相似文献
 共查询到17条相似文献,搜索用时 109 毫秒
1.
采用热分析、极限氧指数、锥形量热法等手段,比较并分析了聚酰亚胺(PI)针刺织物与聚苯硫醚(PPS)针刺织物的热稳定性及燃烧性能.结果表明,PI针刺织物与PPS针剌织物的热分解温度分别为580 ℃和500 ℃,极限氧指数分别为40%和35%,点燃时间分别为38 s和32 s,热释放速率最大值分别为62.6 kW/m2和130.9 kW/m2,烟指数分别为12 MW/m2和35 MW/m2.通过对比研究,得出 PI针刺织物比PPS针刺织物具有更优异的热稳定性和燃烧性能.  相似文献   

2.
为解决聚苯硫醚(PPS)纤维在燃烧过程中热释放和烟释放较高的问题,实现其在热防护服领域的应用,将石墨烯(G)添加至PPS基体中,通过共混造粒与熔融纺丝工艺制备PPS/G纳米复合纤维,对复合纤维的聚集态结构及力学性能进行测试,并研究其燃烧和炭化行为。结果表明:石墨烯可显著提高聚苯硫醚纳米复合纤维的燃烧残炭量及炭层结构的致密性,当石墨烯质量分数达0.3%时,PPS/G纳米复合纤维织物的热释放速率峰值从67 kW/m2降低至28 kW/m2;当石墨烯质量分数为0.7%时,总热释放和总产烟量均下降最多,分别降低62%和66%,燃烧性能得到显著改善;且所得复合纤维能够保持更高的断裂强度和断裂伸长率,有望应用于阻燃防护织物领域。  相似文献   

3.
PPS非织造织物与Nomex织物热稳定性与燃烧性能对比   总被引:1,自引:0,他引:1  
采用热失重、氧指数及锥形量热法分析并对比了PPS非织造织物与Nomex织物的热稳定性及燃烧性能,结果发现PPS非织造织物的热分解温度比Nomex织物高约100℃,热分解时间延迟约48 s;PPS非织造织物与Nomex织物的氧指数分别为39%和31%;PPS非织造织物比Nomex织物的点燃时间延迟长达48 s;PPS非织造织物的热释放速率峰值(pkHRR)及总释放热(THR)分别为Nomex织物的20%和8%;PPS非织造织物的最大比消光面积(SEA)仅为Nomex织物的53%;另外,PPS非织造织物比Nomex织物的最大烟释放速率(RSR)小27 L/s,出现时间也延迟了40 s。以上结果充分说明PPS非织造织物比Nomex织物热稳定性和阻燃性能更好,火灾强度及发烟量也更小。  相似文献   

4.
结合热重分析(TGA)技术和热裂解气相色谱-质谱联用(Py/GC-MS)技术,建立了一种通过统计分析TG特征温度以及特定温度下裂解产物种类及其相对丰度对聚苯硫醚(PPS)纤维进行定性鉴别的方法。通过热重分析,研究了PPS纤维在惰性气氛下的各项特征温度。通过Py/GC-MS,PPS纤维在650℃裂解时,主要特征裂解产物为苯硫醇、二苯二硫醚、1,3-苯二硫酚、噻蒽、二苯并噻吩,其相对丰度分别为:100.00%、52.56%、29.29%、25.25%、17.52%。  相似文献   

5.
聚苯硫醚(PPS)纤维制具有极佳的阻燃性、耐高温性和较好的热稳定性,耐腐蚀性仅次于聚四氟乙烯(PTFE)纤维。本文将PPS纤维通过梳理成网、针刺、后整理等工艺制成非织造材料,并对PPS高温滤料的过滤性能、耐酸性以及后整理工艺对产品性能的影响进行了分析。实验表明:PPS纤维具有一定的耐酸性,经过后整理的PPS针刺材料其过滤性能明显提高。  相似文献   

