二氧化碳气体保护焊在厚板上的应用

板厚为 5 5mm的 16Mn钢采用CO2 半自动气保焊建造大型转炉炉体的可能性和可靠性如何 ?目前尚缺少足够的试验数据。为了给转炉工程的施工焊接提供可靠数据 ,确保焊接质量 ,对板厚 5 5mm16Mn钢CO2 半自动的焊接性能进行了一系列的试验研究     

TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.     

一种微透镜阵列的研制

介绍一种利用表面张力的作用、以光纤作材料、用分离的自聚焦透镜制作微透镜阵型的方法，这种方法具有制作工艺简单、无须昂贵设备等优点，用此方法实际制作了具有良好连续面型的微透镜阵列，并对制作的微透镜阵列进行了测试，效果较好。     

低密度微泡沫压井液的研究与应用

吐哈油田部分区块地层压力系数小于0.9,常规水基压井液对储层伤害大,若使用油基压井液成本高,环境污染严重。通过实验优选出了一种低密度水基微泡沫压井液。该压井液具有密度低、泡沫强度高、稳定性好、携砂能力强等优点。现场应用表明,低密度微泡沫压井液稳定时间大于48 h,密度在0.70~0.99 g/cm3之间可调,抗油污染能力强,抗油大于8%,抗温在100℃以上,岩心污染后渗透率恢复值大于80%;并且施工方便,成本低,具有储层保护能力,使用微泡沫压井液的井表皮系数在0.20~2.34之间。     

NSA-500-1型氩弧焊机VD9不同接法对引弧和稳弧的影响

从一起NSA－500－1型氩弧焊机故障，分析其高压脉冲旁路二极管VD9不同接法对引弧、稳弧及设备安全的影响。     

A novel way to treat refractory waste: Sonication followed by wet oxidation (SONIWO)

The effectiveness of the hybrid system sonication followed by wet oxidation (SONIWO) to treat otherwise refractory waste has been demonstrated. In such a hybrid system homogeneous CuSO₄ catalyst was found to be very efficient.     

Nitric oxide reduction and carbon monoxide oxidation over carbon-supported copper-chromium catalysts

Carbon supported copper-chromium catalysts are shown to be very active for both the reduction of nitric oxide with carbon monoxide and the oxidation of carbon monoxide with oxygen. Mixed copper-chromium oxide active phases have good activity in the simultaneous removal of nitric oxide and carbon monoxide from exhaust gases. The influence of several catalyst variables has been investigated. The activity per volume of catalyst increases with increasing loading, while the intrinsic activity shows a maximum around C/M=100−50. An optimum catalyst for nitric oxide reduction and carbon monoxide oxidation has a copper/chromium ratio of 2/1. The apparent activation energy for the carbon monoxide oxidation over carbon supported copper-chromium catalysts is 77 kJ/mol, suggesting that the Cu---O bond rupture is the rate-limiting process. The reduction of nitric oxide takes place at higher temperatures. Since all catalysts have a low selectivity for molecular nitrogen formation at lower temperatures, the dissociation of nitric oxide is probably rate determining, resulting in a slightly reduced catalyst system. In an excess of carbon monoxide the reaction is first-order in nitric oxide and zero-order in carbon monoxide. Moisture inhibits the reaction by reversible competitive adsorption, whereas carbon dioxide does not. Oxygen completely inhibits the reduction of nitric oxide due to the more rapid reoxidation of the catalytic sites compared to nitric oxide. Therefore, the reduction of nitric oxide takes place only when all oxygen has been converted and, hence, is shifted to higher temperatures. As a possible consequence, the production of nitrous oxide is reduced. Nitric oxide and molecular oxygen react preferentially with carbon monoxide, so, in an excess of oxidizing component, gasification of the carbon support occurs at higher temperatures after carbon monoxide has been completely consumed.     

Dietary α-Tocopheryl Acetate Enhances Beef Quality in Holstein and Beef Breed Steers

The effect of long-term feeding (252 days) of three supplemental levels of α-tocopheryl acetate (actual 0, 360 and 1290 IU/head/day) on meat quality was evaluated in Holstein and beef breed steers. Tissue vitamin E concentrations were increased by each increment of supplementation. The color display life of fresh beef under simulated retail conditions was extended 2 to 5 days by vitamin E and lipid oxidation was markedly reduced. Microbial population was not affected by level of supplementation. No deterioration in sensory quality occurred for steaks from supplemented steers that were displayed until the time steaks from unsupplemented steers discolored.     

异丙苯在Cu-HMS分子筛上的催化氧化

以含Cu的中孔分子筛(Cu-HMS)为催化剂,研究异丙苯的催化氧化。研究发现,Cu-HMS催化剂的加入使异丙苯氧化的诱导期显著缩短。在75℃下,以Cu-HMS为催化剂,O2为氧化剂的纯异丙苯氧化反应,苯乙酮为主要副产物,反应的选择性和转化率都很高。当催化剂用量为1 5×10-4mol/ml时,反应8h后,异丙苯转化率为32 7%,目的产物的累积浓度(质量分数)为37 7%,选择性为99%;反应12h后,异丙苯转化率为42 4%,目的产物的累积浓度为46 3%,选择性为95 6%。     

Preparation, Characterisation and Catalytic Behaviour of a New TeVMoO Crystalline Phase

TeM_xMo_1.7O mixed oxides (M = V and/or Nb; x = 0-1.7) have been prepared by calcination of the corresponding salts at 600 °C in an atmosphere of N₂. A new crystalline phase, with a Te/V/Mo atomic ratio of 1/0.2-1.5/1.7, has been isolated and characterised by XRD and IR spectroscopy. This phase is observed in the TeVMo or TeVNbMo mixed oxide but not in the TeNbMo mixed oxide. The new crystalline phase shows an XRD pattern similar to Sb₄Mo₁₀O₃₁ and probably corresponds to the M1 phase recently proposed by Aouine et al. (Chem. Commun. 1180, 2001) to be present in the active and selective MoVTeNbO catalysts. Although these catalysts present a very low activity in the propane oxidation, they are active and selective in the oxidation of propene to acrolein and/or acrylic acid. However, the product distribution depends on the catalyst composition. Acrolein or acrylic acid can be selectively obtained from propene on Nb-free or Nb-containing TeVMo catalysts, respectively. The presence of both V and Nb, in addition to Mo and Te, appears to be important in the formation of acrylic acid from propene.