钨酸钠及其复配缓蚀剂在模拟海水中对碳钢的缓蚀性能

目的考察在模拟海水中,钨酸钠及其与月桂酰肌氨酸钠复配物对Q235钢的缓蚀性能。方法进行挂片失重法实验,研究缓蚀剂添加量对缓蚀效率的影响;测定电化学极化曲线及阻抗谱,对比单一钨酸钠缓蚀剂与复配缓蚀剂的缓蚀效率以及相关拟合数据。结果钨酸钠单独使用时的缓蚀效果良好,缓蚀效率随着添加量的增加而增大,且在碳钢表面的吸附符合修正了的Langmuir吸附模型;与月桂酰肌氨酸钠复配后,缓蚀效率更高,阴极、阳极的塔菲尔斜率均减小,腐蚀电流密度也降低了很多。结论钨酸钠与月桂酰肌氨酸钠复配后比单独使用效果更好,二者有较好的协同缓蚀增效作用;复配缓蚀剂为混合型缓蚀剂。     

水溶性壳聚糖及其复配的缓蚀性能

钼酸盐、铬酸盐和硫酸锌是目前公认的缓蚀效果优良的缓蚀剂.理论上讲壳聚糖也具有一定的缓蚀作用,为验证水溶性壳聚糖的缓蚀类型及其复配的协同缓蚀效果,对水溶性壳聚糖与钼酸铵、硫酸锌以及铬酸钠复配的缓蚀性能进行了研究.结果表明:钼酸铵与壳聚糖复配使用,会发生严重的絮凝现象;硫酸锌与壳聚糖复配,会降低腐蚀电流密度,提高缓蚀效率,但也有少量絮凝物,并且提高温度絮凝物增多;铬酸钠与壳聚糖复配,无论在常温还是60℃高温条件下,都能产生较好的协同缓蚀效果,不发生絮凝且降低环境污染,适宜复配.     

月桂酰两性基二乙酸二钠的缓蚀性能增效研究

目的研究KI和硫脲对月桂酰两性基二乙酸二钠的缓蚀增效作用。方法首先以静态挂片失重法测定三乙醇胺、乙二胺四甲叉膦酸钠(EDTMPS)、月桂酰两性基二乙酸二钠(M)三种缓蚀剂的缓蚀性能,筛选出缓蚀效果最好的月桂酰两性基二乙酸二钠作为复合缓蚀剂的主要成分,然后对月桂酰两性基二乙酸二钠进行复配增效实验,并采用3D激光共聚焦显微镜对腐蚀过后的挂片表面形貌进行观察,采用EDS及SEM对挂片表面上形成的腐蚀产物膜进行表征。结果当KI和月桂酰两性基二乙酸二钠的质量比为1:5时(M5K),缓蚀率提高了7%,腐蚀速率降低了0.0105 mm/a,缓蚀效果最佳;当硫脲与月桂酰两性基二乙酸二钠以1:10的比例进行复配时(M10S),缓蚀率提高5.8%,腐蚀速率降低0.0114mm/a,此时的缓蚀效果略低于M5K。结论在特定的比例下,KI和硫脲对月桂酰两性基二乙酸二钠的缓蚀性能均有一定的增效作用。KI是增加其吸附性能,而硫脲则是产生鳌合作用,这为两性咪唑啉的缓蚀性能增效研究提供了一定的参考。     

钼酸钠和三乙醇胺对铜的缓蚀作用

利用极化曲线法研究了钼酸钠以及钼酸钠和三乙醇胺以特定的配比形成的复合缓蚀剂对铜的缓蚀作用.结果发现：单独使用钼酸钠时，缓蚀效果不明显;钼酸钠与三乙醇胺的协同作用时，钝化区显著增宽，缓蚀效果提高，且所需剂量更少，表明钼酸钠和三乙醇胺共同作用在去离子水中及在含5×10-3 g/L Cl-的去离子中对铜具有明显的协同缓蚀作用.且当钼酸钠为300 mg/L，三乙醇胺也为300 mg/L时，协同缓蚀效率最高.      

Zn(NO3 ) 2 ·6H2O,Na2MoO4 ·2H2O 与 Na5P3O10对 1Cr18Ni9Ti 的协同缓蚀作用

目的研究硝酸锌、钼酸钠及三聚磷酸钠之间的协同缓蚀作用机理,使其在性能上实现互补。方法以酸性高锰酸钾溶液为基础,通过极化曲线和失重法实验,研究3种缓蚀剂对1Cr18Ni9Ti奥氏体不锈钢的协同缓蚀作用。结果硝酸锌和三聚磷酸钠以抑制不锈钢的阴极反应为主,钼酸钠则主要抑制不锈钢的阳极反应。硝酸锌与钼酸钠表现出明显的拮抗作用,导致缓蚀效果变差。只有当三聚磷酸钠加入后,三者之间才表现出了良好的协同作用,使总的缓蚀性能达到最优,复配后的缓蚀效率可以达到90%以上。结论硝酸锌、钼酸钠及三聚磷酸钠之间存在良好的协同缓蚀作用,可以明显降低1Cr18Ni9Ti不锈钢在酸性高锰酸钾溶液中腐蚀速率,从而延长设备的使用寿命。     

