GaxIn1 ? xBiyAszSb1 ? y ? z/InSb and InBiyAszSb1 ? y ? z/InSb heterostructures grown in a temperature gradient

Heterophase equilibria in the Ga _x In_{1 − x} Bi _y As _z Sb_{1 − y − z} -InSb and InBi _y As _z Sb_{1 − y − z} -InSb systems have been analyzed within the simple solution approximation. Ga _x In_{1 − x} Bi _y As _z Sb_{1 − y − z} /InSb and InBi _y As _z Sb_{1 − y − z} /InSb heterostructures have been grown in a temperature gradient, and their composition and structural perfection have been assessed.     

On the pseudo-binary systems RexM1−xO2 (M=V,Mo, W)

Phase analysis studies on the $\text{Re}{}_{\mathrm{<mtext>x</mtext>}}\text{M}{}_{\mathrm{<mtext>1?</mtext><mtext>x</mtext>}}\text{O}{}_2$ systems ($\text{M}\text{=}\text{V, Mo, W}$) performed by means of X-ray powder photographs of samples prepared 1000K – 1225K have established the existence of the following phases:

$\text{ReO}{}_2\text{?}\text{VO}{}_2\text{:}\text{REo}{}_2\text{(orh) for 1>}{}_{\mathrm{<mtext>x</mtext>}}\text{>0.94 and}\text{VO}{}_2\text{(mon and tetr) for 0<}{}_{\mathrm{<mtext>x</mtext>}}\text{<0.5}$

$\text{ReO}{}_2\text{?}\text{MoO}{}_2\text{:}\text{ReO}{}_2\text{(orh) for 1>}{}_{\mathrm{<mtext>x</mtext>}}\text{>0.70. No. homogenity range of}\text{MoO}{}_2\text{.}$

$\text{ReO}{}_2\text{?}\text{WO}{}_2\text{: No mutual solubility nor anyintermediary phases}$

Metal-metal distances in the orthorhombic rhenium dioxide phases, derived from powder photographs, show slight changes with the $\text{x}$ value.     

Magnetization Processes of (La0.7Pb0.3MnO3)1?x(SiO2)x Composites

The ceramic composites, (La_0.7Pb_0.3MnO₃)_1−x (SiO₂) _x , with diluted magnetic properties are prepared using solid-sate sintering route. Magnetization processes of (La_0.7Pb_0.3MnO₃)_1−x (SiO₂) _x composites are explored in this study. Ferromagnetism is gradually attenuated due to the magnetic dilution induced by the increase of SiO₂ content. Clearly, irreversible behavior is observed in the zero-field cooling and the field cooling (ZFC–FC) curves at a low field of 100 Oe. Saturation magnetization decreases as x increases while ferromagnetic transition temperature remains around 346 K for all composites. All the composites exhibit ferromagnetic hysteresis behavior which can be modeled by the law of the approach to saturation in the form M=M _S(1−a/H). The term a/H expresses the deviation of magnetization from saturation. The smaller factor a for La_0.7Pb_0.3MnO₃-rich samples results in sharper square curve which should be associated with the long-range spin order of ferromagnetic coupling.     

欧盟G/TBT/N/EU/75通报分析

日前,欧盟发布G/TBT/N/EU/75通报,通报了计算机和计算机服务器的ErP指令实施条例草案,规定了计算机和计算机服务器产品的最低能源效率和信息要求,拟批准日期是2013年5月。该实施条例是ErP框架指令(2009/125/EC)下关于计算机产品的具体生态设计要求,该条例要求一旦正式生效,不符合要求的产品将不允许在欧盟市场销售。     

Characterizations of InzGa1?z As1?x?yN xSbyP-i-N structures grown on GaAs by molecular beam epitaxy

