稀土La2O3对Li2O-A12O3-SiO2微晶玻璃结构和性能的影响

本主要研究添加微量稀土La2O3对Li2O-Al2O3-SiO2微晶玻璃晶相组成，显微结构，抗折强度的影响，研究结果表明：添加微量La2O3有利于Li2O-Al2O3-SiO2微晶玻璃中的主晶相β－锂辉石发育成完整的柱状，板状晶体，提高了微晶玻璃的抗折强度。     

Cr2O3及TiO2对CaO-MgO-Al2O3-SiO2微晶玻璃着色及析晶的影响

通过X射线衍射、扫描电子显微镜、综合热分析仪和色差计研究了不同含量的Cr2O3和TiO2对以整体析晶法制备的CaO-MgO-Al2O3-SiO2系微晶玻璃的显色和析晶性能的影响.结果表明:在所研究的组成范围内,Cr2O3和TiO2都不改变微晶玻璃的主晶相,生成颗粒状透辉石晶体.Cr2O3会促进晶体尺寸的增长,但是对晶体含量影响不大.TiO2作为晶核剂效果比较明显,能促进晶体长大.随着Cr2O3含量的增加,微晶玻璃的绿色加深,但亮度降低.随着TiO2含量的增加,微晶玻璃的绿色变浅,但亮度增加.     

P2O5对包钢高炉渣微晶玻璃析晶行为的影响

采用熔融法制备CaO-MgO-Al2O3-SiO2系微晶玻璃,并综合运用DTA、XRD、SEM等分析手段,研究了晶核剂P2O5(由Na3(PO4)·12H2O引入)对基础玻璃核化和晶化温度的影响,检测了制品中晶相的种类、含量和晶体发育的形貌.研究表明,引入少量的P2O5能抑制该玻璃系统的析晶,随着P2O5含量的增加抑制能力增强,含量超过4％时促进了玻璃的整体析晶,并且析晶能力随其含量的增加逐渐增强,晶相种类和形貌同时也发生改变.     

P2O5含量对Al2O3-SiO2-P2O5系统玻璃结构和析晶性能的影响

采用高温熔融冷淬法制备Al2O3-SiO2-P2O(5ASP)系统玻璃,用原位晶化法获得了磷酸盐微晶玻璃;用IR、DSC、XRD、SEM等测试方法表征了玻璃结构及析晶性能,讨论了P2O5含量对ASP玻璃结构和析晶性能的影响。结果表明:P2O5含量在35～50%能形成稳定的ASP玻璃。在磷含量较低时,玻璃结构中的P5 主要以不含P=O双键的[PO4]四面体形式存在,P2O5含量较高时,结构中的P-O-键削弱,P=O双键加强,P5 部分以含P=O双键的[PO4]四面体形式存在。随着P2O5含量的增加,玻璃稳定性变差,析晶趋势增强;晶化后的玻璃以AlPO4为主晶相,同时含有少量的Al(PO)3晶相,当晶化温度由650℃升高到800℃时,晶相含量增加并出现YPO4晶相。     

MgO-Al2O3-SiO2系统微晶玻璃的析晶及热处理工艺研究

用XRD、DTA对MgO-Al2O3-SiO2系微晶玻璃材料的析晶过程进行了研究,讨论了热处理温度及时间对微晶玻璃热膨胀系数的影响,表明了各种晶体的析出特点.     

La2 O3对SiO2-Al2 O3-CaO-MgO系统玻璃结构与性能的影响

采用高温熔融法制备了SiO2-Al2 O3-CaO-MgO系统玻璃,研究添加La2 O3对SiO2-Al2 O3-CaO-MgO系统玻璃密度、耐碱性、弹性模量以及析晶上限温度的影响,并借助红外光谱对玻璃的结构进行研究。结果表明：随着La2 O3含量从0升高至5wt%,玻璃的网络结构发生改变;玻璃的密度和摩尔体积均增大;玻璃的耐碱性能降低;弹性模量从90.5 GPa增加至93.6 GPa后降低,最大值对应的La2 O3含量为3wt%;析晶上限温度从1224℃降低至1209℃后增加至1212℃,最后趋于不变,在La2 O3添加含量为2wt%时达到最低温度。     

稀土La_2O_3对Li_2O-Al_2O_3-SiO_2微晶玻璃结构和性能的影响

本文主要研究添加微量稀土La2O3对Li2O-Al2O3-SiO2微晶玻璃晶相组成、显微结构、抗折强度的影响。研究结果表明:添加微量La2O3有利于Li2O-Al2O3-SiO2微晶玻璃中的主晶相β-锂辉石发育成完整的柱状、板状晶体,提高了微晶玻璃的抗折强度。     

ZrO2对CaO-Al2O3-SiO2系统微晶玻璃烧结过程的影响研究

CaO-Al2O3-SiO2系统微晶玻璃作为微晶玻璃中的一个新品种,具有非常鲜明的特点.本文讨论了在CaO-Al2O3-SiO2系统微晶玻璃中加入ZrO2,研究了ZrO2对CaO-Al2O3-SiO2系统微晶玻璃烧结的影响.随着ZrO2加入量的增加,玻璃颗粒的烧结收缩率下降,说明ZrO2的加入对玻璃颗粒的烧结收缩有一定的阻碍作用.ZrO2的加入对CaO-Al2O3-SiO2系统微晶玻璃中的主晶相(β-硅灰石晶体)的析出没有大的影响.     

