Phase constitution,microstructure and mechanical properties of a Ni-based superalloy specially designed for additive manufacturing

In this study, a kind of Ni-based superalloy specially designed for additive manufacturing (AM) was investigated. Thermo-Calc simulation and differential scanning calorimetry (DSC) analysis were used to determine phases and their transformation temperature. Experimental specimens were prepared by laser metal deposition (LMD) and traditional casting method. Microstructure, phase constitution and mechanical properties of the alloy were characterized by scanning electron microscopy (SEM), transmission scanning electron microscopy (TEM), X-ray diffraction (XRD) and tensile tests. The results show that this alloy contains two basic phases, γ/γ', in addition to these phases, at least two secondary phases may be present, such as MC carbides and Laves phases. Furthermore, the as-deposited alloy has finer dendrite, its mean primary dendrite arm space (PDAS) is about 30-45 μm, and the average size of γ' particles is 100-150 nm. However, the dendrite size of the as-cast alloy is much larger and its PDAS is 300-500 μm with secondary and even third dendrite arms. Correspondingly, the alloy displays different tensile behavior with different processing methods, and the as-deposited specimen shows better ultimate tensile stress (1,085.7±51.7 MPa), yield stress (697±19.5 MPa) and elongation (25.8%±2.2%) than that of the as-cast specimen. The differences in mechanical properties of the alloy are due to the different morphology and size of dendrites, γ', and Laves phase, and the segregation of elements, etc. Such important information would be helpful for alloy application as well as new alloy development.     

基于蜻蜓翅脉结构的连续碳纤维增强树脂基复合材料仿生设计与增材制造

以具有轻质高强优异性能的蜻蜓翅脉结构为设计灵感，在分析翅脉网格结构抗冲击原理的基础上，设计了传统和仿生两类对比结构。采用熔融挤出3D打印机成功制备了具有不同结构的连续碳纤维增强聚乳酸复合材料试样，并对不同结构复合材料试样的拉伸性能和抗冲击性能进行了测试和对比分析。研究分析结果表明：由于拉伸力方向上的连续碳纤维含量相对较少，限制了仿生结构复合材料抗拉强度的提高，但仿生结构的平均抗拉强度为传统结构的1.18倍；当仿生结构复合材料试样受到冲击力时，其内部六边形结构的连接角度会发生变化，从而极大消耗冲击能量，同时具有六边形网格结构的连续碳纤维可以有效阻碍裂纹的扩展，因此仿生结构的平均冲击韧性可以达到传统结构的2.46倍；仿生蜻蜓翅脉结构可以显著提高增材制造复合材料的综合力学性能，且对于抗冲击性能的提高具体突出效果。连续碳纤维增强树脂基复合材料的有效可行的仿生蜻蜓翅脉结构设计和增材制造，可极大扩展其在高冲击载荷领域中的相应应用。     

增材制造技术在超高膨胀封隔器中的应用

石油和天然气行业不断关注增材制造技术在航空航天和汽车行业的应用发展。研发了利用增材制造技术的超高膨胀封隔器,该封隔器的支承环系统由增材制造。增材制造设计大幅减少了支承系统的构件数量,同时显著提高了膨胀能力和额定压力。密封元件系统与增材制造支承环安装在一起,提供了极端膨胀比、零挤压间隙和对不规则孔的良好适应性。分析和测试结果表明:直径膨胀比高达111%,与常规封隔器相比,提高50%以上; 至少涵盖5种线重的套管(外径相同); 在148.89 ℃的温度下,密封元件能够保持压力68.95 MPa。介绍了增材制造技术、增材制造支承环概念、增材制造材料力学性能、密封元件系统优化和测试情况,以期给我国的完井作业提供借鉴。     

Copper–4,4′-dipyridyl coordination compound as solid reagent for spectrophotometric determination of reducing sugar employing a multicommutation approach