6.
为进一步提升聚酰亚胺(PI)纤维的耐热性能,以全刚性的二酐和二胺合成了可纺性良好的聚酰胺酸纺丝液,通过干法纺丝方法以及高温热环化和热牵伸处理制备了力学性能优良的PI纤维,对PI纤维的热性能和机械性能进行分析。结果表明:所制备的PI纤维具有优越的热稳定性,二酐和二胺内部结构中的全刚性链结构苯环密度大,使PI纤维的化学结构稳定;在氮气氛围下,PI纤维质量损失5%和最大质量损失温度分别达600 和649 ℃,PI纤维的拉伸强度为2.1 GPa,在温度为300 ℃分别热老化处理24、48和72 h后,其拉伸强度保持率可分别达到99.8%、87.3%和76.3%;同时,PI纤维具有优异的尺寸稳定性,在50~350 ℃范围内,其热膨胀系数为 -9.1 μm/(m·℃)。  相似文献   

7.
PPS纤维的结构与热性能   总被引:1,自引:0,他引:1  
文章借助于SEM、X衍射、热分析和DMA测试研究了PPS纤维的形态、聚集态结构与热性能。研究显示PPS纤维具有光滑的表面,为半结晶聚合物,其晶型为正交晶系,结晶度56%。PPS纤维的玻璃化转变温度在106~112℃之间,熔点Tm为284℃,热降解初始温度为542℃。  相似文献   

8.
介绍了分别以DMF、DMAc和NMP为溶剂合成了一定固体含量的酮酐型聚酰胺酸(PAA)溶液,经高压静电纺丝、热亚胺化之后得到酮酐型聚酰亚胺(PI)非织造布膜。用扫描电镜(SEM)表征了PI非织造布膜的微观形貌。用TGA测试了PI非织造布膜的耐热性能。分析表明以DMF为溶剂合成的PAA溶液经过静电纺丝、热亚胺化之后得到酮酐型PI非织造布膜的纤维直径最小,纤维直径在150~250nm之间,纤维间的粘连、弯曲现象最为严重。而以NMP为溶剂合成的P从溶液经过静电纺丝、热亚胺化之后得到酮酐型PI非织造布膜的热稳定性最好。  相似文献   

9.
聚苯硫醚纤维的热降解动力学   总被引:1,自引:1,他引:0       下载免费PDF全文
为研究聚苯硫醚(PPS)纤维的热降解动力学,采用热失重法分析了聚苯硫醚纤维在氮气氛中以一定速率升温时的热降解动力学行为。用Kissinger、Flynn-Wall-Ozawa及Friedman 3种方法研究得到PPS纤维在氮气氛中的热降解动力学参数,并对PPS纤维的热稳定性进行了探讨。结果发现,随着升温速率的增加,PPS纤维的初始热降解温度及热降解速率最大时的温度均升高。采用Flynn-Wall-Ozawa及Friedman法得到PPS纤维的平均活化能、反应级数、指前因子分别为:185.0 kJ/mol、1.21、5.7×109;而采用Kissinger法得到PPS纤维在热降解速率最大时的活化能、指前因子分别为:228.3 kJ/mol、2.9×109。  相似文献   

10.
鲍稳  邓炳耀  刘庆生  邢剑  张越  常过 《纺织学报》2012,33(10):51-55
 纺粘法制备聚苯硫醚(PPS)非织造材料,首先对PPS原料进行DSC、TG分析以及熔体流动速率(MFR)测试,结果表明:PPS原料具有较好的热稳定性,熔点为280℃;熔体流动性在315℃时最好,为158.7 g/10min。在此基础上,利用纺粘无纺布实验机成功制备了PPS纺粘非织造布材料,并对其过滤性能进行了测试。结果表明:PPS纺粘非织造材料纤维平均直径为37.6μm,孔径呈正态分布,平均孔径为31.6μm,对10μm以上颗粒具有高达98.1%的过滤效率。  相似文献   

11.
芳砜纶过滤材料在高温烟气净化中的稳定性分析   总被引:2,自引:1,他引:1  
芳砜纶(PSA纤维)稳定的分子结构使其具有良好的热稳定性和耐化学性。PSA针刺毡过滤材料在250℃高温环境下的热力学、热收缩稳定性明显好于PMIA、PPS、PI等其他常用芳香族耐高温纤维过滤材料;耐酸、抗氧化性能较好,经85℃、30%硫酸处理2h及经200℃高温处理200h后用质量浓度17%次氯酸钙溶液处理2h的PSA针刺毡总体断裂强力保持率在90%以上;更适宜应用在酸性工况环境下,在一定高温条件及低浓度酸性条件下,PSA纤维及针刺毡过滤材料的断裂强力还会有所提升。PSA纤维独特的耐温耐化学特性,使其在250℃高温过滤领域具有一定优势,在工业炉窑袋式除尘领域应用前景良好。  相似文献   

