The surface morphologies and spectroscopy analysis of VC coatings on the substrate of Cr12MoV prepared by TD process after salt spray

The normal temperature corrosion of VC coating on the substrate of Cr12MoV prepared by TD process was tested in 5% NaCl aqueous solution, its surface morphologies and corrosion components after salt spray were observed with SEM and EDS, respectively, and the effects of salt spray on micro-structures of VC coating were analyzed. Moreover, the invalidation mechanism of VC coating after salt spray and its effect on substrate material were discussed. The experimental results shown that the uniformity and integrity of VC coating surface are destroyed by salt spray for 120 h, a large number of the pits are produced on the coating surface, and the coating falls off, which speeds corrosion breakage of its substrate; the oxidated film on its surface becomes rougher, broken and discontinuous, and falls off easily, which reduce the ability of resistance salt spray; the failure modes of VC coating after salt spray are expressed with falling off of oxidated film, stress concentration and pore effect and so on, the corrosion breakage of oxidated film is the corrosion result of deoxidization corrosion from oxygen and HCl produced by NaCl and vapor.     

Microstructure and Properties of Graphene Oxide-doped TiO_2 Coating on Titanium by Micro Arc Oxidation

Micro arc oxidation(MAO) coatings doped with graphene oxide(GO) were prepared on pure titanium by adding GO and sodium dodecyl benzene sulfonate(SDBS) into a sodium silicate solution. The as-deposited coatings were comparatively analyzed by scanning electron microscopy(SEM), energydispersive X-ray spectroscopy(EDS) and X-ray diffraction(XRD). The binding forces of the MAO, MAO+GO and MAO+GO+SDBS three coatings were measured by a scratch tester. The mechanical property of the three coatings was analyzed using the nano-indentation technique. The corrosion resistance of the coatings was tested by the electrochemical system in 3.5% NaCl solution. The photocatalytic activity of the prepared samples was evaluated by determining the degradation of methylene blue(MB) solution. The results showed that compared to the MAO coating, the morphologies and phase compositions of MAO+GO and MAO+GO+SDBS composite coatings were significantly different. These two composite coatings all had superior photocatalytic activity. Especially, the MAO+GO composite coating still had enhanced binding force and excellent corrosion resistance. Furthermore, the relationship between the microstructure and the properties of these three MAO coatings was analyzed.     

低温烧结活性瓷釉涂层钢筋耐腐蚀性能试验研究

为了研究低温烧结活性瓷釉（LTCRE）涂层的性能和机理,利用差示扫描量热法（DSC）和热重法（TG）对LTCRE涂层的烧结温度进行优化,采用扫描电子显微镜（SEM）、X射线能谱分析（EDS）和X射线衍射（XRD）分析涂层微观结构和腐蚀过程,通过中性盐雾试验和氙灯老化试验研究LTCRE涂层钢筋的耐腐蚀性能. LTCRE涂层的优化烧结温度为500~540 °C,涂层具有结构致密、孔隙率低的特点,LTCRE涂层钢筋在腐蚀后的质量变化为普通钢筋的1.6%,800 h盐雾腐蚀后人为缺陷孔的剥离半径为0.26 mm,在氙灯照射下耐老化时长超过500 h. 结果表明,LTCRE涂层作为无机陶瓷涂层,具有比环氧树脂涂层更优异的耐老化性能,具备长期稳定的耐腐蚀能力. 涂层密实少孔的结构和烧结时良好的化学反应使得LTCRE涂层钢筋能够有效阻止外界腐蚀物质渗入与蔓延,即使在缺陷孔发生腐蚀后也能够阻止腐蚀加剧,起到涂层自愈合的效果.     

氢氧化钠溶液对硼硅酸盐玻璃光学和润湿性能的影响

为低成本提高硼硅酸盐玻璃光学和润湿性能,采用化学刻蚀法在玻璃表面制备具有减反和自清洁性能的薄层.利用NaOH溶液对预处理后的玻璃进行化学刻蚀,采用扫描电镜(scanning electron microscopy,SEM)对刻蚀前后玻璃表面形貌进行了观察,通过调控刻蚀液浓度,分别采用分光光度计和接触角仪测量玻璃表面的透光率和接触角随浓度的变化趋势.结果表明:经0.05 mol/L的氢氧化钠溶液刻蚀后,在表面形成长约为100 nm、宽约为10nm、分布比较均匀的细微沟槽,玻璃的透过率达94.85%,比原始基片提高了4.15%,接触角从53.13°降至3.25°,玻璃的光学性能和自清洁性能得到了有效的提高.     

