1.
微动疲劳易引起钢丝表面磨损和横截面积损失,进而造成钢丝断裂失效并缩短钢丝绳使用寿命。不同微动疲劳参数(接触载荷、疲劳载荷、钢丝直径和交叉角度)引起差异的钢丝微动疲劳磨损特性,故研究微动疲劳参数对钢丝微动疲劳磨损演化规律影响至关重要。基于摩擦学理论和Marc仿真软件构建钢丝微动疲劳磨损模型,探究接触载荷、疲劳载荷、交叉角度和钢丝直径对钢丝微动疲劳磨损演化的影响规律。结果表明:钢丝微动疲劳磨损体积主要与接触载荷和疲劳载荷有关;疲劳钢丝的磨损深度、磨损率及磨损体积随着接触载荷的增加而增大,且不同接触载荷下疲劳钢丝磨损体积均随着循环次数的增加而呈线性增加;随疲劳载荷幅值的增加,疲劳钢丝的磨损深度、磨损率及磨损体积均呈增加趋势;在不同疲劳载荷范围下疲劳钢丝的磨损体积均随着循环次数的增加而呈线性增加;当接触载荷、疲劳载荷及钢丝间摩擦因数相同时,不同交叉角度和不同加载钢丝直径下疲劳钢丝的磨损体积相同。  相似文献   

2.
微动疲劳寿命的估算方法研究   总被引:3,自引:0,他引:3  
着重分析了零构件由于微动磨损而造成的疲劳失效机制,说明了在这种微动疲劳模式下疲劳寿命的组成情况,用门槛值应力公式估算了当磨蚀坑根部萌生扩展性裂纹时蚀坑的临界深度尺寸,并分析了微动裂纹尖端的应力强度因子,得出了计算微动裂纹萌生尺寸的表达式,最后用上述方法计算了螺纹联接件的微动磨损寿命与裂纹萌生尺寸,用局部应力应变法计算了微动裂纹的萌生寿命,所得到的估测寿命与试验值相符,由此可见,该微动疲劳寿命的估测方法是合理的,有效的。  相似文献   

3.
着重分析了零构件由于微动磨损而造成的疲劳失效机制 ,说明了在这种微动疲劳模式下疲劳寿命的组成情况 ,用门槛值应力公式估算了当磨蚀坑根部萌生扩展性裂纹时蚀坑的临界深度尺寸 ,并分析了微动裂纹尖端的应力强度因子 ,得出了计算微动裂纹萌生尺寸的表达式 ,最后用上述方法计算了螺纹联接件的微动磨损寿命与裂纹萌生尺寸 ,用局部应力应变法计算了微动裂纹的萌生寿命 ,所得到的估测寿命与试验值相符 ,由此可见 ,该微动疲劳寿命的估测方法是合理的、有效的  相似文献   

4.
超高压压缩机填料盘的微动磨损   总被引:1,自引:0,他引:1  
对茂名乙烯超高压压缩机的填料盘异常磨损和开裂进行分析和计算,发现填料盘的磨损是由于填料盘在工作时有微动磨损而引起的,并且造成填料盘微动疲劳,形成微动疲劳裂纹。  相似文献   

5.
微动磨损加速材料疲劳失效,微动疲劳是微动磨损和普通疲劳共同作用的结果;NiTi形状记忆合金具有良好的耐磨性和抗疲劳特性,可以延缓损伤的发生和扩展;改进原有的微动疲劳寿命预测模型,将微动磨损作为影响微动疲劳寿命的重要因素,引入NiTi微动疲劳寿命预测模型中;给出合理有效的NiTi微动疲劳寿命预测模型.  相似文献   

6.
采用SRV-IV微动摩擦磨损试验机研究在干摩擦和水溶液介质中微动振幅对2507超级双相不锈钢微动磨损行为的影响,利用三维轮廓仪和扫描电子显微镜分别对试样的磨痕深度、磨损体积和磨痕表面微观形貌进行表征分析。结果表明:在干摩擦下,随振幅增加微动运行区域发生了由部分滑移区向滑移区的转变,摩擦因数随振幅的增加先增大后趋于稳定,磨痕深度和磨损体积随振幅的增加而增大,磨损机制由局部氧化磨损、局部疲劳磨损转变为氧化磨损、黏着磨损和剥落磨损;水溶液中,海水中摩擦因数随振幅的波动较去离子水中的大,且海水中由于存在腐蚀与磨损交互作用,磨痕深度和磨损体积也都比去离子水中的略大,磨损机制主要是轻微氧化磨损、磨粒磨损伴随疲劳磨损。  相似文献   

