SiC/MoSi2 based coatings for Cf/C composites by two step pack cementation

In order to improve the oxidation resistance of C_f/Cs produced by chemical vapour infiltration, a multilayer coating based on silicon carbide and molybdenum disilicide was produced by two-step pack cementation technique. The inner SiC layer with a thickness up to 25 μm was obtained without promoted reaction additives by varying the composition, and thermal treatment conditions. The SiC/SiC-MoSi₂ coating was produced with a thickness up to 80 μm by two step pack cementation, considering the effect of the inner layer characteristic. The enhancement of the oxidation resistance, observed in SiC/SiC-MoSi₂ coated C_f/Cs by means of thermal analysis in flowing air up to 1500 °C, was due to the formation of SiO₂ promoted by the passive oxidation of silicon carbide and molybdenum disilicide.     

Oxidation resistance of SiC nanowires reinforced SiC coating prepared by a CVD process on SiC‐coated C/C composites

Oxidation protective SiC nanowires‐reinforced SiC (SiCNWs‐SiC) coating was prepared on pack cementation (PC) SiC‐coated carbon/carbon (C/C) composites by a simple chemical vapor deposition (CVD) process. This double‐layer SiCNWs‐SiC/PC SiC‐coating system on C/C composites not only has the advantages of SiC buffer layer but also has the toughening effects of SiCNWs. The microstructure and phase composition of the nanowires and the coatings were examined by SEM, TEM, and XRD. The single‐crystalline β‐SiC nanowires with twins and stacking faults were deposited uniformly and oriented randomly with diameter of 50‐200 nm and length ranging from several to tens micrometers. The dense SiCNWs‐SiC coating with some closed pores was obtained by SiC nanocrystals stacked tightly with each other on the surface of SiCNWs. After introducing SiCNWs in the coating system, the oxidation resistance is effectively improved. The oxidation test results showed that the weight loss of the SiCNWs‐SiC/PC SiC‐coated samples was 4.91% and 1.61% after oxidation at 1073 K for 8 hours and at 1473 K for 276 hours, respectively. No matter oxidation at which temperature, the SiCNWs‐SiC/PC SiC‐coating system has better anti‐oxidation property than the single‐layer PC SiC coating or the double‐layer CVD SiC/PC SiC coating without SiCNWs.     

Siliconization elimination for SiC coated C/C composites by a pyrolytic carbon coating and the consequent improvement of the mechanical property and oxidation resistances

Carbon/carbon (C/C) composites have a wide application as the thermal structure materials because of their excellent properties at high temperatures. However, C/C composites are easily oxidized in oxygen-containing environment, which limits their potential applications to a great degree. Silicon carbide (SiC) ceramic coating fabricated via pack cementation (PC) was considered as an effective way to protect C/C composites against oxidation. But the mechanical properties of C/C composites were severely damaged due to chemical reaction between the molten silicon and C/C substrate during the preparation of SiC coating by PC. In order to eliminate the siliconization erosion, a pyrolytic carbon (PyC) coating was pre-prepared on C/C composites by the chemical vapor infiltration (CVI) prior to the fabrication of SiC coating. Due to the retardation effect of PyC coating on siliconization erosion, the flexural strength retention of the SiC coated C/C composites with PyC coating increased from 46.27 % to 107.95 % compared with the specimen without PyC coating. Furthermore, the presence of homogeneous and defect-free PyC coating was beneficial to fabricate a compact SiC coating without silicon phase by sufficiently reacting with molten silicon during PC. Therefore, the SiC coated C/C composites with PyC coating had better oxidation resistances under dynamic (between room temperature and 1773 K) and static conditions in air at different temperatures (1773?1973 K).     

