Inhibition of Spore Germination of Phakopsora Pachyrhizi Using Crude Extracts of Amaranthus Spinosus

The effectiveness of methanolic and n-hexane crude extracts of Amaranthus spinosus to inhibit the spore germination of Phakopsora pachyrhizi, a causal agent of soybean rust disease was studied. Both methanolic and n-hexane crude extracts inhibited spore germination at concentrations of 0.1% to 5.0%. Methanolic extract of the roots at a concentration of 2.5% inhibited 55% of spore germination, and this result was similar when higher concentration at 5% of methanolic and n-hexane extracts of the flowers was used. The presence of alkaloids, flavonoids, tannins, saponins, and terpenoids in the extract may be responsible for the inhibition. The extract was potential to be utilized as a botanical fungicide.     

荷载对钢-混凝土连接锈蚀栓钉力学性能影响研究

为了研究荷载对钢-混凝土连接栓钉锈蚀程度对其力学特性的影响,对不同锈蚀程度的栓钉连接件的进行荷载试验。根据钢筋的锈蚀原理,利用人工方法加速钢-混凝土的栓钉锈蚀,为荷载试验提供达到相应的锈蚀程度样品,并通过荷载试验分别对四组样品进行极限承载力和变形特性展开研究。由试验结果可知:若栓钉连接件的钉杆发生锈蚀,尤其当锈蚀出现在靠近结合面处,该栓钉连接件的承载力以及变形特性均会受到影响;而且栓钉的锈蚀程度越大,其承载力则越低;当栓钉锈蚀质量损失率达到20.8%时,其极限承载力降低了17%;栓钉连接件大头端部锈蚀质量损失率约20%时,极限承载力下降仅为3%。研究结果为钢-混凝土的试验设计、施工使用等提供参考。     

除油剂除锈剂发黑剂的进展

从逐渐不采用强酸碱的角度回顾了除油、除锈、发黑及电镀等技术近年的进展情况,介绍和评价了这类技术涉及的一些市售商品,提出了进一步推广应用这些材料必须解决的问题。     

海洋工程用钢的大气腐蚀与耐候钢的发展

综述了海洋工程用钢的大气腐蚀行为与耐候钢发展方面的研究,特别是近十余年来国内外的相关成果。首先介绍了钢大气腐蚀的电化学模型,并从耐候钢特殊的锈层结构与合金元素作用两方面论述了耐候钢的锈层保护机制;然后分析了环境因素,包括相对湿度与污染物、光照、锈层损伤等,对耐候钢大气腐蚀行为的影响;最后总结了耐候钢的发展历程以及晶粒尺寸与显微组织等非合金因素在耐候钢发展中的作用,可为新型耐候钢的设计与应用提供指导。     

改性环氧带锈涂料的研究

研究了以改性环氧树脂和聚乙烯醇缩丁醛为基料的钢铁带锈涂料 ,通过对成膜物质、转化剂、渗透剂、颜料等的研究 ,得到了集稳定、转化、渗透为一体的多功能涂料。经过实验测试 ,该涂料的各项性能指标均达到了设计要求 ,并且本工艺方案简单易行、省时高效 ,具有较高的实用价值。     

Hydrogen entry into steel during atmospheric corrosion process

Hydrogen entry and permeation into iron were measured by an electrochemical method during atmospheric corrosion reaction. The hydrogen permeation was enhanced on passive films because the hydrogen adsorption increased by the hydrogen evolution mechanism which is different from that on a bear iron surface. The permeation rate during a wet and dry corrosion cycle showed a maximum in the drying process depending upon the surface pH and the corrosion potential. The pollutant such as Na₂SO₃ which decreases the pH and the corrosion potential causes an increase in the permeation rate. The mechanism of the change in the permeation rate during the wet and dry cycles is explained by the polarization diagram of the electrode covered by thin water layer.     

热镀锌钢白锈产生原因分析及预防

通过扫描电镜观察及X射线衍射测试,对热镀锌钢在海洋环境下产生的白锈进行了分析,结果表明,在海洋环境下白锈由ZnCl2.4Zn(OH)2、2ZnCO3.3Zn(OH)2和ZnO组成,腐蚀产物疏松,不能阻碍腐蚀进一步进行。探讨了白锈形成机理,总结了国内外热镀锌标准有关对热镀锌钢白锈的论述,并提出了有关的防护及处理措施。     

Influence of chromium on the local structure and morphology of ferric oxyhydroxides

The extended X-ray absorption fine structure (EXAFS) method and transmission electron microscopy (TEM) have been used for characterizing the local structure and morphology of ferric oxyhydroxides, α-FeOOH and γ-FeOOH, with and without chromium. These ferric oxyhydroxide powders were prepared from aqueous solutions containing iron and chromium ions. Radial structural functions for iron obtained by Fe K edge EXAFS spectra showed that the linkage of structural units formed by FeO₆ octahedra in γ-FeOOH is distorted by chromium addition, while such distortion in α-FeOOH is not clearly detected. On the other hand, Cr K edge EXAFS spectra showed that the local structure around chromium does not necessarily correspond to the local structure around of iron, which is observed by Fe K edge EXAFS spectra. This suggests that the structural units containing iron and chromium are heterogeneously distributed in these ferric oxyhydroxides. The local structural information was discussed coupled with morphological features of these ferric oxyhydroxides observed by TEM.     

高耐蚀性热镀锌板的钝化处理工艺探讨

介绍了热镀锌板钝化膜的形成机理 ;针对攀钢热镀锌板出现白锈、黑斑等问题 ,分析了钝化液pH值、添加剂及操作条件对钝化膜质量的影响 ,同时提出了改进热镀锌板耐蚀性能的措施     

防锈铝板表面腐蚀原因分析

采用光学金相、扫描电镜、能量色用谱，俄歇电子能谱和X光电子能谱等多种方法分析了防锈铝板表面发生大面积腐蚀的原因，分析结果说明缝隙腐蚀是导致防锈铝板表面发生失效的主要原因。