Bi掺杂PLZT陶瓷纤维/环氧树脂1-3复合材料的制备

选用醋酸铅、醋酸镧、醋酸铋、丙醇锆和钛酸四正丁酯为原料,以乙二醇甲醚为溶剂,用溶胶-凝胶法制备铋和镧掺杂的连续锆钛酸铅纤维。乙酰丙酮作为螯合剂增加醋酸镧的溶解性,并控制其水解程度。该纤维经热解、烧结成陶瓷纤维,直径在25~50μm范围。用扫描电镜(SEM)分析陶瓷纤维截面的形貌,显微照片表明该陶瓷纤维均匀致密。将烧结后的陶瓷纤维与环氧树脂复合,制备出陶瓷纤维/环氧树脂1-3复合材料。压电复合材料片直径为7.8 mm,厚度为0.375 mm,纤维含量为0.45,其压电常数、机电转换常数分别为454 pC/N、0.63。     

BIT/PLZT/BIT多层铁电薄膜的I-V特性研究

为了有效阻止锆钛酸铅镧（PLZT）与半导体界面发生反应和互扩散，根据锆钛酸铅镧和钛酸铋（BIT）各自的铁电性能，采用脉冲准分子激光淀积（PLD）方法制备了BIT／PLZT／BIT多层结构铁电薄膜，测量和分析了它的I-V特性曲线．结果表明，这种结构吸收了锆钛酸铅镧和钛酸铋的优点，提高了铁电薄膜的铁电性能，为进一步研究薄膜的存储特性提供了基础．     

1-3型压电复合材料的制备及性能研究

采用塑性聚合物方法制备了掺Nb的PZT（PZT-5A）陶瓷纤维，且通过排列陶瓷纤维，灌注环氧树脂的方法制备了1-3型压电复合材料研究了陶瓷纤维的结构，分析了1-3型压电复合材料密度和剩余极化随纤维体积分数Vc的变化关系。XRD表明PZT-5A陶瓷纤维为纯钙钛矿结构，SEM显示纤维结构致密，直径为250μm。1-3型压电复合材料的密度和剩余极化随纤维体积分数Vc的变化呈近似线性关系。Vc为85％时1-3压电复合材料的ε^＊、tan δ、kp、k1及Qm分别为638、1．74％、0．31、0．61及3．27，与PZT-5A陶瓷相比较，1-3型压电复合材料厚度方向振动增强，机械品质因素明显降低、     

PZT陶瓷纤维及其柔性复合薄膜的制备与分析

为了探究锆钛酸铅(PZT)陶瓷纳米纤维在柔性复合薄膜中的应用,文中采用"静电纺丝"工艺制备了PZT陶瓷纳米纤维和PZT/TPU柔性复合薄膜,分析了PZT陶瓷纤维的结构,陶瓷纤维及静电纺丝薄膜的形貌,以及薄膜中的元素分布。实验结果表明:文中制备的PZT陶瓷纤维表面光滑,形貌完整,直径为?300 nm～?400 nm,锆钛含量对其无明显影响;陶瓷纤维具有明显的钙钛矿结构,随着钛含量的增加,陶瓷纤维的三方相结构转变为四方相结构;PZT/TPU柔性复合薄膜中陶瓷纤维分散均匀,纤维直径为?400 nm～?600 nm。     

压电阻尼复合材料在船舶承力轴承减振中的应用研究

为了使船舶承力轴承具有良好的降噪减震效果,采用环氧树脂为基体,PMN(铌镁锆钛酸铅)为压电相,导电炭黑为导电相制备了0-3型压电复合材料,DMA(dynamic mechanical analyzer)测试结果表明,PMN/导电炭黑/环氧树脂复合材料具有良好的阻尼性能。以该复合材料作为阻尼层,制备船舶承重轴承缩比模型,阻尼性能研究结果显示结构试件的阻尼性能主要由0-3型压电复合材料提供,试件整体结构阻尼因子为0.415 6,振级落差的数值在4.64～16.79dB,具有良好阻尼减振效果。     

碳纳米管改性0-3型压电复合材料的制备与性能研究

以碳纳米管改性聚偏氟乙烯(PVDF)为基体,锆钛酸铅(PZT)陶瓷颗粒为功能相,运用流延工艺制备了0-3型压电复合薄膜,研究了碳纳米管改性对0-3型压电复合薄膜综合性能的影响.结果表明:适量碳纳米管的掺杂不仅可以提高PVDF基体的介电常数,还可以导致具有压电性的β相基体的形成,以上两个效应均导致了0-3型压电复合薄膜压电性能的提高.     