硫脲对Ni-P镀层腐蚀行为的影响

在镀液中添加硫脲,分析了硫脲对Ni-P镀层沉积速度、表面形貌、孔隙率等的影响,并通过极化曲线和交流阻抗测试了硫脲对Ni-P镀层腐蚀性的影响。结果表明,当镀液中添加1 mg/L硫脲时,镀层的沉积速率加快,腐蚀速率增大。这主要是因为镀液添加硫脲后,镀层的孔隙率加大,促进了腐蚀介质渗入到基体表面,增加了腐蚀微电池的数量,形成了大阴极(镀层)-小阳极（基体）腐蚀微电池,使自腐蚀电流密度增大,电荷转移电阻减小。当镀液中添加硫脲质量浓度大于3 mg/L时,镀液被毒化,无法施镀。     

Effect of Various Additives on Performance of Plasma Electrolytic Oxidation Coatings Formed on AZ31 Magnesium Alloy in the Phosphate Electrolytes

Plasma electrolytic oxidation(PEO) coatings were prepared on AZ31 magnesium alloy using alkaline phosphate as base electrolyte system, and with the addition of sodium silicate(Na_2SiO_3), sodium aluminate(NaAlO_2) and potassium fluorozirconate(K_2ZrF_6) as additives. The microstructure, phase composition and element composition as well as surface profile of the PEO coatings were analyzed by means of scanning electron microscopy(SEM), X-ray diffraction(XRD), energy dispersive X-ray spectroscopy(EDS), and threedimensional(3 D) optical profilometry. The corrosion and wear properties were evaluated by electrochemical potentiodynamic polarization in 3.5 wt% Na Cl solution and ball-on-disc wear tests, respectively. The results showed that the anions of the additives effectively participated in the coating formation influencing its microstructural features, chemical composition, corrosion resistance and tribological behaviour. It was observed that the sample treated by PEO in the electrolyte solution containing K_2ZrF_6 as an additive showed better corrosion and abrasive resistance.     

Ce改性AZ91的微弧氧化膜制备及其耐蚀性能

利用交流恒压微弧氧化技术, 通过Ce改性镁合金基体制备高耐蚀微弧氧化膜. 在100、120和 140 V的外加电压下, 对3种试样: AZ91, 质量分数w(Ce) 分别为0.92%和1.80%改性的AZ91微弧氧化过程、微观结构和组成及氧化膜的耐蚀性能进行研究. 应用电子扫描显微镜(SEM), 电子能谱（EDS）和X射线衍射（XRD）等表征氧化膜的微观结构和化学组成. 利用稳态极化曲线和电化学阻抗谱（EIS）测试了氧化膜在质量分数w(NaCl)为3.5%的溶液中的腐蚀过程. 实验结果表明氧化膜成膜过程可以分为3个阶段; 氧化膜主要由MgO组成, 镁合金中的稀土元素Ce促进成膜过程, 增加膜层的致密性; 稀土改性后镁合金氧化膜的耐蚀性比镁合金基体提高4个数量级, 腐蚀电流密度低至10^-8 A/cm2．     

Sol-gel Preparation Copper-cadmium Halide Doped Photochromic Glass Coating on Plate Glass

Copper-cadmium halide doped photochromic glass coating on plate glass has been prepared by a sol-gel process. The sample shows reversible photochromic effect. The results of X-ray diffraction (XRD) and infrared (IR) spectrum investigations indicate that the photochromic phase of tile coating is CuBr_xCl_(1-x), solid solution, and that the structure network of the coating is connected with the bonds of Si-O-Si, Si-O-B and Si-O-Al.     

电镀法制备Ni-W合金镀层的耐盐雾腐蚀性能

利用电镀法在N80钢表面制备了Ni-W合金镀层,用SEM、EDS分析了镀层表面与界面形貌以及化学元素的分布,通过XRD测试了镀层物相的组成。在5% NaCl溶液中测试了镀层盐雾腐蚀能力,分析了Ni-W镀层抗盐雾腐蚀机理。试验结果表明,镀层厚度约40m,主相为Ni-W,Ni和W以金属形式存在于镀层中;经过高温热处理后,镀层与基体发生了化学元素扩散现象,形成冶金结合;盐雾腐蚀后镀层表面腐蚀物为Fe的氧化物和氯化物,基体无腐蚀现象发生。     

KINETIC FACTORS AFFECTING THE CORROSION OF SiO_2 IN SILICATE GLASSES CAUSED BY ALKALINE SOLUTIONS

The corrosion of a ZrO_2 containing alkali re-sistant silicate glass,float glass and silica glass caused by theaqueous solution of NaOH was studied by use of correlationmethod with spectrophotometry. Effects of the corroding tem-perature,time and solution concentration on the rate of reac-tion and the degree of corrosion were investigated;effects ofthe apparent activation energy and the experimental value offrequency factor on the rate constant were discussed.     

