Performance of BaZrO3/Y2O3 dual-phase refractory applied to TiAl alloy melting

Vacuum induction melting is a potential process for the preparation of TiAl alloys with good homogeneity and low cost. But the crucial problem is a selection of high stability refractory. In this study, a BaZrO₃/Y₂O₃ dual-phase refractory was prepared and its performance for melting TiAl alloys was studied and compared with that of a Y₂O₃ refractory. The results showed the dual-phase refractory consisted of BaZr_1-xY_xO_3-δ and Y₂O₃(ZrO₂), exhibited a thinner interaction layer (30 μm) than the Y₂O₃ refractory (90 μm) after melting the TiAl alloy. Although the TiAl alloys melted in the dual-phase and Y₂O₃ refractory exhibited similar oxygen contamination (<0.1 wt%), the alloy melted in the dual-phase refractory had smaller Y₂O₃ inclusion content and size than that in the Y₂O₃ refractory, indicating that the dual-phase refractory exhibited a better melting performance than the Y₂O₃ refractory. This study provides insights into the process of designing highly stable refractory for melting TiAl alloys.     

Revisit the Pitot static tubes in the standards

A Pitot tube is a popular device used for the measurements of flow fields. To control the accuracy of the Pitot tube coefficient, the international standard organization (ISO), the American Society for Testing and Materials (ASTM), and the Japanese Industrial Standards (JIS) issued guidelines that recommended the shape and working conditions of these devices. However, many Pitot tubes on the market do not follow these guidelines. In the present study, various types of Pitot tubes in the market were tested at the National Metrology Institute of Japan (NMIJ) to determine the effects of the geometry and flow characteristics. The results revealed certain limitations in the existing ISO and JIS standards, specifically with regard to the recommended design parameters of the AMCA Pitot tube, the reference coefficient value for the JIS Pitot tube, and the redefinition and limitation of Reynolds numbers pertaining to Pitot tube working conditions.     

Preparation of Pt/Ce–Zr–Y mixed oxide/anodized aluminium oxide catalysts for hydrogen passive autocatalytic recombination

The use of a Pt-based catalyst was evaluated for autocatalytic hydrogen recombination. The Pt was supported on a mixture of Ce-, Zr- and Y-oxides (CZY) to yield nanosized Pt particles. The Pt/CZY/AAO catalyst was then prepared by the spray-deposition of the Pt/CZY intermediate onto an anodized aluminium oxide (AAO) layer on a metallic aluminum core. The Pt/CZY/AAO catalyst (3 × 1 cm) was evaluated for hydrogen combustion (1–8 vol% hydrogen in the air) in a recombiner section testing station. The thermal distribution throughout the catalyst surface was investigated using an infrared camera. The maximum temperature gradient (ΔT) for the examined hydrogen concentrations did not exceed 36 °C. The Pt/CZY/AAO catalyst was also evaluated for prolonged hydrogen combustion duration to assess its durability. An average combustion temperature of 239.0 ± 10.0 °C was maintained for 53 days of catalytic hydrogen combustion, suggesting that there was limited, or no, catalyst deactivation. Finally, a Pt/CZY/AAO catalytic plate (14.0 × 4.5 cm) was prepared to investigate the thermal distribution. An average surface temperature of 212.5 °C and a maximum ΔT of 5.4 °C was obtained throughout the catalyst surface at a 3 vol% hydrogen concentration.     

