固溶处理对2205双相不锈钢点蚀性能的影响

采用金相显微镜、电子能谱分析仪、透射电子显微镜、FeCl3溶液浸泡法和循环极化曲线法研究了固溶处理对2205双相不锈钢组织和点腐蚀性能的影响.结果表明,经1050℃×2h水冷固溶处理后,实验钢中α和γ两相体积含量约各占一半,组织均匀且细化,在6%FeCl3,溶液中的临界点蚀温度为45℃,在3.5%NaCl溶液中的点蚀电位Eb和保护电位Ep均为1028mV,表现出良好的耐点蚀性能.经950℃固溶处理后组织中析出σ相,σ相导致其抗点蚀性能下降.     

固溶处理对00Cr22Ni5Mo3N双相不锈钢组织和性能的影响

研究了00Cr22Ni5Mo3N双相不锈钢板在不同固溶处理工艺下的组织、力学性能、铁素体含量和耐点蚀性能的变化规律.研究表明:在1020～1250℃,随固溶处理温度的升高,抗拉强度、硬度呈先减小后增加的规律,铁素体含量随温度的升高而增加,奥氏体显微组织结构由纤维状转变成岛状;在1020～1120℃,随温度的升高耐点蚀速率变化不大;在1150～1250℃耐点蚀速率随温度的升高急剧增加.     

固溶处理对节镍型LDX2101及00Cr22Ni5Mo3N双相不锈钢腐蚀行为的影响

采用光学显微镜、扫描电子显微镜、动电位极化法以及慢应变速率拉伸试验,研究了950和1 100℃固溶处理对节镍型LDX2101以及00Cr22Ni5Mo3N(SAF2205)双相不锈钢中析出相、点蚀和应力腐蚀开裂行为的影响。结果表明:950℃固溶处理使两种钢的微观组织均匀性变差,尤其是2205双相不锈钢中σ相的析出使其耐点蚀及应力腐蚀性能明显下降,耐点蚀性能甚至劣于点蚀当量(PREN)较小的LDX2101双相不锈钢; 1 100℃固溶处理对两种钢的点蚀和应力腐蚀开裂的行为影响较小,但钢的塑性略有提高。     

固溶温度对22Cr双相不锈钢组织与性能的影响

采用金相显微镜、扫描电镜、能谱分析、透射电镜和性能测试等方法,研究了固溶温度对22Cr双相不锈钢显微组织和性能的影响.结果表明:在950～1150 ℃范围,实验钢中α、γ两相含量与固溶温度呈近似直线关系;材料的显微硬度(HV)和强度(σb)先降后升,在1050 ℃时达到最小值;当固溶温度为950 ℃,组织中出现了σ相,σ相是导致22Cr双相不锈钢塑性、韧性下降的主要原因;随着固溶温度的升高,Cr、Mo的分配系数K变小,Ni的分配系数K增大,表明合金元素在α和γ相中浓度差别变小.     

固溶处理对Mn-N型双相不锈钢堆焊层耐点蚀性能的影响

为改善钢铁材料的耐点蚀性能,采用等离子堆焊在Q235钢板上制备Mn-N型双相不锈钢堆焊层.分别采用卧式显微镜和配备EDS的扫描电镜,观测经不同温度固溶处理后堆焊层的显微组织,分析各元素在两相中的分布;采用FeCl3溶液对堆焊层进行点蚀浸泡试验,并测量堆焊层在3.5 wt.％NaCl溶液下的电化学交流阻抗谱(EIS),研究固溶处理温度对Mn-N型双相不锈钢等离子堆焊层的耐点蚀性能的影响.结果表明:随着双相不锈钢堆焊层固溶处理温度的升高,其显微组织中铁素体的耐点蚀性能下降,而奥氏体的耐点蚀性能上升,堆焊层整体的耐点蚀性能呈现先上升后下降的趋势;经1230℃固溶处理后,堆焊层点蚀速率最低,为0.0176 g/h;同时,电化学阻抗谱显示,经1230℃固溶处理后,堆焊层具有最高的耐点蚀性能.固溶处理使合金元素在两相中重新分布,是造成不同温度固溶处理后堆焊层的耐点蚀性能产生差异的主要原因.     