Corrosion resistance of plasma sprayed NiCrAl (ZrO_2 Y_2O_3) thermal barrier coating on 18-8 steel surface

1INTRODUCTION Austeniticstainlesssteelisdevelopedtocom pensateforpoorcorrosionresistanceofmartensite stainlesssteelandoverlargebrittlenessofferrite stainlesssteel.Basicconstituentsofitstypicalal loyare18%Crand8%Ni(massfraction),which isusuallycalledas188s…     

氩弧熔覆镍基自熔合金的工艺研究

采用氩弧熔覆工艺在Q235钢基体上获得了F102Fe镍基合金熔覆层.测试了涂层的硬度和耐腐蚀性，借助光学金相显微镜、扫描电子显微镜观察其显微组织，进而对熔覆工艺、合金组织及熔覆层性能之间的关系进行详细阐述.研究结果表明，采用氩弧熔覆工艺可以在Q235钢基表面上获得与基体结合良好、组织细密、具有较高硬度和耐蚀性的F102Fe合金熔覆层.在相同的情况下，增加电流强度或减少熔覆层的厚度，组织由共晶向亚共晶转变；随熔覆层的硬度、耐蚀性降低，塑性有所改善.     

Characterization and wear behavior of WC-0.8Co coating on cast steel rolls by electro-spark deposition

To prepare high wear resistance and high hardness coatings, electro-spark deposition was adopted for depositing an elec trode of a mixture of 92wt%WC+8wt%Co on a cast steel roll substrate. The coating was characterized by classical X-ray diffracto meter (XRD) and scanning electron microscopy (SEM) with energy dispersive X-ray analysis (EDX). The results indicate that the coating shows nanosized particulate structure and dendritic structure including columnar structure and equiaxed structure. The pri mary phases of the coating contain Fe_3W_3C, Co_3W_3C, Fe_2C and Si_2W. The coating has a low friction coefficient of 0.13, its average wear-resistance is 3.3 times that of the cast steel roll substrate and the main mechanism is abrasive wear. The maximum microhard ness value of the coating is about 1573.9 Hv_(0.3) The study reveals that the electro-spark deposition process has the characteristic of better coating quality and the coating has higher wear resistance and hardness.     

铝合金支撑MFI型分子筛膜的合成及耐蚀性能研究

2024型铝合金被广泛应用在航天航空工业,但其耐蚀性差.为改善这一缺点,用原位水热合成法在2024型铝合金表面合成MFI型分子筛膜.采用SEM/EDS对分子筛膜的表面形貌和元素组成进行表征;研究晶化时间对分子筛膜致密性的影响;研究该分子筛膜在中性NaCl、pH=1.0的NaCl-HCl和pH=13.0的NaCl-NaOH介质中的耐蚀性能.结果表明：晶化16 h在合金表面形成的分子筛膜均匀且致密,耐蚀性最好,腐蚀电流密度为0.241 A/cm2,远小于裸铝合金的腐蚀电流密度57.140 mA/cm2,确定为最佳晶化时间;3种介质比较,在碱性和中性NaCl介质中耐蚀性好,尤其在pH =13.0的NaCl-NaOH溶液中耐蚀性最佳,并且在该介质中分子筛膜能提供对铝合金的长期防护.探讨分子筛膜对铝合金的防护机制.由此得出结论,MFI型纯硅分子筛膜耐蚀性很好,对提高2024型铝合金的耐蚀性具有很好的实用价值.     

Ni—Cu—P镀层在氢氟酸溶液中的耐蚀性研究

为了改善20R钢在氢氟酸介质中的耐蚀性,采用化学镀技术在该材料表面制备了Ni—Cu—P三元合金镀层。通过金相显微镜和X射线衍射观察和分析了镀层的表面形貌和组成,通过浸泡法、电化学系统测试了20R钢和镀层在氢氟酸溶液中的腐蚀性能。结果表明：Ni—Cu—P镀层能顺利地在20R钢表面发生沉积,镀层光滑、致密、无裂纹,阻隔了氢氟酸与20R钢的直接接触。镀层在氢氟酸溶液中更容易发生钝化,具有一定的耐蚀性能。     

Microstructure and corrosion resistance of modified AZ31 magnesium alloy using microarc oxidation combined with electrophoresis process

A top electrophoresis coating was deposited on the surface microarc oxidation (MAO) modified ceramic coating on AZ31 magnesium alloy. Microstructure and corrosion resistance of this composite coating were studied by SEM, electrochemical potentiodynamic polarization, and acid corrosion test. The results showed that the composite coating with a top electrophoresis coating on the surface of ceramic coating exhibited a better corrosion resistance compared with the coating formed by chemical conversion film combined with electrophoresis process. Corrosive ions could permeate into the substrate with corrosion time, and the composite coating was firstly destroyed around the scratch. The formation of composite coating with a higher adhesive force due to the porosity of the ceramic coating contributed to the improved corrosion resistance property.     

