Preparation of CaO granules using the granulation method

ABSTRACT

Improving the hydration resistance of CaO particle in manufacturing and application of free CaO-containing materials has practical significance. In this study, CaO granules was made from Ca(OH)₂ particles, which were fabricated by the granulation method. The results showed that the hydration resistance of the CaO granules which was prepared under 1700?r?min^?1 was the best, the CaO granules was sintered well in calcination process, the shell of CaO granules was relatively dense, which improves the hydration resistance of CaO granules, and the rate of hydration weight increment was 0.58% after placed in the air for 20 days under a temperature of 10–14°C and a relative humidity of 57–81%.     

载体比表面积及孔径对Nb_2O_5/α-Al_2O_3催化剂酸性及反应性能的影响

采用浸渍法制备了Nb2O5/α-A l2O3催化剂(简称催化剂)并用于环氧乙烷水合制乙二醇的反应,通过控制α-A l2O3载体中致孔剂的含量来调变载体的孔径、孔分布及比表面积;采用吡啶吸附红外光谱、氨程序升温脱附法研究了载体的比表面积及孔径对催化剂酸性及反应性能的影响。实验结果表明,产物的选择性受扩散因素及催化剂酸性的影响,而催化剂的酸量、酸密度可以通过载体的孔径及比表面积的变化加以调控。比表面积较小及孔径较大的载体对催化剂催化环氧乙烷水合制乙二醇的反应较为有利。当载体的比表面积小于0.80m2/g、孔径为4.00~8.00μm时,在反应温度160℃、反应压力1.5M Pa、n(H2O)∶n(EO)=22、液态空速25h-1的条件下,环氧乙烷的转化率大于99.8%,乙二醇的选择性超过89.9%。     

溶剂对环氧乙烷催化水合制乙二醇的影响

研究了NY催化剂催化环氧乙烷水合制乙二醇(EG)过程中,溶剂、催化剂添加量和水与环氧乙烷的摩尔比(简称水比)对EG选择性的影响。实验结果表明,以丙三醇作为溶剂使催化剂进行循环,能提高EG的选择性,效果好于以生成的EG作为溶剂循环催化剂。催化剂添加量、水比和溶剂添加量对EG选择性具有较大影响,其中溶剂添加量对EG选择性的影响最显著。在低水比(1.0~4.0)条件下,EG质量分数小于30%、催化剂质量分数大于7.2%时,EG选择性稳定在95.63%~97.92%,平均值为96.80%,此结果对于进一步降低EG合成工艺的能耗具有指导意义。     

丙烯醛制备1,3-丙二醇的中型试验研究

对丙烯醛水合、加氢制1，3-丙二醇工艺进行了中试研究，主要对小试技术的可靠性进行验证。结果表明，丙烯醛经水合、加氢制1，3-丙二醇的工艺技术可行，反应器、精馏塔等设备设计合理。中试丙烯醛水合单程转化率为45％～55％，3-羟基丙醛选择性达到了93％左右，3-羟基丙醛加氢收率接近100％，产品1，3-丙二醇的醛基质量分数降至5μg／g以下。与小试结果相比较，中试的水合选择性明显提高，加氢催化剂活性寿命延长。     

连续梁的简便计算

利用三转角方程，对连续梁的内力进行精确的计算，该方法简捷明了，便于应用。     

夏季施工中砼质量存在问题与对策

分析了夏季砼施工中存在的突出问题 ,并论述了质量保证措施。     

工业建筑多层框架的活荷载不利布置

以设防烈度为8度的框架厂房为例，详细分析了活荷载不利布置对框架梁、柱内力的影响，得出何时需要考虑活荷载不利布置、何时不需要考虑活荷载不利布置的结论，可供工程设计参考。     

Use of radial forces for fault detection in tapping

A model-based method for fault detection in tapping based on torque and radial forces is proposed. The method allows the identification of faults typical of a tapping operation including axial misalignment, tap runout, tooth breakage both singly and together. The validation experiments have been run on aluminum 356 workpieces for different combinations of process faults. Results have shown that the model predictions are in good agreement with the experimental radial force and torque signals under various fault conditions.     

Evidence of High Vertical Wave-Number Behavior in a Continuously Stratified Reservoir: Boadella, Spain

High vertical wave-number modes clearly dominate the internal wave field during the stratification period in Boadella reservoir in northeast Spain. In this period, the extraction of hypolimnetic water, due to summer irrigation, brought the surface level down by 6 m in one month and the epilimnetic water progressively occupied the whole water column. The temperature profile, with the exception of a few meters at the surface layer, presented an almost constant temperature gradient of about 0.7°C/m. The period of the main vertical mode is 24 h with an amplitude of around 1 m. Thermistor chain records and meteorological data allow us to deduce that this mode is, at least, a third vertical mode forced by the wind, which normally has a typical periodicity of 24 h. However, when the wind changes direction from south to north, the circulation cells developed due to this forced nonstationary oscillation are destroyed. When this occurs, the Bulk Richardson number is Rib ～ 1. Similar vertical structures as a response to wind forcing should be expected in similar systems, although this has not been reported in the literature.