Friction and wear behaviour of Thordon XL and LgSn80 in sliding against plasma-sprayed Cr2O3 coatings

This paper studies the friction and wear behaviour of two important bearing materials, Thordon XL and LgSn80, in dry and lubricated sliding vs. plasma-sprayed Cr₂O₃ coatings. As a reference, AISI 1043 steel is also studied under the same conditions. SEM, EDS and surface topography were employed to study the wear mechanisms. The results indicate that the Thordon XL/Cr₂O₃ coating pair gives the lowest dry friction coefficient (0.16) under a normal load of 45.3 N (pressure 0.453 MPa) at a velocity of 1 m/s. The dry friction coefficient of Thordon XL/Cr₂O₃ coating increases to 0.38 under a normal load of 88.5 N (pressure 0.885 MPa). The dry friction coefficients of the LgSn80/Cr₂O₃ coating are in the range of 0.31–0.46. Secondly, both dry wear rate under low normal load (45.3 N) and lubricated wear rate under a load of 680 N for Thordon XL are lower than those of LgSn80 in sliding against plasma-sprayed Cr₂O₃ coatings at a speed of 1 m/s. However, under a normal load of 88.5 N the dry wear rate of Thordon XL is much higher than that of LgSn80. Thirdly, a high viscosity lubricant (SAE 140) leads to lower wear for Thordon XL and LgSn80 than a low viscosity lubricant (SAE 30). Finally, the dominating wear mechanism for Thordon XL is shear fracture when against the plasma-sprayed Cr₂O₃ ceramic coating. For LgSn80 against plasma-sprayed Cr₂O₃ ceramic coating, abrasive wear is the governing failure mechanism.     

Sliding wear characteristics of plasma-sprayed Al2O3 and Cr2O3 coatings against copper alloy under severe conditions

Al₂O₃ and Cr₂O₃ coatings were deposited by atmospheric plasma spraying and their tribological properties dry sliding against copper alloy were evaluated using a block-on-ring configuration at room temperature. It was found that the wear resistance of Al₂O₃ coating was superior to that of the Cr₂O₃ coating under the conditions used in the present study. This mainly attributed to its better thermal conductivity of Al₂O₃ coating, which was considered to effectively facilitate the dissipation of tribological heat and alleviate the reduction of hardness due to the accumulated tribological heat. As for the Al₂O₃ coating, the wear mechanism was plastic deformation along with some micro-abrasion and fatigue-induced brittle fracture, while the failure of Cr₂O₃ coating was predominantly the crack propagation-induced detachment of transferred films and splats spallation.     

Friction and wear behaviour of plasma-sprayed Cr2O3 coatings against steel in a wide range of sliding velocities and normal loads

This study investigates the influence of sliding speed and normal load on the friction and wear of plasma-sprayed Cr₂O₃ coatings, in dry and lubricated sliding against AISI D2 steel. Friction and wear tests were performed in a wide speed range of 0.125–8 m/s under different normal loads using a block-on-ring tribometer. SEM, EDS and XPS were employed to identify the mechanical and chemical changes on the worn surfaces. A tangential impact wear model was proposed to explain the steep rising of wear from the minimum wear to the maximum wear. The results show that the wear of Cr₂O₃ coatings increases with increasing load. Secondly, there exist a minimum-wear sliding speed (0.5 m/s) and a maximum-wear sliding speed (3 m/s) for a Cr₂O₃ coating in dry sliding. With the increase of speed, the wear of a Cr₂O₃ coating decreases in the range 0.125–0.5 m/s, then rises steeply from 0.5 m/s to 3 m/s, followed by a decrease thereafter. The large variation of wear with respect to speed can be explained by stick-slip at low speeds, the tangential impact effect at median speeds and the softening effect of flash temperature at high speeds. Thirdly, the chemical compositions of the transfer film are a-Fe₂O₃ in the speed range 0.25–2 m/s, and FeO at 7 m/s. In addition, the wear mechanisms of a Cr₂O₃ coating in dry sliding versus AISI D2 steel are adhesion at low speeds, brittle fracture at median speeds and a mixture of abrasion and brittle fracture at high speeds. Finally the lubricated wear of Cr₂O₃ coating increases sharply from 1 to 2.8 m/s.     