流化床造粒过程层式生长的实验研究

通过在流化床中将碳酸钾溶液雾化后喷涂在处于流化状态的玻璃珠上，研究了流化床造粒过程的层式生长机理。考察了床层温度、流化气速及溶液浓度等对涂覆率的影响。结果表明在实验范围内，造粒过程为典型的层式生长过程，造粒时间对涂覆率影响较小。床层温度对涂覆率影响显著、流化气速及溶液浓度对涂覆率也有较大影响，而且均是非单调的。     

Corrosion resistance of Molybdenum Nitride modified Ti6Al4V alloy in HCl solution

The Mo-N surface modified layer on Ti6Al4V alloy was obtained by the plasma surface alloying technique. The structure and composition of the Mo-N modified Ti6Al4V alloy were investigated by X-ray diffraction （XRD） and glow discharge optical emission spectroscopy （GDOES）. The Mo-N modified layer contains Mo-N coating on subsurface and diffusion layers between the subsurface and substrate. The X- ray diffraction analysis of the Mo-N modified Ti6Al4V alloy reveals that the outmost surface of the Mo-N modified Ti6Al4V alloy is composed of phase Mo2N （fcc） and Mo2N （tetr）. The electrochemical corrosion performance of the Mo-N modified Ti6Al4V alloy in 0.5 mol/L HCl solution was investigated and compared with that of Ti6Al4V alloy. The chemical corrosion performance of the Mo-N modified Ti6Al4V alloy in boiling 37% HCl solution was investigated and compared with that of Ti6Al4V alloy. Results indicate that self-corroding electric potentials and corrosion-rate of the Mo-N modified Ti6Al4V alloy are higher than that of Ti6Al4V alloy in 0.5 mol/L HCl solution. The corrosion-rate of the Mo-N modified Ti6Al4V alloy is lower than that of Ti6Al4V alloy in boiling 37% HCl solution.     

Enhanced Corrosion and Wear Resistances of Zr-based Alloy Induced by Amorphous/Nanocrystalline Coating

To improve corrosion and wear resistances of the Zirconium(Zr) based alloys which are widely applied in nuclear reactors and chemical corrosion-resistant equipment, a new surface modification scheme was designed to deposit a Zr_(75)Cu_(25) coating on Zr substrate by using magnetron sputtering technique. The microstructure and the phase composition were characterized by scanning electron microscope, transmission electron microscope, and X-ray diffraction measurements. The tribological properties and the corrosion resistance were investigated by performing reciprocating tribo-tester and electrochemical tests, respectively.It is found that the Zr_(75)Cu_(25) coating is made up of a mixture of amorphous and a-(Zr) nanocrystalline phases.The nanocrystalline particles with a size of 5-10 nm are homogenously dispersed in the amorphous matrix.The Zr_(75)Cu_(25) coating shows excellent tribological properties, due to the dispersion strengthen caused by the homogeneous distribution of a-(Zr) nano-size particles among the amorphous matrix. In addition, it is revealed that the Zr_(75)Cu_(25) coating makes the Zr substrate exhibit excellent corrosion resistance, due to the robust passive film with a compact structure of the amorphous/nanocrystalline mixture.     

VMS有机-无机杂化膜的制备及其防腐性能研究

以乙烯基三甲氧基硅烷（VMS）为前驱体,采用浸涂法在LY12铝合金表面制备了有机一无机杂化防腐保护膜．分别考察了涂膜次数、固化剂用量和溶剂用量对膜层防腐性能的影响,成膜的最佳工艺条件为：固化剂过氧化苯甲酰（BPO）的加入量为凝胶量的2％（质量分数）;凝胶质量与溶剂质量的比为0．17;涂膜四次．利用动电位极化曲线、盐雾实验和盐水浸泡实验评价了膜层的耐腐蚀性能．结果表明,乙烯基三甲氧基硅烷（VMS）膜层可使腐蚀电流减小到原来的1／300左右,同时也使得试片耐长久腐蚀的能力显著增强．