5052铝合金激光焊接接头组织和性能研究

采用扫描电镜、显微硬度和抗拉强度等测试方法,研究了5052铝合金激光焊接接头组织和性能。研究结果表明,铝合金激光焊接接头热影响区主要为树枝晶,晶粒较为粗大;焊缝区主要为等轴晶,晶粒较母材和热影响区细小。铝合金激光焊接接头显微硬度焊缝区最高,热影响区最低。随着激光功率的增加,铝合金激光焊接接头抗拉强度先增加后降低,激光功率3.0 k W时达到最大值204.5 MPa,拉伸断口为典型的韧窝断口形貌。     

激光-TIG复合热源焊接参数对镁/钢异种材料焊接接头的影响

采用激光-TIG复合热源的焊接方法对镁和钢异种材料进行焊接,探讨了焊接工艺参数包括激光功率、激光离焦量、焊接速度以及TIG焊接电流对焊缝抗拉强度的影响.结果表明,在焊接过程中,随着激光功率的增大、焊接速度的减小,焊缝抗拉强度随之增大;随着激光离焦量的增加,焊缝抗拉强度呈现先增大后减小的特点;而TIG电流的变化对焊缝抗拉强度影响不大.试验证明,在合适的工艺参数下,能够得到成形良好、力学性能优良的镁/钢异种材料的焊接接头,并且在焊接过程中,激光对镁和钢的连接起主要作用.     

SPA-H钢与304不锈钢异种钢焊接接头组织及性能研究

采用钨极氩弧焊对SPA-H钢与304不锈钢进行异种钢焊接,分析测试了不同焊接电流下焊接接头的显微组织、显微硬度和拉伸性能,研究了焊接电流对焊接接头组织及性能的影响。结果表明,随着焊接电流的增加,焊缝组织从定向生长的胞状晶和树枝晶到细化的胞状晶和树枝晶,再到粗大的等轴晶变化;SPA-H母材与焊缝之间存在明显的熔合线,而且随着焊接电流增加,熔合线由窄变宽;焊接接头中的硬度峰值都出现在焊缝区,电流为70 A时焊接接头焊缝和304侧热影响区的硬度值最高,但SPA-H侧热影响区的显微硬度显著低于焊缝区的显微硬度;电流为70 A的试样接头抗拉强度均高于60、80 A的焊接接头,60 A的试样接头抗拉强度和伸长率最低;三种焊接电流下的焊接接头抗拉强度均远高于母材,焊缝满足强度要求。     

X80/X100异种钢激光-MIG复合焊接头显微组织和性能

采用激光-MIG复合焊对X80管线钢和X100管线钢进行焊接,研究了激光功率对复合焊接头的焊缝形貌、显微组织、硬度、强度和韧性的影响规律.结果表明,激光功率从2.0 k W增大至3.5 k W时,盖面焊缝熔宽和熔深增加,激光区熔深明显增加;激光区焊缝中AF含量增加、LB含量减少,X100侧粗晶热影响区和细晶热影响区中条状贝氏体含量减少,X80侧粗晶热影响区和细晶热影响区中准多边形铁素体含量增加.复合焊接头硬度分布并不对称,最高硬度出现在X100侧熔合区部位.复合焊接头的抗拉强度基本不随激光功率变化,拉伸试样断裂位置均为X80侧母材.随着激光功率增大,焊接接头最高硬度和韧性均下降.     

镀锌钢板激光焊焊接接头组织与性能

采用合理的激光焊接工艺参数对镀锌钢板进行焊接,研究了激光参数对焊接接头组织和性能的影响。结果表明:焊接接头的抗拉强度随着激光功率和焊接速度的增加均呈先增大后减小趋势;焊缝区铁素体组织随着焊接功率的增加长大现象明显,而焊缝区铁素体组织却随着焊接速度的增加而变得细密;焊接接头的焊缝区的硬度均匀,且高出母材很多;焊接接头断口表现出明显的延性断裂特征。     

CO_2激光焊接600MPa DP钢接头组织与性能

采用CO2激光对抗拉强度为600MPa,厚度1.4mm的DP钢进行焊接.研究焊接速度对焊缝外观和截面成形的影响、接头的组织特点、硬度、强度和成形能力.结果表明,激光功率相同,焊接速度较低时焊缝易产生气孔,焊接速度较高时易发生飞溅;焊接速度对焊缝熔深及熔宽也有影响.焊缝区组织主要由马氏体构成,从焊缝、焊接热影响区到母材,组织中马氏体含量下降,接头的最高硬度出现在焊缝或热影响区.在平行于焊缝方向,焊接接头的抗拉强度高于母材,垂直于焊缝方向,接头的抗拉强度与母材相当.由于焊缝出现马氏体组织,接头的塑性和韧性降低,板材的冲压成形能力下降.     

