镍基高温合金U720Li的组织稳定性及蠕变行为

研究了新型镍基高温合金U720Li在650和700℃时组织稳定性,蠕变和变形机制。结果表明,在长期时效过程中,初生γ‘、二次γ‘相以及晶界析出相的形态几乎不发生变化,三次γ‘相经历一个粗化长大和溶解消失的过程中,蠕变第一阶段的形变量随着施加应力的增加单调增大,而在700℃蠕变时,蠕变第一阶段的形变量随着施加应力的增加先降后升。合金650和700℃蠕变断裂寿命和最小蠕变速率在低应力区和高应力区服从于不同斜度的双对数线性规律。在高温低应力下,合金的蠕变机制为位错攀移机制,而在低温高应力下,蠕变过程由位错切割机制控制。     

6%Re/5%Ru单晶镍基合金的超高温蠕变行为和影响因素EI北大核心CSCD

通过对6%Re/5%Ru单晶镍基合金(质量分数)进行蠕变性能测试和组织观察,研究了合金的超高温蠕变行为和影响因素。结果表明:测定出合金在(1160℃,120 MPa)的蠕变寿命为206 h。中期稳态阶段,位错在基体中滑移和攀移越过γ′相是合金的变形特征,γ基体中溶解的难熔元素可增加位错在基体中运动的阻力。超高温蠕变期间,随温度提高γ′相发生溶解,可减小筏状γ′相的尺寸,提高位错攀移越过γ′相的速率,特别是当温度大于1170℃时,合金的施加温度敏感性使筏状γ′相的尺寸减小,应变速率提高,这是合金蠕变寿命大幅度降低的主要原因。蠕变后期,基体位错可在位错网破损处切入γ′相,其中,切入γ′相的位错可由{111}面交滑移至{100}面形成K−W锁,抑制位错的滑移和交滑移,可改善合金的蠕变抗力。而在颈缩区域较大的有效应力可开动位错的双取向滑移,致使筏状γ′相扭折,并在扭折区域发生裂纹的萌生和扩展,直至断裂,这是合金在超高温蠕变期间的变形和损伤机制。     

DZ125镍基合金的显微组织与蠕变行为

通过蠕变性能测试及组织形貌观察,研究DZ125合金的高温蠕变行为。结果表明:经完全热处理后,合金在枝晶干/间区域存在明显的组织不均匀性,粗大γ′相存在于枝晶问,细小γ′相存在于枝晶干。蠕变初期合金中γ′相已转变成筏状结构,稳态蠕变期间合金的变形机制是位错攀移越过γ′相,其中,位错攀移期间,易形成位错的割阶,空位的形成和扩散是位错攀移的控制环节。而蠕变后期合金的变形机制是位错在基体中滑移和剪切进入筏状γ′相。在高温蠕变后期,合金中裂纹首先在晶界处萌生与扩展,且不同形态晶界具有不同的损伤特征,其中,沿应力轴成45°角晶界承受蠕变损伤的较大剪切应力可使其发生较大几率的蠕变损伤;而加入的元素Hf促进细小粒状相沿晶界的析出,可抑制晶界滑移,提高晶界强度,是合金蠕变断裂后晶界呈现非光滑表面的主要原因。     

单晶镍基高温合金超高温蠕变期间的变形机制

通过蠕变性能测试及组织形貌观察,研究了6％Re-5％Ru(质量分数)单晶镍基高温合金的超高温蠕变行为和变形机制.结果 表明,该合金在1160℃/120 MPa条件下的蠕变寿命为206 h.稳态蠕变期间,位错在基体中滑移和攀移越过筏状γ'相是合金的变形特征,基体中溶解的高浓度难熔元素可增加位错运动阻力.蠕变后期,切入筏状...     

[111]取向镍基单晶合金的组织结构与蠕变行为

通过蠕变曲线的测定及微观组织形貌观察,研究[111]取向镍基单晶合金在高温低应力条件下的组织结构与蠕变行为。结果表明:经完全热处理后,[111]取向单晶合金的组织结构是立方γ′相以共格方式嵌镶在γ基体中,并沿100方向规则排列;在1 040~1 080℃、137~180 MPa的温度和应力范围内,该取向单晶合金表现出明显的温度和施加应力敏感性。蠕变期间,γ′相沿与应力轴呈一定角度形成筏状组织,蠕变后期在近断口区域筏状γ′相发生粗化和扭折。[111]取向单晶合金在蠕变期间的变形特征是位错在γ基体通道中运动和剪切筏状γ′相,由于形变量较大,较多位错切入筏状γ′相后使其形成亚晶结构,其中,蠕变后期大量位错切入筏状γ′相导致合金的蠕变抗力降低,是合金发生蠕变断裂的主要原因。     

