CaO-La2O3-B2O3-Eu2O3转光玻璃的合成及荧光性质

X射线衍射研究表明CaO-La2O3-B2O3-Eu2O3体系的玻璃化温度在1025℃附近。荧光光谱和ESR谱研究表明,在CaO-La2O3-B2O3-Eu2O3玻璃体系中存在着Eu2 和Eu3 两种价态离子。316,360,379,394,413,462和532nm锐线激发峰和592,616和650红区发射峰分别对应Eu3 的f-f激发跃迁和5D0-7FJ(J=1,2,3)跃迁发射;351nm和427nm宽带激发峰和蓝区发射分别对应Eu2 的5d-4f激发跃迁和发射。     

CaO-SiO2-B2O3:Eu3+玻璃的合成及发光性质研究

用常规的高温合成法合成了CaO-SiO2-B2OaEu2O3玻璃,探讨了玻璃的最佳合成温度、玻璃的网络结构并研究了其发光性质.在CaO-SiO2-B2O3;Eu2O3玻璃体系中观察到了Eu3+的发射光谱.样品的发射光谱有三个主要荧光发射峰,位于591nm左右的发射峰对应于Eu3+的5D0-7F1跃迁发射,位于618nm左右的发射峰对应Eu3+的5D0-7F2跃迁发射,位于650nm左右的发射峰对应于Eu3+的5D0-7F3.研究了掺杂Eu3+浓度对其发光强度的影响.并研究了Eu3+的发光强度与玻璃厚度的关系,玻璃的最佳厚度在2.0mm左右.光谱性质表明,这种玻璃体系能够把太阳光中的紫外光转换成红光,从而增强红光的发射强度.我们可以利用这些玻璃的发光性质来制备农用转光玻璃.     

CaO-SiO_2-B_2O_3∶Eu~(3+)、Bi~(3+)玻璃中的敏化发光及其敏化机理的研究

分别研究单掺Eu3+和Bi3+以及共掺Eu3+、Bi3+的CaO-SiO2-B2O3玻璃的发光性质。单掺Eu3+的CaO-SiO2-B2O3玻璃的发射光谱中位于591nm左右的发射峰对应于Eu3+的5D0—7F1跃迁发射,为磁偶极跃迁;位于618nm左右的发射峰对应Eu3+的5D0—7F2跃迁发射,为电偶极跃迁;位于650nm左右的发射峰分别对应于Eu3+的5D0—7F3。当共掺Bi3+、Eu3+时发现少量的Bi3+对Eu3+有明显的敏化作用。研究了Bi3+的最佳浓度和敏化机理,当Bi3+浓度为0.010%(摩尔分数)时Eu3+发光强度最大。Bi3+→Eu3+的能量传递是以光的再吸收能量传递为主。     

Eu3+激活的Li2Gd4（MoO4）7钼酸盐红色荧光体及其发光性质

由高温固相反应首次合成Li2(Gd1-xEux)4(MoO4)7(0相似文献   

白光LED用LaPO4:Eu3+红色荧光粉的合成与表征

利用水热法制备了性能稳定的红色荧光粉LaPO4:Eu3+,同时研究了不同的Eu3+浓度、煅烧温度对荧光粉发光性能的影响.通过X射线粉末衍射(XRD)和扫描电子显微镜(SEM)来表征荧光粉的晶体结构和颗粒大小及形貌;用激发光谱和发射光谱以及荧光衰减曲线来表征荧光粉的荧光性能.结果表明:未煅烧时前躯体主要是六方晶相LaPO4·0.5H2O,煅烧温度在900℃时,所制备样品为单斜相LaPO4:Eu3+;SEM图像显示5 at.%Eu3+掺杂LaPO4呈椭球形,颗粒长约为500 nm,宽约为300 nm.最大发射波长和激发波长分别为592 nm和393 nm,发射光谱中592 nm和612 nm的发射峰对应的是Eu3+离子的5D0→7F1和5D0→7F2跃迁.其荧光寿命为3.32 ms.     

CaO-SiO2-B2O3玻璃中Sm3+的发光性质

用常规的高温合成法合成了CaO-SiO2-B2O3-Sm2O3玻璃,探讨了玻璃的最佳合成温度、玻璃的吸收光谱并研究了其发光性质.在CaO-SiO2-B2O3-Sm2O3玻璃体系中观察到了Sm3+的发射光谱.样品的发射光谱有三个主要荧光发射峰, 峰值波长分别为568nm、605nm、650nm, 其中最强峰为605nm, 这些荧光峰均为线状峰,可见发射起源于Sm3+ 4f电子的f-f跃迁.其中568nm对应于4G5/2→6H5/2跃迁、605nm对应于4G5/2→6H7/2跃迁、650nm对应于4G5/2→6H9/2跃迁,光谱性质表明这种玻璃体系能够把太阳光中的紫外光转换成红光,从而增强红光的发射强度.可以利用这些玻璃的发光性质来制备农用转光玻璃.     

