1Cr17Ni2钢连接螺栓断裂的原因

起落架连接螺栓在服役过程中发生断裂,通过对断裂螺栓进行材质、工艺、断口、金相组织、能谱等分析,找出其断裂失效原因.结果表明起落架连接螺栓的开裂性质为应力腐蚀开裂,腐蚀性元素为氯离子,1Cr17Ni2螺栓在400～580℃回火后,碳化物在晶界析出,降低了材料的抗腐蚀性能,是造成螺栓断裂的主要原因.     

00Cr13Ni6MoNb 锻件开裂原因分析

通过金相分析、拉伸断口形貌及能谱分析,发现00Cr13Ni6MoNb锻件开裂原因为粒状第二相晶界偏聚,使晶界弱化,引起沿晶脆性断裂。     

EFFECT OF CREEP FRACTURE TOUGHNESS ON CRACK INITIATION AND GROWTH

本文研究了蠕变断裂韧性对二种低合金耐热钢蠕变裂纹开裂和扩展的影响。试验表明:随着蠕变断裂韧性提高,抗蠕变裂纹开裂和扩展能力增加。材料呈韧性或脆性状态时,蠕变裂纹萌生和扩展过程不同。韧性状态时,裂纹为穿晶和晶界二种混合形式:穿晶裂纹可在晶内碳化物处发生,或在晶界上形核后向晶内扩展,晶界裂纹仍是由晶界上空洞形成和相互连接而成,裂纹可沿晶界和晶内扩展,但不连续。脆性状态时,裂纹沿晶界发生,它是由晶界形成空洞和相互连接而成,扩展仅沿晶界发生。     

蠕变断裂韧性对裂纹开裂和扩展的影响

本文研究了蠕变断裂韧性对二种低合金耐热钢蠕变裂纹开裂和扩展的影响。试验表明:随着蠕变断裂韧性提高,抗蠕变裂纹开裂和扩展能力增加。材料呈韧性或脆性状态时,蠕变裂纹萌生和扩展过程不同。韧性状态时,裂纹为穿晶和晶界二种混合形式:穿晶裂纹可在晶内碳化物处发生,或在晶界上形核后向晶内扩展,晶界裂纹仍是由晶界上空洞形成和相互连接而成,裂纹可沿晶界和晶内扩展,但不连续。脆性状态时,裂纹沿晶界发生,它是由晶界形成空洞和相互连接而成,扩展仅沿晶界发生。     

低纬度热带岛礁大气环境中高强度不锈钢螺栓断裂分析

高强度不锈钢05Cr17Ni4Cu4Nb螺栓在低纬度岛礁大气环境中短期服役后出现延迟断裂，通过成分测试、金相观察、力学性能、硬度测试、断口观察等方法进行断裂分析。结果表明:螺栓金相组织无异常，化学成分、力学性能、硬度符合标准要求；断口形貌表明螺栓具有呈现树枝状裂纹、沿晶断口等典型应力腐蚀断裂特征；结合螺栓的装配结构、受力情况和服役环境，可以判断螺栓的环境致脆机理为应力腐蚀开裂。该螺栓在我国海南及其他热带、亚热带、温带等沿海海洋环境长期服役后未发生延迟断裂，这说明干湿交替频繁、盐雾与温湿度较高的低纬度热带岛礁大气环境促进05Cr17Ni4Cu4Nb螺栓在装配结构中应力腐蚀开裂行为的发生。     

某型发动机38CrA螺栓断裂机理分析

通过对某型发动机38Cr A螺栓断口的宏微观形貌观察、能谱分析及现场工艺复查,研究了38Cr A螺栓故障件的断裂机理。结果表明:由于操作不当造成表面应力集中,在螺纹底部产生微裂纹;第一次错误镀锌工序中,异常镉元素沿晶界渗入基体内部,导致失效螺栓断口存在大量镉元素;后续的除氢工序中熔融态镉原子靠其表面的自扩散向裂纹尖端沿晶扩散,使得晶界弱化,最终导致螺栓沿晶脆断。     

发电机定子穿芯螺栓断裂分析

发电机定子穿芯螺栓在运行过程中发生断裂。为确定断裂原因,对其进行解剖检验分析。源区微观形貌为沿晶断裂。通过对缺陷的金相分析,认为奥氏体晶界上存在沿晶界分布的合金碳化物和合金化合物。这些脆性析出物使奥氏体晶界弱化。在周期性应力作用下发生断裂。     

