High energy storage properties of lead-free Mn-doped (1-x)AgNbO3-xBi0.5Na0.5TiO3 antiferroelectric ceramics

In this work, 0.2 wt.% Mn-doped (1-x)AgNbO₃-xBi_0.5Na_0.5TiO₃ (x = 0.00–0.04) ceramics were synthesized via solid state reaction method in flowing oxygen. The evolution of microstructure, phase transition and energy storage properties were investigated to evaluate the potential as high energy storage capacitors. Relaxor ferroelectric Bi_0.5Na_0.5TiO₃ was introduced to stabilize the antiferroelectric state through modulating the M₁-M₂ phase transition. Enhanced energy storage performance was achieved for the 3 mol% Bi_0.5Na_0.5TiO₃ doped AgNbO₃ ceramic with high recoverable energy density of 3.4 J/cm³ and energy efficiency of 62% under an applied field of 220 kV/cm. The improved energy storage performance can be attributed to the stabilized antiferroelectricity and decreased electrical hysteresis ΔE. In addition, the ceramics also displayed excellent thermal stability with low energy density variation (<6%) over a wide temperature range of 20−80 °C. These results indicate that Mn-doped (1-x)AgNbO₃-xBi_0.5Na_0.5TiO₃ ceramics are highly efficient lead-free antiferroelectric materials for potential application in high energy storage capacitors.     

Synthesis and characterization of Ce/SiOC nanocomposites through the polymer derived ceramic method and evaluation of their catalytic activity

Cerium oxide and silicon oxycarbide (Ce/SiOC) porous nanocomposites have been synthesized through the polymer derived ceramic route. In the synthesis of the preceramic precursors, the addition of urea facilitates the deposition of Cerium atoms on the surface of SiO₂ nanoparticles since it prevents the SiO₂ from agglomeration. Both Ce and urea affects the structural and textural parameters of the obtained ceramics. Less crosslinked structures are formed when the urea concentration increases and it also provokes a reduction of the carbon crystallite size. Cerium, on the other hand, induces an increase of the carbon size as well as the number of SiOC units. Pore anisotropy and smoothness of the surface are also dependent on the composition of the material. As expected, the better thermocatalytic behavior against CO₂ decomposition is found at the largest Ce amounts but also, smooth surfaces and low pore anisotropies favor the accessibility of the gases to the thermocatalytic centers.     

Phase-composition dependent domain responses in (K0.5Na0.5)NbO3-based piezoceramics

Lead-free (K_0.5Na_0.5)NbO₃-based (KNN) piezoceramics featuring a polymorphic phase boundary (PPB) between the orthorhombic and tetragonal phases at room temperature are reported to possess high piezoelectric properties but with inferior cycling stability, while the ceramics with a single tetragonal phase show improved cycling stability but with lower piezoelectric coefficients. In this work, electric biasing in-situ transmission electron microscopy (TEM) study is conducted on two KNN-based compositions, which are respectively at and off PPB. Our observations reveal the distinctive domain responses in these two ceramics under cyclic fields. The higher domain wall density in the poled KNN at PPB contributes to the high piezoelectric properties. Upon cycling, however, a new microstructure feature, “domain intersection”, is directly observed in this PPB composition. In comparison, the off-PPB KNN ceramic develops large domains during poling, which experience much less extent of disruption during cycling. Our comparative study provides the basis for understanding the relation between phase composition and piezoelectric performance.     

Remarkably enhanced energy storage properties of lead-free Ba0.53Sr0.47TiO3 thin films capacitors by optimizing bottom electrode thickness

The lead-free Ba_0.53Sr_0.47TiO₃ (BST) thin films buffered with La_0.67Sr_0.33MnO₃ (LSMO) bottom electrode of different thicknesses were fabricated by pulsed laser deposition method on a (001) SrTiO₃ substrate. It was found that the roughness of electrode decreases and substrate stress relaxes gradually with the increase of LSMO thickness, which is beneficial for weakening local high electric field and achieving higher E_b. Therefore, the recoverable energy density (W_rec) of BST films can be greatly improved up to 67.3 %, that is, from 30.6 J/cm³ for the LSMO thickness of 30 nm up to 51.2 J/cm³ for the LSMO thickness of 140 nm after optimizing the LSMO thickness. Furthermore, the thin film capacitor with a 140 nm LSMO bottom electrode shows an outstanding thermal stability from 20 °C to 160 °C and superior fatigue resistance after 10⁸ electrical cycles with only a slightly decrease of W_rec below 1.6 % and 3.7 %, respectively. Our work demonstrates that optimizing bottom electrodes thickness is a promising way for enhancing energy storage properties of thin-film capacitors.     

Excited-state absorption of meso-tetrasulfonatophenyl porphyrin: Effects of pH and micelles

The influence of the environment on the excited state transitions of meso-tetrakis(p-sulfonatophenyl) porphyrin (TPPS) is reported. TPPS was investigated in protonated and non-protonated forms, and in the presence of the cationic cetyltrimethylammonium bromide (CTAB) micelles. The singlet excited-state absorption spectra were measured by using the white-light continuum Z-scan technique and the triplet–triplet absorption spectra were acquired employing an association of laser flash photolysis and Z-scan techniques. Our results show that the perseveration of the molecular symmetry, upon excitation, depends on the state of multiplicity of the molecules, as well as on the environment and structural characteristics of the porphyrin. Additionally, it was observed that for excited molecules, the ring distortion caused by the protonation of porphyrin ring has great influence on the changes observed for the symmetry and vibronic structure. The results clearly show that the porphyrin investigated is a promising candidate for optical limiting applications for all investigated environments.     