12.
Bin Yu 《纺织学会志》2018,109(10):1360-1366
In order to develop efficient and low-cost hot gas filtration medium, composite filters were prepared with PTFE fabric as the substrate, and mixing of OPAN fiber and PPS fibers as functional layers. The fiber entanglement was evaluated via image analysis, and some other characteristics, such as tensile properties, pore size, thermal stability, and filtration performance were also discussed. The results showed that with increasing ratio of PPS fibers, the fiber entanglement, breaking strength, thermal stability, and filtration efficiency increase, while the pore size decreases. Mixing with 40% weight PPS fiber leads to the filtration efficiency of the composite filter increasing from 64.68 to 94.68% for removing particles with a diameter of 2.5 μm.  相似文献   

13.
The combined effect of two structure forming process parameters i.e. punch density and needle penetration on properties of Mesta needle punched nonwoven fabric has been studied using central composite rotatable design. As properties are structure dependent, the relationship between compressional behavior and other functional properties was studied. It was observed that compressional (α) and recovery (β) parameters are well correlated with tensile, air permeability and thermal insulation value of Mesta needle punched fabric. The regression equations were also suggested. Therefore, the α and β may be used for indirect approximation of these properties with reasonable accuracy.  相似文献   

14.
对于一定面密度的针刺非织造布,其热性能即绝热值和热阻值会随着层数的增加得到明显的改善,但层压后织物的冷暖感值是保持不变的。针板上刺针排列方式的设计在多层结构的成型过程中,对水蒸气的传输速率起着重要的作用。多层层压对织物的厚度也有很大的影响。  相似文献   

15.
通过制备相同经纬密度不同织物组织的样布,对聚苯硫醚机织物的耐热性能、热稳定性能以及导热性能进行测试分析.根据实验数据可知,聚苯硫醚织物具有良好的耐热性能和热稳定性能,以及极佳的热防护性能;1/2斜纹相比于平纹和其他三种斜纹织物组织是更适合于防护服外层面料的组织.  相似文献   

16.
为了赋予涤/棉混纺织物良好的阻燃性能,以pH值为5、质量分数为1%壳聚糖溶液和pH值为2、质量分数为1.5%植酸钠溶液,通过静电层层自组装法,对经多巴胺改性后的涤/棉(65/35)混纺织物进行阻燃整理。其中正负离子交替沉积1次记为组装1层,第1层内每次组装15 min,第1层后各次组装时间为5 min,共组装15层。探讨了整理后织物极限氧指数(LOI)、炭长、热重、热释放速率、炭渣形貌等性能。结果表明:多巴胺改性可以提高涤/棉混纺织物的反应性,有利于阻燃整理;整理后织物阻燃性能显著提高,LOI值从未整理时的18.8%提高到28.7%;热分解温度比未整理织物大幅提前,炭渣含量较未整理提高了5.7%;整理后织物点燃时间延长,平均热释放速率(HRR)和峰值热释放速率(PHRR)分别为14.16 k W/m2和51.07 k W/m2,相较未整理涤/棉织物下降了84.62%和78.47%,织物燃烧危险性显著降低。  相似文献   

17.
In this paper, an artificial neural network (ANN) model has been designed to predict the thermal resistance of needle‐punched blankets. Web‐laying (parallel‐ and cross‐laid), fibre fineness, fibre degree of hollowness, fabric weight, depth of needle penetration and needle punch density are considered as input parameters to predict the thermal resistance of needle‐punched nonwoven blankets. In order to reduce the dependency of the results on a specific partition of the data into training and testing sets, three‐way cross validation tests were performed, that is, total data were divided into training and testing sets in three different ways. The predicted thermal resistance correlated well with the experimental thermal resistance. The relative contribution of each parameter to the overall prediction of the thermal resistance was studied by carrying out a sensitivity analysis of the test data set. The results of sensitivity analysis show that web‐laying is the most important input parameter, followed by depth of needle penetration, fabric weight, degree of fibre hollowness, needle punch density and fibre fineness.  相似文献   