固溶温度对铸造双相不锈钢Cr25Mn10Mo4Ni2N组织及耐蚀性影响

通过中频感应炉熔炼制备了经济节Ni型铸造双相不锈钢Cr25Mn10Mo4Ni2N,利用OM、XRD、SEM和电化学工作站研究了1000~1150℃温度区间对其显微组织及固溶处理后在人工海水中耐蚀性能的影响。结果表明,固溶温度处于1000~1100℃区间时,材料的组织由α、γ及σ相组成。随着固溶温度升高,σ相的形貌由细小岛状向粗大岛状变化,且数量不断减少。当固溶温度升高至1120℃时,σ相完全消失,组织仅由α和γ两相组成。节Ni型双相不锈钢Cr25Mn10Mo4Ni2N经1120℃固溶时,其腐蚀电流密度最小,电荷转移电阻最大,耐蚀性能最佳;1150℃固溶时,耐蚀性能次之;在1020~1100℃温度区间固溶时,随着温度的升高σ相含量减少,材料耐蚀性能越好。     

固溶温度对2507双相不锈钢力学性能及耐蚀性的影响

利用光学显微镜、扫描电镜、XRD、拉伸试验机和电化学综合测试仪等研究了不同固溶温度对2507超级双相不锈钢组织、力学性能和耐蚀性的影响。采用Thermo-Calc热力学软件计算了2507双相不锈钢的热力学平衡相图,并与测试结果进行了对比。研究结果表明,经1050 ℃及以上温度固溶后,σ相溶解;随着固溶温度的升高,铁素体相含量增加,奥氏体相含量降低,α/γ相体积分数比增加;1050~1100 ℃固溶30 min并水冷时,双相不锈钢具有较好的综合力学性能,屈服强度、抗拉强度和伸长率分别大于600 MPa、840 MPa和35%。1050 ℃固溶30 min时,双相钢可获得较好的耐蚀性能。     

固溶处理对低镍双相不锈钢耐点蚀及强韧性能的影响

采用“C/N+Mn代Ni”的合金设计方法,制备出了一种具有良好热加工性能的低镍双相不锈钢21Cr-DSS,并研究了固溶处理工艺对新钢种微观组织、强韧性及耐点蚀性能的影响。结果表明:21Cr-DSS在热轧过程中铁素体比奥氏体更容易发生动态软化。固溶温度比保温时间对21Cr-DSS中两相比例的影响更明显,且奥氏体晶粒尺寸稳定性优于铁素体。随固溶温度升高,21Cr-DSS的强韧性得到改善,但当温度超过1100℃后,强韧性下降。在1050℃固溶处理30 min时,21Cr-DSS具有最佳的综合性能,此时强塑积为58.9 GPa%,-40℃低温冲击功为84 J,在3.5%氯化钠溶液中的点蚀电位为0.43V。21Cr-DSS比常规LDX2101具有更优异的热加工性能和强韧性,且耐点蚀性能基本相当。与AISI 304奥氏体不锈钢相比,21Cr-DSS的强度和耐点蚀性能明显更优。     

含铜超级奥氏体不锈钢的固溶行为

通过Thermo-Calc热力学计算软件制定含Cu超级奥氏体不锈钢的固溶处理温度为1000~1200 ℃,保温60 min。通过光学显微镜、SEM与EDS研究了固溶温度对含Cu超级奥氏体不锈钢显微组织、析出相和夹杂物的影响,研究结果发现Cu能促进试验钢的再结晶及析出相的溶解,在1000 ℃以上固溶处理时析出相均为σ相。试验钢的夹杂物类型主要是镁铝氧化物和硫化物。确定1200 ℃为微Cu试验钢的最佳固溶处理温度。     

固溶温度对15-5PH不锈钢耐点蚀性能的影响

用化学浸泡、极化曲线、循环极化曲线和电化学阻抗谱等方法研究了不同温度固溶后直接时效状态的15-5PH马氏体沉淀硬化不锈钢的耐点蚀性能,并用金相显微镜、x射线衍射仪(XRD)和扫描电子显微镜(SEM)分析其显微组织和析出相。结果表明,15-5PH不锈钢随着固溶温度的升高,自腐蚀电位减小,自腐蚀电流和腐蚀速率增大,耐点蚀性能下降。不同温度固溶后时效的基体组织均为板条马氏体和少量奥氏体,且均有NbC相析出。在1000℃下固溶后时效组织较均匀,析出相少,耐点蚀性能优异。在1070℃下固溶后时效组织中有Cu析出,进而导致其耐点蚀性能下降。     