Tribological characteristics of low-pressure plasma-sprayed A12O3 coating from room temperature to 800 °C

The tribological characteristics of low-pressure plasma-sprayed (LPPS) Al₂O₃ coating sliding against alumina ball have been investigated from room temperature to 800 °C. These friction and wear data have been compared quantitatively with those of bulk sintered alumina to obtain a better understanding of wear mechanisms at elevated temperatures. The friction and wear of Al₂O₃ coating show a strong dependence on temperature, changing from a mild to a severe wear regime with the increase of temperature. The coefficient of friction at room temperature is approximately 0.17 to 0.42, depending on applied load. The tribochemical reaction between the coating surface and water vapor in the environment and the presence of the hydroxide film on the Al₂O₃ coating reduce the friction and wear at room temperature as contrasted to those of bulk sintered alumina. At intermediate temperatures, from 400 to 600 °C, the friction and wear behavior of Al₂O₃ coating depends on the inter-granular fracture and pull-out of Al₂O₃ grains. At above 700 °C, formation and deformation of fine grain layer, and abrasive wear in the form of removal of fine alumina grains further facilitate the friction and wear process of Al₂O₃ coating.     

Comparison of wear behaviour of plasma-sprayed Al2O3 coatings with and without laser treatment

This paper studies experimentally the effects of CO₂ laser-treatment on the wear behaviour of plasma-sprayed Al₂O₃ coatings, in linear contact sliding (dry, abrasive and lubricated) against SAE 4620 steel. Tests were carried out using a block-on-ring friction and wear tester, under different loads at different speeds. The wear mechanism and the changes in adherence, porosity and microstructure by laser treatment were also investigated. Results show a better wear behaviour for both laser-treated ceramic coating and its paired steel under dry and abrasive conditions, compared with the case without laser treatment. The lubricated wear behaviour of the laser-treated ceramic coating, however, is not improved. The changes in microhardness, porosity and adherence caused by the laser treatment are responsible for the change in wear behaviour of the ceramic coating.     

Tribological properties of spark-plasma-sintered ZrO2(Y2O3)-CaF2-Ag composites at elevated temperatures

Spark-plasma sintering is employed to synthesize self-lubricating ZrO₂(Y₂O₃) matrix composites with different additives of CaF₂ and Ag as solid lubricants by tailoring the composition and by adjusting the sintering temperature. The friction and wear behavior of ZrO₂(Y₂O₃) matrix composites have been investigated in dry sliding against an alumina ball from room temperature to 800 °C. The effective self-lubrication at different temperatures depends mainly on the content of various solid lubricants in the composites. The addition of 35 wt.% Ag and 30 wt.% CaF₂ in the ZrO₂(Y₂O₃) matrix can promote the formation of a well-covered lubricating film, and effectively reduce the friction and wear over the entire temperature range studied. The friction coefficients at low temperatures were at a minimum value for the composite containing 35 wt.% of silver. At this silver concentration, low and intermediate temperature lubricating properties are greatly improved without affecting high-temperature lubrication by the calcium fluoride in ZrO₂(Y₂O₃) matrix composites. The worn surfaces and transfer films formed during wear process have been characterized to identify the synergistic lubrication behavior of CaF₂ and Ag lubricants at different temperatures.     

Influence of Al2O3 reinforcement on the abrasive wear characteristic of Al2O3/PA1010 composite coatings

In the present study, the abrasive wear characteristics of Al₂O₃/PA1010 composite coatings were tested on the turnplate abrasive wear testing machine. Steel 45 (quenched and low-temperature tempered) was used as a reference material. The experimental results showed that when the Al₂O₃ particles have been treated with a silane coupling agent (γ-aminopropyl-triethoxysilane), the abrasive wear resistance of Al₂O₃/PA1010 composite coatings has a good linear relationship with the volume fraction of Al₂O₃ particles in Al₂O₃/PA1010 composite coatings and the linear correlation coefficient is 0.979. Under the experimental conditions, the size of Al₂O₃ particles (40.5-161.0 μm) has little influence on the abrasive wear resistance of Al₂O₃/PA1010 composite coatings. By treating the surface of Al₂O₃ particles with the silane coupling agent, the distribution of Al₂O₃ particles in PA1010 matrix is more homogeneous and the bonding state between Al₂O₃ particles and PA1010 matrix is better. Therefore, the Al₂O₃ particles make the Al₂O₃/PA1010 composite coatings have better abrasive wear resistance than PA1010 coating. The wear resistance of Al₂O₃/PA1010 composite coatings is about 45% compared with that of steel 45.     

