掺杂RE3+对CaAl2O4:Eu2+,Nd3+发光性能的影响

以燃烧法合成了CaAl2O4∶Eu2+,Nd3+,RE3+紫色长余辉发光材料。实验结果表明,掺杂辅助激活剂Pr3+和Ce3+对CaAl2O4∶Eu2+,Nd3+磷光体发光性能有明显影响。掺杂Pr3+的CaAl2O4∶Eu2+,Nd3+样品的发射峰蓝移;掺杂Ce3+的CaAl2O4∶Eu2+,Nd3+样品的发射峰红移。Pr3+或Ce3+掺杂,可以提高CaAl2O4∶Eu2+,Nd3+磷光体的初始亮度,Pr3+或Ce3+在其中起到增加陷阱密度,提高发光亮度的作用。     

Sr4Al14O25:Eu2+,Dy3+/TiO2-xNx复合材料制备及光催化性能

采用溶胶-凝胶法在长余辉发光材料(Sr4Al14O25:Eu2+,Dy3+)的表面包覆TiO2-xNx。利用X-射线衍射(XRD)、扫描电子显微镜(SEM)对复合材料的结构,形貌进行了表征;并研究了Sr4Al14O25:Eu2+,Dy3+/TiO2-xNx复合材料对甲基橙的光催化降解性能。     

燃烧法合成SrAl2O4∶Eu2+,Nd3+纳米长余辉发光材料

采用燃烧法合成了SrAl2O4∶Eu2+,Nd3+纳米长余辉发光材料。应用正交法优化了合成条件,得到最佳制备条件为,炉温在650℃,硼酸摩尔分数为0.10,n(Al)/n(Sr)为2.0,尿素加入4倍理论用量,Nd2O3物质的量为0.00025mol。研究结果表明,SrAl2O4纯相的铝锶比n(Al)/n(Sr)在1.5～2.0之间,铝锶比从1.0到3.5,依次得到Sr3Al2O6、SrAl2O4、Sr4Al14O25和SrAl12O19的纯相或混相样品。硼酸摩尔分数为0.10的样品发育较完全,晶化程度好。与高温固相法的样品相比,发射峰发生不同程度蓝移。样品平均晶粒尺寸小于100nm。     

PEG对燃烧合成CaAl204：Eu抖，Nd3＋长余辉发光材料的影响

采用燃烧法合成了CaAlO4 Eu2＋,Nd3＋什长余辉发光材料,研究了PEG（聚乙二醇）对其发光性能的影响。采用X-射线衍射（XRD）、荧光光谱对发光材料进行了表征。结果表明,燃烧产物主晶相为单斜晶系的CaAlO24;PEG的添加有效提高了CaAlzot：Eu2＋,Nd3＋长余辉发光材料的初始亮度,但余辉时间没有得到延长。     

Li2SrSiO4:Eu2+,Tb3+中Eu2+和Tb3+的发光特性和能量传递

用高温固相法在N2/H2=95/5(v/v)还原气氛下合成了Li2SrSiO4:Eu2+,Tb3+荧光粉发光材料,通过荧光光谱研究其发光特性,并从理论上探讨了Eu2+与Tb3+之间的能量转移类型。结果表明:该发光材料主发射峰值550nm,与Eu2+在4f7-4f65d1产生跃迁有关;通过掺杂,共存于Li2SrSiO4基质中的Tb3+通过电多级相互作用将能量传递给Eu2+;在500~650nm范围内对Eu2+具有很强的敏化作用,使其在主发射峰550nm的发射强度显著增强;当名义化学组成为Li2Sr0.995SiO4:0.005Eu2+,0.010Tb3+时,发光强度为最佳。     