细颗粒红色荧光粉Y2O3:Eu3+的结构和光谱性质研究

对草酸作为沉淀剂制备的细颗粒红色荧光粉Y2O3Eu3+进行结构和光谱性质研究,结果表明其一次粒径为20nm～30nm,团聚尺寸D50=0.53μm, 粉体细且分布均匀.该荧光粉最大激发峰位于252.2nm,最大发射峰位于612nm,荧光粉色品座标x=0.6479,y=0.3442,符合荧光粉要求.     

Eu2+、Er3+共掺杂Sr3MgSi3O10高亮度蓝色荧光粉的制备及性质研究

采用凝胶-燃烧法在活性炭弱还原气氛下成功合成了高亮度蓝色发光材料Sr3 MgSi3 O10:Eu2+,Er3+.用X射线粉末衍射仪、荧光分光光度计对样品的物相结构和发光性质进行了分析和表征.结果表明,所合成的Sr3 MgSi3O10:Eu2+,Er3+的晶体结构与Sr2 MgSi2 O7的相似,属四方晶系.样品激发光谱是位于250 nm～450 nm的宽带,最大激发峰位于357 nm处;发射光谱也是一宽带,最强的发射峰位于466 nm处,属于Eu2+典型的4f65d1→4f7跃迁,呈蓝光发射.根据光谱测定结果和Van Uitert经验公式,推断Eu2+进入Sr3 MgSi3 O10基质后占据八配位Sr的格位.研究发现,共掺杂Er3+能有效敏化Sr3 MgSi3 O10基质中Eu2+的发光,当Er3+的掺杂摩尔分数为0.04时,样品发光强度最大,约为单掺Eu2+样品发光强度的3.3倍.     

红色Sr1-2xNaxWO4∶Eux3+荧光体的制备与发光性能

采用传统高温固相法,以钨酸锶为基质材料,掺杂稀土Eu3+制备了可被紫色光有效激发的红色荧光粉Sr1-2xNaxWO4∶Eu3x+。通过测定与分析样品Sr1-2xNaxWO4∶Eu3x+的激发和发射光谱,发现激发光谱在395nm处吸收值最大,发射光谱的发射主峰位于613nm处,属于Eu3+的5D0→7F2特征跃迁。不同的Eu3+掺杂浓度下样品发光强度不同,当x=0.07时发光强度最佳。电荷补偿剂Na+对样品发光强度的影响很大,主要原因是Na+的加入会影响基质的晶体结构,当Na+的含量与Eu3+含量相同时样品发光强度最好,Na+含量增加到一定程度后基质结晶不完善,荧光体的发光强度急剧下降。     

红色荧光粉La2O3：Eu3＋的合成及发光性质

利用复合沉淀法制备了性能稳定的红色荧光粉La2O3：Eu3＋,同时研究了煅烧温度及掺杂Eu3＋浓度对La2O3：Eu。’发光性能的影响．通过X射线粉末衍射（XRD）和扫描电子显微镜（SEM）来表征荧光粉的晶体结构和颗粒大小及形貌：用激发光谱和发射光谱以及荧光衰减曲线来袁征荧光粉的荧光性能．结果表明：煅烧温度在900℃时,所制备样品为六方晶系La2O3：Eun;SEM图显示掺杂Eu0＋含量为5％的La2O3颗粒直径为15μm左右．最大发射波长和激发波长分别为626nm和396nm,发射光谱中596nm和626nm的发射峰对应的是Eu3＋离子的0D—F1和5D—F2跃迁,其荧光寿命为0．754ms．     

Al2O3La2O3Y2O3/Cu复合材料的电弧侵蚀特性研究

采用喷射沉积和内氧化法制备出Al₂O₃La₂O₃Y₂O₃/Cu复合材料,研究该材料在直流20 V/20 A的工作条件下触点的电弧侵蚀特性,并与Al₂O₃/Cu材料进行了对比分析.利用电子天平、扫描电镜等方法分析电弧侵蚀后触点的质量变化和表面微观结构.结果表明,通过添加Y₂O₃、La₂O₃稀土氧化物颗粒,可有效降低触头材料的材料转移量.Al₂O₃La₂O₃Y₂O₃/Cu材料的抗熔焊性和抗烧损性优于Al₂O₃/Cu材料的性能.在直流阻性负载条件下Al₂O₃La₂O₃Y₂O₃/Cu阳极触头表面形成凹坑,阴极触头表面形成凸起,触点表面显示出浆糊状凝固物和喷发坑等电弧侵蚀形貌特征.      