40Cr浮头螺栓断裂原因分析

浮头式换热器40Cr紧固螺栓使用时间不到2 a即发生断裂。通过宏观观察、化学成分分析、硬度测试、金相检验和断口分析,确定螺栓的断裂原因。结果表明:由于调质处理不当,螺栓显微组织为保持马氏体位向的回火索氏体,铁素体沿原奥氏体晶界网状析出,硬度值偏高,导致材料抵抗硫化物应力腐蚀能力不足。长期在湿硫化氢环境中服役,在拉应力作用下,发生湿硫化氢应力腐蚀和氢致开裂,导致螺栓断裂。     

��������Ӵ�о��˨���ѷ���

 发电机定子穿芯螺栓在运行过程中发生断裂。为确定断裂原因，对其进行解剖检验分析。源区微观形貌为沿晶断裂。通过对缺陷的金相分析，认为奥氏体晶界上存在沿晶界分布的合金碳化物和合金化合物。这些脆性析出物使奥氏体晶界弱化。在周期性应力作用发生断裂。     

Stavax ESR钢洗衣机面板模具开裂原因分析

针对Stavax ESR钢洗衣机面板模具开裂问题,对模具失效件进行断口扫描电镜及微区能谱分析,以及采用金相显微镜对材料基体组织进行检测,综合检测结果,最终确定造成模具早期开裂的内在原因,是由于组织中沿晶界残留未溶颗粒状及薄片状碳化物,材料强度急剧降低,脆性显著增大。模具在热加工过程中碳化物沿晶界析出形成网状碳化物,在热处理加热保温过程中,网状碳化物经过固溶和聚集,形成未溶颗粒状及薄片状碳化物。热处理加热过程的热应力以及淬火过程的组织应力,导致未溶颗粒状及薄片状碳化物周围产生内裂纹。模具冷却水孔的机加工过程,使沿晶开裂特征的内裂纹显露出来。模具服役承载时产生的工作应力,促使裂纹的进一步萌生和扩展。     

GH4033高温合金螺栓断裂原因分析

催化装置滑阀螺栓使用时发生断裂,导致阀体导轨和阀板脱落.通过对滑阀导轨GH4033螺栓进行宏观观察、化学成分分析、显微组织检查、断口分析、微观观察,确定其断裂原因.结果表明:该螺栓是由高温蠕变损伤引起的沿晶脆性断裂;因热处理不当,螺栓组织中晶粒粗大,第二相和沿晶碳化物较少,弱化细晶强化、第二相强化和晶界强化作用,导致蠕...     

一种制动杠杆螺栓用不锈钢热变形行为及锻造工艺

为研究一种制动杠杆螺栓用不锈钢材料的热变形行为及锻造工艺,利用热模拟试验机对材料进行了高温压缩试验,得到了该材料的真应力-真应变曲线和显微组织。将高温压缩试验得到的数据导入有限元模拟软件Deform-3D中,对制动杠杆螺栓的成形过程进行了数值模拟,分析了成形过程中的载荷-行程曲线、等效应力场分布等,最后根据优化得到的工艺参数设计了相应模具,并做了工艺试验,工艺试验得到的制动杠杆螺栓锻件充填饱满、尺寸符合要求、锻造流线分布合理,且锻件经过机加工后,没有发现锻造缺陷,符合使用要求。该研究对此类零件的生产具有一定的指导意义。     

ZL111铝合金液压制动主缸的开裂分析

ZL111铝合金液压制动主缸体在外观检测时发现主缸开裂,密封检测漏气。为查找铝合金主缸开裂原因,对主缸裂纹、断口形貌、显微组织进行观察,检测其化学成分、相变点。结果表明,主缸的失效是因为组织存在过烧缺陷,降低了材料强度,且晶界存在呈圆角状分布的脆性共晶硅相,并聚集长大,进一步弱化晶界。在淬火应力作用下,缸体开裂,后续加工过程中裂纹扩展至宏观裂纹。讨论并分析主缸开裂的根本原因是成分中Mg元素含量偏高,降低了引起主缸过烧的温度。     

低合金高强度钢消除应力裂缝的研究

以应力松弛法对一组Cr—Ni—Mo—V 系钢的消除应力裂缝倾向进行了测定,并采用扫描电镜、能谱对晶界断面形态和晶面成分进行分析,从而对现行的二次沉淀硬化弱化晶界和回火脆性因素的说法提出了异议。指出:消除应力裂缝的产生,主要取决于晶界高温强度的下降和一次过热中的晶界脆化.     