固相法和水热法制备BNT无铅压电陶瓷及其性能表征

采用固相法和水热法成功制备出钛酸铋钠（Bi0.5Na0.5TiO3,简写为BNT）粉体,并利用此粉体烧结出致密的BNT陶瓷.用XRD、SEM分别对粉体和陶瓷的相组成、粒度、显微结构等进行了表征,并检测了其不同烧结温度下的线收缩率和相对体积密度.固相法所制备的BNT陶瓷具有优良的压电性能,其压电常数d33高达80 pC/N,而机电耦合系数kp也达到了26%.利用水热法只需在160℃下保温16 h就合成了具有单一钙钛矿结构的BNT粉体,其粒径为0.6-1μm.     

氧化铝、碳化硅陶瓷纤维的成型与烧结

本文以纳米级氧化铝和碳化硅微粉为原料 ,采用挤压烧结工艺 ,成功地制备出氧化铝和碳化硅陶瓷纤维。对纤维的烧结特性进行了分析 ,测试了纤维的拉伸强度 ,用SEM观察了纤维断口形貌。结果表明 :由于采用纳米微粉为原料 ,使陶瓷纤维的烧结温度降低 ,氧化铝纤维在 1 2 0 0℃烧结后 ,相对密度达到 99 5 % ,拉伸强度为 840Mpa ;碳化硅纤维 1 80 0℃烧结后 ,密度高于 95 % ,拉伸强度为72 0MPa。     

0．992K0．5Na0．5NbO3-0．008BiFeO3无铅压电陶瓷制备及压电性能研究

以水热法制备的0．992K0．5Na0．5NbO3（BF）粉体等为原料,采用常压烧结法在1065℃下烧结2h制备了0．992K0．5Na0．5NbO3-0．008BiFe03无铅压电陶瓷,并研究了BiFeO3掺杂对0．992K0．5Na0．5NbO3-0．008BiFeO3无铅压电陶瓷结构和压电的影响．研究结果表明：BiFeO3掺杂使K0.5Na0.5NbO3无铅压电陶瓷正交相减弱,晶粒尺寸由6／2m减小到1μm;压电性能有一定提高,压电常数（d33）、机电耦合系数（kp）分别达到120pC／N和37．8,居里温度Tc由444．4℃减少至420．6℃．     

锆钛酸铅材料的Sol—Gel工艺合成及其电性能研究

以丁醇钛、乙醇锆、醋酸铅为原料,采用Sol-Gel工艺,成功地制备出锆钛酸铅陶瓷材料。本文主要对成胶规律、陶瓷材料的电性能进行了研究。结果表明:用该方法制备的陶瓷样品具有优良的介电和压电性能。     

高温氧化对AlN/TiC/TZP材料的组织结构与性能的影响

研究了 Ａｌ Ｎ／ Ｔｉ Ｃ／ Ｔ Ｚ Ｐ复合材料的高温氧化及其对组织与性能的影响．高温氧化实验表明,在１４００ ℃范围内,随氧化温度和时间增加,氧化增重符合抛物线规律,同时复合材料的强度和韧性急剧下降．用 Ｘ Ｒ Ｄ、 Ｓ Ｅ Ｍ 和 Ｔ Ｅ Ｍ 观察分析了氧化前后试样的显微组织结构．探讨了复合材料的高温氧化机理．     

Behavior of pure and modified carbon/carbon composites in atomic oxygen environment

Atomic oxygen （AO） is considered the most erosive particle to spacecraft materials in low earth orbit （LEO）. Carbon fiber, car-bon/carbon （C/C）, and some modified C/C composites were exposed to a simulated AO environment to investigate their behaviors in LEO. Scanning electron microscopy （SEM）, AO erosion rate calculation, and mechanical property testing were used to characterize the material properties. Results show that the carbon fiber and C/C specimens undergo significant degradation under the AO bombing. According to the effects of AO on C/C-SiC and CVD-SiC-coated C/C, a condensed CVD-SiC coat is a feasible approach to protect C/C composites from AO degradation.     