Effect of silicon/graphite ratio and temperature on oxidation protective properties of SiC/ZrB2–SiC coatings prepared by pack cementation

To investigate the silicon/graphite ratio and temperature on preparation and properties of ZrB₂–SiC coatings, ZrB₂, silicon, and graphite powders were used as pack powders to prepare ZrB₂–SiC coatings on SiC coated graphite samples at different temperatures by pack cementation method. The composition, microstructure, thermal shock, and oxidation resistance of these coatings were characterized and assessed. High silicon/graphite ratio (in this case, 2) did not guarantee higher coating density, instead could be harmful to coating formation and led to the lump of pack powders, especially at temperatures of 2100 and 2200 °C. But residual silicon in the coating is beneficial for high density and oxidation protection ability. The SiC/ZrB₂–SiC (ZS50-2) coating prepared at 2000 °C showed excellent oxidation protective ability, owing to the residual silicon in the coating and dense coating structure. The weight loss of ZS50-2 after 15 thermal shocks between 1500 °C and room temperature, and oxidation for 19 h at 1500 °C are 6.5% and 2.9%, respectively.     

碳/碳复合材料表面SiC/c-AlPO_4复合涂层及其抗氧化机制

采用二次包埋法和水热电泳沉积法相结合的工艺在碳纤维增强碳复合材料表面制得SiC/方石英型磷酸铝(cristobalite aluminum phosphate,c-AlPO4)复合涂层。借助X射线衍射仪和扫描电镜对复合涂层的晶相组成和显微结构进行了表征。研究了复合涂层的高温氧化性能,讨论了复合涂层氧化、失效的机理。结果表明:复合涂层具有双层结构,包埋的SiC内层主要由α-SiC,β-SiC和少量的游离硅组成,外层由c-AlPO4颗粒构成,内外层结合紧密。复合涂层在1300～1500℃范围内具有良好的抗氧化性能,其氧化激活能为117.2kJ/mol,氧化过程主要受氧在c-AlPO4层中的体扩散速率所控制;氧化气体逸出留下的孔洞是复合涂层防氧化失效的主要原因。     

Research on microstructure and oxidation resistant property of ZrSi2-SiC/SiC coating on HTR graphite spheres

ZrSi₂-SiC/SiC coating was prepared on the surface of high temperature gas-cooled reactor (HTR) matrix graphite spheres by two-step pack cementation and sintering process. The microstructure, oxidation resistance and thermal shock resistance properties of the as-prepared coatings with different original powder mixtures were investigated. Results show that dense microstructure of the ZrSi₂-SiC/SiC coating and continuous ZrSiO₄-SiO₂-ZrO₂ glass phase generated during the oxidation process were the key factors for the outstanding thermal properties. When the mole ratio of Zr:Si:C reaches 1:7:3 in the second pack cementation powders, the coated graphite spheres have optimum oxidation resistant ability. The weight gain is only 0.6 wt% after 15 times thermal shock tests and 0.12 wt% after isothermal oxidation test at 1500 °C for 20 h in air. The oxidation resistant mechanism of the coating was also discussed. The dense inner SiC layer and the outer glass layer generated during the oxidation process could protect the ZrSi₂-SiC/SiC coating from further oxidation.     

Improved antioxidative and mechanical properties of SiC coated C/C composites via a SiO2-SiC reticulated layer

To improve the oxidation resistances of SiC coated C/C composites by a pack cementation (PC) method at high temperature and alleviate the siliconization erosion of molten silicon on C/C substrate during the preparation of SiC coating, a SiO₂-SiC reticulated layer with SiC nanowires was pre-prepared on C/C composites through combined slurry painting and thermal treatment before the fabrication of SiC coating. The presence of porous SiO₂-SiC layer with SiC nanowires was beneficial to fabricate a compact and homogeneous SiC coating resulting from synergistic effect of further reaction between SiO₂ and pack powders and the reinforcement of SiC nanowires. Therefore, the results of thermal shock and isothermal oxidation tests showed that the mass loss of modified SiC coating was only 0.02 % after suffering 50-time thermal cycles between room temperature and 1773 K and decreased from 5.95 % to 1.08 % after static oxidation for 49.5 h in air at 1773 K. Moreover, due to the blocking effect of SiO₂-SiC reticulated layer on siliconization erosion during PC, the flexural strength of SiC coated C/C composites with SiO₂-SiC reticulated layer increased by 64.8 % compared with the untreated specimen.     

