棕榈藤材的抗拉强度测试方法

基于国内外棕榈藤材抗拉强度测试方法,分别将棕榈藤材加工成总长度均为160mm的哑铃形藤片试样、端头垫片强化整径藤片试样、半哑铃形整藤试样和端头浸胶强化整藤试样进行了抗拉强度的测试,根据试样的测试破坏情况和应力—应变曲线图等测试结果,发现以加工相对较易的含皮整径藤片试样,在万能力学试验机上沿试样顺纹方向匀速施载,使试样在30s～90s内破坏,从而求出藤材的顺纹抗拉强度。     

两种国产藤材的抗弯性能及变异北大核心

抗弯强度和抗弯弹性模量是藤材重要的力学性能指标,对藤材的合理利用及产品开发具有重要作用。本文对我国两种主要材用商品藤—单叶省藤(Calamus simplicifolius)和黄藤(Daemonorops margarita)藤材的抗弯弹性模量(MOE)、抗弯强度(MOR)及其变异进行研究,结果表明:1)两种藤材抗弯性能的株间差异不明显,但在株内生长高度方向上的差异极其显著;2)藤材抗弯性能与其生长年份密切相关,离基部越远,生长高度越大,即生长年份越小,藤材的MOE和MOR越小;藤材梢部的抗弯强度仅为基部的1/2;3)单叶省藤材的MOE和MOR与生长高度的多项式相关因子分别达到了0.96和0.98,黄藤材的MOE和MOR与生长高度的多项式相关因子分别达到了0.98和0.99;4)单叶省藤的破坏强度和破坏应变都比黄藤材大,其韧性系数高达黄藤材近4倍。单叶省藤材可作多种用途,而黄藤材则宜整藤利用。     

两种国产藤材的抗弯性能及变异

抗弯强度和抗弯弹性模量是藤材重要的力学性能指标,对藤材的合理利用及产品开发具有重要作用。本文对我国两种主要材用商品藤—单叶省藤(Calamus simplicifolius)和黄藤(Daemonorops margarita)藤材的抗弯弹性模量(MOE)、抗弯强度(MOR)及其变异进行研究,结果表明:1)两种藤材抗弯性能的株间差异不明显,但在株内生长高度方向上的差异极其显著;2)藤材抗弯性能与其生长年份密切相关,离基部越远,生长高度越大,即生长年份越小,藤材的MOE和MOR越小;藤材梢部的抗弯强度仅为基部的1/2;3)单叶省藤材的MOE和MOR与生长高度的多项式相关因子分别达到了0.96和0.98,黄藤材的MOE和MOR与生长高度的多项式相关因子分别达到了0.98和0.99;4)单叶省藤的破坏强度和破坏应变都比黄藤材大,其韧性系数高达黄藤材近4倍。单叶省藤材可作多种用途,而黄藤材则宜整藤利用。     

黄藤材结构及应用特性

黄藤(Daemonorops margarita)材的解剖结构径向差异显著,纤维长度、胞壁厚度和比量、维管束分布密度、纤维胞壁厚度等自藤皮向藤芯减小,纤维宽度、导管分子长度与宽度、薄壁细胞比量、导管比量、维管束大小、后生木质部导管大小、微纤丝角等自藤皮向藤芯增大;黄藤材藤径中等,纤维比量较大,纤维素结晶度较低,具备良好商用藤材结构特征;整藤塑性好,但藤芯脆弱,宜整藤利用;通过漂白、染色和涂饰等处理,可使其品质大大提高。     

棕榈藤材的温湿度调节性能评价

棕榈藤是仅次于木材和竹材的重要非木材林产品,具有独特的装饰性能。为揭示棕榈藤材作为室内装饰材料对室内环境温湿度的调节机制,采用尺寸为20×20×30cm的不锈钢密闭箱体作为实验体,控制环境温度在20℃~40℃范围内变化,记录箱体内温度T和相对湿度H以及绝对湿度的对数logh随时间的变化情况。结果表明:棕榈藤材对环境湿度具有调节作用,相对湿度和温度之间存在对应关系。绝对湿度的对数logh和T之间存在线性关系,曲线的斜率B值能够评价材料的调湿性能;不同装饰面积的B值不同。装饰面积越大,B值越大,对环境调节性能越好。     