Evolution mechanism of the microstructure and mechanical properties of plasma-sprayed yttria-stabilized hafnia thermal barrier coating at 1400 °C

Yttria stabilized hafnia (Hf_0.84Y_0.16O_1.92, YSH16) coatings were sprayed by atmospheric plasma spraying (APS). The effects of thermal aging at 1400 °C on the microstructures, mechanical properties and thermal conductivity of the coatings were studied. The results show that the as-sprayed coating was composed of the cubic phase, and the nano-sized monoclinic (M) phase was precipitated in the annealed coating. The presence of M phase effectively constrained the sintering of the coating due to its superior sintering-resistance. The Young's modulus kept at a nearly same level of ~78 GPa even after annealing, and the coating annealed for 6 h yielded a maximum value of hardness but revealed a declining tendency in the Vicker's hardness with prolonged sintering time. The thermal conductivity increased from 0.8-0.95 W m^-1 K^-1 at as-sprayed state to 1.6 W m^-1 K^-1 after annealing at 1400 °C for 96 h. The dual-phase coating is promising to serve at temperatures above 1400 °C due to its excellent thermal stability and mechanical properties.     

Homogenization with uncertainty in Poisson ratio for polymers with rubber particles

The main aim of this work is dual computer analysis of probabilistic coefficients for the homogenized tensor of the polymer filled with the rubber particles having randomized Poisson ratios of both constituents. The major issue is to verify an influence of a randomness in rubber Poisson ratio close to the compressibility limit on the uncertainty of the effective tensor probabilistic characteristics. Probabilistic analysis presented here is carried out using mainly the stochastic perturbation technique provided by the common application of the traditional FEM commercial code ABAQUS and the symbolic computations package MAPLE. This FEM-based technique employs polynomial response function of the optimum order recovered from the weighted least squares method and following a set of deterministic solutions obtained for various values of the randomized input parameter. Optimization procedure is released entirely into a symbolic environment, where maximization of the correlation factor together with minimization of the fitting variance and approximation error are applied. Homogenization technique consists in equating of deformation energies for the real composite and the artificial one characterized by the effective elasticity tensor with uncertainty.     

Structure,dielectric properties of novel Ba(Zr,Ti)O3 based ceramics for energy storage application

(1-x) Ba(Zr_0.2Ti_0.8)O₃-x Na_0.5Bi_0.5TiO₃ (x = 0, 10, 20 30, 40, 50 mol%) (BZTN) ceramics are prepared by the traditional solid phase method. All BZTN ceramics exhibit a pseudo-cubic BZT based perovskite structure. Both the average grain size and the relaxor ferroelectricity of BZTN ceramics gradually increase with increasing NBT content. The W_rec of 3.22 J/cm³ and η of 91.2% is obtained for the BZTN40 ceramic at 241 kV/cm. BZTN40 ceramic also exhibits good temperature stability from room temperature to 150 °C and frequency stability from 1 Hz to 100 Hz. A P_D of 0.621 J/cm³ and a t_0.9 of 82 ns is obtained for the BZTN40 ceramic at 120 kV/cm. BZTN ceramics show application potential in energy storage and pulse power capacitors.     

Highly textured and strongly anisotropic TiB2 ceramics prepared using magnetic field alignment (9T)

Highly textured TiB₂ ceramics were prepared by slip casting an aqueous suspension in a magnetic field of 9 T, followed by sintering using Field Assisted Sintering Technology (FAST). Particle size refinement by ball milling improved both the degree of texturing and densification of the material (RD > 98 %). The sintered material exhibited a Lotgering orientation factor of 0.90, with the c-axis of TiB₂ oriented parallel to the magnetic field and FAST pressing direction. The texturing effect induced by the uniaxial pressing was negligible. The textured TiB₂ material exhibited a significant anisotropy in mechanical properties; the values of hardness and indentation elastic modulus measured along directions transverse to the c-axis of TiB₂ were 37 % and 13 % higher than the ones measured along the c-axis direction. Moreover, the specific wear rate of a surface of textured TiB₂ parallel to the field was one order of magnitude lower than a surface perpendicular to the field.     

Enhanced transduction coefficient in piezoelectric PZT ceramics by mixing powders calcined at different temperatures

Large transduction coefficient ($d_{33}\times g_{33}$) is difficult to obtain in piezoelectric ceramics because these two parameters show opposite trends with compositional modifications. Herein, the Pb(Zr_0.53Ti_0.47)O₃ ceramic powders were calcinated under different temperatures (A:830 °C, B:860 °C, and C:890 °C), and then mixed together according to different weight ratios (1A:1B:1C, 1A:2B:1C, 1A:2B:3C and 3A:2B:1C) for ceramics preparation. Both d₃₃ and g₃₃ are improved successfully, and the transduction coefficient with the weight ratio of 1A:2B:3C reaches up to 17,500 × 10⁻¹⁵ m²/N, which is 60 % higher than that with the powders calcinated under 830 °C, and at least twice those of commercial PZT-4, PZT-5A and PZT-8 ceramics. The improved transduction coefficient is owing to the enhanced piezoelectric constant and spontaneous polarization resulted from the increased grain size, relative density and the fraction of tetragonal phase. These results indicate that this is a simple but effective way to tailor the transduction coefficient in piezoelectric ceramics.