山西膨润土提纯、钠化研究及表征

选用山西钙基膨润土为原料,通过浸泡湿筛分级提纯,蒙脱石含量由40.8%增加到78.7%。在提纯土的基础上湿法钠化,通过化学分析、物化性能测试、XRD、差热分析和TEM等手段表征,当纯碱最佳用量为5%时,钠化后胶质价达到2195 mL/15 g、膨胀容达到96.5 mL/g,d（001）层间距从1.5546 nm变为1.2799 nm,钠化土的质量超过铸造土一级土要求。     

干法工艺制备钠化土的实验研究

采用干法工艺,即利用高速粉碎混合机对原土进行高混,常温自然放置进行充分钠化的方法,对甘肃平凉膨润土进行了钠化改性,就不同钠化剂(碳酸钠、氯化钠、氢氧化钠)的选择和配比、钠化高混时间、自然放置时间时钠化土性能的影响进行了研究.将干法制备的钠化土与涅法工艺进行了对比,在制备出性能较好的钠化土的同时,干法工艺具有流程简单、生产效率高等优点,能有效减少能耗、降低成本.用傅立叶红外变换光谱(FTIR)和X-射线衍射(XRD)对钠化土进行分析,发现钠化土在不改变原土结构的同时发生了阳离子交换,有效增大了原土的层问距.     

钙基膨润土锂改性工艺研究

对低品位钙基膨润土进行了锂盐改性研究,考察了锂盐加入量、反应时间、反应温度、固液比、pH值等工艺条件对锂化性能的影响.结果表明钙基膨润土锂改性后性能有较大的提高:24h膨润值和膨胀倍分别为原土的4.3和5.2倍,胶质价为原土的5.3倍.     

新疆乌兰陵格膨润土的开发及性能表征

以新疆乌兰陵格膨润土为原料,进行了原矿湿法提纯、钙基膨润土钠化改型及钠基膨润土有机化改性用于钻井油基泥浆的研究。结果表明,湿法提纯前钠基膨润土的蒙脱石含量为57.55%;提纯后蒙脱石含量为60.91%。而钙基膨润土蒙脱石含量为56.53%,提纯后蒙脱石含量为59.48%。Na2CO3作为改型剂使钙基土的CEC(阳离子交换容量)提高了26.7%,钠化改型后所制得的有机土的粘度达到0.840Pa·s。季铵盐用量在(8.5～9.0)×10-4mol/g时,D1631有机土的粘度出现了明显的突变点。FTIR表明有机插层剂已进入膨润土的层间。XRD特征峰位移表明膨润土的层间距有明显增加。SEM观察也表明膨润土的层间距增大,层间厚度约为72nm。将有机膨润土应用于钻井油基泥浆中,各项指标均已达到要求,研究表明新疆乌兰陵格膨润土的高附加值开发是可行的。     

钠基膨润土及制备工艺研究进展

介绍了国内外关于膨润土钠化改性的修饰原理、工艺及制备过程,阐述了常见钠化剂的选择和使用,以及评价钠基土的各种性能指标和分析方法,分析比较了3种钠化修饰工艺和钠基土生产的关键设备.     

膨润土的综合开发前景

膨润土是一种以蒙脱石为主的粘土。蒙脱石为含水铝硅酸盐矿物，它的矿物层间带有负电荷，能吸收Ca^2 、Mg^2 、K^ 、Na^ 等阳离子，并具有阳离子交换性质。膨润土吸水后蒙脱石层间能沿C轴方向膨胀，分散于水中可形成性能良好的凝胶。天然膨润土一般多为钙基膨润土，其物化性质不甚理想，如将其加工成钠基膨润土、提纯膨润土、颗粒膨润土、有     