在自来水中绿色碳钢缓蚀剂的研究

主要通过挂片法和交流阻抗谱法研究中性自来水介质中钼酸钠、苯并三氮唑及它们之间的复配,分析了钼酸钠与苯并三氮唑可能的缓蚀机理以及其最佳浓度组合.试验结果表明,温度越高,碳钢的腐蚀越严重,温度对其腐蚀的影响较大;腐蚀速度总趋势是随着时间的推移逐渐减小的;钼酸钠在一定用量时对碳钢具有一定的缓蚀作用,随着药剂用量的增加,缓蚀作用增强,把钼酸钠与苯并三氮唑混合使用时用量小,且缓蚀效果好,比较合适的配比为0.0004mol/L钼酸钠加0.0002mol/L苯并三氮唑.     

用于含聚合物钻井液的缓蚀剂研究

    通过线性极化法筛选出单组分缓蚀效果较好的钼酸钠、含硅化合物为复配的基本配方.利用极化曲线法评定复合缓蚀剂的缓蚀效果,并研究其缓蚀机理.结果表明,复配后的缓蚀效果优于未添加缓蚀剂或添加单组分缓蚀剂,说明复合缓蚀剂各组分之间具有一定的协同缓蚀效果,能够有效地在金属表面形成具有互补性的保护膜,能有效提高自腐蚀电位,降低腐蚀电流.用交流阻抗法分析了缓蚀剂的缓蚀机理,并用重量法进行了验证.     

二氧化氯介质中脂肪醇聚氧乙烯醚及其复配缓蚀剂对Q235 钢的缓蚀作用

通过静态失重法、动电位极化曲线法及观察显微形貌,研究了脂肪醇聚氧乙烯醚(平平加O-20)及其复配缓蚀剂在100 mg/L二氧化氯介质中对Q235钢的缓蚀效应。结果表明:平平加O-20对Q235钢有一定的缓蚀效果,但单独使用时的用量较大;平平加O-20与硝酸钠、钼酸钠、苯甲酸钠均有缓蚀协同效果,与苯甲酸钠复配的缓蚀协同效应最明显;当苯甲酸钠和平平加O-20复配的质量浓度比为6:4,总用量为300 mg/L时,最大缓蚀效率可达92.55%。     

复配缓蚀剂在石油沉积水中对Q235钢的缓蚀性能

采用极化曲线和交流阻抗谱法研究十二烷基苯磺酸钠(SDBS)缓蚀剂单独使用及与十六烷基三甲基溴化铵(CTAB)复配缓蚀剂在石油沉积水中对储油罐钢Q235的缓蚀性能。实验结果表明:单独使用SDBS缓蚀剂对Q235钢有一定的缓蚀效果;使用SDBS与CTAB复配缓蚀剂时,缓蚀效果明显提高,当两者复配比例为1:1且浓度都为0.5mmol/L时,缓蚀效率最高为91%,复配缓蚀剂具有很好的协同缓蚀效应。     

环保型无磷缓蚀阻垢剂的制备

以低分子量聚丙烯酸钠(PAAS)为基础,将聚丙烯酸钠、钼酸钠、D-葡萄糖酸钠、苯并三氮唑、六次甲基四胺等物质按一定比例复配成无磷缓蚀阻垢剂配方,采用碳酸钙沉积法评价其阻垢性能,用旋转挂片法和电化学法评价其缓蚀性能。优选出的最佳缓蚀剂配方为:聚丙烯酸钠15mg/L、D-葡萄糖酸钠14mg/L、苯并三氮唑13mg/L、钼酸钠18mg/L、六次甲基四胺14mg/L,其阻垢率为92.63%,缓蚀率为92.78%。该配方具有无磷、无毒、高效、环保等特点,具有重要的经济和利用价值。     

Corrosion Inhibition of Galvanized Steel in NaCl Solution by Tolytriazole

Corrosion inhibition of tolytriazole for galvanized steel was studied in 5 mM NaCl by using potentiodynamic polarization and electrochemical impedance spectroscopy(EIS), scanning vibrating electrode technique(SVET). The results of EIS and polarization tests indicate that tolytriazole is effective in corrosion inhibition of galvanized steel. As the concentration of tolytriazole is increased to 0.01 M, the inhibiting efficiency reaches above 98%. The low values of anodie and cathodic current density in SVET maps suggest that the complex of tolytriazole with galvanized steel inhibits the anodic and cathodie reactions of corrosion of zinc. The adsorption behaviour of tolytriazole is found to conform to Langmuir adsorption isotherm, which is typical chemical adsorption.     

Corrosion Inhibition of Galvanized Steel in NaCI Solution by Tolytriazole

Corrosion inhibition of tolytriazole for galvanized steel was studied in 5 mM NaCl by using potentiodynamic polarization and electrochemical impedance spectroscopy (EIS), scanning vibrating electrode technique (SVET). The results of EIS and polarization tests indicate that tolytriazole is effective in corrosion inhibition of galvanized steel. As the concentration of tolytriazole is increased to 0.01 M, the inhibiting efficiency reaches above 98%. The low values of anodic and cathodic current density in SVET maps suggest that the complex of tolytriazole with galvanized steel inhibits the anodic and cathodic reactions of corrosion of zinc. The adsorption behaviour of tolytriazole is found to conform to Langmuir adsorption isotherm, which is typical chemical adsorption.     

