Effect of Aspect Ratio on Field Emission Properties of ZnO Nanorod Arrays

ZnO nanorod arrays are prepared on a silicon wafer through a multi-step hydrothermal process. The aspect ratios and densities of the ZnO nanorod arrays are controlled by adjusting the reaction times and concentrations of solution. The investigation of field emission properties of ZnO nanorod arrays revealed a strong dependency on the aspect ratio and their density. The aspect ratio and spacing of ZnO nanorod arrays are 39 and 167 nm (sample C), respectively, to exhibit the best field emission properties. The turn-on field and threshold field of the nanorod arrays are 3.83 V/μm and 5.65 V/μm, respectively. Importantly, the sample C shows a highest enhancement of factor β, which is 2612. The result shows that an optimum density and aspect ratio of ZnO nanorod arrays have high efficiency of field emission.     

Improved field emission properties of carbon nanotubes decorated with Ta layer

The field emission (FE) properties of vertically aligned carbon nanotube (CNT) arrays having a surface decorated with Ta layer were investigated. The CNTs with 6 nm thickness of Ta decoration showed improved FE properties with a low turn-on field of 0.64 V/μm at 10 μA/cm², a threshold field of 1.06 V/μm at 1 mA/cm² and a maximum current density of 7.61 mA/cm² at 1.6 V/μm. After Ta decoration, the increased emission centres and/or defect sites on the surface of CNTs improved the field enhancement factor. The work function of CNTs with Ta decoration measured with ultraviolet photoelectron spectroscopy decreased from 4.74 to 4.15 eV with increasing Ta thickness of 0–6 nm. The decreased work function and increased field enhancement factor were responsible for the improved FE properties of the vertically aligned CNTs. Moreover, a significant hysteresis in the cycle-testing of the current density with rising and falling electric field process was observed and attributed to the adsorption/desorption effect, as confirmed by the photoelectron spectrum.     

Highly efficient field emission from aligned ZnO/TiN core-shell nanorods

Novel polycrystalline TiN coated ZnO core-shell heterostructure nanorods have been prepared on carbon paper substrate via a low-temperature hydrothermal and sputtering process. The core-shell emitters exhibit a highly efficient field-emission performance with a low threshold of electric field ∼0.72 V/μm, and a high emission current density ~16.41 mA/cm², a level that is the highest of ZnO emitters reported to date. The improved field-emission characteristics may be attributed to the unique materials combination of ZnO core and TiN shell, resulting in the conductivity enhancement, emission sites increase, and the work function reduction. Our results demonstrate that ZnO/TiN core-shell emitter will be a distinguished candidate for electronic source devices.     

Field Emission Properties and Fabrication of CdS Nanotube Arrays

A large area arrays (ca. 40 cm²) of CdS nanotube on silicon wafer are successfully fabricated by the method of layer-by-layer deposition cycle. The wall thicknesses of CdS nanotubes are tuned by controlling the times of layer-by-layer deposition cycle. The field emission (FE) properties of CdS nanotube arrays are investigated for the first time. The arrays of CdS nanotube with thin wall exhibit better FE properties, a lower turn-on field, and a higher field enhancement factor than that of the arrays of CdS nanotube with thick wall, for which the ratio of length to the wall thickness of the CdS nanotubes have played an important role. With increasing the wall thickness of CdS nanotube, the enhancement factor β decreases and the values of turn-on field and threshold field increase.     

Morphology-dependent field emission properties and wetting behavior of ZnO nanowire arrays

The fabrication of three kinds of ZnO nanowire arrays with different structural parameters over Au-coated silicon (100) by facile thermal evaporation of ZnS precursor is reported, and the growth mechanism are proposed based on structural analysis. Field emission (FE) properties and wetting behavior were revealed to be strongly morphology dependent. The nanowire arrays in small diameter and high aspect ratio exhibited the best FE performance showing a low turn-on field (4.1 V/μm) and a high field-enhancement factor (1745.8). The result also confirmed that keeping large air within the films was an effective way to obtain super water-repellent properties. This study indicates that the preparation of ZnO nanowire arrays in an optimum structural model is crucial to FE efficiency and wetting behavior.     

