Synthesis and characterization of biocompatible hydroxyapatite coated ferrite

Ferrite particles coated with biocompatible phases can be used for hyperthermia treatment of cancer. We have synthesized substituted calcium hexaferrite, which is not stable on its own but is stabilized with small substitution of La. Hexaferrite of chemical composition (CaO)_0.75(La₂0₃)_0.20(Fe₂O₃)₆ was prepared using citrate gel method. Hydroxyapatite was prepared by precipitating it from aqueous solution of Ca(NO₃)₂ and (NH₄)₂HPO₄ maintaining pH above 11. Four different methods were used for coating of hydroxyapatite on ferrite particles. SEM with EDX and X-ray diffraction analysis shows clear evidence of coating of hydroxyapatite on ferrite particles. These coated ferrite particles exhibited coercive field up to 2 kOe, which could be made useful for hysteresis heating in hyperthermia. Studies by culturing BHK-21 cells and WBC over the samples show evidence of biocompatibility. SEM micrographs and cell counts give clear indication of cell growth on the surface of the sample. Finally coated ferrite particle was implanted in Kasaulli mouse to test its biocompatibility. The magnetic properties and biocompatibility studies show that these hydroxyapatite coated ferrites could be useful for hyperthermia.     

Fenton试剂降低采油污水CODCr的研究与应用

针对辽河油区超稠油采油污水的特点，采用Fenton试剂催化氧化，对采油污水处理进行研究。实验研究及现场应用结果表明，此方法对污水的CODCr具有良好的去除效果。处理后污水经过简单生化，进一步降解污染物，能够实现稳定迭标排放，且具有能耗低、运行成本低和操作简单等特点。     

Effect of select parameters on the properties of edible film from water-soluble fish proteins in surimi wash-water

Edible film from water-soluble fish proteins were developed by casting film solution on leveled trays and effects of pH (9.5, 10.0 and 10.5), heating temperature (60, 70 and 80 °C), and heating time (10, 20 and 30 min) of the film solution on various film properties were determined using Response Surface Methodology (RSM). The impact of pH and heating temperature of film solution was more significant, overall, on the film's properties than heating time. Contour plots of tensile strength and elongation at break was highest at pH of 10.0 at 70 °C (2.75-3.02 MPa) but low in elongation at break (6.35-9.16%), while water vapor permeability and oxygen permeability were at their lowest (58.55-65.96 g mm/m² d kPa and 351.33-624.18 cm³ μm/m² d kPa). There was a direct correlation between the films’ and proteins’ solubility on one hand, and heating temperature of film solution on the other, which reversed with change in pH of film solution. Film color was darker and more yellowish with increase in the pH of film solution.     

高导电性原油电脱盐工艺研究

南阳原油中金属含量较高,掺有部分3次采油采出原油,加工时易造成电脱盐装置原油乳化,电导率高,脱盐难度较大。装置投产十几年来脱后含盐一直不合格,经过改造仍然超标,常压塔顶腐蚀严重。为此,对原油进行了电脱盐工艺条件及破乳剂研究,研制出了高效电脱盐设备和生物复合脱盐剂及降电流剂,采用平流弓形电极进行改造,解决了该原油的电脱盐问题,使脱后含盐达到3 mg/L。     

Influence of Polyalkylmethacrylate VII on Boundary Film Formation,Friction,Wear and Efficiency of Lubricants

1 Influence of PAMAon Boundary Fil mFormation and Friction1.1 Experi mental methodsUltra-thin optical interferometry has been used tostudy thinlubricating fil ms for more than a decade and theexperi mental details of this technique have been reportedpreviously[1].The principle of the test setup is shown inFigure1.A polished steel ball is loaded and rolled againstthe flat surface of a glass disc that is coated with a thinsemi-reflecting chromiumlayer and a silica spacer of about500nmthickne…     

TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.     

Nonstationary Simulation Model of Absorber with Falling Film of Suspension

A nonstationary model of SO₂ absorption from a gas phase to a countercurrent falling film of absorbing slurry was developed. Laminar, wavy and turbulent film structures were considered based on published information. Resistances to the mass transfer on the gas and the liquid sides of the interphase were considered, together with chemical reactions in the liquid phase. Relevant chemical equilibria in the liquid phase were modeled. Original experimental data on the neutralization reagent dissolution rate presented as a polydispersed two‐phase system of solids and on the rate of dissolved sulfite oxidation were used. The model was verified with experimental data from a laboratory‐scale falling‐film absorber using a single vertical tube under various geometrical and operating conditions, and a very good agreement was found with the experiment. Parametric sensitivity analysis showed the critical parts of the model.     

化学复合镀层激光处理研究

研究了激光处理对Ni-P -SiC化学复合镀层的影响。借助于扫描电镜、能谱仪、X射线衍射、显微硬度计等设备对激光处理后复合镀层的表面形貌、组织结构及性能进行了综合分析。结果表明 ,对复合镀层进行激光处理可以获得与炉内加热同样的镀层硬度 ,且当激光功率 4 0 0W ,扫描速度 1.5m /min时 ,镀层硬度高于炉内加热的硬度     

Gamma-irradiation-induced Ag/SiO2 composite films and their optical absorption properties

Small Ag particles or clusters dispersed mesoporous SiO₂ composite films were prepared by a new method: First the matrix SiO₂ films were prepared by sol-gel process combined with the dip-coating technique, then they were soaked in AgNO₃ solutions followed by irradiation of γ-ray at room temperature and in ambient pressure. The structures of these films were examined by X-ray diffraction (XRD), high-resolution transmission electron microscope (HRTEM), and optical absorption spectroscopy. It has been shown that the Ag particles grown within the porous SiO₂ films are very small, and they are isolated and dispersed from each other with very narrow size distributions. With increasing the soaking concentration and an additional annealing, an opposite peakshift effect of the surface plasmon resonance (SPR) was observed in the optical absorption measurements.     

双转向垂向控缝技术实验研究及现场应用

针对压裂过程中缝高较难控制的问题，研制开发出新型的油溶性垂向双转向剂，并开展了室内实验研究。首次验证了转向剂对裂缝延伸的控制机理，确定了转向剂的适用浓度及控缝能力。实验表明，转向剂可以增加隔层应力3～4MPa左右。在此基础上研究了控制裂缝高度施工方案的设计方法，并利用全三维软件结合垂向应力剖面对控缝技术进行了优化。现场推广应用30井次，取得了较好的控缝效果。