CaO／MgO比对CaO—MgO—Al2O3—SiO2系玻璃微晶化行为的影响

采用DTA,XRD,SEM等测试分析手段研究了CaO/MgO比对CaO-MgO-Al2O3-SiO2系玻璃微晶化行为的影响,结果表明：在一定热处理制度下,可制备结构均匀致密、耐磨性极好的白色微晶陶瓷,其主晶相为硅灰石和透辉石;随着CaO/MgO比的降低,微晶陶瓷的晶化温度提高,透辉石型晶体含量增加,耐磨性提高。     

MgO-Al2O3-SiO2系硬盘基板用微晶玻璃析晶动力学研究

MgO-A l2O3-SiO2系微晶玻璃是一种优良的磁盘基板备选材料,该材料具有良好的力学性能,能够满足高性能硬盘基板用材料的要求。采用差热分析方法(DTA),得到了以TiO2作为晶核剂的MgO-A l2O3-SiO2系微晶玻璃的析晶动力学参数,研究了该体系微晶玻璃的析晶动力学;利用X射线衍射技术(XRD)确定了经合适热处理后得到的样品的主晶相。结果表明:引入TiO2降低了该体系玻璃的析晶活化能Ea,当TiO2质量分数达到7%时,Ea达到最小值,玻璃析晶晶化指数n达到最大值,这表明TiO2在一定范围内促进了该系统玻璃的析晶。     

晶化时间对MgO-Al2O3-SiO2微晶玻璃相转变及热膨胀性能的影响

采用XRD、DTA、SEM等测试方法,对MgO-Al2O3-SiO2（MAS）系微晶玻璃的析晶和微观结构进行了研究,讨论了不同的晶化时间对MAS微晶玻璃析晶行为及其热膨胀性能的影响。结果表明：在1050℃保温,堇青石能快速地晶化析出。随着晶化时间的增长,堇青石相逐渐增多,当晶化2h时几乎完全析出,析出晶粒大小约为2～5um。MAS系微晶玻璃的热膨胀系数与相组成有着密切的关系,随着晶化时间的延长,热膨胀系数逐渐减小。     

磷酸盐系低温无铅釉的研究

采用熔融法制备了ZnO-B2O3-P2O5系无铅磷酸盐釉，研究了组成对釉玻璃结构、特征温度、热膨胀和化学稳定性的影响。结果表明：B2O3，和P2O5为玻璃网络形成体，ZnO含量较低时可以参与到网络结构中，提高其稳定性；釉的转变点Tg、熔制温度Tm、封接温度Ts、软化点Td都随P2O5／B2O3减小而增加；B2O3／ZnO是影响熔制温度的主要因素；ZnO含量密度和热膨胀系数影响较大。     

Low Li2O content study in Li2O-Al2O3-SiO2 glass-ceramics

The price of lithium-containing minerals and other chemical materials continues to increase, resulting in an increase in the production cost of Li₂O-Al₂O₃-SiO₂ (LAS) system glass-ceramics. In the LAS glass-ceramics component, the reduction in the amount of Li₂O used can reduce the cost of the product. It is worthwhile to study whether it is possible to prepare glass-ceramics with low expansion properties under low Li₂O content. The effect of Li₂O content on the glass-ceramics of LAS system was studied. In this paper, spodumene was used as the main raw material, and TiO₂ and ZrO₂ were added as crystal nucleating agents to prepare transparent glass-ceramics with low expansion coefficient. The effects of the change of Li₂O content on the crystal phase and microstructure of glass-ceramics were investigated by XRD, DSC, FTIR and SEM. The results show that the main crystalline phase of the low expansion transparent glass-ceramics is β-quartz solid solution. When Li₂O content is in the range of 2.99 wt% to 4.13 wt%, low expansion glass ceramics can be prepared by an appropriate method. With the increase of Li₂O content, the average coefficient of thermal expansion (CTE) in the temperature range of 30 °C–300 °C shows a decreasing trend. When Li₂O content is in the range of 3.51 wt% to 4.13 wt%, the thermal expansion coefficient of the glass ceramics is extremely small, and even a negative expansion coefficient occurs.     

