High performance asymmetric supercapacitor based on 3D microsphere-like 1T-MoS2 with high 1T phase content

1T phase molybdenum disulfide (1T-MoS₂) has aroused extensive concern in energy storage devices such as supercapacitors due to its large interlayer spacing, high conductivity and good hydrophilicity. However, it is struggle to synthesize 1T-MoS₂ with stable 1T phase with high content. Herein, Ammonium ion intercalation molybdenum disulfide (A-MoS₂) with high 1T content and stable 3D microsphere structure was successfully synthesized using a facile hydrothermal method. We explained the feasibility of ammonium ion (NH₄⁺) intercalation through density functional theory (DFT) calculations and proved the successful intercalation of NH₄⁺ by XRD and XPS. Through XPS fitting, the 1T phase content is calculated as high as 83.1%. The as-prepared A-MoS₂ presents a stable 3D microsphere structure with the interlayer spacing expanded to 0.93 nm, which provides a wide ion diffusion channel that allows ions to pass through quickly. Moreover, the high 1T content increases the hydrophilicity of MoS₂, thereby improving the wettability of the electrode, which contributes to the interaction between the electrolyte and electrode. In 1 M Na₂SO₄, A-MoS₂ electrode material displays high specific capacitance of 228 F g^?1 at 5 mV s^?1 and retains 127 F g^?1 at 80 mV s^?1, which proves the good rate capability. Furthermore, the assembled α-MnO₂//A-MoS₂ asymmetric supercapacitor (ASC) displayed a wide operating voltage of 2.1 V. The assembled ASC displays a high energy density of 35.8 Wh?kg^?1 at a power density of 525.0 W kg^?1, which indicates excellent energy storage performance.     

Stress-deformable state of isotropic double curved shell with internal cracks and a circular hole

This work is devoted to the stress–strain state of isotropic double curved shell with defect system. The construction is weakened by two non-through thickness (internal) cracks of different length and by a circular hole located between cracks. In this study we use the line-spring model. Within the framework of this model cracks are modeled as mathematical cuts of shell’s middle surface. This leads to a two-dimensional problem. The problem is reduced to a system of eight boundary integral equations. To ensure the uniqueness of solution an additional equation is added. In the numerical solution of the problem special quadrature formulas for singular integrals of Cauchy type and the finite difference method are applied. The influence of defects on each other for double curved shell has been investigated. The given theoretical results can be used for the calculation of structural elements with holes, cracks on the strength and fracture toughness in various branches of engineering.     

胜利油田污水储罐腐蚀防护方法评价

对胜利油田纯粱采油厂A3钢制生产污水（水温约60℃）储罐使用寿命过低的原因进行了实验考察。水质分析数据表明氯离子浓度高（45-48gm）是污水腐蚀性强的主要因素。A3钢在60℃污水中的腐蚀速率，由极化曲线数据计算的值大大高于失重法测定值，敞开系统中失重法测定值又高于密闭系统中测定值，挂片上出现蚀孔，说明储罐中A3钢发生了氧存在下氟离子引起的局部腐蚀（孔蚀）。元素分析结果表明．储罐阴极保护所用的牺牲阳极铝材含铁等元素量超标。牺牲阳极密封不良，在实验污水中7天后电流效率仅为2．92％，失去阴极保护能力。处于实验污水环境中的有涂层保护的A3钢．14天后出现腐蚀极化电流，表明涂层已失去完整性。要提高该采油厂及胜利油田其他采油厂污水储罐的使用寿命，必须改用合格的牺牲阳极和保护涂层材料。图3表2参7。     

机械力化学研究进展

本文介绍了机械力化学的概念、机械力化学效应、影响因素、反应机理、应用及研究机械力化学的设备、表征技术,对机械力化学应用的一些优缺点等做了评述,并对其发展进行了展望。     

纸塑复合用丙烯酸酯乳液胶粘剂的制备

采用半连续法制备了一种纸塑复合用丙烯酸酯乳液胶粘剂,讨论了乳化剂的用量、松香乳液的用量、交联剂的用量等因素对胶粘剂性能的影响。结果表明,当乳化剂的用量为4.5%、松香乳液用量为10%,胶粘剂的性能较好;另外,加入一定量的交联剂,可显著提高该胶粘剂的耐水性。     

氧化锌对高胶凝性水泥熟料矿物形成及强度的影响

采用工业原料配料，对以硅酸三钙（C3S，C=CaO，S=SiO2）、硫铝酸钙（C4A3 S^-，C=CaO，A=Al2O3，S^-=SO4^2-）为主导矿物的含C4A3 S^-矿物硅酸盐水泥熟料的矿物形成及其强度进行了研究。借助X射线衍射和热重一差热分析研究了矿物形成过程；探讨了微量元素ZnO对熟料性能的影响及在熟料体系中的固溶情况。研究结果表明：生料中掺入ZnO可使C4A3 S^-和CaS等矿物通过低温反应形成，共存于同一熟料体系中，并可提高熟料的强度；过高的ZnO含量亦会降低C4A3 S^-矿物的分解温度。     

氧化铁对硫铝酸钙矿物形成的影响

借助化学分析方法、X射线衍射、差示扫描量热法等测试手段研究了Fe2O3对无水硫铝酸钙矿物(C4A3S)形成过程的影响.研究表明:掺杂Fe2O3可促进熟料中游离氧化钙(f-CaO)的吸收,增加液相量,改善C4A3-S矿物生料的易烧性;不掺杂Fe2O3的矿物生料,C4A3-S单矿物在850℃以下几乎不生成,在1 000℃开始大量生成,在1 300℃达到最高值;掺杂1?2O3的试样中C4A3S含量与不掺杂试样在同温度下达到最大值,但绝对含量有一定幅度的下降;掺杂3%及5?2O3的试样中C4A3S含量在1 350℃达到最大值,达到最大值的时间比原来延迟0.5h,并且绝对含量有较大幅度的下降;掺杂Fe2O3的试样在1 200℃至1400℃时,Fe3 和C4A3-S中的Al3 发生置换,使Fe3 固熔到C4A3-S中形成固熔体C4(A0.95F0.05)6O12(SO4).     

氧化锌对阿利特和硫铝酸钙的形成及共存温度范围的影响

借助差热分析、X射线衍射及化学分析等,研究了ZrO对含硫铝酸钙的硅酸盐水泥熟料中阿利特和硫铝酸钙矿物形成及共存温度范围的影响.结果表明:在生料中掺入1%(质量分数)ZnO,可降低阿利特的形成温度,并促进低温下硫铝酸钙矿物的形成;1 300℃时阿利特生成的质量分数达59.23%,较未掺ZnO样品提高14.76%;掺入ZnO后,扩大了硫铝酸钙与阿利特矿物的共存温度范围,达50℃.     

金属皂类热稳定剂对RPVC流变性能的影响

采用Brabender转矩流变仪，分析并探讨了硬酯酸钡（BaSt2）、硬酯酸铅（PbSt2）、硬酯酸钙（CaSt2）、硬酯酸锌（ZnSt2）4种硬酯酸金属皂类热稳定剂以及复配BaSt2／PbSt2热稳定剂对硬质聚氯乙烯（RPVC）流变性能的影响。结果表明，BaSt2，CaSt2能够促进RPVC的塑化，而PbSt2和ZnSt2却推迟RPVC的塑化；在复配BaSt2／PbSt2稳定剂体系中，随着BaSt2比例的增大，塑化时间缩短，但BaSt2与PbSt2按分子数1：1比率时，RPVC熔体粘度增幅较大。