Synergistic effect of Fe and Ag co-doping on the persistent photoconductivity of vertical ZnO nanorods

Undoped, doped and co-doped vertically aligned ZnO nanorods (NRs) are synthesized using sonicated sol-gel immersion method. A significant variation in structural, morphological, optical and photoconductivity properties of ZnO NRs after incorporation of transition metal ions (Fe or/and Ag) is obtained. XRD analysis revealed that incorporation of Fe ameliorates while that of Ag deteriorates the c-axis growth of NRs. The diameter of the NRs is tuned from 236 nm to 103 nm. The Fe-doped ZnO NRs exhibit significantly thinner diameter, longer length, and highest aspect ratio. The doping and co-doping reduces the optical band gap of ZnO by 20 meV and 10 meV respectively. A reduction in near band edge emission whereas enhancement in defect-related-green-emission is obtained. Noticeable enhancement in the light harvesting efficiency and significant quenching of the persistent photoconductivity is obtained by co-doping.     

Synthesis and enhanced gas sensing properties of flower-like ZnO/α-Fe2O3 core-shell nanorods

This paper reports a facile two-step synthesis route for the preparation of flower-like ZnO/α-Fe₂O₃ nanorods (NRs). Flower-like ZnO NRs with the average diameter about 810 nm and length about 4.5 µm were firstly synthesized via a chemical solution method, and then ZnO NRs was coated with a continuous α-Fe₂O₃ layer to form ZnO/α-Fe₂O₃ core-shell structure through an ionic-layer adsorption and reaction method. The gas-sensing results show that the ZnO/α-Fe₂O₃ NRs exhibit excellent sensitivity, selectivity, and response-recovery capacity to ethanol vapor at a low optimum temperature of 240 °C. In particular, compared with pure ZnO NRs and α-Fe₂O₃ nanoparticles (NPs), the ZnO/α-Fe₂O₃ NRs show an obvious improvement in gas sensing properties. The substantial improvement of sensing properties may be attributed to the unique microstructure and heterojunction formed between ZnO and α-Fe₂O₃.     

Preparation and photoelectrochemical properties of CdS quantum dot-sensitized ZnO nanotube arrays

CdS/ZnO nanotubes (NTs) arrays were synthesized on a transparent conductive glass (FTO) substrate by hydrothermal method, chemical bath etching and successive ionic layer adsorption and reaction (SILAR) method, which were used in semiconductor-sensitized photoelectrochemical cells (PECs). The crystal structure, morphology and photoelectrochemical conversion properties of different photoanodes were investigated by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscope (TEM), high resolution transmission electron microscope (HRTEM), and electrochemical workstation. The results show a heterojunction has been formed between ZnO and CdS QDs. The ZnO NTs and CdS QDs played a remarkable controllability for PEC performances. The photoelectrochemical conversion efficiency of ZnO NTs photoanodes was 3 times that of ZnO nanorods (NRs) arrays photoanodes. After sensitization of CdS quantum dots, the photoelectrochemical conversion efficiency of CdS/ZnO NRs was improved by 7 times and the CdS/ZnO NTs was increased by 4 times. These results demonstrate that the CdS/ZnO core-shell structure can provide a facile and compatible frame for the potential applications in nanotube-based solar cells.     

