烧成温度对铁尾矿墙体材料性能的影响

研究了以90.8%的某铁尾矿、4.2%的水泥、5%的黏土为原料生产的新型墙体材料试样的物理性能、结构特征、化学成分受烧成温度的影响；比较了900 ℃下烧成的新型墙体材料试样与目前市场上的墙体材料的体积密度、隔热性能、耐压强度等重要性能指标。研究表明，900 ℃下烧成的试样基本具备新型轻质隔热墙体材料的性能。     

气化炉渣对铁尾矿烧结墙体材料性能的影响

为了降低铁尾矿烧结墙体材料体积密度和提高保温隔热性能,在尾矿中添加部分气化炉渣,采用挤出成型方法制备了铁尾矿烧结墙体材料.结果表明,在950℃烧结时,添加20%气化炉渣可以制备出密度低于1.45g/cm3导热系数低于0. 23 W/(m·K)、抗压强度高于30 MPa的墙体材料,为利用尾矿制备具有节能、利废、保温、隔热、低密度的新型墙体材料提供了一条新的途径.     

利用BIF尾矿制备轻质墙体材料的试验研究

在综合分析BIF尾矿基本特性的基础上，以BIF尾矿为主要原料，选择不同的粘结剂制备轻质墙体材料。研究结果表明，最佳工艺参数为铁尾矿、无机粘结剂和碱液改性生物质粘结剂的质量比90∶5∶5、烧结温度1 200±10 ℃、烧结时间30min。在最佳条件下制备的产品，体积密度1.314 g/cm³、显气孔率30.98%、抗压强度达到MU7.5标准。     

铁尾矿基轻质高强陶粒的制备及应用研究

以铁尾矿为主要原料烧制轻质高强度陶瓷颗粒,研究铁尾矿含量、发泡剂添加量和烧成温度对陶粒性能的影响.结果表明,采用100％铁尾矿为原料,0.1％碳化硅(SiC)为发泡剂,在1150℃保温20 min,制得陶粒的堆积密度为0.99 t/m3,筒压强度为16.3 MPa,吸水率为4.25％.再以此陶粒作为骨料制备陶粒混凝土,...     

大比例掺用铁尾矿制备轻质保温墙体材料

以水泥为胶凝剂、黄石市灵乡铁矿尾矿为主要原料制备轻质保温墙体材料,研究了轻骨料膨胀珍珠岩、铁尾矿及其碱性激发剂掺量和水灰比对试件抗压强度、容重、导热系数的影响。结果表明：试验用碱性激发剂对铁尾矿的活性有显著的激发作用,从而可提高铁尾矿的掺用比例、减少水泥用量;当水泥、铁尾矿、激发剂、膨胀珍珠岩的质量比为1∶2.5∶0.25∶0.63,水灰比为0.8时,试件28 d的抗压强度＞5 MPa、容重＜900 kg/m3、导热系数<0.231 W/（m·k）,满足轻质保温墙体材料的性能要求。     

利用矿山废弃高塑性红黏土制备轻质陶粒的研究

生产上多取用农田黏土制备轻质陶粒，以红黏土为主要原料的技术还未见报道。某矿山在开采过程产生大量剥离红黏土，长期堆存无法利用。以该红黏土为主要原料，添加普通黏土、化合物L、石灰石、煤粉进行轻质陶粒制备试验，考察原料配比及焙烧制度对烧成陶粒性能的影响。结果表明，加入适量普通黏土、化合物L可有效降低陶粒烧制过程中的炸裂率，烧成陶粒强度、表观密度随普通黏土、化合物L、煤粉的添加量及焙烧温度的增加而降低，适量添加石灰石可增强烧成陶粒强度；以红黏土、普通黏土、化合物L、石灰石、煤粉质量比为85.5∶7.0∶3.5∶3.0∶1.0混合制得陶粒生球，在105 ℃下干燥4 h、450 ℃预热30 min、1 170 ℃焙烧12 min，可制得轻质陶粒。工业投笼试验所得成品陶粒的关键性能指标均达到GB/T 17431.1-2010中对500级陶粒的质量要求，说明该技术具有实际生产应用价值。研究成果突破了轻质陶粒对原料的严格限制，为矿山剥离高塑性红黏土的高附加值利用提供了新途径。     