Micro Four‐Layer SiC Coating on Matrix Graphite Spheres of HTR Fuel Elements by Two‐Step Pack Cementation

A micro four‐layer SiC coating, which includes inner transition layer, fine‐grained layer, dense bulk layer, and outer loose layer, was fabricated on the matrix graphite spheres of high‐temperature gas‐cooled reactor fuel elements to improve the oxidation‐resistant property by a two‐step pack cementation process. According to the experiment results, the micro four‐layer can be differentiated by SiC grain size and microstructure variation. The oxidation tests at 1773 K for 200 h reveal that the coating structure could effectively improve the oxidation resistance of matrix graphite spheres with a weight gain of 0.52 wt%, and the fine‐grained and dense bulk layers are evidenced as two main antioxidation layers. Although the thermal expansion coefficients of SiC and matrix graphite do not match each other so well, no obvious stress cracking was observed after thermal shocking tests from 1773 K to room temperature for 100 times.     

In-situ synthesis of SiC nanofibers for improving the oxidation resistance of graphite

In order to improve the oxidation resistance of graphite, a SiC/ZrO₂-SiC nanofibers multiphase coating was developed on a graphite substrate using the pack cementation and slurry painting techniques. The microstructure of the coating was characterized by X-ray diffraction and scanning electron microscopy. The HSC chemistry software package was used for the thermodynamic calculations. The isothermal oxidation test of the coated samples was performed at 1773 K in air. A 500 µm thick gradient C–SiC transition layer was formed at the graphite-coating interface SiC nanofibers with the diameter in the range of 32–88 nm were observed on the coating whose growth was ascribed to the gas phase reaction of SiO with CO. The oxidation test results revealed that the SiC nanofibers and thermally stable phase ZrSiO₄ were the mainly effective tools protecting graphite from oxidation.     

A Si–SiC oxidation protective coating for carbon/carbon composites prepared by a two-step pack cementation

To prevent carbon/carbon (C/C) composites from oxidation, a Si–SiC coating has been prepared by a two-step pack cementation technique. X-ray diffraction (XRD) and scanning electron microscopy (SEM) analysis show that the coating obtained by the first step pack cementation is a porous β-SiC structure, and a dense structure consisting α-SiC, β-SiC and Si is obtained after heat-treatment by the second step pack cementation. By energy dispersive spectroscopy (EDS) analysis, a gradient C–SiC transition layer can be formed at the C/C-coating interface. The as-received coating has excellent oxidation protection ability and can protect C/C composites from oxidation for 166 h at 1773 K in air. The weigh loss of the coated C/C is due to the formation of bubble holes on the coating surface and through-coating cracks in the coating.     

Oxidation protection of C/C composites with a multilayer coating of SiC and Si + SiC + SiC nanowires

An oxidation protective Si–SiC coating with randomly oriented SiC nanowires was prepared on the SiC-coated carbon/carbon (C/C) composites by a two-step technique. First, a porous network of SiC nanowires was produced using chemical vapor deposition. This material was subjected to pack cementation to infiltrate the porous layer with a mixture of Si and SiC. The nanowires in the coating could efficiently suppress the cracking of the coating by various toughening mechanisms including nanowire pullout, nanowire bridging, microcrack deflection and good interaction between nanowire/matrix interface. The results of thermogravimetric analysis and thermal shock showed that the coating had excellent oxidation protection for C/C composites between room temperature and 1500 °C. These results were confirmed by two additional oxidation experiments conducted at temperature of 900 and 1400 °C, which demonstrated that the coating could efficiently protect C/C composites from oxidation at 900 °C for more than 313 h or at 1400 °C for more than 112 h.     