Enhanced field emission properties from titanium-coated carbon nanotubes

The effect of titanium (Ti) coating over the surface of carbon nanotubes (CNTs) on field emission characteristics was investigated. Vertically aligned CNTs were grown by inductively-coupled plasma-enhanced chemical vapor deposition (ICP-CVD). In order to reduce the screening effect of electric field due to densely packed CNTs, as-grown CNTs were partly etched back by DC plasma of N₂. Ti with various thicknesses from 5 nm to 150 nm was coated on CNTs by a sputtering method. Since thick Ti coating with thickness of 100 nm or more resulted in the shape of a metal post by merging an individual CNT in a bundle, it was inadequate to a field emission application. On the other hand, thin Ti-coated CNTs with thickness of 10 nm or less showed a lower turn-on field, a higher emission current density, and improved emission uniformity compared with pristine CNTs. The improved emission performance was mainly attributed to the low work function of Ti and the reliable and lower resistance contact between CNTs and substrates.     

Electron field emission from semiconducting nanowires

In this paper we report on investigations of field emission (FE) properties of semiconducting (SiC, ZnO) one-dimensional (1D) nanostructures – nanowire/nanorod arrays, and fabrication of low-voltage field emission display (FED) devices based on these 1D nanomaterials. SiC nanowires were grown on Ni-coated Si substrates using a thermal metal-organic chemical vapor deposition (MOCVD) technique, and ZnO nanostructures were grown on gold-coated Si substrates by a thermal CVD method. Electron field emission properties of SiC and ZnO nanostructures were examined in plane geometry using a flat phosphor screen. The interrelation between the FE characteristics (emission thresholds, current density, surface uniformity, etc.) and microstructure and surface morphology of the produced 1D nanostructures was established. Diode-type FED devices (flat vacuum lamps) with SiC-nanowire-based cathodes were developed and fabricated. The FEDs are characterized by low threshold and operating electric fields – lower 2 V/μm and 5 V/μm, respectively, high current density and brightness, and stable performance of the nanowire-based cathodes.     

Core-shell TiO2@ZnO nanorods for efficient ultraviolet photodetection

Core-shell TiO(2)@ZnO nanorods (NRs) have been fabricated by a simple two step method: growth of ZnO NRs' array by an aqueous chemical technique and then coating of the NRs with a solution of titanium isopropoxide [Ti(OC(3)H(7))(4)] followed by a heating step to form the shell. The core-shell nanocomposites are composed of single-crystalline ZnO NRs, coated with a thin TiO(2) shell layer obtained by varying the number of coatings (one, three and five times). The ultraviolet (UV) emission intensity of the nanocomposite is largely quenched due to an efficient electron-hole separation reducing the band-to-band recombinations. The UV photoconductivity of the core-shell structure with three times TiO(2) coating has been largely enhanced due to photoelectron transfer between the core and the shell. The UV photosensitivity of the nanocomposite becomes four times larger while the photocurrent decay during steady UV illumination has been decreased almost by 7 times compared to the as-grown ZnO NRs indicating high efficiency of these core-shell structures as UV sensors.     

Synthesis and characterization of ZnO NRs with spray coated GO for enhanced photocatalytic activity

Zinc oxide nanorods, ZnO NRs, were synthesized on a clean glass and coated with graphene oxide (GO) using spray coating method to enhance the photocatalytic activity in wastewater treatment. The ZnO NRs were synthesized using the solution process synthesis that was optimized using Taguchi method. Several synthesis parameters have been optimized and studied to determine the best synthesis parameter to grow ZnO NRs for the photodegradation of organic contaminants. Field emission scanning electron microscopy (FESEM) with EDX, X-ray diffraction (XRD), Raman, ultraviolet visible near-infrared (UV-VIS-NIR), and photoluminescence (PL) spectroscopies were used to investigate the structural and optical properties of the produced nanorods. FESEM images revealed the vertical growth of ZnO NRs as well as layers of GO covering the ZnO NRs' top surface. The Raman study demonstrates the combination peak of GO and ZnO, hence proving the GO layer's successful coating. After the GO coating, decrease in the bandgap of the synthesized photocatalyst was detected by PL and UV–Vis absorption measurements. Under UVC exposure with treatment time of 6 h, the degradation of MB with ZnO NRs/GO photocatalyst reached a degradation percentage of 97.86%, which is greater than the degradation percentage achieved using pristine ZnO NRs, which is 93.28%. The results validated that the coating of GO enhances the photocatalytic activity of the host material, ZnO NRs.     