Sr2+的掺入对CaAl2O4∶Eu2+,Nd3+,La3+陷阱分布和余辉性能的影响

用固相反应法制备了发射峰为446 nm的蓝紫色长余辉材料CaAl2O4∶Eu2+,Nd3+,La3+,它有两个激发峰276 nm和335 nm.Sr2+的加入使材料的激发和发射主峰向短波方向发生了移动.不同Sr2+含量样品的X射线衍射分析表明随着Sr2+含量的增加,材料中的杂相CaAl4O7逐渐消失,变为纯的CaAl2O4;从测得的相应的热释光曲线分析,热释峰由强度较弱、分布分散的5个峰(峰值温度分别为153,180,327,355 K和399 K),逐渐变为分布集中、强度较大的2个峰(峰值温度分别为175 K和346 K),这说明材料中的陷阱能级分布趋于集中.用一般阶动力学模型对热释光曲线进行拟合,得出了它们的陷阱参数.在Sr2+添加量为0.20 mol时,材料的余辉性能最好,它的两个热释峰所对应的陷阱深度分别为0.17 eV和0.37 eV.陷阱分布趋于集中的状况和合适的深度使材料的余辉性能得到了很大的提高.     

SrAl2O4:Eu2+,Dy3+,Pr3+纳米长余辉发光材料的制备与表征

以硝酸盐和尿素为基质,采用燃烧法在650℃合成了SrAl2O4:Eu2+,Dy3+,Pr3+长余辉发光粉体.研究了样品的晶体结构、晶粒大小及发光性能.结果表明:Eu2+,Dy3+,Pr3+共掺杂的磷光体没有改变铝酸锶的晶体结构,平均晶粒尺寸为41.5nm;激发和发射光谱分别为360nm和515nm的宽带谱,与SrAl2...     

水解对SrAl2O4∶ Eu2+,Dy3+稳定性的影响

研究了SrAl2O4: Eu2+, Dy3+长余辉材料在模拟潮湿环境条件下的稳定性.采用了2种模拟环境方法对样品进行了预处理.第1种方法为样品于室温条件下在去离子水中浸泡3 d; 第2种方法为样品在70 ℃的水中浸泡10 h,或者经过人工加速老化试验制备产物.结果显示: 第1种方法的预处理产物没有发生明显的分解,然而与未经处理的样品比较,发现其发光强度和发射光谱的峰值位置都发生了变化.而通过第2种预处理方法得到的产物发生了明显的分解分层.将溶液过滤蒸干得到两层的粉末状固体,分别记作上层产物和下层产物.通过X射线衍射和X射线能谱分析产物晶体结构,上层产物是Sr3Al2(OH)12,下层产物是Sr3Al2(OH)12和SrAl3O5(OH)的混合物.下层产物具有长余辉特性,为SrAl3O5(OH):Eu2+,Dy3+发光,发射光谱峰值位于485 nm,而原样品SrAl2O4: Eu2+, Dy3+的发射光谱峰值为520 nm.实验结果表明SrAl2O4: Eu2+, Dy3+长余辉材料在高温或潮湿条件中应用时,需要进行包膜处理.     

掺铕长余辉铝酸锌荧光粉合成条件研究

以ZnAc2、Al(NO3)3和Eu(NO3)3为原料,采用燃烧法制备掺杂Eu的ZnAl2O4:Eu2+长余辉荧光粉。探讨加入不同量的稀土Eu(NO3)3、不同燃烧温度和不同燃烧时间条件下,合成的ZnAl2O4:Eu2+长余辉荧光粉的发光效果。结果发现,当稀土加入量n(Eu)/n(Al)1/25,燃烧温度500～700℃,燃烧时间30 min时,制得的荧光粉发光效果最好。     

正交法优化纳米SrAl2O4:Eu2+,Dy3+制备工艺

采用溶胶-凝胶法合成了SrAl2O4:Eu2+,Dy3+纳米长余辉发光材料,利用正交设计法优化了制备工艺.在传统溶胶-凝胶法基础上,添加了硼酸,在950℃生成单一晶相,该法能使SrAl2O4生成温度降低150℃,生成的磷光体发光强度高、余辉时间长,平均晶粒尺寸为25～90nm.     

