TA1表面制备Ni/Al涂层的反应扩渗及抗氧化行为

为了提高纯钛的高温抗氧化性能,采用电弧喷涂和等离子喷涂方法在纯钛表面制备Ni/Al涂层.对试件进行900℃×5 h热处理后,再进行900℃×40 h连续氧化实验,探索其高温抗氧化行为.结果表明,经过表面改性处理的Ni/Al涂层可以显著提高纯钛的高温抗氧化性.在热处理过程中Ni/Al涂层中的Al发生熔化扩散并与Ni和Ti形成以NiAl与TiAl₃相为主的扩散层.在氧化过程中Ni/Al涂层表面形成连续且致密的α-Al₂O₃,同时表面扩散层中的富铝相可为涂层表面提供充足的Al元素,进而对纯钛基体提供有效的高温抗氧化保护作用.     

TA1表面制备Ni/Al涂层的反应扩渗及抗氧化行为

为了提高纯钛的高温抗氧化性能,采用电弧喷涂和等离子喷涂方法在纯钛表面制备Ni/Al涂层.对试件进行900 ℃×5 h热处理后,再进行900 ℃×40 h连续氧化实验,探索其高温抗氧化行为.结果表明,经过表面改性处理的Ni/Al涂层可以显著提高纯钛的高温抗氧化性.在热处理过程中Ni/Al涂层中的Al发生熔化扩散并与Ni和Ti形成以NiAl与TiAl₃相为主的扩散层.在氧化过程中Ni/Al涂层表面形成连续且致密的α-Al₂O₃,同时表面扩散层中的富铝相可为涂层表面提供充足的Al元素,进而对纯钛基体提供有效的高温抗氧化保护作用.     

NiAl/Al复合涂层高温抗氧化性能与扩散机制

为了延长纯钛在高温环境下的工作寿命,采用电弧喷涂方法在纯钛表面制备了NiAl/Al复合涂层.在热处理炉中进行800℃×50 h连续氧化实验,根据NiAl层与纯Al层反应生成的金属间化合物性能,考察涂层的高温抗氧化行为和高温防护机制.结果表明,复合涂层在体系中具有足够的Al、Ni元素,可在涂层外表面形成以Al₂O₃为主的氧化物防护层,从而阻碍氧向内侵入.在高温氧化过程中NiAl/Al涂层中的Al发生熔化扩散,并与Ni和Ti形成以NiAl、Ni₂Al₃、NiAl₃及TiAl₃富Al相为主的扩散阻挡层.NiAl/Al复合涂层显著提高了纯钛的高温抗氧化能力.     

NiAl/Al复合涂层高温抗氧化性能与扩散机制

为了延长纯钛在高温环境下的工作寿命,采用电弧喷涂方法在纯钛表面制备了NiAl/Al复合涂层.在热处理炉中进行800 ℃×50 h连续氧化实验,根据NiAl层与纯Al层反应生成的金属间化合物性能,考察涂层的高温抗氧化行为和高温防护机制.结果表明,复合涂层在体系中具有足够的Al、Ni元素,可在涂层外表面形成以Al₂O₃为主的氧化物防护层,从而阻碍氧向内侵入.在高温氧化过程中NiAl/Al涂层中的Al发生熔化扩散,并与Ni和Ti形成以NiAl、Ni₂Al₃、NiAl₃及TiAl₃富Al相为主的扩散阻挡层.NiAl/Al复合涂层显著提高了纯钛的高温抗氧化能力.     

Ti表面改性Al涂层及其抗氧化性能

为了提高钛材的抗高温氧化性能,利用电弧喷涂工艺方法在工业纯钛表面制备了纯Al涂层,对喷涂态纯Al涂层分别进行炉中加热及激光重熔改性处理,以得到具有一定抗高温氧化性能的Ti-Al金属间化合物涂层.对改性处理后的试件进行了800℃/60 h的氧化试验.结果表明,经750℃/5 h炉中加热改性处理后,钛基体表面可形成厚约300μm的TiAl_3金属间化合物层,而经激光重熔改性处理后,钛基体表面形成的TiAl_3金属间化合物层较薄.经高温氧化试验后,炉中加热改性Al涂层的微观组织形貌未发生明显变化,而激光重熔改性Al涂层的微观组织形貌变化较为明显.相比于激光重熔改性处理,经炉中加热改性处理后Al/Ti试件的抗高温氧化性能更佳.     

激光重熔等离子喷涂涂层研究现状与展望

综述了等离子喷涂涂层的激光重熔表面技术的研究现状,从激光重熔机理和等离子喷涂涂层的特征,分析了激光重熔后涂层的组织结构和性能变化,介绍了激光重熔的数值模拟,探讨了激光重熔等离子喷涂层工艺过程中存在的一些问题和解决途径以及今后的发展方向.     