Synthesis and field emission properties of vertically aligned carbon nanotube arrays on copper

We report the synthesis of periodic arrays of carbon nanotubes (CNTs) with different densities on copper substrate by employing nanosphere lithography (NSL) and plasma enhanced chemical vapor deposition. At a growth pressure of 8 torr and temperature of 520 °C, vertically aligned bamboo-like CNTs were formed with a catalyst particle on the tip. Electrical properties of CNTs with different densities were investigated for the possible applications in field emission (FE). The investigation of FE properties reveals a strong dependence on the density of CNTs. Experimental results show that NSL patterned low density CNTs exhibit better field emission properties as compared to the high density CNTs. Low-density CNTs exhibit lower turn-on and threshold electric fields, and a higher field enhancement factor. The high density of CNTs results in the deterioration of the FE properties due to the screening of the electric field by the neighboring CNTs.     

On the Morphology,Structure and Field Emission Properties of Silver-Tetracyanoquinodimethane Nanostructures

Silver-tetracyanoquinodimethane(Ag-TCNQ) nanostructured arrays with different morphologies were grown by an organic vapor-transport reaction under different conditions. The field emission properties of nanostructured arrays were studied systematically. Their morphology and crystal structure were characterized by SEM and XRD, respectively. It was found that the field emission properties were strongly dependent on the reaction temperature and the initial Ag film thickness. The lowest turn-on field with 10-nm-thick silver film is about 2.0 V/μm, comparable to that of carbon nanotubes. The film crystal structure and the morphology are contributed to the final emission performance.     

Highly stable field emission properties from well-crystalline 6-Fold symmetrical hierarchical ZnO nanostructures

Herein, we report the growth, characterization and field emission application of well-crystalline 6-fold symmetrical hierarchical ZnO nanostructures grown on silicon substrate by thermal evaporation process. The detailed morphological characterizations revealed that the prepared material possess six-fold structures in which ZnO nanoneedles are symmetrically grown on each facets of core hexagonal ZnO nanorods in such a manner that they made beautiful 6-fold symmetrical hierarchical structure. The detailed structural studies confirmed that the grown hierarchical structures possess well-crystallinity with wurtzite hexagonal phase. The room-temperature photoluminescence (PL) spectrum exhibited a strong UV emission confirming good optical properties. The Raman-scattering revealed the wurtzite hexagonal phase for as-grown hierarchical structures. The field emission properties of the 6-fold symmetrical hierarchical ZnO nanostructures were tested and a turn-on voltage equal to 2.8 kV, corresponds to emission current of 65 nA, was observed. A threshold voltage of 4.6 kV with a maximum emission current of about 9.36 µA was also recorded. A high emission current stability profile over a period of ~7000 s was noted for the fabricated FE device.     

Seedless Pattern Growth of Quasi-Aligned ZnO Nanorod Arrays on Cover Glass Substrates in Solution

A hybrid technique for the selective growth of ZnO nanorod arrays on wanted areas of thin cover glass substrates was developed without the use of seed layer of ZnO. This method utilizes electron-beam lithography for pattern transfer on seedless substrate, followed by solution method for the bottom-up growth of ZnO nanorod arrays on the patterned substrates. The arrays of highly crystalline ZnO nanorods having diameter of 60 ± 10 nm and length of 750 ± 50 nm were selectively grown on different shape patterns and exhibited a remarkable uniformity in terms of diameter, length, and density. The room temperature cathodluminescence measurements showed a strong ultraviolet emission at 381 nm and broad visible emission at 585–610 nm were observed in the spectrum.     