高铁刹车盘用CrMoV钢的高温热塑性

采用Gleeble-3800热模拟试验机研究了600~1350 ℃范围内高铁刹车盘用CrMoV钢的高温热塑性,利用扫描电镜观察断口形貌,利用光学显微镜观察断口截面显微组织。结果表明:试验钢在600~1350 ℃范围内存在3个脆性温度区间,即熔点~1320 ℃的第Ⅰ脆性区、1100~1000 ℃区间的第Ⅱ脆性区和800~650 ℃区间的第Ⅲ脆性区,晶界V(C,N)和VN的析出是造成第Ⅱ脆性区塑性恶化的主要原因,在制定轧制工艺时应避开这些区域。     

Spannungsrißkorrosion von hochlegierten Manganstählen in wäßrigen Chloridlösungen

Stress corrosion cracking of high alloy manganese steels in aqueous chlorides In tensile tests made without applied current in aerated solutions a stabilization of the austenitic structure by increasing Mn and N contents yields increased times to failure. The potential-time-to-failure curves determined by potentiostatic tensile tests reveal a compley joint action of constitution and passivation behaviour of the steels. The intercrystalline stress corrosion cracking of the steel X 40 MnCr 19 with chromium carbide precipitations at the grain boundaries can be attributed to an electrochemical differentiation of the chromium-depleted grain boundary region. Steels of this type are characterized by a pronounced sensitivity to intercrystalline stress corrosion cracking the precipitation annealed state, and by a certain sensitivity to transcrystalline corrosion cracking after solution annealing. Low carbon Mn steels containing up to 4 % Cr are susceptible to transcrystalline stress corrosion cracking irrespective of the heat treatment. As to the temperature dependence of times-to-failure, constitution and layer formation have different effects. Increasing the Cr content to 8 % gives rise to a transition from stress corrosion cracking to pitting type corrosion. In terms of electron optics, an increased chromium content gives rise to a changed dislocation pattern, so that there may be an effect of the type of gliding processes on stress corrosion, The increased stress corrosion resistance of MnCr steels containing at least 8% Cr may be due to the lower height Of the gliding step and to an increasing tendency to repassivation of damaged surface layers.     

Metallurgical factors contributing to HAZ cracking susceptibility in cast alloy 718 welds and its improvement by cerium addition

A study was carried out to determine the effect of cerium addition on HAZ cracking susceptibility in cast alloy 718 welds. The cause of HAZ cracking was also investigated using commercial cast alloy 718 varying in grain size at three levels. The hot cracking test results for commercial cast alloy 718 indicated that the fine-grained alloy was less sensitive to HAZ cracking. Furthermore, cerium addition of up to 0.3 wt.% was found to have a beneficial effect in reducing HAZ cracking susceptibility. When cerium addition exceeds 0.3 wt%, HAZ cracking susceptibility increased further. The mechanism of HAZ cracking was found to be related to intergranular liquation caused by the eutectic melting of sulfur containing a laves cluster at the grain boundaries. The degree of grain boundary liquation in the fine-grained specimen was less than that of the coarse-grained specimen due to a decrease in the amount of laves cluster and sulfur segregation in it at the grain boundaries, which seems to be responsible for a reduction in hot cracking susceptibility in the fine-grained specimen. Microscopic observation suggested that the improved HAZ cracking susceptibility in cerium containing alloy could be attributed to a reduction in the amount of laves cluster and sulfur segregation in it at grain boundaries due to the grain size reduction and sulfur-scavenging effects of cerium.     

螺柱断裂分析及机制探讨

通过断口宏微观形貌观察、能谱分析、金相组织检查、硬度及拉伸性能测试、带状组织评级等手段,对螺柱断裂原因进行分析。结果表明:螺柱的断裂性质为氢脆断裂;起裂部位为螺柱中心位置,此处硬度远高于其他部位;能谱分析和金相组织检查发现裂纹起始处存在严重的碳偏析和合金元素偏析,这是造成螺柱在心部发生氢脆断裂的根本原因。     

冷轧Cu-15Cr原位复合材料性能及Cr纤维相高温稳定性

采用冷轧变形结合中间退火得到形变Cu-15Cr原位纤维增强复合材料。利用扫描电镜、电子拉力试验机及数字微欧计研究退火温度对材料的Cr纤维形貌、抗拉强度及导电性能的影响。结果表明:Cr纤维的高温不稳定性是边缘球化和晶界开裂的结果;随退火温度升高,Cr纤维的高温失稳过程为Cr纤维发生边缘球化、球化向Cr纤维中心扩展、Cr纤维晶界开裂(三叉晶界处)、Cr纤维断裂。随退火温度升高,Cu-15Cr原位复合材料抗拉强度逐渐降低,导电率先逐渐升高,在550℃达到峰值84.4%IACS后迅速下降;经450℃退火,能得到具有较好综合性能的冷轧Cu-15Cr原位复合材料,其抗拉强度达到656 MPa,导电率达到82%IACS。