Modification of Optical Properties of SrAl_2O_4：Eu~（2＋）,Dy~（3＋） Phosphor by Terbium Doping

以尿素为燃料,采用快速燃烧法在650℃合成了Tb3＋掺杂的SrAl2O4：Eu2＋,Dy3＋新型长余辉光致发光材料。研究了Tb3＋掺杂对Eu2＋,Dy3＋共激活的铝酸盐长余辉发光材料的发光特性的影响。X射线衍射分析结果表明：当Tb3＋的掺杂量x=0.17%时,合成的样品结构为单相SrAl2O4单斜晶系。光致发光测试结果表明：样品的激发光谱为峰值位于345nm附近的连续宽带谱,发射光谱为峰值位于510nm左右的连续宽带谱。余辉衰减曲线结果表明：Tb3＋的适量掺杂可以提高铝酸锶的余辉性能。与SrAl2O4：Eu2＋,Dy3＋相比,掺杂Tb3＋有利于形成结晶度良好的固溶体,样品中的晶体细密紧凑,颗粒粒径约为100nm。     

Persistent deNOx Ability of CaAl2O4:(Eu, Nd)/TiO2-xNy Luminescent Photocatalyst

CaAl2O4:(Eu, Nd)/TiO2-xNy composite luminescent photocatalyst was successfully synthesized by a simple planetary ball milling process. Improvement of photocatalytic deNOx ability of TiO2-xNy, together with the persistent photocatalytic activity for the decomposition of NO after turning off the light were realized, by coupling TiO2-xNy with long afterglow phosphor, CaAl2O4:(Eu, Nd). The novel persistent photocatalytic behavior was related to the overlap between the absorption wavelength of TiO2-xNy and the emission wavelength of the CaAl2O4:(Eu, Nd). It was found that CaAl2O4:(Eu, Nd)/TiO2-xNy composites provided the luminescence to persist photocatalytic reaction for more than 3 h after turning off the light. GRAPHICAL CaAl2O4:(Eu, Nd)/TiO2-xNy composite luminescent photocatalyst with persistent deNOx activity after turning off the light was successfully synthesized by a simple planetary ball milling process. The novel persistent photocatalytic behavior was related to the overlap between the absorption wavelength of TiO2-xNy and the emission wavelength of the CaAl2O4:(Eu, Nd).     

多彩长余辉发光陶瓷的研究

采用高温固相反应法,分别制备了绿色(SrAl_2O_4:Eu~(2 ),Dy~(3 ))、蓝色(CaAl_2O_4:Eu~(2 ),Nd~(3 ))和红色(CaTiO_3:Pr~(3 ))长余辉发光材料。光谱分析表明,样品均在紫外至可见光范围内均能有效激发,SrAl_2O_4:Eu~(2 ),Dy~(3 )的发光峰值位于520nm,CaAl_2O_4:Eu~(2 ),Nd~(3 )的发光峰值位于440nm,CaTiO_3:Pr~(3 )的发光峰值位于612nm,用锌硼硅系统作为基础釉料,与发光材料混合制得发光釉料,在陶瓷基片上制备了具有一定图案的多彩长余辉发光陶瓷。     