热力耦合对一种第四代镍基单晶高温合金1100℃蠕变组织演变的影响

以一种第四代镍基单晶高温合金为研究对象,采用变截面蠕变试样,在1100℃、43~96 MPa条件下进行200 h蠕变中断实验,利用SEM和TEM观察了微观组织演变规律,利用同步辐射高能XRD和EPMA分析了高温低应力条件下镍基单晶高温合金的蠕变组织演变。结果表明:随着应力的增大,镍基单晶高温合金的γ′相体积分数降低,筏化程度增大且筏排厚度下降,同时,γ相通道宽度逐渐增大,而γ/γ’两相界面位错网间距逐渐减小。固溶强化元素Re、Mo和Cr等在γ相中的富集导致γ/γ’两相错配度绝对值增大。蠕变过程中γ’相体积分数降低和γ’相筏排厚度减小显著降低了合金的强度。另外,位错在γ′相溶解所导致的弯曲相界处的塞积,使位错易于切入γ′相,也是镍基单晶高温合金室温硬度下降的重要原因。     

一种含Re单晶镍基合金的组织结构与蠕变性能

通过组织形貌观察及蠕变曲线测定,研究了一种含Re镍基单晶合金在高温的蠕变行为。结果表明,合金经完全热处理后的组织结构是立方γ′相以共格方式嵌镶在γ基体中。在试验的温度和应力范围内,与无Re合金相比较,含Re合金有较好的蠕变抗力及较长的蠕变寿命,并测算出合金在稳态期间的蠕变激活能与应力指数。通过分析位错攀移越过筏状γ′相及影响合金应变速率的因素,研究了合金在稳态蠕变期间的变形机制,其中,元素Re溶入γ基体后可有效阻碍位错运动,降低合金的应变速率,是使合金具有较低应变速率和较长蠕变寿命的主要原因。     

定向凝固DZ17镍基高温合金的蠕变位错亚结构

本文通过金属薄膜电镜观察,研究了DZ17镍基高温合金在750℃,647MPa条件下,蠕变三个阶段的位错亚结构,以及它们与合金的强化相γ′的相互作用。据此认为,DZ17合金的高温蠕变过程受控于位错切割过强化相γ′粒子的机制。     

一种2%Ru镍基单晶合金的高温蠕变行为及断裂特征

通过蠕变性能测试和组织形貌观察,研究了一种新型2%Ru镍基单晶高温合金的蠕变行为及断裂特征。结果表明,合金在1 070～1 100℃、127～147 MPa条件下具有较好的蠕变性能,合金在稳态蠕变阶段的表观蠕变激活能Q=410.5 kJ/mol,应力指数n=4.74。合金在蠕变稳态阶段的变形机制是位错在基体中滑移和攀移越过γ′相,蠕变后期,位错可剪切进入γ′相。在高温/低应力条件下,合金中的γ′相可形成筏状组织,裂纹由筏状γ′相与基体相界面处萌生,随裂纹扩展、聚集、连通,合金蠕变抗力急剧下降,最终导致合金蠕变断裂。     

含Mo单晶镍基合金的高温蠕变及损伤行为

通过蠕变性能测试及组织形貌观察,研究含3%和5%(质量分数)Mo无Re单晶镍基合金的高温蠕变和损伤行为。结果表明:与3%Mo单晶合金相比,5%Mo无Re单晶合金具有较好的蠕变抗力和较长的蠕变寿命,测定出5%Mo单晶合金在1040℃、137 MPa的蠕变寿命为556 h。在施加的温度和应力范围内,测定出合金在稳态蠕变期间的表观蠕变激活能Q=484.7 kJ/mol。合金在稳态蠕变期间的变形机制是位错在基体中滑移和攀移越过筏状γ′相;合金在蠕变较后阶段的变形机制是位错剪切进入筏状γ′相。随蠕变进行,位错的交替滑移致使合金中筏状γ′相发生扭曲,并在筏状γ′/γ两相界面发生裂纹的萌生和扩展,直至断裂,是合金在高温蠕变后期的损伤与断裂机制。     

Three-Dimensional Growth of Coherent Ferrite in Austenite: A Molecular Dynamics Study

Coherent second phase often exhibits anisotropic morphology with specifi c orientations with respect to both the second and the matrix phases. As a key feature of microstructure, the morphology of the coherent particles is essential for understanding the second-phase strengthening eff ect in various industrial alloys. This letter reports anisotropic growth of coherent ferrite from austenite matrix in pure iron based on molecular dynamics simulation. We found that the ferrite grain tends to grow into an elongated plate-like shape, independent of its initial confi guration. The fi nal shape of the ferrite is closely related to the misfi t between the two phases, with the longest direction and the broad facet of the plate being, respectively, consistent with the best matching direction and the best matching plane calculated via the Burgers vector content(BVC) method. The strain energy calculation in the framework of Eshelby's inclusion theory verifi es that the simulated orientation of the coherent ferrite is energetically favorable. It is anticipated that the BVC method will be applicable in analysis of anisotropic growth and morphology of coherent second phase in other phase transformation systems.     

