碳纳米管/铅锡合金复合镀层的摩擦磨损性能

在镀液中加入不同含量的碳纳米管,用复合电沉积工艺制备了碳纳米管/铅锡合金复合镀层,测试了其在不同载荷下的摩擦因数和磨损量,并对其磨损形貌和磨损机理进行了分析。结果表明:在相同条件下,碳纳米管/铅锡合金复合镀层的摩擦因数和磨损量均低于普通铅锡合金镀层的;当镀液中的碳纳米管含量为2 g·L~(-1)时,复合镀层的摩擦因数和磨损量最小;复合镀层的磨损机理为磨粒磨损,而不含碳纳米管的铅锡合金镀层的为粘着磨损。     

纳米PTFE复合镀层的组织和摩擦性能

采用扫描电镜、透射电镜和X-射线衍射仪分析了纳米PTFE复合镀层的表面形貌和组织结构,利用微米划痕法在MXTX S/X型划痕试验仪上研究了纳米复合镀层的摩擦因数随PTFE含量变化的情况。研究结果表明:纳米PTFE的加入明显细化复合镀层。纳米PTFE以颗粒形式存在于镀层中。纳米复合镀层的摩擦因数明显低于未加纳米的镀层。当纳米PTFE的含量为15.0 g/L时,纳米复合镀层的摩擦因数最小(0.046)。     

Ni-P-PTFE复合镀层工艺及摩擦学行为研究

在化学沉积Ni-P镀层的工艺基础上,制备Ni-P-PTFE复合镀层,利用SEM和XRD分析镀层的表面形貌和组织结构,探讨镀液中活性剂和PTFE含量对复合镀层结合力、硬度、摩擦因数、磨损率以及复合镀层PTFE粒子含量的影响,采用MRH-3摩擦磨损试验机研究复合镀层摩擦学行为,分析复合镀层的磨损机制,确定最佳工艺条件.结果表明在最佳工艺条件下制备的Ni-P-PTFE复合镀层具有良好的摩擦学性能,其磨损机制为黏着和轻微磨粒磨损.     

PTFE对复合镀层摩擦特性的影响

研究了PTFE添加量对Ni基电刷镀PTFE复合镀层的摩擦特性和磨损机制的影响.采用扫描电镜、X射线衍射仪和能谱仪分析了摩擦前后的磨损表面的形貌、组织和成分变化.结果表明:PTFE添加量对复合镀层的组织和摩擦特性有较大的影响.当PTFE体积分数为3%和4%时,复合镀层的摩擦因数最小;当PTFE体积分数为2%时,复合镀层的耐磨性最好.在磨损面上富含PTFE复合层的形成和面积随PTFE添加量的变化影响了复合镀层的摩擦特性及其磨损机制.     

Ni-P-金刚石化学复合镀层的耐磨性

研究了Ni-P镀层、Ni-P-纳米金属石及Ni-P-微米金刚石复合镀层在不同的热处理温度、载荷及金刚石含量下的耐磨性，并分析了复合镀层提高基质金属耐磨性的机理。结果表明：三种镀层的磨损量均随着热处理温度的提高而下降，并在400℃时达到最小值；载荷增加，磨损量增大，在不同热处理温度及载荷下，Ni-P-微米金刚石复合镀层均显示出最好的耐磨性。当微米金刚石加入量在4-8g/L时，镀层的耐磨性最好。复合镀层提高耐磨性的原因在于复合粒子在基质金属表面形成突起，起到了支撑载荷、避免粘着磨损及减小摩擦系数的作用。     