CaO含量对CaF2-Al2O3-CaO-Ce2O3渣系中Ce2O3行为的影响

在Fe-Cr-Al合金中添加微量的稀土元素可显著改善合金的使用性能, 文中以电渣重熔生产Fe-Cr-Al合金所用稀土渣为研究对象, 根据离子-分子共存理论(IMCT)建立了1 823 K时CaF₂-Al₂O₃-CaO-Ce₂O₃四元渣系热力学质量作用浓度模型.结果表明:当渣系中CaO和Al₂O₃的质量百分数之比维持在1:1, 即w_CaO /w_Al2O3=1时, 随着Ce₂O₃含量增加, 渣中铈铝酸盐Ce₂O₃·Al₂O₃质量作用浓度(活度)显著增加, 但炉渣物相种类没有变化.渣系中Ce₂O₃含量分别在10 %, 20 %, 30 %, 40 %时, w_CaO /w_Al2O3值对组元活度的影响各不相同但有共同特征, 表现在处于约1.0~1.8时, CaO活度增加最迅速, Ce₂O₃活度增加, Ce₂O₃·Al₂O₃活度下降, 说明渣中CaO含量增加促进了Ce₂O₃·Al₂O₃分解而导致Ce₂O₃活度增加, 选取渣系进行熔融和X射线衍射实验, 用jade 5.0软件分析物相, 实验结果与计算一致.      

La2O3对ZrO2-Y2O3-Ta2O5陶瓷材料结构及性能的影响

采用固相合成法在氧化钇部分稳定氧化锆(YSZ)陶瓷材料的基础上引入氧化物Ta2O5以及稀土氧化物La2O3取代部分Y2O3,获得一种新型的La2O3-ZrO2-Y2O3-Ta2O5陶瓷材料。分别利用X射线衍射仪、扫描电子显微镜和STA-449C热膨胀仪对材料的物相组成、微观结构及热膨胀性能进行表征。结果表明,陶瓷材料的主晶相仍为四方相,晶粒尺寸减小,在RT～1200℃温度范围内热膨胀系数有所减小。     

Al2O3-V2O5体系的热力学优化

在对Al₂O₃-V₂O₅体系相图、热力学数据以及晶体结构数据进行综述与评估的基础上，采用相图计算方法对Al₂O₃-V₂O₅体系进行热力学优化.液相采用修正的似化学模型进行描述，利用对近似处理液相中存在的短程有序.将液相模型的最大短程有序设置在AlVO₄处，将VO₄3-当作液相中V₂O₅的基本组成单元.体系中AlVO₄相看作线性化合物.计算结果很好的重现了选定的实验数据，获得了一套合理、可靠、自洽的模型参数用来描述体系中各相的热力学性质，为Al₂O₃负载V₂O₅型催化剂催化性能的提高打下坚实的基础.      

Solubility of carbon in CaO-B2O3 and BaO-B2O3 slags

The solubility of carbon in molten CaO-B₂O₃ and BaO-B₂O₃ slags at high temperatures was measured to understand the dissolution mechanism of carbon into the slags. The B₂O₃-bearing slags, which have a wide range of liquids, at the temperature of interest have been applied to investigate the effect of basicity on the solubility of carbon from the saturation of acidic or basic components. The solubility of carbon, as a function of the composition of slags, shows a minimum value, and it is suggested that carbon dissolves by different mechanisms in the acidic and basic slags, respectively. From the infrared spectra measurements, the wave number indicating the B-C bond was found to be about 1150 cm⁻¹ in the acidic region of slags; hence, the incorporation of carbon into the borate network was confirmed qualitatively. The carbide capacity was compared to the nitride capacity, showing that the dissolutions of carbon and nitrogen into the slags are similar.     

Research on Y2O3：Eu Phosphor Coated with In2O3

Y2O3：Eu red phosphor for FED application was prepared by high temperature solid-state reaction. The In2O3 coating by precipitation method to the phosphor was applied and the analyses of XRD, Zeta potential, SEM, EDS and low voltage cathodoluminescence （CL） were conducted for investigating the coating effect. The results showed that In2O3 coating promoted the low voltage CL of the phosphor efficiently. The promotion was possibly due to the enhancement of the surface conductivity of the phosphor grains.     