Synthesis and field emission properties of different ZnO nanostructure arrays

In this article, zinc oxide (ZnO) nanostructures of different shapes were fabricated on silicon substrate. Well-aligned and long ZnO nanowire (NW) arrays, as well as leaf-like ZnO nanostructures (which consist of modulated and single-phase structures), were fabricated by a chemical vapor deposition (CVD) method without the assistance of a catalyst. On the other hand, needle-like ZnO NW arrays were first fabricated with the CVD process followed by chemical etching of the NW arrays. The use of chemical etching provides a low-cost and convenient method of obtaining the needle-like arrays. In addition, the field emission properties of the different ZnO NW arrays were also investigated where some differences in the turn-on field and the field-enhancement factors were observed for the ZnO nanostructures of different lengths and shapes. It was experimentally observed that the leaf-like ZnO nanostructure is most suitable for field emission due to its lowest turn-on and threshold field as well as its high field-enhancement factor among the different synthesized nanostructures.     

Large-scale growth of patterned SiC nanowire arrays and their field emission performance

Fabrication of patterned one-dimensional (1D) nanostructures was recognized as the key process for the construction of functional display devices. In current investigation, we put forward the large-scale and uniform growth of patterned 3C-SiC nanowire arrays assisted by the patterned Au catalysts on SiC wafer substrate. The as-fabricated SiC nanowires presented tapered configuration with a typical bamboo-like body as well as clear and sharp tips. The as-fabricated SiC nanoarray cathode has outstanding field emission (FE) characteristic that has a low turn-on field (E_to) of ~ 1.54 V/μm. The mechanism for their electron emission behaviors has been proposed.     

Catalyst-free,self-assembly,and controllable synthesis of graphene flake–carbon nanotube composites for high-performance field emission

Catalyst-free and self-assembled growth of graphene flakes (GFs) on carbon nanotube (CNT) arrays have been realized by using microwave plasma enhanced chemical vapor deposition. The shape of GFs was highly manipulated by adjusting the growth time, C concentration, and microwave power. We qualitatively discussed the nucleation and growth mechanism of GFs based on the growth parameter–GF shape studies. The field emission (FE) properties of graphene flake–carbon nanotube (GF–CNT) composites for different GF shapes were measured and found to be strongly influenced by the GF distribution. The optimal shape of GFs for FE had small scales, sharp edges, and sparse distribution on CNTs. The best FE properties with the optimal shape were observed with a low turn-on electric field of 0.73 V/μm and excellent stability, which are superior to those of the as-grown CNT arrays and GF–CNT composites covered by densely distributed GFs. We consider that the large aspect ratio of CNTs and the unique FE stability of GFs play a synergetic effect on the improved FE properties.     

Enhanced near band edge luminescence of Ti/ZnO nanorod heterostructures due to the surface diffusion of Ti

Information on the mechanistic differences in the luminescence properties of Ti/ZnO nanorods (NRs) has been obtained through the preparation of heterostructures by (a) varying the thickness of Ti from 1 nm to 20 nm keeping the substrate temperature at 400 °C, (b) varying the substrate temperature from room temperature (RT) to 500 °C while keeping the metal thickness constant at 10 nm and (c) annealing the RT Ti sputtered NRs at temperatures of 400 °C and 500 °C. The photoluminescence (PL) spectra show that the near band edge luminescence of ZnO in the ultraviolet (UV) region is enhanced as the thickness of Ti increases up to 5 nm and, thereafter, it falls. Sputtering of Ti on ZnO NRs at RT does not cause any UV enhancement but when sputtered at and above 400 °C, the UV intensity is enhanced. Annealing of RT Ti sputtered NRs at and above 400 °C also results in the enhancement of the UV peak, although with a lesser magnitude. Analysis of the PL results, supported by X-ray diffraction, field emission scanning electron microscopy, elemental mapping, high resolution transmission electron microscopy, Fourier transform infrared spectroscopy and electrical I-V measurement results, show a clear indication that the surface diffusion of Ti causes a reduction in the surface defects.