稀土尾矿制备多孔陶瓷及其性能

以稀土尾矿为主要原料,高岭土尾矿为黏结剂,长石为助熔剂,外掺碳化硅为造孔剂,制备多孔陶瓷材料。研究碳化硅用量及烧结温度对多孔陶瓷气孔率、抗折强度、体积密度以及吸水率的影响,并对制品的表观形貌和物相组成进行分析。结果表明,碳化硅用量与烧结温度对多孔陶瓷性能有明显影响,随着碳化硅用量的增加和烧结温度的升高,多孔陶瓷的气孔孔径明显增大。在碳化硅用量为0.5%,烧结温度为1 140℃,保温时间为20 min的条件下,可制得性能优异的多孔陶瓷材料,此时制品气孔率为73.5%,抗折强度为1.72 MPa,体积密度为438 kg/m~3,吸水率为1.5%,气孔孔径介于2～4 mm,满足T/CECS 480-2017《发泡陶瓷保温板应用技术规程》性能要求。烧结后多孔陶瓷物相组成主要为石英、白榴石和莫来石。     

斑岩型铜尾矿制备连通孔陶瓷透水材料的试验研究

以斑岩型铜矿尾矿、高岭土、玻璃粉为主要原料,制备连通孔陶瓷透水材料。研究了骨料配比、结合料用量、成型压力和烧成制度对连通孔陶瓷透水材料抗折强度和透水系数的影响。当m(铜尾矿):m(高岭土):m(玻璃粉)为7:3:2、成型压力为1 MPa、烧成温度为1 150 ℃、保温时间为90 min时,工艺流程最佳。此时,连通孔陶瓷透水材料抗折强度为3.9 MPa,透水系数为2.7×10-2 cm/s,劈裂抗拉强度为3.7 MPa,耐磨性磨坑长度为25.2 mm,抗冻性为D50。      

钼尾矿制备陶瓷透水砖的研究

以钼尾矿为主要原料,配以适量高温黏结剂,采用模压成型法制备陶瓷透水砖。研究了钼尾矿含量、烧结温度、保温时间和成型压力对陶瓷透水砖性能的影响,结果表明:随着钼尾矿含量的增加陶瓷透水砖的抗折强度逐渐降低;而透水系数则先增加后降低,当钼尾矿用量为80%时达到最大。试验得到的最佳工艺条件为:钼尾矿用量80 %,烧成温度1 200 ℃,保温时间30 min,成型压力15 MPa,在此工艺条件下,制得透水砖的抗折强度为4.6 MPa;透水系数2.6×10~(-2) cm/s。研究成果为钼尾矿的综合利用提供了一条新途径。     

煤矸石陶粒滤料的制备及性能研究

以煤矸石为原料,分别采用破碎法和成球法制成滤料生料,经快升温或慢升温焙烧获得陶粒滤料.对所制备陶粒滤料的气孔率、气孔孔径和酸碱可溶率等指标进行了分析比较.结果表明:各种陶粒滤料制品均性能优良;制品的气孔率都随着焙烧温度的升高由小变大,又逐渐降低,成球法制品的气孔率普遍要高于破碎法;快烧制品的气孔孔径分布范围较窄,慢烧制品的气孔孔径分布范围则很宽,2种焙烧方式所得制品中孔径大于100μm的气孔都随着焙烧温度的升高而增加;制品的酸碱可溶率均随焙烧温度的升高而降低.实际生产时,可根据煤矸石特性、产品的性能要求、生产成本等确定煤矸石陶粒滤料的制备工艺.     

China rare earth market review

正November 1~10,2014Chinese rare earth market was still inactive.Demand for rare earth products was weak.Consumers took a wait-and-see attitude for lower price.As it was an off season for rare earth products,it was expected that prices of rare earth could continue turbulence at the bottom in short terms.Due to a sharp drop,demand for rare earth from downstream recovered.Affected by new energy vehicles,wind powder and energy-efficient appliances,production of rare earth permanent     

China rare earth market review

正August 1~10,2014 There was some good news in rare earth industry recently.Restructuring plans of rare earth groups led by Baotou IronSteel Group and Xiamen Tungsten Group respectively have been approved by MIIT.And rare earth storage policy,which had been expected for a very long time,has been launched officially.Pushed by the good news,rare earth price started to rebound since August 5.Price of didymium oxide and dysprosium oxide rose about 1% to 2%,averagely.About 10% of     