In this work a multicommuted flow system employing copper–4,4′- dipyridyl coordination compound as the solid-phase reagent for the spectrophotometric determination of reducing sugar was developed. The coordination compound was synthesized through a reaction of the 4,4′-dipyridyl and copper (II) nitrate, under hydrothermal conditions. The complex was characterized by infrared spectroscopy (FTIR), power X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) and thermogravimetric analysis (TGA). Based on the characterization, a multicommuted spectrophotometric procedure for the determination of reducing sugar using copper (II) complex as solid reagent is proposed. The proposed method was based on the redox reaction between a monosaccharide, such as fructose and glucose (reducing sugar) and Cu(II). This reaction, mediated in an alkaline medium, produces a yellow compound that can be determined by absorption electronic spectroscopy (λ_ABS = 420 nm). Under optimum experimental conditions, a linear response ranging from 1.0 to 20.0 g L⁻¹ (R = 0.9978 and n = 5), a detection (3σ criterion) and quantification (10σ criterion) limit estimated at 0.23 and 0.75 g L⁻¹, respectively, a standard deviation relative of 4.7% (n = 7), for a reference solution of 10.0 g L⁻¹ reducing sugar, and a sampling rate of 75 determinations per hour were achieved. The proposed system was applied to the determination of reducing sugars in coconut water and juices. The analysis of ten samples and the application of the t-test to the results found, and those obtained using reference procedures (AOAC), provided no significant differences at a 95% confidence level. This system enabled the analysis of reducing sugar with ease and simplicity, providing a significant economy of the solid reagent (600 μg per determination) and reducing effluent generation.     

Performance improvement of conventional and inverted polymer solar cells with hydrophobic fluoropolymer as nonvolatile processing additive

The morphology of the photoactive layer critically affects the performance of the bulk heterojunction polymer solar cells (PSCs). To control the morphology, we introduced a hydrophobic fluoropolymer polyvinylidene fluoride (PVDF) as nonvolatile additive into the P3HT:PCBM active layer. The effect of PVDF on the surface and the bulk morphology were investigated by atomic force microscope and transmission electron microscopy, respectively. Through the repulsive interactions between the hydrophilic PCBM and the hydrophobic PVDF, much more uniform phase separation with good P3HT crystallinity is formed within the active layer, resulting enhanced light harvesting and improved photovoltaic performance in conventional devices. The PCE of the conventional device can improve from 2.40% to 3.07% with PVDF additive. The PVDF distribution within the active layer was investigated by secondary ion mass spectroscopy, confirming a bottom distribution of PVDF. Therefore, inverted device structure was designed, and the PCE can improve from 2.81% to 3.45% with PVDF additive. Our findings suggest that PVDF is a promising nonvolatile processing additive for high performance polymer solar cells.     

Fenton氧化法去除酱油生产废水中焦糖色素的研究

着重考察了Fenton试剂对水中焦糖色素降解的影响因素.从试验中得出,这些影响因素包括pH、催化剂的投加方式、催化剂与氧化剂的化学计量数以及反应时间等.Fenton反应中,pH4的条件下处理效果最好,反应进行40min时去除率达到90%.     

添加剂对工业齿轮油性能影响的研究

研究了硫化烯烃、磷酸酯胺盐、硫磷酸酯极压抗磨剂,含氮杂环衍生物多功能添加剂和防锈剂等,对工业齿轮油抗乳化性能、极压抗磨性能、防锈性能的影响;以及硫化烯烃、磷酸酯盐极压抗磨剂与含氮杂环衍生物多功能添加剂之间的协和效应。试验结果表明:1.2%~1.6%复合添加剂调制的CKD220工业齿轮油中,磷酸脂盐的正确选用可以提高齿轮油的抗乳化性能、防锈性能和减少防锈剂用量。硫化烯烃与磷酸脂盐、含氮杂环衍生物多功能添加剂的合理组合,可以提高齿轮油的极压抗磨性能和防锈性能,减少添加剂总加剂量。     

高温酸化助排剂HC2-1的研究

为了满足高温油藏和深井酸化作业残酸返排的需要，通过表面活性剂的筛选和复配研究，得到了高温酸化助排剂HC2—1。其性能评价结果表明，HC2—1具有使用浓度低、表面活性高的特点，在20％的HCI溶液中，当其浓度为50mg／L时，表面张力为20．7mN／m；具有良好的耐温性能，在180℃下恒温48h，HC2—1仍保持较高的表面活性；具有良好的耐盐能力，加有HC2—1的20％HCl溶液和CaCO3反应至HCl完全消耗，整个反应过程体系无新相生成且表面张力基本不变；可增大酸液体系的润湿角，进一步降低毛细管阻力，使酸液返排率由46％提高到97％，在促进酸液返排的同时与原油不发生乳化反应。     

BEM 系列原油流动性改进剂的应用

对BEM系列原油流动性改进剂的基本原理以及在中洛、濮临、东临、东黄、鲁宁、魏荆等几条原油长输管道工业应用的现场测试情况进行了介绍。结果表明，BEM系列原油流动性改进剂在降低原油凝点和粘度方面性能良好，能满足管道安全，平稳运行的要求。