Extraction and characterization of hydroxyapatite-based materials from grey triggerfish skin and black scabbardfish bones

The conversion of food industry by-products to compounds with high added value is nowadays a significant topic, for social, environmental, and economic reasons. In this paper, calcium phosphate-based materials were obtained from black scabbardfish (Aphanopus carbo) bones and grey triggerfish (Balistes capriscus) skin, which are two of the most abundant fish by-products of Madeira Island. Different calcination temperatures between 400 and 1000°C were employed. Materials obtained from calcination of bones of black scabbard fish were composed by homogeneous mixtures of hydroxyapatite (Ca₁₀(PO4)₆(OH)₂, HAp) and β-tricalcium phosphate (β-Ca₃(PO₄)₂, β-TCP). Because of the high biocompatibility of HAp and the good resorbability of β-TCP, these natural biphasic materials could be very relevant in the field of biomaterials, as bone grafts. The ratio between HAp and β-TCP in the biphasic compound was dependent on the calcination temperature. Differently, the material obtained from skin of grey triggerfish contained HAp as the main phase, together with small amounts of other mineral phases, such as halite and rhenanite, which are known to enhance osteogenesis when used as bone substitutes. In both cases, the increase of calcination temperature led to an increase in the particles size with a consequent decrease in their specific surface area. These results demonstrate that from the fish by-products of the most consumed fishes in Madeira Island it is possible to obtain bioceramic materials with tunable composition and particle morphology, which could be promising materials for the biomedical field.     

NSA-500-1型氩弧焊机VD9不同接法对引弧和稳弧的影响

从一起NSA－500－1型氩弧焊机故障，分析其高压脉冲旁路二极管VD9不同接法对引弧、稳弧及设备安全的影响。     

φ1m氨合成塔20钢异径管失效分析

分析了氨合成塔底部副线20钢异径管爆破的原因。结果表明：异径管长期处于200℃以上工作，管内H2与管材中的碳或Fe3发生化学反应，生成CH4致使管内脱碳并产生裂纹，异径管强度降低脆性增加，导致爆破。     

DXDK800自动充填包装机料袋长度的调整

本文主要介绍了在DXDK800自动充填包装机中 ,采用一种新型的齿轮—蜗轮、蜗杆差速器来对膜片的进给速度进行微量的调整。及采用一种新型的可调式偏心链轮来调整横封辊的瞬时线速度 ,使其与料袋膜的进给速度相一致     

上海市用电负荷管理系统主站异地冗灾备份方案研究

对上海市用电负荷管理系统主站灾备系统的建设进行可行性研究,根据系统现有结构,结合主流技术提出建议性的方案.重点对各种设备技术进行分析,包括涉及计算机、网络、软件等各方面的设备技术,提出建设原则及实施建议.     

东安石灰石矿爆破降震新技术

本文介绍了湘钢东安石灰石矿和长沙矿冶研究院合作进行降震技术试验研究的结果．异步分区起爆综合降震技术既可显著降震，由于振动频率提高，降低了周围民房的地震效应，减轻了房屋的摆动程度．     

Vibrations of stretched damped beams under non-ideal boundary conditions

A simply supported damped Euler-Bernoulli beam with immovable end conditions are considered. The concept of non-ideal boundary conditions is applied to the beam problem. In accordance, the boundaries are assumed to allow small deflections and moments. Approximate analytical solution of the problem is found using the method of multiple scales, a perturbation technique.     

Phase Composition of Oxide Scales during Reheating in Hot Rolling of Low Carbon Steel

Low carbon steel was oxidized over the temperature range 1000‐1250°C in O₂‐CO₂‐H₂O‐N₂, O₂‐H₂O‐N₂, and O₂‐CO₂‐N₂ gas mixtures. Oxidation times were 12‐120 min. and the scales were 50‐2000 μm thick. The variations of these parameters were chosen to elucidate the phase composition of oxide scales under conditions similar to those of reheating furnaces in hot strip mills, using either thin slab casting or conventional casting and rolling technology. Two types of scales have been observed which are influenced by the furnace atmosphere, oxidation time, and temperature. The first type is a crystalline scale with an irregular outer surface, composed mostly of wustite (FeO), and a negligible amount of magnetite (Fe₃O₄). The second type is the classical three‐layer scale, composed of wustite (FeO), magnetite (Fe₃O₄), and hematite (Fe₂O₃). In general, the experiments showed that an increase in oxidation time decreased the percentage of wustite while the percentages of magnetite and hematite increased. A rise in oxygen concentration in the gas mixture increased the percentages of magnetite and hematite, confirming earlier experimental findings. In water vapour‐free atmospheres O₂‐CO₂‐N₂, the oxide scales had a low percentage of wustite, and high percentage of magnetite and hematite. Carbon dioxide showed a small influence at 1100°C, and a negligible one at 1250°C.     

热分析在PVA纤维预处理中的应用

用差热、热重法对原丝的热性能及由不同预处理方法所引起的PVA纤维的热行为变化进行了研究;并通过模拟脱水条件,用不同升温速率,求出了经不同预处理纤维的脱水反应活化能。结果表明,PVA原丝在230℃有一软化点,三种预处理都不同程度地影响了原丝的热效应变化;纤维在180～340℃主要为脱水反应;原丝及经脱水剂、O_3和O_3综合脱水剂处理的纤维,其脱水反应的表观活化能分别为:164.3kJ/mol,92.9kJ/mol,130.5kJ/mol和117.6kJ/mol。     

对我厂防治加热管内碳酸钙垢的思索

分析了我厂两碱法原卤净化后,加热管内壁结碳酸钙垢的原因,探讨了我厂采取加盐酸、加阻垢剂、用超声波阻垢器的方法,以及对加热管内碳酸钙垢防治的情况和存在的问题.