基于Anycasting的齿圈座的铸造工艺优化

运用AnyCasting对齿圈座铸件工艺方案进行模拟,结果表明铸件存在铸造缺陷。针对原工艺存在的不足,对工艺进行了优化,包括浇注系统和冒口的设计、冷铁的放置等。工艺优化后,铸件缺陷出现的概率大大降低,铸件工艺出品率得到提高。     

机床滑枕铸造工艺数值模拟与优化

针对机床滑枕体积大、结构复杂,铸造加工中膨胀难以控制,易出现缩松、缩孔缺陷的问题,在对原滑枕铸造工艺及实际生产中出现缺陷分析的基础上,使用Pro CAST模拟软件对铸件凝固过程进行数值模拟。根据模拟结果对铸造工艺从浇注系统、冒口设计、冷铁布置等方面进行优化。最终克服铸件缩松、缩孔缺陷的出现,得到滑枕铸件铸造工艺的最佳方案。     

ZG270-500大臂架铸造工艺优化

针对高速工程车大臂架铸造合格率不高问题,对大臂架的原铸造工艺方案进行分析,并运用AnyCasting进行数值模拟。对分型面、浇注系统、冒口及冷铁设置进行优化改进,并对优化后的工艺方案进行数值模拟验证。模拟结果表明,铸件按工艺设计进行顺序凝固,铸造缺陷可以解决。经过小批量生产验证,铸件出现铸造缺陷的概率大幅降低,合格品率由70%提高到92.5%。     

绞车滚筒铸铁件的铸造工艺设计和数值模拟

对铸铁件JH-20型回柱绞车滚筒进行铸造工艺设计.根据铸件形状对称的特点,设计了底注式浇注系统,采用两个内浇道同时对铸件浇注.利用CAD软件建立铸件的三维模型,并用ViewCast铸造模拟软件对铸件的凝同过程进行了数值模拟.模拟显示,在滚筒与法兰连接处会产生缩孔、缩松缺陷.根据数值模拟结果并结合理论分析,对铸造工艺方案进行工艺改进.通过增设冒口的方法,利用冒口对铸件进行补缩,以实现铸件的顺序凝固.结果表明,优化后的工艺有效地消除了缩松缩孔缺陷,从而获得了合理的铸造工艺方案.     

ZG270-500后桥的铸造工艺优化北大核心

针对轮式挖掘机后桥铸件合格率不高的问题，对后桥的原铸造工艺方案进行分析并运用AnyCasting进行数值模拟。分析原工艺的铸造缺陷原因，对浇注系统、补缩系统进行优化改进，并对优化设计的铸造工艺方案进行数值模拟验证，模拟结果表明后桥按工艺设计完成顺序凝固，原铸造缺陷问题得到解决。经过小批量生产验证，后桥铸件的合格率有明显提高，工艺出品率由43.4%提高到64.2%。     

蜗轮箱盖的数值模拟及铸造工艺优化

对铸铁件涡轮箱盖进行了铸造工艺设计.根据铸件形状的特点,设计了顶注式浇注系统和3个内浇道同时对铸件浇注.利用CAD软件建立铸件的三维模型,并用View Cast铸造模拟软件对铸件的凝固过程进行了数值模拟.模拟显示,在涡轮箱盖壁与壁的连接处会产生缩孔、缩松缺陷.根据数值模拟结果并结合理论分析,对铸造工艺方案进行工艺改进.通过去除胃口和增设冷铁的方法,增加圆形区域的冷却速度.结果表明,优化后的工艺有效地消除了缩松、缩孔缺陷,从而获得了合理的铸造工艺方案.     

基于均衡凝固理论的锌锭模铸造工艺数值模拟

基于铸件均衡凝固理论,拟定锌锭模铸件的浇注方案及浇注系统的设计计算;然后利用Pro/E和Procast软件,模拟锌锭模铸件的浇注工艺过程.对比结果表明,两者基本吻合.通过模拟可以预知铸件可能产生的铸造缺陷,优化铸造工艺.     

大直径铝合金活塞的模具设计和铸造工艺优化

在原铸造工艺基础上,利用德国MAGMA铸造凝固模拟分析软件,对大直径铝活塞毛坯铸件的浇注、凝固过程进行数值模拟,预测了铸件产生铸造缺陷的可能部位.根据模拟结果,对模具结构和原有铸造工艺进行改进和优化.改进后模拟效果良好,经生产验证,铸件质量明显提高,达到大幅度缩短活塞的试制周期,节约试制成本,提高产品质量的目的.     

门框底衬铸钢件的铸造工艺设计及数值模拟

运用传统方法设计了门框底衬铸钢件的铸造工艺:包括分型面、浇注位置的选择、铸造工艺参数的确定以及浇注系统、冒口、冷铁的设计.根据铸件形状较复杂的特点,设计了两个内浇道;将铸件划分为4个补缩区域进行补缩,并配合冷铁来实现铸件的顺序凝固.用Pro/E软件建立了铸件的三维模型,采用ViewCast铸造模拟软件对铸件的凝固过程进行了模拟计算.模拟结果显示,在门框底衬凸台处会产生缩孔、缩松缺陷.根据数值模拟结果并结合理论分析,对铸造工艺方案进行了优化.通过改进工艺,最大程度地消除了铸造缺陷,从而获得了合理的铸造工艺方案.     

刹车卡钳叠型铸造数值模拟分析及工艺优化

采用有限元分析软件Procast对某轿车刹车系统卡钳叠型铸造时充型和凝固过程进行了模拟和研究,预测了缩孔、缩松等铸造缺陷出现的位置.结果表明,这些模拟缺陷与实际缺陷位置基本一致.同时,根据模拟分析结果对铸造工艺进行优化,采用反向浇注、切断分支直浇道的优化工艺稳定了浇注系统中的铁液,改善了缸体部位的缩孔、缩松.提高了铸件的合格率.     

