辽特试制成功430FR易切削铁素体超低碳不锈钢

日前，辽宁特钢集团成功试制出超低碳易切削铁素体不锈钢—430FR。     

超低碳铁素体不锈钢EB26-1管材工艺浅析

通过对EB26-1超低碳铁素体不锈钢无缝管的生产加工工艺探讨，分析出超低碳铁素体不锈钢在生产中需考虑的如脱碳、475℃脆性、晶粒长大倾向、酸洗等问题，并提出了解决问题的方法和措施。     

K-OBM-S冶炼超纯铁素体不锈钢控氮工艺研究

对K-OBM-S转炉冶炼超纯铁素体不锈钢w(N)的变化规律进行分析,找出了K-OBM-S控氮的关键控制点。结果表明,转炉出钢增氮对炉后w(N)的控制影响大,通过控制钢水w(Si)、扩大出钢控内径、加强出钢口维护等措施,可有效减少出钢增氮量,降低炉后w(N)。     

VOD冶炼超纯铁素体不锈钢脱碳脱氮

要利用VOD冶炼超纯铁素体不锈钢脱碳脱氮模型,研究了在吹氧脱碳阶段氧气利用率以及脱氮能力与初始碳含量的关系,分析了自由脱碳阶段的VOD脱碳和脱氮能力,并讨论了停氧后碳含量对脱碳以及温度控制的影响.研究结果为VOD冶炼超纯铁素体不锈钢合理脱碳脱氮提供技术指导.     

VOD冶炼超纯铁素体不锈钢的脱氮研究

分析了VOD冶炼超纯铁素体不锈钢过程的脱氮热力学和动力学,得出其脱氮反应接近二级反应,可用Δ(1/w[N])来表示脱氮效果。用前期开发的脱氮模型计算并分析了VOD的脱氮过程,在VOD吹氧脱碳阶段,脱氮效果Δ(1/w[N])与脱碳量Δw[C]成正比,可用脱氮指数Δ(1/w[N])/Δw[C]来表征此阶段的脱氮能力,铬含量为11.6%、17.6%及20.5%的钢液脱氮指数计算值分别为208%-2、109%-2及81%-2,实际生产数据分析得出的对应的脱氮指数略高于计算值,而在VOD自由脱碳阶段,Δ(1/w[N])随时间变化的计算曲线基本不受初始氮含量的影响,温度是影响脱氮的主要因素。     

430铁素体不锈钢脱氮工艺

430铁素体不锈钢中的氮能恶化晶间腐蚀、低温冲击韧性、缺口敏感性以及焊接等性能。在热力学分析的基础上,研究了430铁素体不锈钢冶炼过程中初始碳质量分数、温度、氩氧比以及冶炼时间等工艺参数与对终点氮质量分数的影响。研究表明,在一定范围内,初始碳质量分数越高,氩氧比越大,脱氮效果越好;吹氩20min左右时脱氮效果最好,脱氮率可达到60%左右,继续延长冶炼时间会有回氮现象发生。     

汽车排气系统用铁素体不锈钢的应用及腐蚀失效评价

最近几年,随着对全球环境问题的关注,汽车燃油的经济性和汽车尾气排放的等级化要求不断提高,铁素体不锈钢更多用于汽车排气系统零部件。铁素体不锈钢性能得到了明显改善,使铁素体不锈钢具有低的价格和良好性能,欧美及日本汽车几乎全部使用超纯铁素体不锈钢用于排气系统零部件制造。介绍了汽车排气系统的构成及对各部件常用不锈钢的性能要求、排气系统零部件的主要失效形式和所用不锈钢材料的腐蚀评价方法。     

铌与钛对铁素体不锈钢析出和成形性的影响

研究了铌、钛对铁素体不锈钢析出相、织构和成形性的影响。结果显示:添加铌、钛后的析出相主要是TiN和(Nb,Ti)C,其析出尺寸分别为4μm和200 nm;同时,铌、钛的添加抑制了冷轧薄板α纤维织构的生长,促进了γ纤维织构强度的增加。添加稳定化元素铌、钛后,冷轧薄板的平均r值由1.05增加到1.46,起皱高度也由29.1μm下降到18.9μm,薄板成形性能的改善同再结晶织构的变化密切相关。     

提高铁素体不锈钢质量的主要措施

介绍了易于在铁素体不锈钢中出现的主要缺陷,包括室温敏感性高和起皱。总结了改善铁素体不锈钢质量的主要措施。     

热处理工艺对12%Cr铁素体不锈钢组织性能的影响

以12%Cr铁素体不锈钢为研究对象,研究了不同退火方式、退火工艺对12%Cr铁素体不锈钢热轧板和冷轧板组织、力学性能、耐腐蚀性能、成形性能的影响。结果显示,12%Cr铁素体不锈钢高温下存在铁素体—奥氏体相变过程,在双相区退火快冷后有马氏体组织生成。通过在热退过程中引入奥氏体相变和马氏体相变,可以显著细化最终产品晶粒,提高最终冷轧产品的强度、硬度,同时保持材料耐腐蚀性能不变。该工艺生产的产品可以适用于高强度的应用场合,打破了传统12%Cr铁素体不锈钢热轧后只能采用罩式炉退火的束缚,针对产品的最终用途可以采用不同的退火方式和退火工艺进行生产。     