Wear behavior of SiC nanowire-reinforced SiC coating for C/C composites at elevated temperatures

To improve the wear resistance of SiC coating on carbon/carbon (C/C) composites, SiC nanowires (SiCNWs) were introduced into the SiC wear resistant coating. The dense SiC nanowire-reinforced SiC coating (SiCNW-SiC coating) was prepared on C/C composites using a two-step method consisting of chemical vapor deposition and pack cementation. The incorporation of SiCNWs improved the fracture toughness of SiC coating, which is an advantage in wear resistance. Wear behavior of the as-prepared coatings was investigated at elevated temperatures. The results show that the wear resistance of SiCNW-SiC coating was improved significantly by introducing SiC nanowires. It is worth noting that the wear rate of SiCNW-SiC coating was an order of magnitude lower than that of the SiC coating without SiCNWs at 800 °C. The wear mechanisms of SiCNW-SiC coating at 800 °C were abrasive wear and delamination. Pullout and breakage of SiC grains resulted in failure of SiC coating without SiCNWs at 800 °C.     

碳纤维增强碳复合材料表面多层复合涂层中SiC和TiC内层的比较(英文)

采用包埋法制备了碳纤维增强碳(carbon fiber reinforced carb on composites,C/C)复合材料表面多层涂层,包括SiC,TiC内层,SiC,TiC中间层以及SiC+TiC复合外层。利用场发射扫描电镜和X射线衍射对其表面和断面的结构进行研究。结果显示:和TiC内层相比较,SiC内层较厚而且致密,具多孔结构且和C/C复合材料结合紧密;TiC内层较薄且和C/C复合材料结合松散。制备的SiC+TiC复合外层由SiC,TiC和Ti3SiC2组成。     

Effect of the incorporation of SiC nanowire with double protective layers on SiC coating for C/C composites

To maintain the thermal stability of SiC nanowires during SiC coating fabrication process, carbon and SiC double protective layers were covered on the surface of nanowires. And SiC nanowires with double protective layers toughened SiC coating were prepared by pack cementation. The results showed that after introducing the SiC nanowires with double protective layers, the fracture toughness of the SiC coating was increased by 88.4 %. The coating protected C/C for 175 h with a mass loss of 3.67 %, and after 51 thermal shock cycles, the mass losses of the oxidized coating were 3.96 %. The double protective layers are beneficial to improve the thermal stability of nanowires, leading to good fracture toughness and thermal shock resistance of SiC coating. SiC nanowires consume the energy of crack propagation by fracture, pullout and bridging, leading to an increase in fracture toughness.     

Oxidation resistance and mechanical properties of LaB6-MoSi2-SiC ceramic coating toughened by SiC nanowires

To improve the high-temperature tolerance of carbon/carbon composites, a compact SiC-nanowires toughened LaB₆-MoSi₂-SiC/SiC (SiCnws-LMS/SiC) coating was designed and fabricated by combination of multiple methods including pack cementation, chemical vapor deposition and supersonic atmospheric plasma spraying. Isothermal oxidation results indicated that the mass loss of LMS/SiC coating decreased from 4.34?±?0.28% to 1.12?±?0.23% after oxidation for 200?h at 1773?K benefit from the addition of SiCnws. Absence of obvious cracks and voids in the coating after oxidation test indicated that the interfaces between various phases and SiCnws could obstruct the crack propagation by releasing the thermal stress in the coating. Meanwhile, after the introduction of SiCnws, the bonding strength and flexural strength of the coating were respectively increased by 54.54% and 59.77% compared to the LMS/SiC coating without SiCnws. The improved mechanical properties could be attributed to the pullout and bridging effects of SiCnws, which created multi-scaled reinforcements, thereby enhancing the load bearing capacity to increase the fracture toughness of the coating.     