圆锥破碎壁的铸造工艺与模拟

为提高ZGMn13圆锥破碎壁锰钢铸件的耐磨性,减少缩松、缩孔及裂纹等缺陷,对原工艺的浇注系统、冒口等进行改进。利用procast软件对铸件充型和凝固过程进行数值模拟并验证改进后的工艺,对模拟结果进行分析。结果证明,改进后的工艺提高了产品质量,减少了铸件缺陷。     

基于数值模拟的大型薄壁铝合金件差压铸造工艺设计

将传统工艺和现代计算机模拟技术相结合,利用View Cast软件对薄壁铝合金筒体铸件凝固过程进行了分析,通过凝固过程时间分布预测了缩孔缩松产生的位置。采用加设缝隙式内浇道和增大冒口尺寸的方法对初始铸造工艺方案进行了优化。再次模拟表明,改进后的方案合理可行,铸件实现了充分补缩和顺序凝固,消除了缩孔（松）等缺陷。     

Optimization of investment casting process for K477 superalloy aero-engine turbine nozzle by simulation and experiment

In order to reduce the shrinkage porosity of nickel-based superalloy castings in the investment casting process, the effects of different gating systems on mold filling, solidification process, and prediction of shrinkage porosity of aero-engine turbine nozzle castings were investigated by simulation and experimental methods. Results show that the design of the vertical runner would cause greater turbulence of the melt in the riser during the mold filling process, and the outer runner is not necessary. With the decrease in number of runners, the hot spot moves down towards the casting, and the shrinkage and porosity defects are formed in the casting below the riser. In the original designs, a certain tendency of shrinkage and porosity defect is found in the vanes, inner rings, and outer rings of the castings by both simulation prediction and experiment. Finally, based on the processing optimization, the aero-engine turbine nozzle casting with no shrinkage and porosity defects is obtained.

     

计算机模拟在冷却机轮毂铸造工艺设计上的应用

运用传统的铸造工艺设计方法对轮毂铸钢件铸造工艺进行了初步设计;利用V-Cast模拟软件,对轮毂初始工艺的凝固过程进行了模拟,分析了初始工艺产生缺陷的部位和原因.在此基础上通过添加、调整冷铁,进行工艺优化,最终获得了合适的工艺方案.模拟结果显示,优化工艺实现了轮毂的顺序凝固,消除了缩孔、缩松缺陷.     

铸钢后桥V法铸造数值模拟及工艺优化

运用ViewCast模拟软件对某铸钢汽车后桥V法铸造的凝固过程进行了数值模拟,预测了原工艺方案所产生缩孔、缩松缺陷的位置和大小。根据模拟结果,对原工艺方案进行了改进,增设横浇道和冷铁,铸件实现了顺序凝固,消除了缩孔、缩松缺陷,从而获得了合理的铸造工艺方案并通过工厂的生产验证。     

ZM6镁合金大型薄壁铸件数值模拟

用MAGMASOFT专业铸造软件对ZM6镁合金砂型薄壁件铸造过程进行了数值模拟,研究了铸件在充型和凝固过程中的温度场分布,预测了铸造过程中出现的各种缺陷.结果显示在铸件内浇道部位易出现气孔和氧化夹杂,而在铸件中部与补缩冒口连接处易出现缩孔、疏松缺陷.通过对铸件进行金相、SEM、EDAX分析,得出实际浇注铸件产生的缺陷与模拟结果相符合.     

基于数值模拟分析的铝合金缸盖罩压铸工艺优化

利用铸造模拟分析软件AnyCasting,对铝合金缸盖罩铸件进行了凝固过程数值模拟,预测其在铸造过程中可能产生缺陷的位置,分析了铸件预铸孔部位产生缩孔缺陷的原因,对压铸模具进行反复修改和优化。模拟计算了多种改进措施,通过在铸件最后凝固部位增设冷却水管及补缩通道等方法,达到减少或消除缩孔缺陷的目的。模拟结果表明：采用改进的工艺方案可明显改善缩孔缺陷,有利于提高铸件质量。     

薄壁铝合金铸件低压铸造的数值模拟与工艺优化

利用ViewCast软件研究了薄壁铝合金筒状铸件的低压铸造充型凝固过程,获得了低压铸造过程中温度场、流动速度场的分布.模拟结果显示,铸件上法兰处将产生缩孔、缩松缺陷.根据模拟结果及理论分析改进初始工艺,在产生缺陷的上法兰处安放冒口.对改进后的工艺重新进行模拟,结果表明,冒口有效地补缩了上法兰部位,消除了缩孔、缩松缺陷.     

一种解决垂直线铸件缩松的工艺方法

利用MAGMA凝固模拟软件预测垂直造型线铸件热节部位和缩松缺陷,模拟结果表明凝固后期形成的孤立热节是产生缩松的主要原因。采用顺序凝固原则可以解决部分缩松问题,但不能解决所有补缩问题。通过优化铸造工艺,改变内浇口位置并重新模拟,发现孤立热节得到了消除,试验结果与模拟吻合,缩松问题得到了彻底解决,利用凝固模拟优化冒口成功提高了铸件质量和成品率。     

球铁轮毂的凝固数值模拟及铸造工艺优化

采用华铸CAE软件,对客车的球墨铸铁轮毂铸件的凝固过程进行了数值模拟,根据对铸造工艺方案的凝固模拟和实验结果分析,获得了1种合适的铸造工艺用于轮毂铸件生产,有效地消除了轮毂生产过程的缩孔、缩松缺陷。