织物马鞍状弯曲试验研究

为更好地表征织物在实际弯曲状态下的力学特性,使用自制的织物马鞍状弯曲测试装置,分别选用两种不同厚度和面密度的纸、塑料薄膜与织物为试样,在马鞍状弯曲情况下采用单因素分析法探讨了织物长度、宽度和加载速度等测试条件对织物受力负荷-位移的影响,并确定出织物马鞍状弯曲测试参数。结果表明当评价指标为抗弯刚性时,在下端距离16mm,试样宽度50mm,加载速度50mm/min条件下,采用马鞍状弯曲测试方法测定织物弯曲性能与采用斜面法测定性能相比,具有较好的一致性。     

单叶省藤发育过程中主要显微解剖特征的变异

藤茎的解剖特性对其物理力学性能及利用有重要影响,为揭示棕榈藤材材性优劣的微观原因,以单叶省藤为研究对象,采用生物解剖学方法系统研究了藤材组织比量、纤维形态、导管直径随藤龄变化的规律。结果表明:随着藤龄的增加,薄壁组织比量逐渐降低,纤维比量总体呈上升趋势,后生木质部大导管比量基部和梢部比中部大,原生木质部小导管和筛管比量变化无明显规律;纤维长度随藤龄没有稳定的变化规律,纤维宽度表现为基部比梢部大,纤维双壁厚随藤材生长出现明显的增厚,纤维腔径反之减小;后生木质部导管直径变化规律为先减小后增加。单叶省藤材纤维比量、纤维双壁厚变异均较小,显示较好的材质均一性,优于国产黄藤材。     

木材内部微爆破处理对杨木干燥速率的影响

以杨木为试材,以微爆破处理材和未处理材的平均干燥速率为考察指标,分析比较了不同初含水率、微爆破次数和压力对平均干燥速率的影响。结果表明,经微爆破处理的试材的平均干燥速率是未处理材的1.93～2.25倍,而且随着初含水率、微爆破次数和压力的增加,平均干燥速率也会增大;在实验条件下,试材的初含水率对平均干燥速率的影响最大,微爆破次数和压力的影响较为接近,但次数的影响大于压力。     

高比重钨合金准静态和动态断裂韧性研究

文章研究了高比重钨合金95W-3.5Ni-1.5Fe在准静态和动态加载下的断裂特性,开展实验测试了该材料在准静态和动态加载下的断裂韧性.准静态试验利用三点弯半圆形试样在万能试验机上加载,并根据测试标准ASTM E399得到了准静态断裂韧性.动态加载则是利用三点弯半圆形试样在霍普金森压杆上进行冲击加载,分析了试样在冲击过程中的动态力平衡条件,并依照准静态方法计算了钨合金在不同冲击速率下的动态断裂韧性,最后讨论了加载速率对钨合金断裂韧性的影响.     

改性人工林杨木阻燃性能分析

以人工林杨木为研究对象,采用实验室自制多功能木材改性液与硼酸、硼砂阻燃剂对其进行改性处理,采用氧指数仪和锥形量热仪分析了改性处理材的阻燃性能。结果表明:经过不同质量分数的MMFU溶液及其与硼酸、硼砂阻燃剂复配的改性液处理后,试材的氧指数均有所提高,热释放速率峰值降低且出现时间延迟,总热释放量、质量损失速率与总烟释放也显著降低。其中采用MMFU与硼酸、硼砂复配改性液处理的试材阻燃效果相比最好,氧指数比素材提高了127%,点燃时间是素材的1.7倍,试材的热释放速率曲线非常平缓,第一峰与第二峰值都约为素材的50%,其中第二峰出现比素材晚了4.5min,总热释放量为素材的46%,质量损失速率相比素材降低了1/4,总烟释放为素材的7%。     

棕榈藤藤条采收工具和方法

棕榈藤的藤条是仅次于木材和竹材的重要林产品,目前藤材资源紧缺,但需求量却在不断增加.针对棕榈藤的生长特性、采收特性以及现有采收工具和方法进行了概述和分析,对棕榈藤藤条采收工具的发展提出了一些建议.     