TWIP钢激光焊接接头的显微组织和力学性能

研究了孪晶诱导塑性(TWIP)钢经3种不同工艺参数激光焊接后的焊接接头的显微组织和力学性能。结果表明:焊接接头焊缝区为全奥氏体组织,与母材相比,焊缝区的Mn含量略有降低;较大的焊接热输入可以保证焊缝的连续性,但也会导致焊缝组织粗大、粗晶区宽度增大;焊缝熔融区为树枝晶组织,热影响区含0. 3～0. 4 mm宽的软化区和0. 5～0. 6 mm宽的硬化区;焊接接头的最高抗拉强度和断后伸长率分别为900 MPa和33%,约为母材的90%和50%。     

激光功率对304不锈钢薄板搭接接头组织和性能的影响

研究了在1.2 mm/s焊接速度下,激光功率对304不锈钢薄板搭接接头组织和性能的影响。结果表明,焊缝区熔合线附近组织为树枝晶组织,焊缝中心为等轴晶,随着激光功率的提高,枝晶变长,枝晶间距变大,等轴晶区域减小,晶粒粗化。焊缝区的显微硬度随激光功率的提高而增大,高于母材硬度。不同激光功率条件下制备的接头强度不同,激光功率为5 kW时,接头的抗拉强度最优,略高于母材的强度。     

铜/钛合金电子束焊接工艺优化

研究了QCr0.8/TC4电子束焊接工艺及接头组织,由于铜合金热导率高而熔化量较小,以及焊缝中生成大量脆性金属间化合物相,因此对中焊时接头强度较低.采用偏铜侧进行非对中电子束焊接,接头抗拉强度随偏束量的增大而增高,偏束量为0.8mm时接头最高抗拉强度为270.5MPa.断裂发生在TC4侧熔合线处,为脆性准解理断裂特征.偏铜焊时接头成形得到改善,焊缝包括熔合区及TC4侧反应层两部分.熔合区主要由铜基固溶体组成,硬度较TC4母材有所降低.反应层成分过渡较大,含有多种金属间化合物相.随着工艺参数的变化,反应层厚度也发生变化,从而对接头性能产生影响.     

钢侧偏束电子束焊接纯铝/Q235异种金属接头试验

采用钢侧偏束电子束焊接方法对铝/钢异种金属接头进行了连接,对接头组织和相组成进行了分析,并对接头抗拉强度进行了了测试.结果表明,钢侧结合良好,焊缝组织均匀,铝侧熔合区存在过渡层,其内有金属间化合物层存在.适当的钢侧偏束量能够提高接头强度,在文中试验范围内,在偏束量为0.5 mm时获得了相对最高的抗拉强度69 MPa.金属间化合层的存在弱化了接头强度,断裂呈脆性特征.     

Nd:YAG激光焊接800 MPa TRIP钢的接头组织与性能

采用Nd:YAG激光对强度为800MPa,厚度为1.2mm的TRIP钢板进行焊接.研究焊接速度对焊缝外观和截面成形的影响及接头的组织特点、硬度、强度和成形能力.激光功率相同,焊接速度较低时焊缝易产生气孔,速度较高时易发生飞溅;焊接速度对焊缝熔深及熔宽也有影响.焊缝组织主要由马氏体构成,从焊缝、热影响区到母材,组织中马氏体含量下降,接头的最高硬度出现在焊缝或热影响区.在平行于焊缝方向,焊接接头的抗拉强度高于母材,垂直于焊缝方向,接头的抗拉强度与母材相当.由于焊缝中出现马氏体,接头的塑性和韧性降低,板材的冲压成形能力下降.     

Characteristics of Nd： YAG laser welded 600 MPa grade TRIP steel

Microstructures and mechanical properties of Nd: YAG laser welded transformation induced plasticity (TRIP) steel with tensile strength of 645 MPa were studied. Due to high cooling speed of laser welding, the weld metal mainly consists of martensite different from the base metal, which is composed of ferrite matrix with bainite and a little retained austenite. Therefore, the weld metal has maximum hardness at welded joint. The yield strength and tensile strength of welded specimens tested perpendicular to weld line were almost equal to those of the base metal. But the yield strength and tensile strength of welded specimens tested parallel with weld line were a little higher than those of the base metal. The formability of laser welded TRIP steel was decreased compared with that of the base metal.     

Nd:YAG laser micro-welding of ultra-thin FeCo–V magnetic alloy: optimization of weld strength

The main aim of this research is to optimize the tensile strength of laser welded FeCo–V alloy. A mathematical relationship was developed to predict tensile strength of the laser beam welded FeCo–V foils by incorporating process parameters such as lamping current, welding speed, pulse duration and focused position. The procedure was established to improve the weld strength and increase the productivity. The results indicate that the pulse duration and welding speed have the greatest influence on tensile strength. The obtained results showed that the tensile strength of the weld joints increase as a function of increasing pulse duration reaching to a maximum at a pulse duration value of 2.25 ms. Moreover, the tensile strength of joints increases with decrease in welding speed reaching to a maximum at a welding speed of 125 mm/min. It has been shown that increase in pulse duration and decrease in welding speed result in increased effective peak power density and hence formation of more resistant welds. At higher pulse durations and lower welding speeds, the tensile strength of weld joints decreases because of formation of solidification microcracks in the fusion zone.     