聚四氟乙烯工程材料的摩擦磨损性能研究

用MPV-200型摩擦磨损试验机研究了干摩擦条件下磨损时间、滑动速度、载荷、填料等对聚四氟乙烯(PTFE)工程塑料摩擦磨损性能的影响，结果表明：PTFE材料的摩擦因数和磨损率先随速度的增大而减小，然后又随着速度的增大而增大；随磨损时间的增长而降低，最后趋于稳定值；另外，摩擦因数大体上随载荷的增大而减小，磨损量则随载荷的增大而增加；填料可将PTFE的磨损量降低2个数量级，其中石墨使PTFE的摩擦因数降低，玻璃纤维和碳纤维则增大了PTFE的摩擦因数，而MoS2对PTFE摩擦因数的影响较小。对PTFE工程塑料的摩擦磨损特性进行系统分析，为优化设计提供理论基础。     

水润滑橡胶轴承的制备及摩擦磨损性能研究

以丁腈橡胶(NBR)为基体,制备水滑润橡胶轴承;研究填料、载荷、转速、润滑介质、NBR品种等因素对橡胶轴承在水润滑介质中的摩擦磨损性能的影响,并分析其摩擦和磨损机制。结果表明,炭黑量和二硫化钼添加量明显影响橡胶轴承的摩擦因数和磨损量;随着载荷的增大,橡胶轴承的摩擦因数和磨损量均呈现先增大后减小再明显增大的趋势;随着转速的增大,橡胶轴承的摩擦因数和磨损量均明显减小,并且在海水中的摩擦因数和磨损量均大于在淡水中的摩擦因数和磨损量。     

水润滑橡胶轴承摩擦磨损性能的研究

以丁腈橡胶（ＮＢＲ） 为基体,制备水滑润橡胶轴承;研究填料、载荷、转速、润滑介质、ＮＢＲ品种等因素 对橡胶轴承在水润滑介质中的摩擦磨损性能的影响,并分析其摩擦和磨损机制。结果表明,炭黑量和二硫化钼添加量明 显影响橡胶轴承的摩擦因数和磨损量;随着载荷的增大,橡胶轴承的摩擦因数和磨损量均呈现先增大后减小再明显增大 的趋势;随着转速的增大,橡胶轴承的摩擦因数和磨损量均明显减小,并且在海水中的摩擦因数和磨损量均大于在淡水 中的摩擦因数和磨损量。     

高速摆动下PTFE编织复合材料干摩擦研究

利用高速摩擦试验机对PTFE编织复合材料进行干摩擦试验,研究不同条件(载荷、速度和湿度)下PTFE编织复合材料干摩擦磨损性能;并利用扫描电子显微镜对不同条件下的磨屑形貌进行分析。结果表明:单因素变化条件下,摩擦因数随载荷和相对湿度的增大而减小,随摩擦速度的增大而增大;磨损量随载荷和速度的增大而增大,但相对湿度的增加可降低磨损;载荷及速度的增加显著影响材料磨损状况。     

纳米耐磨和减摩复合镀层的研究

分析了将纳米三氧化二铝(Al2O3)和聚四氟乙烯(PTFE)颗粒加入常规电刷镀液中制备纳米耐磨和减摩复合镀层的组织、显微硬度、耐磨性和摩擦因数。结果表明：纳米颗粒的加入使复合镀层组织明显细化和致密。随着纳米Al2O3颗粒含量的增加，复合镀层的显微硬度和耐磨性有明显的提高，纳米PTFE的加入有助于减少复合镀层的摩擦因数。     

表面镀层极限PV值测试初探

本文用ＭＭ２００磨损试验机，以Ｎｉ－Ｐ－ＰＴＦＥ化学镀层为实例，对表面镀层极限ＰＶ值的测试进行了初次尝试。文中提出以摩擦力矩剧烈波动作为镀层破坏标志，分析Ｎｉ－Ｐ－ＰＴＦＥ的极限ＰＶ值变化规律，并对试验方法作了探讨。     

载荷和转速对HDPE多元复合材料摩擦学性能的影响

为改善高密度聚乙烯(HDPE)的力学性能、自润滑性和耐磨性,以HDPE为基体,通过填充六钛酸钾晶须(PTW)、聚四氟乙烯(PTFE)和滑石粉制备一种HDPE复合材料.在MMW-1型摩擦磨损试验机上测试复合材料在不同载荷和转速下的摩擦因数、磨损率,采用扫描电镜(SEM)分析磨痕形貌,探讨HDPE复合材料的摩擦磨损规律.结...     