新疆夏子街钙基膨润土的高附加值开发

以新疆夏子街钙基膨润土为原料,进行了原矿湿法提纯、钠化改性及钠基土有机化改性及其应用研究.结果表明,湿法提纯前钙基膨润土的蒙脱石含量为91.79%,是一种高品位钙基膨润土,提纯后蒙脱石含量达到95.97%.钠化正交实验结果表明,NaF效果优于传统的钠化剂Na2CO3.在优化条件下钠化改性膨润土的阳离子交换容量(CEC)可达97.5 mmol/100g土,比原矿提高17.25 mmol/100g土.以钠化改性膨润土为原料制得的有机膨润土的粘度达到5.4 Pa*s.FTIR表明有机插层剂已进入膨润土的层间.XRD特征峰位移表明有机膨润土的层间距达到2.143 nm,比钙基膨润土层间距增加0.754 nm.SEM得到的结论与FTIR、XRD表征结果相吻合.将有机膨润土应用于涂料中,其各项检测指标均满足要求.有机膨润土对于金属离子废水的吸附效果优于钙基膨润土.由此可知新疆夏子街钙基膨润土的高附加值开发是可行的.     

利用钙基膨润土合成有机膨润土的工艺研究

以天然钙基膨润土为原料，进行了有机膨润土的合成试验．研究了不同有机改性剂的改性效果以及有机改性剂的用量、反应时间、反应温度对有机土性能的影响。研究表明，采用天然钙基膨润土通过钠化提纯、季铵盐有机改性的方法，可以制备出性能优良的有机膨润土。通过对钠化改性和有机改性样品的结构参数和性能研究表明：钠化处理后，蒙脱石的d(001)值由15．40A减小为12．65A．离子交换容量由58．75mmol／100g增加为117．80mmol／100g．钠化膨润土经过不同有机季铵盐处理后，有机蒙脱石的d(001)增大为17～29A，并随着结构参数的不同，所合成的有机凝胶性能不同。     

正交实验法制备有机膨润土研究

以天然钙基膨润土为原料，经碳酸钠钠化后，用溴代十六烷基三甲胺进行有机包覆，制得有机膨润土；通过TG分析和正交实验，探讨了有机膨润土结构及最佳制备工艺。     

铁硅改性膨润土对废水有机污染物的吸附性能研究

以钠基膨润土为原料，制备了铁硅交联土、铁硅有机复合土，以CODCr的去除率为指标，对原土、铁硅交联土、铁硅有机复合土进行了筛选，结果表明：铁硅有机复合土对CODCr的去除率明显好于铁硅交联土和原土；将铁硅有机复合土应用于造纸废水，探讨了其用量、废水PH值、搅拌时间等对CODCr去除率的影响，通过正交实验确定了最佳条件，并在此条件下考察了其对废水CODCr、色度、浊度的去除率，结果表明：以上指标分别可达到87．69％、98．00％、98．18％；最后对铁硅改性膨润土对废水有机污染物的吸附机理进行了探讨。     

新型有机膨润土用于印染废水处理的实验研究

采用二乙烯三胺、环氧氯丙烷合成了一种阳离子型铵盐,用其与十六烷基三甲基溴化铵对钠基膨润土进行复合插层改性,制备得到一种新型有机膨润土;以模拟染料废水和实际印染废水为处理对象,使用改性膨润土进行了吸附脱色实验,吸附完成后加入聚合氯化铝混凝。实验结果表明,与单独投加聚合氯化铝相比,采用改性膨润土吸附后再混凝的方法处理废水,可显著提高脱色率和COD去除率;处理活性艳红X-3B、酸性大红GR与活性艳蓝X-BR三种模拟染料废水时,脱色率分别可达99.4%、84.8%和96.1%;以中试规模处理实际印染废水调节池原水时,COD和色度去除率分别可达51.6%和85.9%;处理实际印染废水好氧生化出水,COD可由121.3mg/L降至65.4mg/L,色度由32倍降至8倍以下。     

有机膨润土的制备及其在涂料中的应用

以内蒙古某地天然膨润土为原料，探讨了有机膨润土制备的最佳工艺并用红外光谱仪对产品进行了表征。流变性实验表明，有机膨润土是一种非牛顿型触变体系，对改善涂料的使用性能非常有效。     

膨润土锂化工艺研究

通过对膨润土锂化改性及其过程各主要因素的讨论．得出锂基膨润土制备的最佳工艺。并对在最佳条件下制得的改性膨润土进行了物化性能测试和分散性实验．结果表明．改性膨润土的分散性、悬浮性、吸附性均得到很大的提高。     