China rare earth market review

正July 1~10,2014Due to weak demand from downstream industry and slow transactions,rare earth market remained weak and price of rare earth products continued to decline.There was no sign of recovery in downstream market.The market of NdFeB magnetic materials and phosphor was depressed.Catalyst,     

New energy vehicle:an opportunity for rare earth magnets

<正>Extracted from Securities Guide 1.Popularity of new energy vehicles—an irresistible market trend1.1 Progress of new energy vehicles Chinese Premier Li Keqiang said recently on a visit to Xi'an BYD Autos that new energy vehicles,especially new energy bus,can lessen environment and noise pollution.He encouraged the use of new     

注浆加固技术在十三矿-685 m进风大巷中的应用

针对煤矿开采深度不断向深部延伸，掘进巷道受深部高应力的影响越来越大，巷道围岩整体稳定性差，矿山压力显现越剧烈现象，一般锚网喷加锚索支护无法从根本上控制巷道的变形。总结了平煤股份十三矿-685 m进风大巷注浆加固技术，依据对巷道掘进之后变形监测数据的采集，对巷道变形机理进行分析研究，并对注浆时段进行了合理选择，在对巷道的注浆工艺进行了充分论证的基础上，对巷道进行了注浆。注浆后效果表明:巷道滞后注浆时间段的选择非常重要，巷道在恰当的时间内进行注浆加固施工，能有效控制巷道的变形，巷道注浆后变形量明显减小，岩体的稳定性明显增强，减少了巷道日常维修工作，降低了矿井的生产成本，保障了矿井的安全生产。     

Brief news

正China Minmetals Rare Earth Construction of Jianghua Separation Plant is set to complete at the yearend Civil works of Jianghua Separation Plant have been finished and the company is installing and debugging equipments now.It is estimated that construction of Jianghua Separation Plant will be     

Brief news

正Total transactions of rare earth in Rare Earth Ex-change Center of Hunan South Rare and Precious Metal Exchange neared 40 billion yuan from January to October From the opening in January of this year to the end of October,the total transaction of rare earth products in Rare Earth Exchange Center of Hunan South Rare and Precious Metal Exchange neared40 billion yuan.There are 16 varieties including dysprosium oxide and terbium oxide traded on the exchange center,one of the largest trading platforms for rare earth oxides in China.     

Theoretical basis for optimal collector concentrations and pulp pH values during flotation of sulfide-free minerals

A hypothesis that associates optimal conditions of mineral flotation with a zero charge of their surface is put forward. This hypothesis serves as a basis for a methodology to obtain and verify quantitative physical-chemical models for a minimal necessary concentration of a collector during flotation of sulfide-free minerals. These models may be of use for upgrading engineering processes of flotation and as a job for the concentration plant automation systems. __________ Translated from Fiziko-Tekhnicheskie Problemy Razrabotki Poleznykh Iskopaemykh, No. 2, pp. 89–99, March–April, 2006.     

基于LPWAN技术的采煤沉陷区杆塔倾斜监测系统

随着地下采煤活动不断加大，越来越多的输电杆塔不可避免地被建设在煤矿沉陷区。目前，现有手段采用靠人力去进行定期检查一定会浪费大量的人力和物力，因而需开展对位于煤矿沉陷区的杆塔进行实时在线检测。基于NB-IoT和LoRa提出了一种新的算法——低功耗广域网（LPWAN）技术，提出了一种新型的输电杆塔倾斜监测系统，其中包含1个主节点和多个子节点，以适应地域广和远距离的需求信息监控。该系统通过LoRa多节点网络的数据传输，将杆塔的倾斜参数通过NB-IoT上传至在线实时监控系统。管理人员可以从后台得出监测数据并分析结果，及时对处于煤矿沉陷区的有故障的输电杆塔进行针对性的维护。     

基于AutoCAD的复杂曲线绘制的实现

介绍了如何利用其他软件在AutoCAD中精确绘制各种不同规划曲线的技巧 ,很好地解决了在AutoCAD中绘制多义线方法形成复杂曲线的误差问题 ,取得了较好的效果 ,具有实际意义。