含孔玻璃纤维/环氧树脂复合材料-铝合金层板的拉伸损伤行为与热暴露响应

采用试验和数值方法研究了含孔玻璃纤维/环氧树脂(GF/EP)复合材料-铝合金层板在不同热暴露温度下的拉伸剩余强度和损伤失效模式,揭示了层间损伤、纤维损伤及基体损伤的演化过程。结果表明:随着热暴露温度升高,含孔GF/EP复合材料-铝合金层板剩余强度不断下降,拉伸破坏呈现出明显的纤维断裂与层间分层混合失效模式。热暴露温度越高或开孔直径越大,GF/EP复合材料-铝合金层板的层间分层损伤区域越小。随着载荷的增大,沿加载方向的0°纤维和基体的损伤分别呈现出类似“漏斗”形和“花瓣”状的损伤演化形式,而层间损伤区域呈现出一对相对开孔对称的三角形损伤演化形式。基于GF/EP复合材料-铝合金层板的剩余强度和损伤失效模式的数值仿真与试验结果吻合较好。      

Tension-tension fatigue behavior of GFRP woven laminates at low temperatures

This paper describes an experimental study on the fatigue damage behavior of GFRP woven laminates in terms of stiffness degradation and residual strength under cyclic loading at low temperatures. Uniaxial, load-controlled, tension-tension fatigue tests were conducted at room and low temperatures. The applied stress versus cycles to failure (S-N) relationships and fatigue limits were obtained for the GFRP woven laminates and the microcrack evolution due to fatigue loading was characterized using optical microscopy. Temperatures were also measured using a thermocouple embedded in the center of the specimens.     

Mixed-mode interlaminar fracture and damage characterization in woven fabric-reinforced glass/epoxy composite laminates at cryogenic temperatures using the finite element and improved test methods

The present research examines experimentally and analytically the mixed-mode interlaminar fracture and damage behavior of glass fiber reinforced polymer (GFRP) woven laminates at cryogenic temperatures. The mixed-mode bending (MMB) tests were performed with the improved test apparatus, at room temperature, liquid nitrogen temperature (77 K) and liquid helium temperature (4 K). The energy release rates at the onset of delamination crack propagation were evaluated for the woven GFRP specimens using both beam theory and finite element analysis. The fracture surfaces were also examined to verify the fracture mechanisms. In addition, the initiation and growth of damage in the specimens were predicted by a damage analysis, and the damage effect on the mixed-mode interlaminar fracture properties at cryogenic temperatures was explored.     

Cryogenic through-thickness tensile characterization of plain woven glass/epoxy composite laminates using cross specimens: Experimental test and finite element analysis

This paper investigates the through-thickness tensile behavior of woven glass fiber reinforced polymer (GFRP) composite laminates at cryogenic temperatures. Tensile tests were carried out with cross specimens at room temperature and liquid nitrogen temperature (77 K), and the through-thickness elastic and strength properties of the woven GFRP laminates were evaluated. The failure characteristics of the woven GFRP laminates were also studied by optical and laser scanning microscopy observations. A three-dimensional finite element analysis was performed to calculate the stress distributions in the cross specimens, and the failure conditions of the specimens were examined. It is found that the cross specimen is suitable for the cryogenic through-thickness tensile characterization of laminated composite materials. In addition, the through-thickness Young's modulus of the woven GFRP composite laminates is dominated by the properties of the matrix polymer in the given temperature, while the tensile strength is characterized by both, the fiber to matrix interface energy and the cohesion energy of the matrix polymer.     

基于纤维束增强树脂基复合材料测试的单向层合板层间剪切性能的预估方法

纤维束增强树脂基复合材料（FBC）及其单向层合板在标准Iosipescu剪切实验中表现出非常相似的破坏特征,然而测量得到的剪切强度却有明显差异。本文使用两种碳纤维和两种环氧树脂制备了3种FBC和单向层合板,对FBC剪切强度和单向层合板层间剪切强度进行了测量与分析。应用界面单元方法分析了纤维束与基体之间的界面应力场,发现FBC剪切试件中纤维束/基体界面附近的应力状态为拉剪耦合,而单向层合板中界面处于纯剪切应力状态,这一差异导致FBC剪切实验测量的强度低于单向层合板的剪切强度。本文基于Yamada-Sun强度理论建立了FBC剪切强度与单向层合板剪切强度之间的关系模型,应用该模型预测的单向层合板剪切强度与实测强度之间达到良好的一致性,相对偏差为10%左右。根据本文提出的方法,通过制样较简单的FBC试验能够预测和评估相应单向层合板的层间剪切性能。     