7.
对茂名石化乙烯工业公司低密度聚乙烯装置二次压缩机填料盘过度磨损和开裂的原因进行了分析和研究。结果表明。相邻两块填料盘之间存在着微动磨损,同时填料环的腐蚀和磨损加速了填料盘的微动,大大降低了填料盘的疲劳寿命,使填料盘疲劳开裂。  相似文献   

8.
在不同弯曲载荷下,对40CrNi2MoA合金钢进行弯曲微动疲劳试验,建立其弯曲微动疲劳下的循环次数-应力曲线;通过对微动损伤区的微观分析,研究该合金钢的弯曲微动疲劳特性。结果表明:40CrNi2MoA钢弯曲微动疲劳应力曲线不同于常规疲劳应力曲线,呈现"C"型曲线特征;随着弯曲载荷的增加,微动依次运行于部分滑移区、混合区和滑移区;相对于另外两个区域,混合区试样的裂纹更易萌生、扩展且微动疲劳寿命最短;试样表面的磨损机制主要为磨粒磨损、氧化磨损和剥层;由于接触应力和弯曲应力的影响程度不同,弯曲微动疲劳裂纹的扩展分为三个阶段,即接触应力控制阶段、接触应力与弯曲疲劳应力共同控制阶段和完全受弯曲应力控制阶段。  相似文献   

9.
车用柴油机功率密度和轻量化要求不断提高,往往导致发动机零部件的刚度不足,部件接触面之间产生微位移和微动磨损,对零部件和整机的可靠性产生较大影响。对一款车用柴油机,建立曲轴、轴瓦、螺栓、机体、连杆多体接触有限元模型,根据发动机运行工况,分析一个循环内的载荷和应力分布变化规律;结合微动磨损的Archard模型和微动疲劳的SWT(Smith,Watson and Topper)准则,分析机体-轴瓦的微动磨损和疲劳规律;考虑结构和材料参数的分散性,结合可靠性理论,得到微动损伤可靠性随时间的变化规律。结果表明第四主轴承下轴瓦侧面和第二主轴承上下瓦结合面分别是微动磨损和疲劳的危险点;微动磨损的可靠度下降要快于微动疲劳的可靠度。研究结果为提高整机的可靠性提供了建议和参考。  相似文献   

10.
为了分析空心轴与实心轴过盈配合结构微动磨损与疲劳行为的差异,建立了两种过盈配合结构的微动磨损-微动疲劳联合仿真模型。该联合仿真模型基于Archard磨损方程和有限元软件ABAQUS的自适应网格技术实现了循环微动磨损的仿真,基于线性累积损伤理论和修正的SWT临界平面法实现了微动疲劳寿命预测。分析结果表明:空心轴的微动磨损比实心轴严重,微动磨损显著降低了过盈配合边缘附近的应力集中,同时在配合内部引起了新的应力集中,并导致微动裂纹萌生位置出现在配合内部。受到微动磨损的影响,空心轴的微动疲劳寿命仅约为实心轴的40%,但两种结构的微动裂纹萌生位置几乎一致。  相似文献   

11.
对茂名乙烯超高压压缩机的填料盘异常磨损和开裂进行分析和计算,发现填料盘的磨损是由于填料盘在工作时有微动磨损而引起的,并且造成填料盘微动疲劳,形成微动疲劳裂纹。  相似文献   

12.
The influence of oil lubrication on the fretting wear behaviors of 304 stainless steel flat specimens under different fretting strokes and normal loads has been investigated. The results proved that fretting regimes and fretting wear behaviors of 304 stainless steels were closely related to the fretting conditions. In general, the increase in normal load could increase wear damage during sliding wear. However, according to the results, a significant reduction in wear volume and increase in friction coefficient was observed when the normal load was increased to critical values of 40 and 50 N at a fretting stroke of 50 μm due to the transformation of the fretting regime from a gross slip regime to partial slip regime. Only when the fretting stroke further increased to a higher value of 70 μm at 50 N, fretting could enter the gross slip regime. There was low wear volume and a high friction coefficient when fretting was in the partial slip regime, because oil penetration was poor. The wear mechanisms were fatigue damage and plastic deformation. There was high wear volume and low friction coefficient when fretting was in the gross slip regime, because the oil could penetrate into the contact surfaces. Unlike the wear mechanisms in the partial slip regime, fretting damage of 304 stainless steels was mainly caused by abrasive wear in the gross slip regime.  相似文献   