Sr^2＋的掺入对CaAl2O4：Eu^2＋，Nd^3＋，La^3＋陷阱分布和余辉性能的影响

用固相反应法制备了发射峰为446 nm的蓝紫色长余辉材料CaAl2O4：Eu^2 ，Nd^3 ，La^3 ，它有两个激发峰276 nm和335 nm。Sr^2 的加入使材料的激发和发射主峰向短波方向发生了移动。不同Sr^2 含量样品的X射线衍射分析表明：随着Sr^2 含量的增加，材料中的杂相CaAl4O7逐渐消失，变为纯的CaAl2O4；从测得的相应的热释光曲线分析，热释峰由强度较弱、分布分散的5个峰(峰值温度分别为：153，180，327，355K和399K)，逐渐变为分布集中、强度较大的2个峰(峰值温度分别为175K和346K)，这说明材料中的陷阱能级分布趋于集中。用一般阶动力学模型对热释光曲线进行拟合，得出了它们的陷阱参数。在Sr^2 添加量为0．20 moll时，材料的余辉性能最好，它的两个热释峰所对应的陷阱深度分别为0．17 eV和0．37 eV。陷阱分布趋于集中的状况和合适的深度使材料的余辉性能得到了很大的提高。     

光照对Sr4Al14O25：Eu^2＋，Dy^3＋／TiO2-xNx复合材料光催化性能的影响

采用溶胶-凝胶法制备出Sr4Al14O25：Eu^2＋,Dy^3＋／TiO2-xNx复合材料。该复合材料对甲基橙具有较高的光催化效果,复合材料经紫外激发后,其光催化效果高于没有经紫外激发的复合材料的光催化效果,而且明显高于Sr4Al14O25：Eu^2＋,Dy^3＋／TiO2-xNx光照激发后光催化效率之和,同时讨论了Sr4Al14O25：Eu^2＋,Dy^3＋／TiO2-xNx复合材料的光催化机理。     

柠檬酸凝胶燃烧法制备Nd3+,Yb3+:Y2O3多晶原料及其相组成和荧光特性的研究

本文采用柠檬酸凝胶燃烧法合成了性能优良的Nd3+,Yb3+:Y2O3多晶原料。XRD、IR和SEM测试结果表明样品在900℃煅烧可获得纯相的Nd3+,Yb3+:Y2O3,平均粒径约为40 nm;TG-DTA测试结果表明样品在30～600℃之间失重约为49.28%;从荧光光谱上可以看出两个主要发射峰位于970～1100 nm之间,最强发射峰位于1030nm,对应Yb3+的2F5/2→2F7/2能级跃迁。     

Ca12Al14O33∶Eu2＋,Nd3＋长余辉发光粉的合成及其发光性能

采用燃烧法合成出Ca12Al14O33∶Eu2＋,Nd3＋靛蓝色长余辉发光粉.利用XRD和FE-SEM对产物的物相结构和形貌进行了表征,用激发光谱、发射光谱和余辉衰减曲线对样品的发光性能进行了分析.通过正交试验设计,以余辉时间为指标,研究了Eu2＋的掺杂量、Nd3＋的掺杂量、H3B03的用量以及尿素的用量对制备条件的影响.研究结果表明：最优化方案制备的Ca12Al14O33∶Eu2＋,Nd3＋长余辉发光粉的发射光谱呈宽发射谱带,波长范围为390～530 nm,发光峰值位于443 nm,余辉时间长达3240 s.     

水热法合成SrAl2O4:Eu2+,Dy3+长余辉材料

研究了SrAl2O4：Eu^2 ，Dy^3 长余辉材料的一种新合成方法。首先利用水热法制备出该发光材料的前驱体，然后将此前驱体粉体在还原气氛下高温烧结，得亮度高，余辉时间长的洲SrAl2O4：Eu^2 ，Dy^3 超细长余辉材料，并对其发光性能进行了研究。并对水热法和复合沉淀法合成的此种材料进行了比较。     

红色荧光粉CaWO4:Eu3+,Gd3+的合成及其发光性能的研究

利用高温固相法合成了CaWO4:Eu3+,Gd3+红色荧光粉,通过X射线衍射、X射线光电子能谱和荧光光谱等对该荧光粉进行了表征。结果表明,CaWO4:Eu3+,Gd3+的荧光强度明显高于CaWO4:Eu3+,钆离子的最佳掺杂量为0.04。同时说明了钆离子引入到CaWO4:Eu3+中对其发光性能影响的机理以及不同浓度的钆对发光强度的影响。