基于连续介质损伤力学的复合材料层合板低速冲击损伤模型

基于连续介质损伤力学（CDM）方法,建立了分析复合材料层合板低速冲击问题的三维数值模型。该模型考虑了层内损伤（纤维和基体损伤）、层间分层损伤和剪切非线性行为,采用最大应变失效准则预测纤维损伤的萌生,双线性损伤本构模型表征纤维损伤演化,基于物理失效机制的三维Puck准则判断基体损伤的起始,根据断裂面内等效应变建立混合模式下基体损伤扩展准则。横向基体拉伸强度和面内剪切强度采用基于断裂力学假设的就地强度（in-situ strength）。纤维和基体损伤本构关系中引入单元特征长度,有效降低模型对网格密度的依赖性。层间分层损伤情况由内聚力单元（cohesive element）预测,以二次应力准则为分层损伤的起始准则,B-K准则表征分层损伤演化。分别通过数值分析方法和试验研究方法对复合材料典型铺层层合板四级能量低速冲击下的冲击损伤和冲击响应规律进行分析,数值计算和试验测量的接触力-时间曲线、分层损伤的形状和面积较好吻合,表明该模型能够准确地预测层合板低速冲击损伤和冲击响应。     

Analysis of mixed-mode interlaminar fracture and damage behavior of GFRP woven laminates at cryogenic temperatures

The objective of this work is to investigate the interlaminar fracture and damage behavior of glass fiber reinforced polymer (GFRP) woven laminates loaded in a mixed-mode bending (MMB) apparatus at cryogenic temperatures. The finite element analysis (FEA) is used to determine the mixed-mode interlaminar fracture toughness of MMB specimen at room temperature (RT), liquid nitrogen temperature (77 K) and liquid helium temperature (4 K). A FEA coupled with damage is also employed to study the damage distributions within the MMB specimen and to examine the effect of damage on the mixed-mode energy release rate. The technique presented can be efficiently used for characterization of mixed-mode interlaminar fracture and damage behavior of woven laminate specimens at cryogenic temperatures.     

Analysis of mode II interlaminar fracture and damage behavior in end notched flexure testing of GFRP woven laminates at cryogenic temperatures

Summary Interlaminar fracture and damage behavior of glass fiber reinforced polymer (GFRP) woven laminates at cryogenic temperatures is investigated for end notched flexure (ENF) pure Mode II configuration. The corrected beam theory (CBT) and finite element analysis (FEA) are used to calculate the Mode II interlaminar fracture toughness of ENF specimen at room temperature (RT), liquid nitrogen temperature (77 K) and liquid helium temperature (4 K). A FEA coupled with damage is also employed to study the damage distributions within the specimen and to examine the effect of damage on the Mode II energy release rate. The numerical results show that damage occurs at the matrix and causes a decrease in the energy release rate. The technique presented can be efficiently used for the characterization of cryogenic Mode II interlaminar fracture and damage behavior of woven laminate ENF specimens.     

复合材料层合板缺口强度的CDM三维数值模型

针对复合材料层合结构缺口强度问题,基于连续损伤力学（CDM）提出了一种三维损伤数值模型。模型区分了层内损伤（纤维失效、纤维间失效）和层间分层损伤的不同失效模式。采用三维Puck准则与Aymerich准则对上述2类损伤进行判定,材料失效后基于CDM中线性软化模型对材料损伤进行演化。模型考虑了复合材料层合板子层的就位效应和剪切非线性行为。对Carlsson的AS4/3501-6缺口拉伸强度试验进行数值模拟。结果表明:分析结果与试验结果吻合良好,证明了该模型能够准确地预测含缺口复合材料层合板面内拉伸强度。      

Hygrothermal influence on the interlaminar shear strength of Kevlar-graphite/epoxy hybrid composites

The hygrothermal influence on the interlaminar shear strength of Kevlar 49-graphite/epoxy hybrid composite was investigated in the temperature range –50 to 150 ° C. Moisture was introduced into the specimen by immersion in distilled water until a specified weight gain occurred. Two material lay-up were used in this investigation. In Kev 49/T-300/Kev 49, Kevlar 49 and graphite prepreg tapes were used as outer and centre layer, respectively and in T-300/Kev 49/T-300, it was vice versa. In both cases the tapes were alternated until the total thickness was achieved. The results show that interlaminar shear strength change with the ply sequence of hybrid laminates. The interlaminar shear strength of T-300/Kev 49/T-300 is relatively higher than that of Kev 49/T-300/Kev 49. The interlaminar shear strength of both T-300/Kev 49/T-300 and Kev 49/T-300/Kev 49 decrease with the increase of temperature in the range –50 to 150 ° C. The addition of moisture further degrade the interlaminar shear strength in the same temperature range. Close physical observation showed clear evidence of interlaminar shear failure for most of the specimens.     