304不锈钢薄板列置双TIG高速焊缝组织与性能

相比常规速度不锈钢焊接,高速焊接过程中焊缝金属的凝固过程及组织形态将会发生变化,从而影响焊缝组织和性能. 对1.2 mm厚304不锈钢薄板对接,采用列置双TIG焊在焊接速度为3.0 m/min时获得了良好焊缝成形,并与常规速度单TIG焊接工艺相比,采用非标准拉伸试样测试了焊缝性能,并分析了其组织. 结果表明,高速双TIG焊接焊缝中心生成等轴晶,两侧树枝晶未形成对向生长的定向晶粒,焊缝抗拉强度及断后伸长率略低于母材;相比常规单TIG焊接工艺,高速双TIG焊接热影响区晶粒平均直径降低了10.3%,但焊缝中心晶粒平均直径增大了12.9%;焊缝抗拉强度和断后伸长率分别提高了4.3%和23.2%,焊缝中心硬度值略高于母材.     

铝合金/镀锌钢板Nd:YAG激光+MIG电弧复合热源熔-钎焊接头的组织与性能(英文)

基于铝合金和镀锌钢在熔点上的差异,以ER4043(AlSi5)为填充材料,采用大光斑Nd:YAG激光+MIG电弧复合热源焊接工艺实现两者的熔-钎焊接,研究熔钎焊接头组织和性能。铝合金/镀锌钢板熔钎焊接头分为熔焊接头和钎焊缝两部分,熔焊缝组织由α(Al)等轴晶和晶界上短棒状的Al-Si共晶组织组成,焊趾处的富锌区为α-Al-Zn固溶体和Al-Zn共晶组织。钎焊缝为Fe-Al金属间化合物层,厚度为2~4μm,金属间化合物包括FeAl2、Fe2Al5和Fe4Al13,其中FeAl2和Fe2Al5位于近钢侧的紧密层,而Fe4Al13则呈舌状或锯齿状向熔焊缝内生长。接头抗拉强度随着焊接电流和激光功率的增大呈先增大后减小的趋势,最高可达247.3 MPa。拉伸断裂位置一般位于熔焊缝的熔合区,为以韧性断裂为主的混合断裂。接头内硬度的最大值位于钎焊缝处,然后分别沿着两侧钢板和铝合金熔焊缝逐步降低。     

基于光纤激光的LY12铝合金焊接试验分析

在飞机制造领域,铝合金主要用于制造飞机蒙皮、梁、桁条和框架等结构.采用多模光纤激光器进行了1.4 mm厚LY12铝合金的激光焊接试验,研究了焊接工艺参数对铝合金焊缝形貌的影响规律,并对焊接接头的显微硬度及断口形貌进行了分析.结果表明,大功率高速度连续激光焊缝的成形具有不稳定性,当功率为2 200 W,焊接速度为55 mm/s,保护气体流量为10 L/min时,可以获得成形良好且无宏观缺陷的焊接接头.接头的平均抗拉强度约为388 MPa,达到母材抗拉强度的63.98%,断裂类型为韧脆混合型断裂.     

TRIP800高强度钢激光焊工艺

针对TRIP800高强度钢进行激光焊接工艺研究。实验结果表明:1.8 mm厚的TRIP800高强度钢在纯度大于99.9%的氩气保护下,采用光纤激光器焊接,在焊接速度7 mm/s、激光功率570 W、离焦量0 mm的工艺参数条件下可以获得优质的焊缝;焊接接头的抗拉强度660 MPa,断裂方式为塑性断裂。最佳工艺参数条件下的焊缝硬度呈现"M"形分布,接头的最高硬度出现在热影响区,焊缝区硬度较高,母材硬度最低。     

10Ni3CrMoV钢CO2激光多层焊的接头组织与性能

与传统电弧焊相比,激光焊接厚板优势明显。采用纯激光焊和激光电弧复合焊等多道焊接技术实现了28 mm厚10Ni3CrMoV钢的高效焊接,采用光学显微镜分析焊缝、热影响区和焊缝重叠区的组织,激光复合焊缝组织主要为针状铁素体,纯激光焊缝、粗晶区和细晶区组织主要为板条马氏体,激光复合焊缝重叠区组织为粒状贝氏体+马氏体,纯激光焊缝和激光复合焊缝重叠区组织为马氏体+少量粒状贝氏体。测试了焊接接头的力学性能,结果表明,激光复合焊缝金属的冲击韧性较高,焊接接头的抗拉强度和屈服强度与母材相当,延伸率略小于母材,焊接接头的最大硬度小于360 HV,弯曲性能合格。     

1420铝锂合金双光点激光焊接头组织性能

在2mm厚1420铝锂合金双光点激光焊接试验的基础上,研究接头的组织与性能。对比分析单、双光点激光焊接头各区域的组织、显微硬度及室温拉伸力学性能,并观察断口形貌。结果表明:1420铝锂合金双光点激光焊接头组织与单光点激光焊接头组织分布类似,从熔合区至焊缝中心依次是等轴细晶、柱状晶和等轴树枝晶,但较单光点接头细化;双光点激光焊接头各区域硬度低于母材,但高于单光点激光焊接头;双光点激光焊接头焊态抗拉强度较母材下降,但略高于单激光焊接头,可达母材的86%。