Inclusions for Ultra-pure Ferritic Stainless Steels Containing 21% Chromium

As stabilizing elements added into ultra-pure ferritic stainless steels, niobium and titanium react with carbon and nitrogen to form carbonitrides and have great effects on the ratio of equiaxed zone and the grain size of solidification structure of ingots, which remarkably affect the quality of cold-rolled sheets. Combined with thermodynamic calculation, style and precipitation progress of inclusions in ultra-pure ferritic stainless steels were investigated by optical microscopy, scanning electron microscopy, transmission electron microscopy and energy dispersive spectroscopy. The results indicate that the inclusions are mainly Ti-Al-N-O system inclusions in ultra-pure ferritic stainless steels. Al₂O₃ starts to precipitate firstly and then TiO_x and TiN precipitates sequently. The inclusions are mainly single TiN particles and complex inclusions with Al₂O₃-Ti₂O₃ as cores and covered with TiN under the condition of 0.31% titanium addition and mainly Al₂O₃ under the condition of 0.01% titanium addition. A few (Nb, Ti) N particles precipitate because of no enough titanium to react with nitrogen when titanium addition is 0.01%. In addition, fine Nb(C, N) particles with size of less than 500 nm precipitate at relatively low temperature.     

建筑用高耐蚀性铁素体不锈钢B445R的研制

宝钢研制出了建筑屋顶装饰用铁素体不锈钢B445R毛面产品。该产品的耐蚀性比奥氏体不锈钢SUS316L更优越,成本也比SUS316L低,采用常规的成形方法就可以将其加工成屋顶面板。此外,由于该产品的热膨胀系数比SUS316L小,故其热变形也比SUS316L小,同时由于进行了毛化处理,其表面具有较低的光反射能力。所有这些优点使其有能力成为沿海地区建筑物的屋顶装饰材料。     

铁素体不锈钢铸轧薄带凝固组织对冷轧退火带晶粒簇的影响

 研究了Cr17铁素体不锈钢铸轧薄带凝固组织对其冷轧退火带晶粒簇、成形性和皱折特性的影响。利用电子背散射衍射技术对Cr17铁素体不锈钢铸轧薄带及相应的冷轧退火带进行了显微织构分析。结果表明：①Cr17铁素体不锈钢铸轧薄带冷轧退火带的晶粒簇依赖于初始铸轧薄带的凝固组织类型;②柱状晶组织的铸轧薄带具有显著的{001}∥ND晶体取向特征,而等轴晶组织的铸轧薄带晶体取向随机、分散;③等轴晶组织铸轧薄带比柱状晶组织铸轧薄带的冷轧退火带具有更少的{001}<110>晶粒簇和更多的{111}<112>、{111}<110>晶粒簇;④铸轧薄带的等轴晶组织比柱状晶组织有利于提高冷轧退火带的成形和抗皱性能。     

异步轧制对SUS430铁素体不锈钢织构和深冲性能的影响

利用X射线衍射技术和金相显微镜观察等手段,研究异步轧制工艺对SUS430铁素体不锈钢组织织构与深冲性能的影响。结果表明:异步轧制技术可以适当细化再结晶晶粒,但是晶粒大小、分布不均匀。织构分析表明,采用异步一次冷轧工艺沿着板厚方向可获得均匀、完整的γ纤维织构,但强度相对较弱,而应用异步二次冷轧,经过两次退火工艺,再结晶织构弱化,获得接近随机的取向织构。综合分析表明,异步一次轧制有利于提高材料的深冲性能。     

439铁素体不锈钢的研制

439是在430不锈钢基础上降低C＋N含量，添加Nb、Ti等稳定化元素发展起来的新型不锈钢材料，已逐步代替304不锈钢应用于电梯面板等行业。为开发满足用户使用要求的439不锈钢，试验室研究了成分、热处理制度对439不锈钢性能的影响，结果表明：Ti、Nb稳定化元素的添加对改善439不锈钢综合性能比较有利、热轧439退火再冷轧可明显改进深冲性能。生产试制结果表明，宝钢生产的439冷轧产品完全能满足用户对材料的性能要求。     

初始凝固组织对Cr17铁素体不锈钢组织、织构及成形性的影响

 研究了初始凝固组织对Cr17铁素体不锈钢组织、织构、成形性的影响。分别对柱状晶、等轴晶铸坯进行热轧、退火、冷轧、退火实验。结果表明,等轴晶铸坯热轧试样在退火过程中的再结晶率高于柱状晶铸坯热轧试样。再经相同的冷轧退火工艺后,与柱状晶铸坯冷轧退火试样相比,等轴晶铸坯冷轧退火试样的{001}∥ND织构较弱,{111}∥ND γ织构较强,而且rm值较高。