Al涂层对Ni基合金高温氧化性能的影响

为了研究Al涂层对Ni基合金高温氧化性能及氧化机理的影响,采用磁控溅射方法在Ni基合金表面制备了Al涂层,在600℃下对涂层进行了真空扩散退火和预氧化处理,并研究了涂层在1 100℃下的高温氧化性能.利用扫描电子显微镜和能谱仪分析了氧化膜的截面形貌及组成.结果表明,Ni基合金氧化动力学曲线近似服从抛物线规律,且合金的氧化增重最大.经过1 100℃高温氧化后,Ni基合金表面形成三层氧化膜,外层为Ni O、Cr_2O_3、Al_2O_3的混合氧化物和少量尖晶石氧化物,中间层主要为Ni的氧化物,内层为Al_2O_3.Al涂层试样的氧化增重相对较小,表明Al涂层在一定程度上提高了Ni基合金的抗氧化性能.     

TiAl合金电弧喷涂Al涂层的高温氧化性能

为了提升TiAl合金的高温抗氧化能力,采用电弧喷涂工艺在TiAl合金表面制备了纯铝涂层,并分别在900℃和1 000℃进行了恒温氧化试验.通过绘制氧化动力学曲线,对比了有无涂层试样的抗氧化性能.运用SEM、EDS、EPMA和XRD分析其氧化前后涂层的微观形貌、成分组成、元素分布和相组成.结果表明：纯铝涂层均匀致密、无裂纹.在900℃空气中氧化100 h后,涂层表面形成了致密的Al₂O₃氧化膜,次表层为TiAl₃相,扩散层为TiAl₂相.在1 000℃空气中氧化100 h后,涂层表面氧化膜由Al₂O₃和少量TiO₂组成,次表层为TiAl₃相,扩散层为TiAl₂相.电弧喷涂铝涂层提高了TiAl合金的高温抗氧化能力.     

激光重熔对氧化铝涂层的组织结构及性能的影响

用ＲＳ—１７００ＳＭ型轴流式ＣＯ２激光器对Ａｌ２Ｏ３涂层进行了重熔，降低了原始涂层中的孔隙，消除了涂层的层状结构，得到了致密均匀的涂层，使重熔层的显微硬度明显提高．高温氧化试验表明：激光表面重熔提高了Ａｌ２Ｏ３涂层的抗高温氧化性     

304N不锈钢表面电弧喷涂复合涂层高温氧化防护机制

为了延长奥氏体不锈钢部件在高温环境下的工作寿命,采用电弧喷涂方法在304N不锈钢表面制备45CT/Al复合涂层,对复合涂层试件进行1 100℃×350 h的连续氧化实验,考察其高温氧化行为,通过研究复合涂层的微观组织变化,探索其高温防护机制.实验结果表明,复合涂层以两种方式为304N不锈钢基体提供有效的高温氧化保护.一方面保证在涂层体系中具有足够的Al、Cr元素,在涂层外表面形成以Al2O3为主的氧化物防护层,阻止氧化介质的向内侵入;此外,在复合涂层下的基体金属中形成层状分布的AlN扩散阻挡层,延缓复合涂层体系中Al、Cr抗氧化元素的质量分数减少,使复合涂层保持持久的高温氧化防护能力.     

Oxidation performance of Fe-Al/WC composite coatings produced by high velocity arc spraying

Fe-Al intermetallics with remarkable high-temperature intensity and excellent erosion, high-temperature oxidation and sulfuration resistance are potential low cost high-temperature structural materials. But the room temperature brittleness induces shape difficult and limits its industrial application. The Fe-Al intermetallic coatings were prepared by high velocity arc spraying technology with cored wire on 20G steel, which will not only obviate the problems faced in fabrication of these alloys into useful shapes, but also allow the effective use of their outstanding high-temperature performance. The Fe-Al/WC intermetallic composite coatings were prepared by high velocity arc spraying technology on 20G steel and the oxidation performance of Fe-Al/WC composite coatings was studied by means of thermogrativmetic analyzer at 450, 650 and 800°C. The results demonstrate that the kinetics curve of oxidation at three temperatures approximately follows the logarithmic law. The composition of the oxidized coating is mainly composed of Al₂O₃, Fe₂O₃, Fe₃O₄ and FeO. These phases distribute unevenly. The protective Al₂O₃ film firstly forms and preserves the coatings from further oxidation. Foundation item: Project(50235030) supported by the National Natural Science Foundation of China; Project(98BK014) supported by the Foundation of State Economy Trade Committee of China     

Oxidation performance of Fe-Al/WC composite coatings produced by high velocity arc spraying