The GaAs-based double-heterojunction P-i-N structures using In_zGa_1–zAs_1–x–yN_xSb_y as the i-layer is investigated for the first time using solid source molecular beam epitaxy. High quality coherent bulk InGaAsN_3.45%Sb (0.5 m) with a lattice-mismatch of 2.6 × 10^–3 can be achieved due to the surfactant properties of antimony, while the bulk InGaAsN_2% at 0.5 m with 1.06× 10^–3 mismatch is fully relaxed. Rapid thermal annealing (RTA) resulted in 25 meV low temperature (LT) photoluminescence (PL) full-width half-maximums (FWHM) for the bulk InGaAsNSb layers. InGaAsNSb experiences 30% less blueshifting with subjected under the same annealing conditions as InGaAsN with similar N content. Room temperature (RT) absorption measurements are in the range of 0.9–1.4 eV. The absorption edge of 1.41 m is achieved for sample D4.     

Relation of Structure and Superconductivity in Self-compensated Y1?xCaxBa2Cu3?xAlxOz System

The co-doped compounds of Y_1−x Ca _x Ba₂Cu_3−x Al _x O _z , with x from 0.1 to 0.4, were synthesized through a solid-state reaction method. Structural and superconducting properties have been investigated by X-ray diffraction, Rietveld refinement, and DC magnetization measurement. The lattice constant a decreases while b increases with the addition of x. The difference between a and b diminishes gradually. Careful study of the crystalline structure shows that the critical temperature (T _c ) changes monotonically with some local structural parameters, such as the difference between Ba and Cu(2) atoms’ Z coordinates, the bond length of Cu(2)–O(4), and the bond angle of Cu(2)–O(2)–Cu(2), which are all closely related to the interaction between the perovskite block and the rock salt block in the unit cell. The results indicated that the influence of the crystalline structure on superconductivity is important and independent of the carrier concentration.     

Superconductivity of YBa2?xNdxCu3Oy Solid Solution

The solubility of Nd at the Ba sites and the superconductivity of YBa_2–x Nd _x Cu₃O _y were investigated by X-ray powder diffraction and measurements of the electrical resistance and ac susceptibility. The single Re123 phase was obtained for x0.30. The onset transition temperature is insensitive to the Nd content x in the region of x0.40. All are higher than 95 K. The zero resistance transition temperatures , however, exhibits two-step variation with the increase of x. For x0.25, are all above 92 K. The highest of 94 K was obtained for x=0.25. For x0.3 drops sharply to about 84 K. Finally falls to 30 K and is below 10 K for x=0.5. The two-step variation of T _c might be an indication of the existence of two trap levels for holes.     

The Effects of Substitution of Sn for Cu in Bi1.75Pb0.25Sr2CaCu2.3?xSnxSnxOy

The influence of Sn doping on superconductivity in the Bi-based 2212 phase is studied in this paper. For the samples R–T relations and magnetic hysteresis loops were measured. X-ray powder diffraction analysis was also performed. For Bi_1.75Pb_0.25Sr₂CaCu_2.3–x Sn _x O _y , the experimental results show that by adding the proper amount of Sn the superconductivity of the samples can be improved. As x = 0.15, the critical temperature T _c, the critical current density J _c, and the magnetic pinning force density F reach a maximum. At T = 11 K, the critical state parameters H _c1, H _c2, , , and are calculated and compared with the results reported by other researchers. The experimental results also show that the Sn doping is able to speed up the growth of the 2223 phase. In brief, Sn doping is an effective way of improving the superconductivity in Bi-based superconductors.     

Electrical properties of Zn2(TiaSnb)1 ? xZrxO4 solid solutions

The electrical conductivity, band gap, dielectric permittivity, and molar polarizability of Zn₂(Ti _a Sn _b )_{1 − x} Zr _x O₄ solid solutions have been determined. All of the synthesized samples are dielectrics with semiconducting behavior of conductivity. The phase diagram of the Zn₂TiO₄-Zn₂SnO₄-Zn₂ZrO₄ system is presented.