ROLE OF TOUGH INTERFACIAL LAYERS IN FIBRE REINFORCED COMPOSITES

By analysing rheological properties of inter-facial materials and structures and comprehensive mechanicalproperties and stress transfer in the interfaces of composites, itis realized that great emphasis should be put on the effectsand design of tough interfacial layers in manufacturing andstudying composite materials. The comprehensive properties ofcomposites can be improved if such tough interfacial layersare introduced into composite systems.     

Effect of the silicon powder content on the properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiC-Me composites

By means of transient plastic phase process, the Al₂O₃-SiC-Me composites were produced throungh adding metal aluminium and silicon-powder to Al₂O₃-SiC materials. Under the condition of the same content of silicon and aluminium mixed-powder, the effect of silicon powder addition on properties of Al₂O₃-SiC-Me composites was studied by means of XRD and EPMA analyses in the temperature range of 300°–1600°C. The results indicated that the content of metal phase in the sample at 1600°C increases with increasing silicon powder content. At the same time, when the temperature is lower than 1100°C, the strength of samples gradually increases with increasing temperature. However when the temperature is higher than 1100°C, the strength of samples gradually decreases with increasing temperature, and this change is very small. The results also indicated that at the same sintering temperature, the sample with 6% silicon powder has the maximum strength. Supported by the Chen Yunbo Academician Fund (Grant No. 2007CY021)     

Carbonized Zn-MOF/PANI的合成及其电容性能研究

通过简单的方法将煅烧过的金属有机框架(MOF)与聚苯胺(PANI)复合,形成了简单的MOF/PANI复合材料.通过X射线衍射(XRD)、扫描电子显微镜(SEM)、傅立叶转换红外线光谱(FTIR)对其进行了表征,并用循环伏安法(CV)对其电化学性能进行了测试.结果证明了MOF/PANI的比容量在电流密度为1 A/g下可高达477 F/g.     

金属间化合物/Al2O3,TiC陶瓷基复合材料的研究进展

概述了国内外有关金属间化合物／Al2O3,TiC陶瓷基复合材料的研究现状,特别是工艺、结构和性能间的关系以及增韧补强的机理,指出了存在的问题及今后的发展趋势．目前金属间化合物陶瓷基复合材料(I／CMC)大多是以高纯单质或化合物粉为原料,采用粉末冶金或原位合成等工艺来制备．而以天然钛铁矿为原料,原位合成制备金属间化合物／Al2O3-TiC陶瓷基复合材料是I／CMC发展的趋势之一．     

Effect of the silicon powder content on the properties of Al_2O_3-SiC-Me composites

By means of transient plastic phase process, the Al2O3-SiC-Me composites were produced throungh adding metal aluminium and silicon-powder to Al2O3-SiC materials. Under the condition of the same content of silicon and aluminium mixed-powder, the effect of silicon powder addition on properties of Al2O3-SiC-Me composites was studied by means of XRD and EPMA analyses in the temperature range of 300℃―1600℃. The results indicated that the content of metal phase in the sample at 1600℃ increases with increasing silicon powder content. At the same time, when the temperature is lower than 1100℃, the strength of samples gradually increases with increasing temperature. However when the temperature is higher than 1100℃, the strength of samples gradually decreases with increasing temperature, and this change is very small. The results also indicated that at the same sintering temperature, the sample with 6% silicon powder has the maximum strength.     

石墨烯／氧化锰／聚苯胺微纳米复合材料的制备及其超级电容器性质的研究

本文主要对石墨烯／氧化锰／聚苯胺微纳米复合物作为超级电容器电极材料的制备及其电容性质进行了研究。红外光谱、X一射线光电子能谱和扫描电镜等测试结果表明已成功合成了三元微纳米复合物。通过循环伏安测试和恒电流充放电测试表明石墨烯与氧化锰以1：5的质量比进行复合得到的产物电化学储能性质最好。三元复合时,随着苯胺的增加,三元复合物的充放电时间逐渐增长,苯胺与石墨烯／氧化锰复合材料的质量比为2：1时,复合物的比电容为311F／g,比石墨烯／氧化锰的比电容（171F／g）高出近一倍,由此可知,聚苯胺的加入显著提高了二元复合物的比电容。     

水溶性包装用纤维复合材料的研究

介绍了开发水溶性纤维复合材料的方法原理 ,分析了影响产品力学性能的主要因素 ,指出该产品具备各类包装材料所要求的力学性能。在 90℃的水中可溶解 ,溶解物可回收再利用。