P2O5-V2O5-B2O3-ZnO系无铅低熔电子封接玻璃的性能

研究了P2O5-V2O5-B2O3-ZnO系无铅封接材料,考察了V2O5和B2O3含量对低熔玻璃软化温度、热膨胀系数及热稳定性的影响. 结果表明,玻璃的软化点随V2O5含量增加而降低,提高B2O3含量使软化温度先升高后降低,出现硼反常现象. 当V2O5和B2O3摩尔含量为15%和8%时,低熔玻璃的软化温度、热膨胀系数及热稳定性能满足低温封接要求,但化学稳定性较差,而添加少量Al2O3和Fe2O3能明显提高低熔玻璃的化学稳定性. 优化组成为26.0P2O5-17.3V2O5-7.7B2O3-45.0ZnO-2.0Al2O3-2.0Fe2O3的玻璃转变温度为340℃,热膨胀系数为7.5×10-6 ℃-1 (25~300℃),在90℃的去离子水中恒温10 h,失重为0.63 mg/cm2,化学稳定性与传统的含铅封接玻璃相当,综合性能基本满足无铅低熔玻璃的要求.     

复合晶核剂TiO2/ZrO2对MgO-Al2O3-SiO2系统微晶玻璃的影响研究

本文制备了Mg0-Al2O3-SiO2系微晶玻璃,用XRD、DTA等方法对该系统微晶玻璃材料进行了研究;讨论了复合晶核剂对材料热膨胀性能及热处理温度的影响.结果表明TiO2/ZrO2复合晶核剂中,少量ZrO2(＜0.5wt%)能够降低微晶玻璃材料的热处理温度和热膨胀系数.     

Fe2O3对CaO-SiO2玻璃和微晶玻璃性能的影响

利用溶胶-凝胶法制得Fe2O3-CaO-SiO2系基础玻璃,研究不同含量的Fe2O3对CaO-SiO2玻璃和微晶玻璃性能的影响.经分析,不同组分的玻璃凝结时间不同,处于低共熔点的样品凝结时间最短,而离低共熔点最远的样品凝结时间最长.样品的密度并不随成分而变化.溶胶凝胶转变过程中,不同组分所得的凝胶玻璃有一定的耐酸碱性.而微晶玻璃的耐酸碱性比玻璃都略有增强.微晶玻璃的饱和磁化强度和磁铁矿在玻璃中所占的体积分数有关.随着玻璃中Fe2O3含量的增加,饱和磁化强度增大.     

玻璃组成对Li2O-Al2O3-SiO2系统微晶玻璃膨胀系数的影响

以Li2O-Al2O3-SiO2系统微晶玻璃的标准样的组成为基础配方,改变玻璃组成中各种氧化物的含量,采用传统的熔融法制备了Li2O-Al2O3-SiO2系统微晶玻璃,利用SEM、XRD、DTA及热膨胀系数测定等分析手段,重点研究了玻璃组成中Li2O、Al2O3、SiO2的含量对微晶玻璃热膨胀系数的影响.研究结果表明:在标准试样的基础上,改变Li2O的含量,对热膨胀系数影响很大;热膨胀系数随Al2O3含量增大而增大,而SiO2含量的变化,对热膨胀系数影响不大.     

CaO-Al2O3-SiO2系统微晶玻璃的冲蚀磨损研究

CaO-Al2O3-SiO2系统微晶玻璃装饰板材是一种新型建筑装饰材料。本文利用冲蚀磨损实验研究了影响CaO-Al2O3-SiO2系统烧结法微晶玻璃装饰板材磨蚀行为。讨论了微晶玻璃组成、结构、磨粒粒径、冲蚀角、冲蚀时间对CaO-Al2O3-SiO2系统微晶玻璃的冲蚀性的影响。结果表明:随着微晶玻璃中晶相含量的增加,磨料对其表面的冲蚀磨损量明显下降。微晶玻璃的冲蚀量随冲蚀角的增大、冲蚀时间的增长、磨粒粒度的增大而增加。     

ZnO-B2O3-P2O5系封接玻璃的研究

采用熔融法制备了ZnO-B2O3-PO5 系无铅磷酸盐封接玻璃，研究了组成对玻璃结构、特征温度、热膨胀和化学稳定性的影响。结果表明：B2O3和P2O5为玻璃网络形成体，ZnO含量较低时可以参与到玻璃网络结构中，提高玻璃的稳定性；玻璃转变点Tg、熔制温度Tm、封接温度Ts、软化点Td都随P2O5／B2O3减小而增加；B2O3／ZnO是影响玻璃熔制温度的主要因素；ZnO含量对玻璃密度和热膨胀系数影响较大。ZnO-B2O3-PO5 系玻璃在中性环境下的化学稳定性较好。。