Fe-Al intermetallics with remarkable high-temperature intensity and excellent erosion, high-temperature oxidation and sulfuration resistance are potential low cost high-temperature structural materials. But the room tem perature brittleness induces shape difficult and limits its industrial application. The Fe-Al intermetallic coatings were prepared by high velocity arc spraying technology with cored wire on 20G steel, which will not only obviate the problems faced in fabrication of these alloys into useful shapes, but also allow the effective use of their outstanding high-temperature performance. The Fe-Al/WC intermetallic composite coatings were prepared by high velocity arc spraying technology on 20G steel and the oxidation performance of Fe-Al/WC composite coatings was studied by means of thermogrativmetic analyzer at 450, 650 and 800 ℃. The results demonstrate that the kinetics curve of oxidation at three temperatures approximately follows the logarithmic law. The composition of the oxidized coating is mainly composed of Al2 O3, Fe2 O3, Fe3 O4 and FeO. These phases distribute unevenly. The protective Al2 O3 film firstly forms and preserves the coatings from further oxidation.     

激光熔覆Ni+Cr_2O_3复合涂层的耐蚀性

研究了激光搭接熔覆Ni+Cr2 O3复合涂层在 0 .5mol/LH2 SO4 +0 .5mol/LNaCl水溶液中的电化学行为 .试验表明Cr2 O3粒子在激光熔池中发生了完全溶解 ,涂层具有胞状枝晶组织特征 .激光熔覆Ni+Cr2 O3复合涂层比单一熔覆Ni合金涂层和 2Cr13马氏体不锈钢基材具有更低的维钝电流密度和更宽的钝化区范围 ,明显改善了在该腐蚀介质中的抗点蚀能力 .     

Cr-Si-Al复合涂层的结构与耐蚀耐热性研究

应用Ｐ－Ｃ法对中碳钢进行Ｃｒ－Ｓｉ－Ａｌ复合涂覆,用光学显微镜观察了涂层的形貌。用电子 探针及扫描电镜测定了涂层的表面成分及Ｃｒ,Ｓｉ,Ａｌ在涂层中的分布,用Ｘ射线衍射测定了涂层的结构。将经涂覆后的试样进行盐水腐蚀和高温氧化试验,结果表明,其耐蚀和抗氧化性大幅度提高。     

锅炉受热面NiCr涂层抗高温热腐蚀机制与性能的研究

针对电站锅炉受热面高温腐蚀的影响,通过采用电弧喷涂工艺,研究了Q235钢板表面电弧喷涂PS45、FeCrAl、4Cr13合金涂层后在高温条件下的热腐蚀机制与性能.热腐蚀动力学试验和分析结果显示,在700℃下腐蚀77 h、Na2SO4＋K2SO4盐膜量为3-4 mg/cm2的试验条件下,测试得到的PS45、FeCrAl、4Cr13合金涂层的热腐蚀速度分别为υ=0.38t-0.59、υ=1.35t-0.12和υ=1.79t-0.23.涂层表面的成分和组织分析结果表明,Q235钢板表面的PS45涂层之所以表现出比FeCrAl、4Cr13涂层更高的抗热腐蚀（Na2SO4/K2SO4）性能,其原因在于PS45镍基合金中含有最多的Cr,涂层表面的Cr2O3膜层具有较高的连续性、致密性和稳定性.     

锅炉受热面NiCr涂层抗高温热腐蚀机制与性能的研究

针对电站锅炉受热面高温腐蚀的影响,通过采用电弧喷涂工艺,研究了Q235钢板表面电弧喷涂PS45、FeCrAl、4Cr13合金涂层后在高温条件下的热腐蚀机制与性能.热腐蚀动力学试验和分析结果显示,在700℃下腐蚀77 h、Na2SO4+K2SO4盐膜量为3~4 mg/cm2的试验条件下,测试得到的PS45、FeCrAl、4Cr13合金涂层的热腐蚀速度分别为υ=0.38t-0.59、υ=1.35t-0.12和υ=1.79t-0.23.涂层表面的成分和组织分析结果表明,Q235钢板表面的PS45涂层之所以表现出比FeCrAl、4Cr13涂层更高的抗热腐蚀(Na2SO4/K2SO4)性能,其原因在于PS45镍基合金中含有最多的Cr,涂层表面的Cr2O3膜层具有较高的连续性、致密性和稳定性.     

Effect of nano-size nickel particles on wear resistance and high temperature oxidation resistance of ultrafine ceramic coating

1　INTRODUCTIONImprovementsinaerogasturbineengineandartilleryrecoilabsorberperformanceintermsofpower ,efficiencyandmassnecessitatetheuseofhighspecific strengthandlow densitymaterials,whichresultsinthedevelopmentofawiderangeoftitaniumalloysinthecompressorsectionof modern gasturbinesandartilleryrecoilabsorber .Titaniumalloys,ingeneral,easilyabsorboxygen ,leadingtooxidationandalphaphaseformationwhenexposedtohightemperature ( >5 0 0℃ )inair,whichlimitsthehightemperaturecapabilityofalloysdueto…