Preparing the SiC coated C/C composites with excellent mechanical and antioxidative properties using a buffer layer

The preparation of SiC coating on C/C composites via a pack cementation method would cause serious mechanical damage to C/C substrate due to the siliconization corrosion by molten silicon during the ultra-high-temperature preparation process (2173–2373 K). In order to prepare SiC coated C/C composites with excellent mechanical and antioxidative properties, we applied a buffer layer on the surface of C/C to inhibit siliconization corrosion and densify coating. Results showed that the siliconized area ratio of the C/C substrate was decreased from 60.9% to 24.8%, and its bending strength was increased from 36.9 MPa to 60.6 MPa. Moreover, the mass loss of the modified SiC coated C/C sample has reduced by ~4.14 times after oxidation for 144 h in air at 1773 K and decreased from 2.44% to ? 0.15% after suffering 50 thermal cycles between room temperature and 1773 K.     

Microstructures and oxidation behaviors of Al-modified and Al2O3-modified SiC coatings on carbon/carbon composites via pack cementation

Al₂O₃-modified SiC (AOSC) and Al-modified SiC (ASC) coatings were prepared on carbon/carbon (C/C) composites by one-time pack cementation (PC). Their microstructures and anti-oxidation performances were studied. Compared with ASC coating, AOSC coating shows more conspicuous defects (micro-cracks and holes) and lower densification. ASC coating can offer better oxidation resistance and thermal shock resistance to C/C composites than AOSC coating. Al additive can more efficiently improve the sinterability of SiC, which causes the above results. Besides, Al₂O₃ oxidation product is more stable than SiO₂ (l) of oxidized SiC at 1500 °C based on the thermodynamic analysis.     

Oxidation protection of carbon/carbon composites with SiC/indialite coating for intermediate temperatures

In order to improve the oxidation resistance of carbon/carbon composites at intermediate temperatures, a novel double-layer SiC/indialite coating was prepared by a simple and low-cost method. The internal SiC transition layer was prepared by pack cementation and the external indialite glass–ceramic coating was produced by in situ crystallization of ternary MgO–Al₂O₃–SiO₂ glass. The microstructures and morphologies of coating were determined by scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS). Oxidation resistance of the as-coated C/C composites was evaluated in ambient air at temperature from 800 °C to 1200 °C. Nearly neglectable mass loss was measured after 100 h isothermal oxidation test, indicating that SiC/indialite coating possesses excellent oxidation protection ability. The as-coated samples have a good thermal shock resistance and no obvious damage was found in the coating even after suffered more than 11 thermal cycles between test temperature and room temperature. The oxidation protection mechanism of this coating was also discussed.     

炭/炭复合材料MoSi2/SiC抗氧化涂层的研究

采用包埋法制备C／C复合材料抗氧化MoSi2／SiC梯度涂层，同时对抗氧化涂层的形成、组织结构以及抗氧化性能与渗料的关系和抗氧化机理进行了研究。结果表明：采用包埋法制备的C／C复合材料抗氧化MoSi2／SiC梯度涂层致密，但有少量裂纹，涂层有良好的抗氧化效果。当Si与SiC保持一定的比例时，渗料中MoSi2的含量为50％时，涂层具有最好的抗氧化效果；当MoSi2与SiC保持一定的比例时，渗料中Si的含量为20％时，涂层具有最好的抗氧化效果。     

Dual layer SiC coating on matrix graphite sphere prepared by pack cementation and fluidized‐bed chemical vapor deposition

A dual layer silicon carbide (SiC) coating including inner porous SiC (p‐SiC) layer and outer dense SiC (d‐SiC) layer was fabricated on the matrix graphite (MG) spheres of high‐temperature gas‐cooled reactor fuel elements by pack cementation and fluidized‐bed chemical vapor deposition process to improve the oxidation‐resistant property. Microstructure of the coating demonstrates different density and structure of the two SiC layers with no obvious boundaries between them. Weight gain curves of oxidation tests at 1773 K for 200 hours show that the coating could effectively protected the MG sphere by isolating the air infiltration with p‐SiC layer as the main functional layer and d‐SiC layer as the transition layer to improve the bond strength. Due to the transition function of p‐SiC layer, the coated spheres could understand more than 50 times thermal shocking tests from 1773 K to room temperature with no stress cracking.