含苯并噁唑半芳香聚酰胺的合成与表征 总被引:2,自引:0,他引:2
为了得到同时具有优良耐热性能和易加工性能的新型半芳香聚酰胺,以5-氨基-2-(对氨基苯)苯并噁唑(ABO)和己二酸基于Yamazaki磷酸化过程合成了聚己二酰对苯撑苯并噁唑二胺(BO6).研究了反应温度对聚合物分子量的影响,并通过FTIR、1H-NMR对其结构进行了表征;利用DSC、TG对其热性能进行了研究.结果表明:反应温度在90℃左右时高聚物获得了最高的粘数.该聚合物的耐热性较脂肪族聚酰胺有较大幅度的提高,同时该聚合物具有较好的耐溶剂性能. 相似文献
4.
In order to obtain a novel polyamide having excellent heat-resistant properties which could be anticipated as a thermal modifier for aliphatic polyamide,a series of new semi-aromatic polyamides (BO6,BO8,BO10) containing benzoxazole unit were synthesized based on 5-amino-2-(p-aminophenyl) benzoxazole (ABO) and aliphatic acids (adipic,suberic and sebacic acid) by means of Yamazaki phosphorylation method.The effect of reaction temperature on the inherent viscosity of the polymers was studied,and the structures of products were characterized by FTIR,1 H-NMR,and the heat resistance of the polymers was studied by DSC and TG.The results showed that the reaction temperature gives the polymers the highest viscosity at around 90 ℃,130 ℃ and 130 ℃ for BO6,BO8 and BO10,respectively.The heat resistance of the new semi-aromatic polyamides is much higher than that of the common aliphatic polyamides.In addition,the products show good solvent resistance and crystallization properties. 相似文献
5.
6.
7.
多壁碳纳米管/环氧树脂复合材料性能研究 总被引:1,自引:0,他引:1
采用物理机械方法与化学方法相结合的手段,制备了多壁碳纳米管(MWNTS)/环氧树脂(Epoxy)复合材料。通过力学拉伸试验测试了MWNTs/Epoxy复合材料拉伸强度和拉伸模量与MWNTS添加量的关系,利用扫描电镜(SEM)分析了MWNTS/Epoxy复合材料的拉伸断面,并用表面电阻测试仪对所制备的碳纳米管复合材料进行了电学性能测试。结果表明:经过化学酸化的方法处理后的MWNTS在复合材料中的分散得到了改善,力学性能也得到了明显的提高,但酸处理后的复合材料的电学性能明显低于未处理的复合材料。 相似文献
1