阳极氧化工艺对纤维-铝合金层板力学性能的影响

通过改变铝合金表面阳极氧化工艺参数, 研究了阳极氧化电压和时间对玻璃纤维-铝合金(GLARE)层板抗拉强度和层间剪切强度的影响。通过SEM观察了铝合金表面Al₂O₃多孔膜和层板断面形貌, 分析了铝合金/树脂胶接界面对层板力学性能的影响。结果表明, 阳极氧化电压为20 V时, GLARE层板抗拉强度和层间剪切强度随着阳极氧化时间延长而增大, 在20 min时出现最大值, 继续延长阳极氧化时间, 层板强度随之下降; 阳极氧化时间为20 min时, GLARE层板抗拉强度和层间剪切强度随着阳极氧化电压增大而增大, 在20 V时出现最大值, 继续增大电压, 强度随之下降。     

Interlaminar shear properties of composite insulation systems for fusion magnets at cryogenic temperatures

This paper reports the cryogenic interlaminar shear properties of composite insulation systems for the superconducting magnet coils in the International Thermonuclear Experimental Reactor (ITER). Short beam shear tests were performed at room temperature, liquid nitrogen temperature (77 K) and liquid helium temperature (4 K) on three insulation systems consisting of woven glass fiber reinforced plastic (GFRP) composites with different polymer resins and polyimide films, and the dependence of their apparent interlaminar shear strength on the temperature and the polymer resins was discussed. A detailed observation of failed specimens was made to verify the failure mechanisms. Insulation systems subjected to gamma irradiation at room temperature were also considered, and the effect of irradiation on the cryogenic interlaminar shear properties was examined.     

Acoustic emission and fracture behavior of GFRP woven laminates at cryogenic temperatures

This paper describes an experimental and analytical study on fracture and damage behavior of GFRP woven laminates at cryogenic temperatures. CT (compact tension) tests were carried out at room temperature, liquid nitrogen temperature (77 K) and liquid helium temperature (4 K) to evaluate the critical values of the fracture mechanics parameters. During the CT tests, AE (acoustic emission) method was implemented. AE signals can identify the critical load at which gross failure occurs. A FEA (finite element analysis) was also applied to calculate the fracture mechanics parameters. The failure criteria (Hoffman criterion and maximum strain criterion) or the damage variable based on the continuum damage mechanics was incorporated into the model to interpret the experimental measurements and to study the damage distributions within the specimen. Several methods of calculating J-integral are discussed.     

MWCNTs对碳纤维非褶皱无纺布/环氧层合板力学性能的影响

将羧基化多壁碳纳米管(MWCNTs)添加到TDE85环氧树脂中,然后与碳纤维非褶皱无纺布(C-NCF)复合,制备成[0°/90°/+45°/-45°]_S层合板。采用三点弯曲、短梁剪切和单边切口弯曲测试方法以及动态力学性能分析方法,研究了不同含量的MWCNTs对层合板弯曲性能、层间剪切强度(ILSS)、Ⅱ型层间断裂韧性(G_ⅡC,以及玻璃态转变温度(T_g)的影响。并采用SEM对Ⅱ型试样的断面进行分析。结果表明,MWCNTs的加入显著提高了NCF层合板的力学性能。与空白试样相比,当MWCNTs在树脂中的质量分数为2.0%时,弯曲强度和模量分别提高了约26%和6%;当MWCNTs的质量分数为0.5%时,ILSS、G_ⅡC、T_g分别提高约14%、27%和14%。     

Hybrid multi-scale epoxy composite made of conventional carbon fiber fabrics with interlaminar regions containing electrospun carbon nanofiber mats

Herein we report the development and evaluation of hybrid multi-scale epoxy composite made of conventional carbon fiber fabrics with interlaminar regions containing mats of electrospun carbon nanofibers (ECNs). The results indicated that (1) the interlaminar shear strength and flexural properties of hybrid multi-scale composite were substantially higher than those of control/comparison composite without ECNs; in particular, the interlaminar shear strength was higher by ∼86%; and (2) the electrical conductivities in both in-plane and out-of-plane directions were enhanced through incorporation of ECNs, while the enhancement of out-of-plane conductivity (∼150%) was much larger than that of in-plane conductivity (∼20%). To validate the data reduction procedure, a new shear stress formula was formulated for composite laminates, which took into account the effect of layup and inter-layers. The study suggested that ECNs could be utilized for the development of high-performance composites, particularly with the improved out-of-plan properties (e.g., interlaminar shear strength).     