Nano‐addition of raw bentonite enhances polypropylene (PP) properties

Bntonite (BNT) is the cheapest raw material source for making commercial nanoclay, which is approximately 250 times more expensive than BNT. Perhaps this may be one of the reasons why we do not find a translation of good scientific work on polymer nanocomposites into commercial reality. In this work, it is demonstrated that PP nanocomposites were made using 3% raw bentonite via Master batch (MB) route with maleated PP. This product has 9.5% greater tensile strength, 18.6% greater flexural strength, and 27% greater flexural modulus than neat PP. The repeat extrusion of PP/bentonite was carried out, which had beneficial effects on tensile modulus and flexural strength and less so on other properties. This study opens a Pandora's box full of possibilities, such as cheap polymer nanocomposites being available for many different applications. Increase in the previously mentioned properties of PP‐BNT adduct cannot be explained by the nucleation effect of BNT on PP. X‐ray diffraction, internal surface area, TGA, and DSC measurements were made on the above samples. Addition of 3% raw bentonite increases the crystallization of PP by 7.5°C (nucleation effect). Since this is just a pilot study, this opens a vast commercial scope for making nanocomposites from raw clays. The stakes for doing this are very high, because BNT is $0.10/kg and can be available consistently from mineral producers in Gujarat and Rajasthan in India. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 99: 1004–1009, 2006     

膨润土制备A型分子筛的实验研究

以膨润土为基础原料 ,用低温水热合成技术合成A型分子筛。探讨了残存膨润土、碱度、晶化温度、晶化时间对反应的影响。     

十六烷基溴化铵有机改性天然钠基膨润土的研究

本论文以吉林省刘房子天然钠基膨润土为原料,十六烷基溴化铵为改性剂对钠基膨润土进行有机改性。以灼失率为指标,获得了制备有机膨润土的最佳条件,反应温度为70℃,反应时间为1h,pH值为9,改性剂用量为阳离子交换容量CEC的150%,并通过X-射线衍射、红外光谱分析手段对有机膨润土的结构进行了表征。     

球团矿中膨润土的作用机理研究

本文从机理方面详尽介绍了膨润土对球团性能的影响，并在文章中引入了膨润土纤维结构的观点．同时对润磨工艺进行了研究，结果表明：润磨有利于纤维结构的形成．可提高生球强度，降低膨润土用量和提高预热球、成品球的强度。     

膨润土载体缓释肥料的制备工艺优化

以天然廉价的多孔矿物膨润土作为磷酸二氢铵的载体,再加入脲醛树脂胶粘剂经混合、压片固化制得膨润土载体缓释胞。通过单因素实验,考察了膨润土类型、土肥比（膨润土与磷酸二氢铵的质量比,下同）、脲醛树脂用量（以土肥总量计,下同）、碳酸铗用量（以土肥总量计,下同）对缓释肥缓释效果的影响。结果表明,在以钠基膨润土为载体、土肥比为8;2、脲醛树脂用量为20％、碳酸镁用量为9％的条件下,所制得的膨润土载体缓释肥料的缓释效果最好。     

Adsorption of methylene blue and zinc ions on raw and acid-activated bentonite from Morocco

Adsorption of methylene blue (BM) and zinc ions on raw and acid-activated Moroccan bentonite composed of montmorillonite (88 mass%), a mixture of quartz and K-feldspar (9 mass%), calcite (3 mass%) and insignificant amounts of organic matter was evaluated at 25 °C using UV–visible and atomic absorption spectrometry. The adsorption capacity of MB and Zn ions by raw bentonite were about 2.2 and 1.1 mmol/(g of bentonite) and the best-fit isotherm models were those of Harkins–Jura and Langmuir. Acid-activation of the bentonite reduced the maximum uptake of MB and Zn ions by 30 and 95% and the best-fit models of the isotherms were Freundlich and Dubinin–Radushkevich for MB and Zn ions respectively. The reduced adsorption was associated with partial collapse of the montmorillonite particles and the formation of amorphous silica.