工艺 ,制备了 Au/ PZT/ p- Si结构铁电存储二极管 .在氧气氛 35 0℃低温沉积、原位 5 30℃快速退火工艺条件下 ,获得了多晶纯钙钛矿结构的 Pb (Zr0 .5 2 Ti0 .48) O3(PZT)铁电薄膜 . PZT薄膜的铁电性能测试显示较饱和的、不对称的电滞回线 ,其剩余极化和矫顽场分别为 13μC/ cm2和 48k V/ cm.从C- V和 I- V特性曲线观察到源于铁电极化的回滞现象 ,记忆窗口约 1.1V,+4 V偏压下电流密度为 3.9× 10 - 6 A/cm2 .     

沉积温度及热处理对AZO纳米叠层薄膜性能的影响

采用原子层沉积技术(ALD)在石英片和n型(100)Si上沉积高阻氧化锌铝(AZO)纳米叠层薄膜,通过扫描电镜(SEM)、原子力显微镜(AFM)和X射线衍射仪(XRD)和体积表面电阻率测试仪对薄膜的表面形貌、晶体结构及电学性能进行表征分析,分别研究了不同沉积温度及退火温度对薄膜结构及性质的影响。研究结果表明AZO薄膜存在最优的生长温度窗口为170～200℃,同时发现,经过退火处理的薄膜电阻率明显增大,且适当的退火有助于薄膜结构的优化,经过400℃下退火4 h后的薄膜电阻趋于稳定,可作为微通道板(MCP)打拿极高阻导电层材料。     

微波与光通信用单晶Bi:YIG性能表征

通过液相外延方法制备出单晶Bi和Gd取代YIG薄膜,并研究了其微波铁磁共振特性与红外磁光性能。测试结果表明,样品结晶质量较好,无多余物相,平均表面粗糙度0.4 nm,比饱和磁化强度值25 emu/g,饱和外磁场650 Oe左右。在0～20 GHz的频率范围内,铁磁共振线宽ΔH小于8 Oe,且频率与共振线宽呈线性关系。在红外1 550 nm波长下,饱和状态的比法拉第转角约为0.1 (°)/μm,两片叠加条件下可以实现±45°法拉第旋转。在1 550 nm左右透过率接近90%,吸收系数低于16 cm^-1。该材料在红外磁光器件、微波通信器件方面具有重要的应用价值。     

Definition of function of squares amount of angular part of film element

By means of exact conformal mapping method we have defined character of dependence of squares amounts of angular part of film element on angled part dimension. We propose relations, approximating obtained dependence. Calculation results and experimental researches of large-scale models are represented.     

Temperature dependence of index of refraction of polymericwaveguides

The temperature dependence of refractive index of polymer films was determined for a number of slab waveguides by a grating coupling method. This dependence was examined as a function of parameters such as molecular weight and glass transition temperature of the polymer. Temperature-induced changes in N_TE-N_TM , N being the effective index, were studied systematically for different slab waveguide compositions. It is shown that with proper device design and choice of polymeric materials, thermal effects can be reduced     

Application of model of mixture of probabilistic distributions for definition of the signals of radiophysical probing

The article describes a model representation of radar probing data in form of a mixture of background and target samples, which is the sum of two random variables with very different parameters. For model development we research the behavior of the central moments of the distribution mix without assuming the distribution law form. An example it is described the detection of the signal at the output of compression system of chirp ionosonde.     

部分偏振光的表示方法

随着光纤通信和光纤传感的快速发展,人们时光的偏振态提出了越来越高的要求.光是一种横波,其偏振态大致分为:完全偏振光、部分偏振光和自然光.文中介绍了完全偏振光的几种表示方法,给出了几种部分偏振光的描述方法.并阐述了它们之间的差异与联系.     

NTRUsign式计算量分析

介绍了NTRUsign签名算法的密钥生成过程,其在实现的过程中需要进行上百位的大数运算问题,这些数字远远超出了普通电脑存贮范围。而要进行大数运算,就得用数组存贮,进行模拟运算,这就大大增加了运算量。文中分析了这个算法实现过程中的运算量,分析结果说明NTRUsign的运算量过大,以致实际并非一个实用算法。     

浅析IP网服务质量(QoS)

解决IP网QoS问题是目前通信领域的研究热点之一.虽然研究已经取得了一定的进展,但人们对于IP 网QoS本身的含义及相关的问题还有着不同的理解.本文将从IP网QoS的定义入手讨论相关的一些问题以及解决IP网QoS问题所做的各种努力.     

Interpretation of responses of visual cells of limulus

Assuming that visual responses are due to the action of particles on the membrane of the visual cells, the stochastic variability of the response should be a function of the number of particles producing it. Quantitative predictions can be made with the aid of a model proposed in previous articles. It is found that responses produced in visual cells of Limulus by absorption of a single photon have the stochastic properties which would be expected if the response to one photon were brought about by 25 particles. It is concluded from this that the processes leading to visual responses produce multiplication of particles. The effects of temperature and of metabolic poisons suggest that these processes are of chemical nature.     

电子行业标准制修订项目计划管理信息化的实现

论述了推进电子行业标准制修订项目计划管理信息化的必要性.并提出了具体措施;详细介绍了电子行业标准制修订项目计划管理数据库的设计思路和实现方法.阐述了对后续工作的几点思考.     

影响镀镍层内应力的因素及排除方法

对影响镍镀层内应力的因素做了介绍和分析,提出了对收缩应力的一种解释,提供了排除这些因素影响的方法,指出重视镀液的管理是减少各种影响内应力因素的主要办法。     

Terminology of carcinogenesis in light of the current concepts of the mechanisms of action of chemical carcinogens

The approaches to prepare a uniform and unified scientific terminology of chemical carcinogenesis are presented. The main definitions proposed (carcinogen, initiation, promotion, mutagen, multistage carcinogenesis, anti-carcinogen, cocarcinogen, carcinogenic risk, etc.) are based on the current state of comprehending mechanisms of the action of chemical carcinogens.