中国棕榈藤产业现状及展望

基于我国商用棕榈藤的品种与资源分布情况、棕榈藤材的分类和利用等,对我国棕榈藤产业的发展现状和趋势进行了分析和讨论.目前资源不足和产业结构涣散严重制约我国棕榈藤材产业的可持续发展,建议通过行业整合、深加工、建立资源基地和产业发展基地等途径加强我国棕榈藤材的资源建设和产业发展     

Experimental study on the bending fatigue behaviors of 3D five directional braided T-shaped composites

The static three-point bending properties and cyclic bending fatigue performances of three-dimensional five-directional braided T-beam composite (3D5DBTC) have been investigated at room temperature. The fatigue life of 3D5DBTC under different stress levels was analyzed based on the obtained S–N curves. The load–displacement hysteresis loops curves and stiffness degradation curves were recorded to reveal the relationship between stiffness degradation and damage evolution. It is shown that there were three distinct stages corresponding respectively to matrix cracks, interface debonding, and fiber breaking in the whole fatigue loading. In addition, to understand the ultimate fracture failure mechanism of 3D5DBTC under the different fatigue loading conditions, the damage morphologies of 3D5DBTC after fatigue testing were observed by macrographs and SEM micrographs. The matrix crack and the resin–yarns interface debonding occurred on the flange while fiber breakages occurred in the web. Meanwhile, macrographs and SEM images confirm that fiber breaking is the dominant damage under the high stress level, while matrix cracking and interfacial debonding are the main failure modes at low stress level.     

糙米正面破碎特性与裂纹扩展规律

目的:研究碾米室中糙米破碎特性。方法:利用万能材料试验机进行糙米力学试验,通过数字显微镜观察糙米中裂纹及其扩展变化。结果:糙米受力时会经历屈服阶段与强化阶段的交替过程,直至断裂;在挤压载荷作用下,内部微孔洞处产生裂纹,裂纹的快速扩展造成了米粒破碎或断裂,在三点弯曲和剪切载荷下,糙米从支撑端底面产生裂纹,并扩展至正面;糙米的抗挤压变形能力最大、抗三点弯曲变形能力次之、抗剪切变形能力最小;与挤压载荷相比,糙米在三点弯曲和剪切载荷下的破碎强度和破碎能较小。结论:在对碾米机结构进行设计时,要尽量减少弯曲、剪切作用对糙米的影响;同等条件下,粳型糙米的力学特性优于籼型糙米。     

纱线弯曲刚度测量

分析了测试纱线弯曲刚度各种方法的优缺点 ,着重提出采用改进电子单纤维强力仪法 ,测量毛涤混纺纱的最大弯曲强力等参数 ,来求得弯曲刚度。同时探讨了纱线弯曲刚度与纱线混纺比、捻幅与细度的相关性     

棕榈藤材的制备和加工

对藤材制备的采收、油浴、漂白等初加工工艺和藤材制品生产的精加工工艺进行了系统论述,分析了国内外藤材工业的发展现状和目前藤材工业面临的主要问题,指出藤材的基础研究有待进一步加强,以便更好地开发利用藤材,提高藤材利用率和藤制品价值.     

椅类藤家具静载荷力学试验方法的研究

主要参考了《菲律宾柳藤类家具标准》及《家具力学性能实验.椅凳类强度和耐久性》等国内外标准,对椅类藤家具进行了静载荷力学性能试验,并在试验过程中对试验方案和数据进行了归纳总结,提出了出椅类藤家具静载荷力学试验的方法。     

Fracture Resistance of Cashew Nuts as Influenced by Pre-Shelling Treatment

The fracture resistance of raw and pre-treated cashew nuts during uni-axial compressive loading was investigated. Cashew nut samples were subjected to two pre-shelling treatments, namely: steam boiling and roasting in hot cashew nut shell liquid. Two loading rates of 2.5 and 50 mm/min and two loading orientations (longitudinal and transverse) were considered for fracture resistance of pre-treated cashew nuts using a 50 kN capacity Instron testing machine. The data obtained were subjected to analysis of variance. The average values at 2.5 mm/min were 342 and 318 N for raw nuts, 321 and 242 N for roasted nuts, and 341 and 309 N for steam boiled nuts during longitudinal and transverse loading, respectively; whereas corresponding values at 50 mm/min were 784 and 763 N for raw nuts, 517 and 464 N for roasted nuts, and 436 and 398 N for steam boiled nuts, respectively. In each of the pre-treatment methods and loading rates, more force was required to crack cashew nuts during longitudinal loading than transverse loading; and for each loading rate, pre-treated nuts generally required less force than raw nuts.