Effect of Short-Time Aging on the Pitting Corrosion Behavior of a Novel Lean Duplex Stainless Steel 2002

The effect of short-time aging in the temperature range between 400 and 1000 °C on the pitting corrosion behavior and mechanical property of a novel lean duplex stainless steel(LDSS) 2002 was investigated through the potentiostatic critical pitting temperature(CPT) tests and the Charpy impact tests. Both the pitting corrosion resistance and the toughness of aged specimens degraded due to the precipitation of detrimental secondary phases and the most significant reduction of CPT and impact energy emerged at 650 °C concurrently. The CPT of LDSS 2002 specimen aged at 650 °C decreased by 28 °C, and the impact energy dropped from 69 to 29 J/cm~2 compared with the solution-annealed sample. Transmission electron microscopy characterization showed that the main precipitates in LDSS 2002 were Cr_2N and M_(23)C_6 along the ferrite–austenite grain boundaries.     

INTRODUCTION TO PATENTS

The invention provides a method of making a mold which can reduce SOx generation rate while preventing decrease in hardening rate in the case of using sulfuric acid for a hardener composition. The method has a mixture step in which fire-resistant particles, a hardener composition and a binder composition are mixed to obtain a composition for a mold. The hardener composition contains sulfuric acid. In the mixture step, sodium carbonate is added. A molar ratio of the sulfuric acid to the sodium carbonate is 0.5 or more and 4.0 or less.     

China Foundry Week 2014

China Foundry Week, hosted by the Foundry Institution of Chinese Mechanical Engineering Society （FICMES） each year, is a large academic event in China. It is one of the ten high-impact activities sponsored by the Chinese Mechanical Engineering Society.     

17th Conference of Hydrodynamic and Electromechanical Control Engineering Call for papers

正1.Contents In order to promote the academic exchanges and technical communication of the research in the field of fluid power transmission and control,fluid control engineering specialized committee of the Chinese Society of Theoretical and Applied Mechanics will hold the 17th Conference of Hydrodynamic and Electromechanical Control Engineering on July 27-29,2014 in Tibet,Lhasa city.     

Information for Contributors

正The Transactions of Nonferrous Metals Society of China,founded in 1991 and sponsored by The Nonferrous Metals Society of China,is published monthly now and mainly contains reports of original research which reflect the new progresses in the field of nonferrous metals science and technology,including mineral processing,extraction metallurgy,metallic materials and heat treatments,metal working,physical metallurgy,powder metallurgy,with the emphasis     

Preface

<正>We are pleased to present this Special Issue of Transactions of Nonferrous Metals Society of China containing selected papers from the First Asian Conference on Aluminum Alloys(ACAA-2013),held in Beijing,China,13–17 October 2013.This conference has been initiated,with approval of     

Information for Contributors

The Transactions of Nonferrous Metals Society of China, founded in 1991 and sponsored by The Nonferrous Metals Society of China, is published monthly now and mainly contains reports of original research which reflect the new progresses in the field of nonferrous metals science and technology, including mineral processing, extraction metallurgy, metallic materials and heat treatments, metal working, physical metallurgy, powder metallurgy, with the emphasis on fundamental science. It is the unique preeminent publication in English for scientists, engineers, under/post-graduates on the field of nonferrous metals industry. This journal is covered by many famous abstract/index systems and databases such as SCI Expanded, Ei Compendex Plus, 1NSPEC, CA, METADEX, AJ and JICST.     

FORMULAS OF TENSION OF CONTINUOUS ROLLING PROCESS

The development of computer controlled continuous rolling process calls for a mathematical expression that can express the inequality condition of "constant flow". Tension is the link of the continuous rolling process. From the condition of dynamic equilibrium, a differential equation of tension is given out. On the basis of the physical rules established from the industrial practice and experimental studies, the law of volume constancy, the linear relation of forward slip and tension, the state equation of continuous rolling, the formula of dynamic tension, and the formula of static tension have been obtained. These formulae reflect the functional relations between tensions, thickness, roll velocity, and time in the continuous rolling process. It is implied that the continuous rolling process is a gradually steady, controllable, and measurable dynamic system. An assumption of predicting the thickness of a steel plate using these tension formulae is also put forward.     

Bulletin of the Awards in 2013

<正>Five reviewers and 9 published articles are selected as the Excellent Rewewerand Excellent Article in 2013 respectively.Excellent Reviewers:Prof.Z ongyi Ma(Institute of Metal Research,CAS,C hina);Prof.Y ongbo Xu(Institute of Metal Research,CAS,C hina);Prof.Guangping Zhang(Institute of Metal Research,C AS,C hina);Prof.Z hendui Cui(Tianjin University,China);