Synthesis and characterization of biocompatible hydroxyapatite coated ferrite

Ferrite particles coated with biocompatible phases can be used for hyperthermia treatment of cancer. We have synthesized substituted calcium hexaferrite, which is not stable on its own but is stabilized with small substitution of La. Hexaferrite of chemical composition (CaO)_0.75(La₂0₃)_0.20(Fe₂O₃)₆ was prepared using citrate gel method. Hydroxyapatite was prepared by precipitating it from aqueous solution of Ca(NO₃)₂ and (NH₄)₂HPO₄ maintaining pH above 11. Four different methods were used for coating of hydroxyapatite on ferrite particles. SEM with EDX and X-ray diffraction analysis shows clear evidence of coating of hydroxyapatite on ferrite particles. These coated ferrite particles exhibited coercive field up to 2 kOe, which could be made useful for hysteresis heating in hyperthermia. Studies by culturing BHK-21 cells and WBC over the samples show evidence of biocompatibility. SEM micrographs and cell counts give clear indication of cell growth on the surface of the sample. Finally coated ferrite particle was implanted in Kasaulli mouse to test its biocompatibility. The magnetic properties and biocompatibility studies show that these hydroxyapatite coated ferrites could be useful for hyperthermia.     

TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.     

Al-10Mg型固溶合金自然时效稳定性研究

测定了ZL30 5合金自然时效 33年的力学性能变化 ,观察了晶界的析出相 ,研究了组织和性能的关系 ,从而确定了ZL30 5合金具有长期自然时效稳定性。     

化学复合镀层激光处理研究

研究了激光处理对Ni-P -SiC化学复合镀层的影响。借助于扫描电镜、能谱仪、X射线衍射、显微硬度计等设备对激光处理后复合镀层的表面形貌、组织结构及性能进行了综合分析。结果表明 ,对复合镀层进行激光处理可以获得与炉内加热同样的镀层硬度 ,且当激光功率 4 0 0W ,扫描速度 1.5m /min时 ,镀层硬度高于炉内加热的硬度     

T8钢－聚有机硅氧烷仿生减粘降阻复合涂层的特性

研究了Ｔ８钢－聚有机硅氧烷仿生减粘降阻复合涂层的表面润湿性、磨料磨损特性及对土壤的减粘降阻性能与金属材料相比，仿生复合涂层的表面憎水性显著提高，水在其表面上的接触角达９２°；与４５钢相比，其磨料磨损的体积相对耐磨系数为６３％，降阻率达１５．２２％～２２．２７％     

Improving Wear Resistance of the Ni-base Thermal Spray-Welding Coating Using Rare Earths

ＩｍｐｒｏｖｉｎｇＷｅａｒＲｅｓｉｓｔａｎｃｅｏｆｔｈｅＮｉｂａｓｅＴｈｅｒｍａｌＳｐｒａｙＷｅｌｄｉｎｇＣｏａｔｉｎｇＵｓｉｎｇＲａｒｅＥａｒｔｈｓＺｈａｉＧｕａｎｇｊｉｅ（翟光杰）（ＩｎｓｔｉｔｕｔｅｏｆＰｈｙｓｉｃｓ，ＡｃａｄｅｍｉｃａＳｉ...     

埋地管道涂层检测技术现状

文章对各种埋地管道涂层检测技术进行了综述,并指出了各种技术的优缺点及应用前景.     

Mechanical behavior of 30–50 nm thick aluminum films under uniaxial tension

We present uniaxial tensile test results for 30–50 nm thick freestanding aluminum films. Young’s modulus and ductility were found to decrease monotonically with grain size. Reverse Hall–Petch behavior was observed with no appreciable room temperature creep. Non-linear elasticity with small irreversible deformation was observed for 50 nm thick specimens.     

硼酸铝晶须增强环氧树脂和双马来酰亚胺树脂体系的研究

本文以硼酸铝晶须为增强剂，以4，5-环氧环己烷-1，2-二甲酸二缩水甘油酯(TDE-85)，甲基纳狄克酸酐(MNA)、N，N’-二胺基二苯甲烷型双马来酰亚胺(BMI)/O，O′-二烯丙基双酚A(BA)体系分别作为基体制备晶须增强复合材料。研究了晶须对树脂的尺寸、表面处理方法、含量对树脂体系力学性能和热性能的影响；通过扫描电子显微镜(SEM)分析了浇注体的弯曲、冲击断口，研究晶须的增强机理。     

Influence of inhibitor addition on the corrosion protection performance of sol–gel coatings on AA2024

Sol–gel films are actively investigated during the last decade as possible candidates for environmentally friendly pre-treatments. However, the important drawback in this case is the lack of active corrosion protection and self-healing ability.