13.
在自制的微动疲劳试验机上开展中性腐蚀环境下单根钢丝的微动疲劳实验,考察在相同接触载荷下,不同振幅对钢丝的微动疲劳行为的影响,并用扫描电子显微镜观察疲劳钢丝的磨痕和断口形貌,研究钢丝微动疲劳断裂机制.结果表明:在较大的振幅下,钢丝的微动区均处于滑移状态,而在较小振幅下,钢丝的微动区从滑移状态逐渐转变为黏着状态;磨损机制主要为磨粒磨损、疲劳磨损、腐蚀磨损和塑性变形;钢丝疲劳寿命随着微动振幅的增大而减小;钢丝的疲劳断口可分为3个区域,即疲劳源区、裂纹扩展区及瞬间断裂区.  相似文献   

14.
钢丝微动疲劳过程中,钢丝裂纹萌生特性直接影响其裂纹扩展特性,进而制约钢丝微动疲劳寿命,因此开展钢丝微动疲劳裂纹萌生寿命预测研究具有重要意义。基于有限元法、摩擦学理论和断裂力学理论,运用Smith-Watson-Topper(SWT)多轴疲劳寿命准则建立考虑磨损的钢丝微动疲劳裂纹萌生寿命预测模型,基于多种不同的钢丝疲劳参数估算方法对钢丝的微动疲劳裂纹萌生寿命进行了预测,并探究接触载荷、疲劳载荷、交叉角度及钢丝直径等微动疲劳参数对钢丝微动疲劳裂纹萌生寿命的影响规律。结果表明:基于中值法的预测结果最接近实际值;在微动疲劳过程中,钢丝微动疲劳裂纹萌生寿命主要与接触载荷和疲劳载荷相关。通过引入微动损伤参数建立简化的适用于钢丝绳的钢丝微动疲劳裂纹萌生寿命预测模型,通过与考虑磨损的预测模型计算结果进行对比验证了该模型的准确性。  相似文献   

15.
TC4合金微动疲劳损伤研究   总被引:2,自引:1,他引:1  
研究了TC4合金在柱面-平面接触务件下的微动疲劳行为,分析了其微动疲劳损伤机制。结果表明:在试验务件下,微动区边缘的损伤特征以粘着磨损为主,而微动区中部则以磨粒磨损和接触疲劳为主。疲劳裂纹易于在微动区.特别是在蚀坑处萌生和扩展。促使微动疲劳裂纹萌生的因素:一是法向应力和切向摩擦力引起的材料表层塑性变形,二是微动磨损破坏了材料的表面完整性,造成了缺口应力集中效应。  相似文献   

16.
准确实时地获取行驶过程中的状态信息是汽车动态控制系统研究的关键,为此提出了一种新的汽车状态估计器。建立了包含不准确模型参数和未知时变统计特性噪声的非线性汽车动力学模型,针对该非线性系统提出一种双重扩展自适应卡尔曼滤波算法(DEAKF)。该算法采用两个卡尔曼滤波器并行运算,状态估计和参数估计互相更新,同时将带遗忘因子的噪声统计估值器嵌入到状态校正过程和参数校正过程之间,以解决系统的噪声时变问题。基于ADAMS的虚拟试验和实车试验结果表明,该算法的状态估计精度高于EKF方法和DEKF方法的状态估计精度,同时具有良好的模型参数校正能力,对汽车动态控制系统中估计器的设计具有理论指导意义。
  相似文献   

17.
TiAlZr合金微动磨损性能研究   总被引:1,自引:0,他引:1  
采用高精度液压式微动磨损试验机研究了TiA lZr合金在不同微动运行区域的微动磨损行为,建立了其运行工况微动图。试验结果表明:滑移区、混合区和部分滑移区的摩擦因数随循环次数变化呈现不同的规律,其中部分滑移区摩擦因数较低,磨损体积随着位移幅值的增大而增大;滑移区、混合区磨损体积随着法向载荷的增加而增大,而部分滑移区磨损体积随着法向载荷的增加而减小;滑移区磨屑堆积于中心区域,磨损以磨粒磨损和剥层机制为主;混合区磨损机制主要表现为粘着磨损与磨粒磨损并存;部分滑移区磨损轻微。  相似文献   

18.
汽车发动机链条的微动磨损现象研究   总被引:2,自引:0,他引:2  
通过对汽车发动机链条进行高速磨损试验和道路行驶试验,研究了汽车发动机链条的摩擦磨损性能。结果表明,试验后链条的套筒与内链板以及销轴与外链板之间的压出力和扭矩均有所下降,这就说明了微动磨损现象的存在。通过对磨斑形貌的分析,探讨了其磨损机制,表明粘着磨损、疲劳磨损和磨粒磨损是主要磨损机制。对汽车发动机链条微动损伤防护方法进行了探讨,表明通过对链板孔采用挤孔工艺,增加套筒与内链板,销轴与外链板的过盈配合量以及改进链板、销轴和套筒的表面处理工艺来提高其疲劳强度,可增加抗微动损伤的能力。  相似文献   