Ekonol/石墨/MoS2填料对PTFE力学和摩擦磨损性能的影响

研究了Ekonol含量对Ekonol／石墨／MoS2／P，PTFE复合材料的力学性能、摩擦磨损性能的影响，以及滑动速度、载荷对材料摩擦磨损性能的影响；用扫描电子显微镜观察了复合材料磨损后的表面形貌，并探讨了其磨损机制。结果表明：加入填料降低了材料的拉伸强度和弯曲强度，但提高了弯曲模量和硬度；同时填料能提高材料的磨损性能，但使摩擦因数升高了；当Ekonol含量较低时，磨损机制为粘着磨损，随着填料含量的增加，Ekonol分散到基体中，起到了承载作用，阻止了PTFE基体的带状破坏，磨损机制为疲劳磨损和轻微的粘着磨损；摩擦因数随载荷的增大而减小，随滑动速度的增大而增大，在相同的滑动时间内，磨痕宽度随载荷和滑动速度的增大而增大。     

干摩擦工况下Si3N4/PTFE配副材料摩擦磨损特性与转移膜形成分析

为使全陶瓷轴承在干摩擦工况下可靠运转,选用四氟乙烯(PTFE)材质的保持架为全陶瓷轴承提供润滑.利用Rtec销/盘摩擦磨损试验机,以PTFE盘与氮化硅(Si3 N4)销为摩擦副,研究Si3 N4/PTFE在不同载荷和转速条件下的摩擦磨损性能,通过SEM对Si3 N4表面的转移膜形貌进行观察,分析转移膜形成原因.结果表明...     

Tribological Behavior of TiC/a-C:H-Coated and Uncoated Steels Sliding Against Phenol–Formaldehyde Composite Reinforced with PTFE and Glass Fibers

Tribological experiments on phenol–formaldehyde composite reinforced with polytetrafluoroethylene (PTFE) and glass fibers were performed against 100Cr6 steel and TiC/a-C:H thin film-coated 100Cr6 steel. In both cases, the coefficient of friction increases with increasing sliding distance until a steady-state value is reached. Although the steady-state values of the coefficient of friction are very close and ultralow, the wear rate of the PTFE composite liner at a long sliding distance (1,000 m) is reduced when the steel ball is coated with the TiC/a-C:H coating. This behavior is mainly attributed to the smoother surface after long sliding and the improved wear resistance of TiC/a-C:H coating. PTFE transfer films are evident on the surfaces of the hard counterparts. The average thickness of the transfer film on TiC/a-C:H-coated surfaces is about 3.8 nm. On the surface of uncoated steel ball, a continuous but non-uniform transfer film of around 13.9 nm average thickness was found.     

Tribological Behavior of WC-12Co Air Plasma–Sprayed Coating at Elevated Temperatures

The friction and wear performance of WC-12Co air plasma–sprayed (APS) coating at temperatures of 25–650°C under loads of 8 and 28 N in at atmospheric environment have been studied by a ball-on-disc tribometer. The effect of temperature and load on the tribological behavior of WC-Co coating was investigated. The results show that under a load of 8 N, the wear volume of the coating increases at 250°C due to the coating splat delamination and then it gradually decreases at 350–500°C. The friction could promote the formation of double oxide (CoWO₄), which is beneficial to reduce friction and wear. At higher temperatures, the wear volume increases again due to the removal of oxides. Under a load of 28 N, the wear volume of the coating increases enormously at 250°C due to the serious splat delamination. At 350°C, the load promotes double oxide formation, resulting in an early decrease in the coefficient of friction and a rapid reduction in wear volume. Although the wear volume decreases at 350–500°C, it is 10-fold higher than that under a load of 8 N. Above 500°C, the differences of the wear volumes of coatings under the two loads become less obvious, and similar trends also appear for the coefficients of friction. The synergistic effect between the load and temperature on the friction and wear mechanism of WC-12Co APS coating is discussed.     

