Low cycle fatigue behavior of a eutectic 80Au/20Sn solder alloy

The eutectic 80Au/20Sn solder alloy is widely used in high power electronics and optoelectronics packaging. In this study, low cycle fatigue behavior of a eutectic 80Au/20Sn solder alloy is reported. The 80Au/20Sn solder shows a quasi-static fracture characteristic at high strain rates, and then gradually transforms from a transgranular fracture (dominated by fatigue damage) to intergranular fracture (dominated by creep damage) at low strain rates with increasing temperature. Coffin-Manson and Morrow models are proposed to evaluate the low cycle fatigue behavior of the 80Au/20Sn solder. Besides, the 80Au/20Sn solder has enhanced fatigue resistance compared to the 63Sn/37Pb solder.     

WDM传输系统中泵浦配置对光纤拉曼放大器增益特性的影响

通过理论分析和模拟运算,研究了光纤拉曼放大器泵浦优化的一般规律。     

Interfacial reactions in In-Sn/Ni couples and phase equilibria of the In-Sn-Ni system

The In-Sn-Ni alloys of various compositions were prepared and annealed at 160°C and 240°C. No ternary compounds were found; however, most of the binary compounds had extensive ternary solubility. There was a continuous solid solution between the Ni₃Sn phase and Ni₃In phase. The Sn-In/Ni couples, made of Sn-In alloys with various compositions, were reacted at 160°C and 240°C and formed only one compound for all the Sn-In alloys/Ni couples reacted up to 8 h. At 240°C, Ni₂₈In₇₂ phase formed in the couples made with pure indium, In-10at.%Sn and In-11at.%Sn alloys, while Ni₃Sn₄ phase formed in the couples made of alloys with compositions varied from pure Sn to In-12at.%Sn. At 160°C, except in the In/Ni couple, Ni₃Sn₄ formed by interfacial reaction.     

Low-cycle fatigue properties of eutectic solders at high temperatures

This paper details the deformation mechanism and low‐cycle fatigue life of eutectic solder alloys at high temperature (around 0.8T_m). Grain boundary sliding generally nucleates a wedge‐type cavity that reduces the low‐cycle fatigue life of metals. In this study, grain boundary sliding has promoted intergranular failure contributing to the reduction in fatigue life of Sn–Ag–Cu alloy. However, grain boundary sliding has exerted no deleterious effects on fatigue resistance of eutectic Pb–Sn and Bi–Sn alloys. The phase boundary sliding with very fine microstructure induces exceptional ductility in these alloys leading to superior low‐cycle fatigue endurance for theses eutectic Pb–Sn and Bi–Sn alloys.     

Effect of strain waveform on creep-fatigue life for Sn–8Zn–3Bi solder

This paper describes the creep‐fatigue life of Sn–8Zn–3Bi under push–pull loading. Creep‐fatigue tests were carried out using Sn–8Zn–3Bi specimens in fast–fast, fast–slow, slow–fast, slow–slow and hold–time strain waveforms. Creep‐fatigue lives in the slow–slow and hold‐time waveforms showed a small reduction from the fast–fast lives but those in the slow–fast and fast–slow waveforms showed a significant reduction from the fast–fast lives. Conventional creep‐fatigue life prediction methods were applied to the experimental data and the applicability of the methods was discussed. Creep‐fatigue characteristics of Sn–8Zn–3Bi were compared with those of Sn–3.5Ag and Sn–37Pb.     

印制板液态感光阻焊油墨的工艺控制

本文介绍印制板液态感光阻焊油墨的工艺流程、工艺控制，并对生产中较常出现的几种质量问题进行讨论，进而提出解决措施。     

Effect of Cu concentration on the reactions between Sn-Ag-Cu solders and Ni

The reaction between the Sn-Ag-Cu solders and Ni at 250°C for 10 min and 25 h was studied. Nine different Sn-Ag-Cu solders, with the Ag concentration fixed at 3.9 wt.% and Cu concentrations varied between 0.0–3.0 wt.%, were used. When the reaction time was 10 min, the reactions strongly depended on the Cu concentration. At low-Cu concentrations (≦0.2 wt.%), only a continuous (Ni_1−xCu_x)₃Sn₄ layer formed at the interface. When the Cu concentration increased to 0.4 wt.%, a continuous (Ni_1−xCu_x)₃Sn₄ layer and a small amount of discontinuous (Cu_1−yNi_y)₆Sn₅ particles formed at the interface. When the Cu concentration increased to 0.5 wt.%, the amount of (Cu_1−yNi_y)₆Sn₅ increased and (Cu_1−yNi₆)₆Sn₅ became a continuous layer. Beneath this (Cu_1−yNi_y)₆Sn₅ layer was a very thin but continuous layer of (Ni_1−xCu_x)₃Sn₄. At higher Cu concentrations (0.6–3.0 wt.%), (Ni_1−xCu_x)₃Sn₄ disappeared, and only (Cu_1−yNi_y)₆Sn₅ was present. The reactions at 25 h also depended strongly on the Cu concentration, proving that the strong concentration dependence was not a transient phenomenon limited to a short reaction time. The findings of this study were rationalized using the Cu-Ni-Sn isotherm. This study shows that precise control over the Cu concentration in solders is needed to produce consistent results.     

织构对铟凸点剪切强度的影响

制作了2种形式的铟凸点：即直接蒸发沉积的铟柱和将铟柱回流得到的铟球。同时对比了铟柱和铟球2种凸点的剪切强度，测试结果表明铟球剪切强度为5.6MPa，铟柱的剪切强度为1.9MPa，前者约为后者的2.9倍。对铟凸点微观结构的X光衍射分析发现：铟柱剪切强度低是织构弱化所致；铟球剪切强度高是由于回流破坏了铟柱的理想（101）丝织构模式，从而提高了铟球的剪切强度。     

Structural integrity in electronics

With continuing miniaturisation, increased performance demands and the requirement to remove lead from solder alloys, the challenges to structural integrity and reliability of electronic equipment are substantial and increasing. This paper outlines typical features in electronic equipment of which the structural integrity community may be generally unaware. Potential failure modes in service are described, and the problems of scale and material characteristics are considered. Progress in the application of fracture mechanics to the life prediction of interconnections is reviewed. The limited evidence available suggests that the crack growth resistance of silver‐containing lead‐free solders is superior to that of the traditional Sn‐37Pb under cycle‐controlled conditions but there is no difference when time‐dependent conditions prevail. In several respects, it is contended that the electronics sector is faced with challenges at least equivalent to those encountered in gas turbines and nuclear power generation.     

臭氧在食品加工用水处理工程上的应用

本文叙述了臭氧的一些特性 ,并以烟台某食品加工公司食品加工用水处理工程为例 ,介绍了臭氧的产生及应用情况 ,提供了处理前后水中各项指标的对照