Investigation of stress fields for non-standard sized glass plates loaded by ring-on-ring

A ring-on-ring (ROR) test is a prevailing test method for evaluating the equi-biaxial strength of glass materials. However, current ROR test standards limit the strength and size of glass to prevent a nonlinear behavior. In this study, the feasibility of ROR testing for non-standard, high-strength glass, such as tempered or ion-exchanged rectangular glass is investigated. To this end, ROR simulation based on theory and experiment is conducted for thirty non-standard glasses with widths of 100–300 mm and aspect ratios of 1.0–2.0. As a result, the maximum measurable stress was about 215.6 MPa for 100 × 200 mm glass and 481.3 MPa for 300 × 600 mm glass with a 3% deviation, which is well above the strength of regular tempered glass. The main purpose of this work is to understand the range of aspect ratio of horizontal and vertical widths of a glass plate that can be evaluated by the standard ROR test.     

Controlling Au electrode patterns for simultaneously monitoring electrical actuation and shape recovery in shape memory polymer

This paper presents an effective approach to achieve efficient electrical actuation and monitoring of shape recovery based on patterned Au electrodes on shape memory polymer (SMP). The electrically responsive shape recovery behavior was characterized and monitored by the evolution change in electrical resistance of patterned Au electrode. Both electrical actuation and temperature distribution in the SMP have been improved by optimizing the Au electrode patterns. The electrically actuated shape recovery behavior and temperature evolution during the actuation were monitored and characterized. The resistance changes could be used to detect beginning/finishing points of the shape recovery. Therefore, the Au electrode not only significantly enhances the electrical actuation performance to achieve a fast electrical actuation, but also enables the resistance signal to detect the free recovery process.     

Characteristics and formation mechanism of porosities in CFRP during laser joining of CFRP and steel

An experimental investigation on the mechanism of porosity formation during the laser joining of carbon fiber reinforced polymer (CFRP) and steel is presented. The porosity morphology and distribution were characterized by optical and scanning electron microscopy, and the thermal pyrolysis behaviors were investigated by thermal analysis and designed back-side cooling experiments. The results show that there are two types of porosities in CFRP. Porosity I only appears when the heat input is more than 77.8 J/mm. It has a smooth inner wall and distributes near the bonding interface between CFRP and steel at the central area of melted zone, which is caused by gaseous products such as CO₂, NH₃, H₂O, and hydrocarbons produced by the pyrolysis of CFRP. Porosity II can be seen under all joining conditions. It has a rough inner wall and distributes far away from the bonding interface, concentrating at the final solidification locations. Porosity II is caused by the shrinkage of melted CFRP during solidification stage.     

Hierarchical multi-reservoir optimization modeling for real-world complexity with application to the Three Gorges system

High dimensionality in real-world multi-reservoir systems greatly hinders the application and popularity of evolutionary algorithms, especially for systems with heterogeneous units. An efficient hierarchical optimization framework is presented for search space reduction, determining the best water distributions, not only between cascade reservoirs, but also among different types of hydropower units. The framework is applied to the Three Gorges Project (TGP) system and the results demonstrate that the difficulties of multi-reservoir optimization caused by high dimensionality can be effectively solved by the proposed hierarchical method. For the day studied, power output could be increased by 6.79 GWh using an optimal decision with the same amount of water actually used; while the same amount of power could be generated with 2.59 × 10⁷ m³ less water compared to the historical policy. The methodology proposed is general in that it can be used for other reservoir systems and other types of heterogeneous unit generators.     

A novel combination of precursor pyrolysis assisted sintering and rapid sintering for construction of multi-composition coatings to improve ablation resistance of SiOC ceramic modified carbon fiber needled felt preform composites

A double-layer coating composed of MoSi₂–SiO₂–SiC/ZrB₂–MoSi₂–SiC was designed and successfully constructed by a novel combination of precursor pyrolysis assisted sintering and rapid sintering to improve the ablation resistance of SiOC ceramic modified carbon fiber needled felt preform composites (CSs). The ZrB₂–MoSi₂–SiC inner layer coating was in relatively uniform distribution in the zone of 0–3 mm from the surface of CSs through the slurry/precursor infiltration in vacuum and SiOC precursor pyrolysis assisted sintering, which played a predominant role in improving oxidation and ablation resistance and maintaining the morphology of CSs. The MoSi₂–SiO₂–SiC outer layer coating was prepared by the spray and rapid sintering to further protect CSs from high-temperature oxidation. The ablation resistance of CSs coated with double-layer coating was evaluated by an oxygen-acetylene ablation test under the temperature of 1600–1800 °C with different ablation time of 1000 and 1500 s. The results revealed that the mass recession rates increased with the rise of ablation temperature and extension of ablation time, ranging from 0.47 g/(m²·s) to 0.98 g/(m²·s) at 1600–1800 °C for 1000 s and from 0.72 g/(m²·s) to 0.86 g/(m²·s) for 1000–1500 s at 1700 °C, while the linear recession rates showed negative values at 1700 °C due to the formation of oxides, such as SiO₂ and ZrO₂. The ablation mechanism of the double-layer coating was analyzed and found that a SiO₂–ZrO₂–Mo_4.8Si₃C_0.6 oxidation protection barrier would be formed during the ablation process to prevent the oxygen diffusion into the interior CSs, and this study provided a novel and effective way to fabricate high-temperature oxidation protective and ablation resistant coating.     

