Effect of Sb on microstructure and mechanical properties in Mg-10Zn-5Al high zinc magnesium alloys

In view of high strength and poor impact toughness of the high-zinc magnesium alloys,the method of micro-alloying was adopted to improve the impact-toughness of Mg-10Zn-5Al high zinc magnesium alloys by adjusting the addition of Sb.The results show that:the dystectic Mg3Sb2 particles formed by Sb and Mg are distributed in the front of dendrite,restrain the growth of the secondary phase and then change the morphology of the secondary phases,which refines the matrix in some extent and improves the impact-toug...     

Effect of Nd and Yb on the Microstructure and Mechanical Properties of Mg-Zn-Zr Alloy

研究了稀土元素Nd、Yb对Mg-5.5Zn-0.6Zr合金组织与性能的影响。结果表明:单独添加Nd或Yb元素后,试验合金的组织明显细化,同时在晶界处形成了γ((Mg,Nd)Zn2)或γ((Mg,Yb)Zn2)三元稀土相;而复合添加Nd和Yb元素后,试验合金的组织不但没有细化,而且在晶界处形成了呈网状分布的γ((Mg,Nd+Yb)Zn2)四元稀土相,并且晶界变宽。经过T4固溶处理后,Mg-5.5Zn-0.6Zr合金中的共晶组织完全溶入基体,而添加Nd、Yb元素后的Mg-5.5Zn-0.6Zr合金晶界处仍有未溶的化合物相存在。其中,添加Yb元素后的Mg-5.5Zn-0.6Zr合金经固溶处理后在晶界处形成了一种新的Mg-Zn-Yb三元球状颗粒相,其常温下的抗拉强度、屈服强度和伸长率分别达到了255.6 MPa、163.6 MPa和17.4%,这主要是因为加入稀土元素Yb后固溶处理产生了复合强化效果。在高温条件下,复合添加稀土元素Nb、Yb后的试验合金具有很好的热稳定性,但其高温塑性比较差。     

稀土元素Nd、Yb对Mg-Zn-Zr合金组织与性能的影响(英文)

研究了稀土元素Nd、Yb对Mg-5.5Zn-0.6Zr合金组织与性能的影响。结果表明:单独添加Nd或Yb元素后,试验合金的组织明显细化,同时在晶界处形成了γ((Mg,Nd)Zn2)或γ((Mg,Yb)Zn2)三元稀土相;而复合添加Nd和Yb元素后,试验合金的组织不但没有细化,而且在晶界处形成了呈网状分布的γ((Mg,Nd+Yb)Zn2)四元稀土相,并且晶界变宽。经过T4固溶处理后,Mg-5.5Zn-0.6Zr合金中的共晶组织完全溶入基体,而添加Nd、Yb元素后的Mg-5.5Zn-0.6Zr合金晶界处仍有未溶的化合物相存在。其中,添加Yb元素后的Mg-5.5Zn-0.6Zr合金经固溶处理后在晶界处形成了一种新的Mg-Zn-Yb三元球状颗粒相,其常温下的抗拉强度、屈服强度和伸长率分别达到了255.6 MPa、163.6 MPa和17.4%,这主要是因为加入稀土元素Yb后固溶处理产生了复合强化效果。在高温条件下,复合添加稀土元素Nb、Yb后的试验合金具有很好的热稳定性,但其高温塑性比较差。     

Sm对AM60合金显微组织和力学性能的影响

借助光学显微镜、扫描电镜、X射线衍射仪和DNS100电子万能试验机研究AM60合金中加入Sm后的显微组织和力学性能,并分析Sm对合金显微组织和力学性能的影响。结果表明,添加元素Sm可以细化镁合金的晶粒,改变β相的形态和大小,从连续或断续网状、长条状,变为卵石状或颗粒状均匀弥散分布在α-Mg基体上,显著改善合金的显微组织。Sm的加入可形成稳定性较高的颗粒状Al2Sm高温化合物相。随着Sm含量的增加,合金的抗拉伸强度和伸长率呈现先升后降的趋势,当Sm含量为1.0%(质量分数,下同)时抗拉伸强度和伸长率分别达到最大值210MPa和6.9%。室温下AM60合金的断口呈解理断裂,加入Sm变质后其断口形貌表现为准解理+局部韧性断裂特征。