Tribological properties of Ni3Al-Cr7C3 composite coating under water lubrication

The tribological properties of Ni₃Al-Cr₇C₃ composite coating under water lubrication were examined by using a ball-on-disc reciprocating tribotester. The effects of load and sliding speed on wear rate of the coating were investigated. The worn surface of the coating was analyzed using electron probe microscopy analysis (EPMA) and X-ray photoelectron spectroscopy (XPS). The results show the friction coefficient of the coating is decreased under water lubrication. The wear rate of the coating linearly increases with the load. At high sliding speed, the wear rate of the coating is dramatically increased and a large amount of the counterpart material is transferred to the coating worn surface. The low friction of the coating under water lubrication is due to the oxidizing of the worn surface in the wear. The wear mechanism of the coating is plastic deformation at low normal load and sliding speed. However, the wear mechanism transforms to microfracture and microploughing at high load with low sliding speed, and oxidation wear at high sliding speed. It is concluded that the contribution of the sliding speed to an increase in the coating wear is larger than that of the normal load.     

GF/PTFE自润滑纤维复合材料磨损性能热衰退研究

针对高频摆动关节轴承摩擦热对自润滑纤维复合材料摩擦磨损性能的影响,研制了高频使用条件下的玻璃纤维增强聚四氟乙烯(GF/PTFE)自润滑纤维复合材料,利用MYB～500高频高载摆动摩擦磨损试验机,对其进行不同摩擦温度下的摩擦磨损性能测试,研究摩擦热作用下材料自润滑性能和磨损性能衰退特征,分析磨损产物和摩擦表面以及不同摩擦温度下材料的磨损机理。结果表明,摩擦热对材料自润滑性能影响显著,适当的摩擦温度范围能够保证材料的自润滑性能,摩擦温度和摩擦因数之间互为耦合作用,对材料的磨损性能具有一定的影响;高摩擦热作用于自润滑过程及机理的改变,造成材料的磨损性能衰退现象。因此,不同温度下材料的磨损特征具有明显的差异化,其中低摩擦温度下(60～120℃)材料自润滑性能优异,磨损率很低;140℃摩擦温度条件下材料摩擦磨损性能开始衰退;材料在高摩擦温度下(140～180℃)的磨损初期自润滑性能良好、磨损轻微,而中后期磨损严重。微观分析表明,低摩擦温度下材料的磨损机理以轻微粘着和疲劳磨损为主;高摩擦温度下材料的磨损以片状剥落、纤维剪切破坏为主,且磨损面局部损伤特征明显,磨损严重。     

聚苯酯填充聚四氟乙烯复合材料摩擦学行为研究

采用聚苯酯（Ekonol）、Ekonol／PAB纤维增强聚四氟乙烯（PTFE）制备利用转移膜润滑的摩擦副材料，并研究了两组材料在于摩擦条件下与9Cr18轴承钢对摩时的摩擦学性能；运用扫描电镜分析了两组材料磨损表面形貌和磨损机理。结果表明：随着Ekonol含量的增大，Ekonol填充PTFE复合材料的摩擦因数逐渐增大，当Ekonol质量分数超过25％时摩擦因数略有下降，磨损方式由以犁削磨损为主转变为以疲劳磨损为主；而Ekonol／PAB纤维填充门FE复合材料的摩擦因数，随Ekonol含量的增大而增大，磨损方式由以粘着磨损为主转变为以疲劳磨损为主。Ekonol／PAB纤维填充PTFE复合材料的摩擦学性能优于Ekonol填充PTFE复合材料。