The improvement of the self-healing ability of MoSi2 coatings at 900–1200 °C by introducing SiB6

The brittleness of MoSi₂ ceramic and the thermal mismatch between MoSi₂ coating and C / C composite lead to brittle cracking of the coating at 900−1200 °C. This problem has been overcome in this studyby introducing submicron-SiB₆ into the coating. The pre-fabricated cracks and a kinetics model of hot-pressed SiB₆-MoSi₂ ceramic could quantitatively predict the glass growth and crack healing. As expected, enhancing temperature and SiB₆ content increased the growth rate of the borosilicate glass and the crack healing ability of MoSi₂ ceramic, which was ascribed to the lower oxidation activation energy and larger specific surface area of submicron-SiB₆. For the plasma sprayed coating, SiB₆ with submicron structure was benefit for cracking inhibition and formation of borosilicate glass during oxidation, reducing the oxygen permeability and the consumption of inner coating. Hence, the 15 % SiB₆-MoSi₂ coatings raised the protection times to 84 and 120 h at 900 and 1200 °C respectively, presenting favorable oxidation protective performance.     

High strength and high modulus carbon fibers

Carbon fibers have been processed from gel spun polyacrylonitrile copolymer on a continuous carbonization line at Georgia Tech (GT) with a tensile strength in the range of 5.5–5.8 GPa, and tensile modulus in the range of 354–375 GPa. This combination of strength and modulus is the highest for any continuous fiber reported to date, and the gel spinning route provides a pathway for further improvements in strength and modulus for mass production of carbon fibers. At short gauge length, fiber tensile strength was as high as 12.1 GPa, which is the highest value ever reported for a PAN based carbon fiber. Structure analysis shows random flaws of about 2 nm size, which results in limiting tensile strength of higher than 20 GPa. Inter-planar turbostratic graphite shear modulus in high strength carbon fibers is 30 GPa, while in graphite the corresponding value is only 4 GPa.     

Fabrication and microwave absorption properties of magnetite nanoparticle–carbon nanotube–hollow carbon fiber composites

Absorbents with “tree-like” structures, which were composed of hollow porous carbon fibers (HPCFs) acting as “trunk” structures, carbon nanotubes (CNTs) as “branch” structures and magnetite (Fe₃O₄) nanoparticles playing the role of “fruit” structures were prepared by chemical vapor deposition technique and chemical reaction. Microwave reflection loss, permittivity and permeability of Fe₃O₄–CNTs–HPCFs composites were investigated in the frequency range of 2–18 GHz. It was proven that prepared absorbents possessed the excellent electromagnetic wave absorbing performances. The bandwidth with a reflection loss less than −15 dB covers a wide frequency range from 10.2 to 18 GHz with the thickness of 1.5–3.0 mm, and the minimum reflection loss is −50.9 dB at 14.03 GHz with a 2.5 mm thick sample layer. Microwave absorbing mechanism of the Fe₃O₄–CNTs–HPCFs composites is concluded as dielectric polarization and the synergetic interactions exist between Fe₃O₄ and CNTs–HPCFs.     

Microstructure and mechanical properties of laser beam welded Al–Li alloy 2060 with Al–Mg filler wire

Alloy 2060-T8 is a newly developed high-strength Al–Li alloy for applications in aircraft industry. Crack-free welds were obtained in laser beam welding with 5087 filler wire under optimized welding conditions. In this paper, fusion zone microstructure and joint mechanical properties were investigated. Microstructure typical for the weld metal consists of α-Al matrix with a few nanoscale precipitates inside and a coarse icosahedral quasicrystalline T₂ phase at the dendritic and grain boundaries. The quasicrystalline occurred normally in Al–Li–Cu alloys with higher Li contents. Our investigations show that the icosahedral quasicrystalline phase T₂ phase forms in the laser-welded Al–Li alloy 2060 with lower Li content as a result of segregation and replacement of Mg element. The joint tensile strength in as-welded condition is around 317 MPa, about 63% of that of the base metal, and fracture occurs within the fusion zone.