A study on friction and wear characteristics of nanometer Al2O3 /PEEK composites under the dry sliding condition

The friction and wear properties of the polyetheretherketone (PEEK) based composites filled with 5 mass% nanometer or micron Al₂O₃ with or without 10 mass% polytetrafluroethylene (PTFE) against the medium carbon steel (AISI 1045 steel) ring under the dry sliding condition at Amsler wear tester were examined. A constant sliding velocity of 0.42 m s⁻¹ and a load of 196 N were used in all experiments. The average diameter 250 μm PEEK powders, the 15 or 90 nm Al₂O₃ nano-particles or 500 nm Al₂O₃ particles and/or the PTFE fine powders of diameter 50 μm were mechanically mixed in alcohol, and then the block composite specimens were prepared by the heat compression moulding. The homogeneously dispersion of the Al₂O₃ nano-particles in PEEK matrix of the prepared composites was analyzed by the atomic force microscopy (AFM). The wear testing results showed that nanometer and micron Al₂O₃ reduced the wear coefficient of PEEK composites without PTFE effectively, but not reduced the friction coefficient. The filling of 10 mass% PTFE into pure PEEK resulted in a decrease of the friction coefficient and the wear coefficient of the filled composite simultaneously. However, when 10 mass% PTFE was filled into Al₂O₃/ PEEK composites, the friction coefficient was decreased and the wear coefficient increased. The worn scars on the tested composite specimen surfaces and steel ring surfaces were observed by scanning electron microscopy (SEM). A thin, uniform, and tenacious transferred film on the surface of the steel rings against the PEEK composites filled with 5 mass% 15 nm Al₂O₃ particles but without PTFE was formed. The components of the transferred films were detected by energy dispersive spectrometry (EDS). The results indicated that the nanometer Al₂O₃ as the filler, together with PEEK matrix, transferred to the counterpart ring surface during the sliding friction and wear. Therefore, the ability of Al₂O₃ to improve the wear resistant behaviors is closely related to the ability to improve the characteristics of the transfer film.     

Tribological properties of Ni3Al-Cr7C3 composite coating under water lubrication

The tribological properties of Ni₃Al-Cr₇C₃ composite coating under water lubrication were examined by using a ball-on-disc reciprocating tribotester. The effects of load and sliding speed on wear rate of the coating were investigated. The worn surface of the coating was analyzed using electron probe microscopy analysis (EPMA) and X-ray photoelectron spectroscopy (XPS). The results show the friction coefficient of the coating is decreased under water lubrication. The wear rate of the coating linearly increases with the load. At high sliding speed, the wear rate of the coating is dramatically increased and a large amount of the counterpart material is transferred to the coating worn surface. The low friction of the coating under water lubrication is due to the oxidizing of the worn surface in the wear. The wear mechanism of the coating is plastic deformation at low normal load and sliding speed. However, the wear mechanism transforms to microfracture and microploughing at high load with low sliding speed, and oxidation wear at high sliding speed. It is concluded that the contribution of the sliding speed to an increase in the coating wear is larger than that of the normal load.     

Tribological Properties of Muscovite/La2O3 Composite Powders as Lubricant Additives

Muscovite/La₂O₃ composite powders were prepared by ball-milling solid-state chemical reaction at room temperature. The phase composition and micromorphology of the composite powders were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDX). The tribological properties of different samples were tested and compared using four-ball wear testing on an MMW-1A multifunctional friction and wear testing machine. The SEM micrography and energy spectrum of the composite powders illustrated that La₂O₃ particles were coated on the surface of muscovite particles. The results of the friction tests indicated that lubrication oil with muscovite/La₂O₃ composite powders presents better friction reducing and antiwear properties than that of the base oil, and the friction coefficients and diameters of wear scars decreased by 47.6 and 11.2% using 500SN base oil with 0.6g/L of muscovite/La₂O₃ composite powders as additives, respectively. The composite powders with 5 wt% La₂O₃ present the best comprehensive tribological properties. The micromorphology and chemical composition of the worn surface were analyzed by SEM and EDX, which confirm that the composite powders directly participate in the complicated physicochemical process of reactions on the worn surfaces, therefore improving the tribological properties of the base oil.