干熄焦锅炉炉管失效机理分析

通过对干熄焦锅炉炉管及腐蚀产物开展系统研究，提出炉管失效原因为氧化/硫腐蚀＋高温粉尘冲刷。长寿命炉管仅耐磨层发生了较为严重的氧化及硫腐蚀，而近基体层发生了轻微氧化及硫腐蚀，基体只发生了轻微氧化；短寿命炉管耐磨层、近基体层以及基体裂纹内均发生了较为严重的氧化及硫腐蚀，且存在珠光体球化、内表面产生全脱碳层等缺陷。推测短寿命炉管存在超温现象，而超温可加剧氧化及硫腐蚀反应。此外，短寿命炉管遭受了较为严重的高温粉尘冲刷，不仅可造成炉管减薄，还会导致炉管表面温度升高。因此，减少循环气体中粉尘量尤其是大颗粒，可有效减弱冲刷以及控制炉管表面温度，是提高炉管使用寿命的关键。     

变形铝合金表面锆基化学转化膜的研究现状

化学转化膜是金属表面主要的处理方法之一，具备良好的附着力和耐蚀性，能为铝合金提供一定的临时防护。传统的六价铬酸盐化学转化膜在日渐严苛的环保压力下已经逐渐淘汰，取而代之的是近几年发展迅猛的三价铬及无铬锆基化学转化膜。铝合金可分为铸造铝合金和变形铝合金，按照所含主要合金元素和热处理状态可分为若干个系列和型号。本文选取几种典型的变形铝合金，综述了不同铝合金微观组织对转化膜成膜过程的影响，化学转化液添加剂、预处理和后处理工艺对转化膜性能的调控及作用机理，以及几种典型商业钝化剂在变形铝合金表面的应用。总结了目前变形铝合金表面锆基化学转化膜仍面临的问题和发展趋势，未来化学转化膜需在满足新型铝合金发展要求的基础上，通过不同有机、无机添加剂以及外场作用对转化膜的成膜均一性、完整性进行调控，以提高转化膜的综合性能。     

基于神经网络和遗传算法的锭子弹性管性能优化

为得到减振弹性管对下锭胆的支承弹性和锭子高速运动下的稳定性等性能的最优匹配效率,依据减振弹性管的等效抗弯刚度及底部等效刚度系数公式,利用MatLab数值分析软件构建弹性管抗弯刚度和底部挠度数学模型。首先,结合Isight优化软件基于径向基神经网络构建其近似模型,且使精度达到可接受水平,并以模型的关键结构参数弹性模量、螺距、槽宽、壁厚为设计变量,结合遗传算法对弹性管抗弯刚度和底部挠度进行多目标优化设计,得到Pareto最优解集和Pareto前沿图,确定出减振弹性管结构工艺参数的优化方案。通过对优化数据进行分析发现,该方案在保证减振弹性管弹性的同时,其底部振幅明显减弱。     

Experimental study on the heat transfer and flow characteristics of nanorefrigerants inside a corrugated tube

The heat transfer and flow characteristics of MWCNT-R141b nanorefrigerant with different mass fractions have been studied through experiments. Experimental results were compared with existing correlations. A two-step method was used to prepare the nanorefrigerants. Span-80 was used as surfactant with an average particle diameter of 20 nm. Transmittance method was used to evaluate the stability of nanorefrigerants. Results showed that the stability of MWCNT-R141b nanorefrigerant, which is the added dispersant, was good during the experiments. The 0.3 wt% MWCNT-R141b nanorefrigerants had optimal heat transfer enhancement effects compared with pure refrigerants. The maximum Nusselt number increased by 40%. The specific pressure drop of nanorefrigerant increased as the Reynolds number (Re) increased, and the specific pressure drop of the pure refrigerant was minimum, which is similar to R141b.     

东兴铝业嘉峪关分公司铝灰渣循环利用研究

铝灰渣是铝熔铸过程中产生的废弃物。本文主要介绍了酒钢东兴铝业嘉峪关分公司铝灰渣的产生量、排放、利用情况、化学成分及表面特征,并简要介绍了铝灰渣、铝灰的循环利用途径。     

Φ177mm PQF无缝管连轧机前横移系统改进

对鞍钢股份无缝钢管厂连轧机前毛管坯横移装置存在的设计缺陷进行了分析,并提出改进方案,将原横移装置由高架轨道横移机构及上下升降链传动装置,改进为地面轨道横移系统及同步旋转臂实现取管、放管过程。实施后消除了生产故障,缩短了轧制周期,降低生产成本。