Spectral properties and energy transfer of Tm^3＋/Ho^3＋-codoped Ga2O3-Bi2O3-GeO2-PbO glasses

The 2.0 μm emission originating from Ho^3＋：^5I7→^5I8 were investigated upon excitation with 808 nm laser diode （LD） transition in Ho^3＋/Tm^3＋-codoped gallate-bismuth-germanium-lead glasses Energy transfer （ET） process between Tm^3＋： ^3F4 level and Ho^3＋： ^5I7 level was also discussed. It was noted that the measured peak wavelength and stimulated emission cross-section of Ho^3＋-doped bismuth-germanium-lead glasses were -2.02 μm and 5.1×10^-21 cm^2, respectively. Intense emission of Ho^3＋ in Tm^3＋/Ho^3＋-codoped GBPG glass were observed, which resulted from the ET between Tm^3＋： ^3F4 and Ho^3＋： ^5I7 level upon excitation with 808 nm LD.     

CaO--TiO2--Fe2O3三元系中Ca3TiFe2O8的生成机理

钒钛磁铁矿是烧结矿重要的原料之一,Ca₃TiFe₂O₈作为钒钛烧结矿中矿物被发现之后,其生成机理尚不明确.本文采用X射线衍射分析、元素能谱分析和TG-DSC分析相结合的方法,研究了Ca₃TiFe₂O₈的生成机理以及不同温度、CaO与TiO₂含量下Ca₃TiFe₂O₈的生成规律.实验结果表明,Ca₃TiFe₂O₈由Ca₂ Fe₂O₅和CaTiO₃反应生成,即CaO和Fe₂O₃反应生成Ca₂ Fe₂O₅;其后,与CaTiO₃反应生成Ca₃TiFe₂O₈.反应时间越长,Ca₃TiFe₂O₈的生成量越大,但反应温度对Ca₃TiFe₂O₈生成的影响并不明显.另外,还发现CaO含量越高,Ca₃TiFe₂O₈越易于生成,而且等摩尔Fe₂O₃和CaO下只要存在TiO₂,就会有Ca₃TiFe₂O₈生成.      

Synthesis of Al2O3/TiCN-0.2%Y2O3 Composite by Hot Pressing

Al2O3/TiCN composites were synthesized by hot pressing.The influences of components and HP temperature on mechanical properties,such as bending strength,breaking tenacity and Vickers hardness were investigated.The results showed that the mechanical properties of Al2O3/TiCN composite increased with temperature when hot pressing temperature is below 1650 ℃.The mechanical properties reached their maximums when the composites were sintered at 1650 ℃ for 30 min under hot pressing pressure of 35 MPa,the value of bending strength,breaking tenacity and Vickers hardness was 1015 MPa,6.89 MPa·m1/2,and 20.82 MPa,respectively.When hot pressing temperature was above 1650 ℃,density decreased because of decomposition with increased temperature,and mechanical properties dropped because of rapid growth of grains in size at high temperature.Microstructure analysis showed that the addition of Y2O3 led to the formation of YAG phase so as to inhibit the growth of crystals.This helped to improve breaking tenacity of the composites.TiCN particles with diameters of 1 μm dispersed at Al2O3 grain boundaries,inhibited grain growth and enhanced mechanical properties of the composites.SEM study of the propagation of indentation cracks showed that the bridge linking behavior between matrix and strengthening phase might lead to the formation of the coexisted field of crack deflection,branching and bridge linking.The mechanism of this phenomenon was that the addition of Y2O3 improved the dispersion of TiCN particles so as to enhance the tenacity of the composites.The breaking tenacity was changed from 5.94 to 6.89 MPa·m1/2.     

高铁赤泥制备CaO-SiO2-Fe2O3-Al2O3系微晶玻璃

以高铁赤泥、SiO₂等成分为原料，通过熔融-热处理法制备CaO-SiO₂-Fe₂O₃-Al₂O₃体系的赤泥基微晶玻璃.表征母玻璃和热处理后的微晶玻璃的物相组成、微观形貌，计算结晶度以及测试抗弯强度性能等.通过Rietveld全谱拟合方法对各组微晶玻璃的结晶度进行计算，对比分析发现，热处理后微晶玻璃的结晶度增加，随着SiO₂的添加会使得微晶玻璃的结晶度降低.对微晶玻璃进行抗弯强度测试，抗弯强度随着SiO₂/赤泥的增加而增大.