Prediction of low velocity impact damage in carbon–epoxy laminates

It is well known that composite laminates are easily damaged by low velocity impact. This event causes internal delaminations that can drastically reduce the compressive strength of laminates. In this study, numerical and experimental analyses for predicting the damage in carbon–epoxy laminates, subjected to low velocity impact, were performed. Two different laminates (0₄,90₄)_s and (0₂,±45₂,90₂)_s were tested using a drop weight testing machine. Damage characterisation was carried out using X-rays radiography and the deply technique. The developed numerical model is based on a special shell finite element that guarantees interlaminar shear stresses continuity between different oriented layers, which was considered fundamental to predict delaminations. In order to predict the occurrence of matrix failure and the delaminated areas, a new failure criterion based on experimental observations and on other developed criteria, is included. A good agreement between experimental and numerical analysis for shape and orientation of delaminations was obtained. For delaminated areas, reasonable agreement was obtained.     

Mechanisches Verhalten von kohlenstoffaserverstärkten Duromeren im Tieftemperaturbereich

Investigations on the suitability of carbon fiber reinforced epoxy for using at cryogenic temperatures The following investigations show the mechanical properties of some carbon fiber reinforced epoxies under quasistatic load. Both prepregs and wet laminates are tested to get a suitable fiber/matrix-combination for using at cryogenic temperatures. Therefore the material research is done at room temperatures. Therefore the material research is done at room temperature and at liquid nitrogen atmosphere. The characteristics, which serve for the basis of valuation are ultimate strength, elongation at fracture and modulus of elasticity. At liquid nitrogen temperature ultimate tensile strength and elongation at fracture show a decrease in comparison to room temperature, but Young's Modulus increases insignificantly with tensile loading. In the compression test all the characteristics grow larger. Furthermore the influence of the testing temperature on the mechanical characteristics of prepregs and wet laminates is pronounced differently. The experiments also show, that the dependence of the temperature on the mechanical properties may be influenced by the kind of the reinforcing fibers. This statement applies especially to the value of the obtainable interlaminar shear strength.     

Failure Analysis of Bolted Joints in Cross-ply Composite Laminates Using Cohesive Zone Elements

A strength prediction method is presented for double-lap single fastener bolted joints of cross-ply carbon fibre reinforced plastic (CFRP) composite laminates using cohesive zone elements (CZEs). Three-dimensional finite element models were developed and CZEs were inserted into subcritical damage planes identified from X-ray radiographs. The method makes a compromise between the experimental correlation factors (dependant on lay-up, stacking sequence and joint geometry) and three material properties (fracture energy, interlaminar strength and nonlinear shear stress-strain response). Strength of the joints was determined from the predicted load-displacement curves considering sub-laminate and plylevel scaling effects. The predictions are in a reasonable agreement with the experimental data.     

Experimental and numerical investigation on bolted joint in glass–fiber reinforced composites

In this paper, vacuum assisted resin injection technique was employed to prepare the composite laminates with different plies ways. The macro-mechanical performances of the bolted joint of the composite laminates were investigated by experimental and finite element simulation. The influence mechanism of different parameters on the joint performance and failure models of the composite laminates were analyzed. A VUMAT subroutine was developed, according to the failure criteria and corresponding stiffness degradation criteria, to describe the progressive damage process of bolted joint composite laminates through finite element analysis method. The results indicated that the failure strength of composite laminates would be improved with the increasing of tightening torque, and the strength of three-ply-way hybrid composite laminates is higher than that of two-way hybrid laminates. The comparisons between numerical simulation results and experimental results showed that the developed subroutine can effectively predict the macroscopic response of bolted joint glass–fiber reinforced composite laminates.     

碳纤维/聚苯硫醚热塑性复合材料电阻焊接工艺

本文针对航空器结构用碳纤维/聚苯硫醚(CF/PPS)复合材料为研究对象，开展电阻焊接工艺研究；利用CF/PPS复合材料混编织物作为电阻元件，成功制备了CF/PPS复合材料层板电阻焊接接头；重点利用Taguchi方法和方差分析获取CF/PPS复合材料层板电阻焊接最佳工艺参数(电流为12 A，压力为1.5 MPa，时间为30 min)及各参数对焊接接头剪切强度的贡献(电流为83.37%，压力为9.55%，时间为6.02%)。最佳焊接工艺参数焊接的接头单搭接剪切强度约为17.88 MPa；同时，对最佳参数焊接试样(H-LSS)和较低剪切强度试样(L-LSS)的焊接接头截面和剪切失效断口形貌进行了观察和分析。结果表明:H-LSS试样的焊缝区域树脂填充和浸润良好，且主要剪切失效形式为层间剪切失效，即为纤维与树脂基体脱黏及CF/PPS织物复合材料断裂混合失效；L-LSS试样的焊缝区域树脂填充和浸润较差，存在较多空隙，且剪切失效形式为焊缝界面脱黏失效。