N,N′-二苯基硫脲对Q235钢在酸性介质中的缓蚀作用及其与十二烷基磺酸钠的协同效应

用动电位扫描极化曲线、电化学阻抗法和量子化学法,研究了N,N′-二苯基硫脲（DPH-TU）在5%H_2SO_4介质中对Q235钢的缓蚀作用机理,及其与十二烷基磺酸钠（SDBS）的协同缓蚀效应结果表明N,N′-二苯基硫脲是一种缓蚀效果显著的混合型缓蚀剂.当DPH-TU和SDBS共存时呈现协同缓蚀效果,两者浓度比为1：1时...     

聚环氧琥珀酸及其复配物的缓蚀性能研究

用旋转挂片法研究了聚环氧琥珀酸与锌盐复配对碳钢缓蚀作用的协同效应;同时研究了聚环氧琥珀酸与苯并三氮唑的复配对黄铜的缓蚀协同效应.实验结果表明:聚环氧琥珀酸与Zn2+质量比为6∶4时,协同增效作用最佳.以此比例在模拟水中,使用量为60 mg/L,缓蚀率达到97.57%.当聚环氧琥珀酸与苯并三氮唑复配时,在使用量聚环氧琥珀酸为20 mg/L,苯并三氮唑为1 mg/L时,缓蚀率达到82.14%,缓蚀协同效果也较好.     

Corrosion control of galvanized steel using a phosphate/calcium ion inhibitor mixture

The corrosion inhibition of galvanized steel was studied in artificial acid rain solution using extracts of pigments normally used in organic coatings for corrosion control. It was established that a combination of zinc phosphate/molybdate and calcium ion exchange silica has a significant synergetic anticorrosion effect in the acid rain solution compared to the pigments used alone. Further, the charge transfer resistance of galvanized steel in acid rain solution saturated by the above pigment blend approaches that of strontium chromate in artificial acid rain solution. Use of the pigment blend was found to lead to development of a protective film, which is thought to be a complex mixture of calcium phosphates and zinc phosphate.     

木质素磺酸钠对3.5%NaCl溶液中AZ31镁合金的缓蚀作用

采用失重法,极化曲线,电化学阻抗谱和扫描电子显微镜研究木质素磺酸钠(SLS)在质量分数为3.5%NaCl溶液中对AZ31镁合金的缓蚀作用。结果表明:在298 K时SLS可有效抑制AZ31在Na Cl介质中的腐蚀。当SLS为4.0 g·L~(-1)时,缓蚀率可达到最大。提高浓度后,其缓蚀率会下降。SLS是阴极型缓蚀剂,并且SLS在AZ31表面的吸附符合Langmuir吸附模型。由吸附自由能?G~0及Arrhenius活化能E_a可知,SLS在AZ31镁合金表面是化学吸附。     

核桃青皮提取物和十二烷基硫酸钠对冷轧钢在H3PO4溶液中的缓蚀协同效应

目的研究核桃青皮提取物(WGHE)和阴离子表面活性剂十二烷基硫酸钠(SDS)混合复配后,对冷轧钢(CRS)在H3PO4中的缓蚀协同效应,揭示缓蚀协同性能影响规律,并探究缓蚀协同机理。方法采用回流提取法从农林废弃物核桃青皮中提取制备出WGHE。利用失重法、电化学法、紫外光谱(UV)、扫描电子显微镜(SEM)、原子力显微镜(AFM)研究WGHE和SDS的复配缓蚀协同性能、电化学作用机理、紫外吸收曲线以及钢表面的微观形貌。结果高浓度的WGHE对冷轧钢在1.0 mol/L H3PO4中具有较好的缓蚀作用,但低浓度时的缓蚀效果较差。单独SDS使用时,最大缓蚀率不超过60%;将WGHE与SDS复配后,缓蚀性能可进一步提升,尤其在WGHE用量为10～40 mg/L时,复配协同作用显著。缓蚀率随着缓蚀剂浓度的增加而升高,但随着温度的上升有所降低,WGHE、SDS复配前后在钢的表面吸附均符合Langmuir吸附等温式。动电位极化曲线表明,WGHE、SDS为阴极抑制型缓蚀剂,但WGHE/SDS为混合抑制性缓蚀剂。Nyquist图在高频区呈单一弥散容抗弧,而在低频区出现小段感抗弧,WGHE与SDS复配后电荷转移电阻显著增大。协同体系中WGHE和SDS会发生相互作用。SEM和AFM所呈现的微观形貌更加清晰地表明WGHE/SDS具有良好的缓蚀协同性能。结论 WGHE和SDS对冷轧钢在1.0 mol/L H3PO4中具有明显的缓蚀协同效应,复配后缓蚀性能进一步提升,同时有效抑制了钢的阴极和阳极腐蚀反应。