胫骨生物陶瓷复合材料的微结构增韧机理

扫描电镜观察显示胫骨是一种由羟基磷灰石和胶原蛋白组成的自然生物陶瓷复合材料.羟基磷灰石具有层状的微结构并且平行于骨的表面排列.观察也显示这些羟基磷灰石层又是由许多羟基磷灰石片所组成,这些羟基磷灰石片具有长而薄的形状,也以平行的方式整齐排列.基于在胫骨中观察到的羟基磷灰石片的微结构特征,通过微结构模型分析及实验,研究了羟基磷灰石片平行排列微结构的最大拔出能.结果表明,羟基磷灰石片长而薄的形状以及平行排列方式增加了其最大拔出能,进而提高了骨的断裂韧性.     

Features of formation of the structure in production of blanks of disks of heat-resistant nickel alloys

Conclusions To provide a high level of mechanical properties in wrought blanks of cast ÉP741NP and ÉP962 alloys it is necessary to form controlled structures. A necklace-type structure formed in homogenizing isostatic treatment, subsequent thermomechanical working including alternation of the operations of deformation in the (+)-area and recrystallization anneals, and final heat treatment is preferable. The temperature conditions of all stages of thermomechanical working are strictly controlled, especially the final operation of deformation and heating for hardening. To eliminate hardening cracks and distortions it is necessary to use molten salts at t=600°C as quenchants. The use of multiple production operations makes it possible to significantly reduce the structural inhomogeneity related to inhertance of the original dendritic structure. However, the structure of the final semifinished product is nevertheless characterized by a difference in occurrence of the processes of polygonization and recrystallization between the former dendritic cells and the interdendritic spaces in deformation and heat treatment.To obtain structurally homogeneous blanks for gas turbine engine parts it is necessary to use basically new methods of remelting such as vacuum double electrode remelting and electron beam remelting with an intermediate vessel.Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 12, pp. 25–29, December, 1991.     

Ab-initio calculation of enthalpies of formation of intermetallic compounds and enthalpies of mixing of solid solutions

A large number of ab-initio calculations of energies of formation of intermetallic compounds have been performed in the last 15 years. The currently used methods are listed. The paper presents a review of the aluminium based compounds which have been studied. Comparisons of calculated and experimental enthalpies of formation are provided for aluminim-3d and-4d transition metal alloys at equiatomic composition. The modelling of the enthalpies of mixing of solid solutions based on a given lattice is described.     

试论洋务派教师聘任的思想

洋务派在洋务学堂的办学活动中,为了解决西学专业学科的教学困难,采用了聘请外籍教师的应急措施.他们以真才实学,合同制管理作为主导思想,并认为这种解决师资的途径只是权宜之计,并非久远.从客观上看,洋务派的教师聘任思想有深刻的历史影响.     

Prospects of the Use of Synergetic Approach to Solution of Problems of the Science of Nanomaterials

A synergetic approach to solution of problems of self-controlled synthesis of nanostructures and creation of self-organizing nanotechnologies is considered in connection with the superproblem of creation of materials with functional properties resembling those of biosystems. __________ Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 7, pp. 55 – 61, July, 2005.     

Kinetics of the oxidation of metals — Influence of self-diffusion of metal

The importance of the self-diffusion of a metal during its oxidation by a gas is treated for the cases of nonstoichiometric oxides having either interstitial cation or cation vacancies. We have established a general relationship for the reaction rate when a mixed diffusion process occurs. From this relationship, we have shown that the pressure dependence can be different, according to whether the rate-determining process is the self-diffusion through the metal or through the product.     

FeCrAIW电弧喷涂层组织的致密化研究

采用激光辐照对FeCrAlW电弧喷涂层的组织进行致密化处理,借助扫描电镜和X衍射对涂层的组织进行了分析.测试了涂层的显微硬度.结果表明:涂层组织致密度提高,孔隙率明显降低.随着激光扫描速度的增加,涂层的显微硬度降低.在较低的扫描速度下,涂层与基体之间形成互熔区,涂层与基体之间产生良好的冶金结合.