异种铁素体耐热钢接头界面组织及其影响

综述了铁素体与铁素体异种金属焊缝（dissimilar metal welds，DMWs）接头界面组织及其影响。结果表明，在焊后热处理或运行温度下的铁素体钢DMWs接头的不均匀界面组织中，通常会形成脱碳层和增碳层。在铁素体钢DMWs焊接接头界面组织影响因素中，焊缝金属的化学成分有重要影响；焊后热处理规范（温度和时间）、工作温度下运行时间的影响较为突出；焊接工艺参数的影响亦不可忽略。异种钢接头界面处近缝区裂纹的产生，以及接头的蠕变强度随Larson Miller 参数增大而下降等不利影响，均为异种钢界面碳迁移行为所导致。焊缝成分控制法是接头界面组织控制或改善的必要条件，而脱碳层部位转移法能有效防止裂纹发生，亦是接头安全运行的重要工艺措施之一。     

Deformation-Strength Relationships in Short-Term Tension of Heat-Resistant Materials

The analysis of 124 curves obtained in short-term tensile tests demonstrate that they can be described by varying strain hardening and softening characteristics. Different stress–strain curves can be produced at invariable yield strength and ultimate strength and interrelated proportional variations of the above characteristics. To determine some specific stress–strain curve, it is necessary to take account of yield strength and ultimate strength as well as strain corresponding to the latter. The relations between yield strength, ultimate strength and hardening and their practically complete absence between these parameters and softening were statistically established.     

Wear and Creep Characteristics of a Carbon‐Derived Si3N4/SiC Micro/Nanocomposite

In the presented work some properties of a recently developed Si₃N₄/SiC micro/nanocomposite have been investigated. The material was tested using a pin on disc configuration. Under unlubricated sliding conditions using Si₃N₄ pin at 50 % humidity, the friction coefficient was in the range of 0,6 ‐ 0,7. The reduction of humidity resulted in a lower coefficient of friction, in vacuum the coefficient of friction had a value of about 0,6. The wear resistance in vacuum was significantly lower then that in air. The wear patterns on the Si₃N₄+SiC disc revealed that mechanical fracture was the wear controlling mechanism. Creep tests were realized in four point bending configuration in the temperature interval 1200‐1400 °C at stresses 50,100 and 150 MPa and the minimal creep deformation rate was established for each stress level. The activation energy, established from the minimal creep deformation had a value of about 360 kJ/mol and the stress exponent values were in the range of 0.8‐1.28. From the achieved stress exponents it can be assumed that under the studied load/temperature conditions the diffusion creep was the most probable creep controlling mechanism.     

A new monitoring system for piping systems in fossil fired power plants

A CEC-funded project has been performed to tackle the problem of producing an advanced Life Monitoring System (LMS) which would calculate the creep and fatigue damage experienced by high temperature pipework components. Four areas were identified where existing Life Monitoring System technology could be improved:

1. 1. the inclusion of creep relaxation

2. 2. the inclusion of external loads on components

3. 3. a more accurate method of calculating thermal stresses due to temperature transients

4. 4. the inclusion of high cycle fatigue terms.

The creep relaxation problem was solved using stress reduction factors in an analytical in-elastic stress calculation. The stress reduction factors were produced for a number of common geometries and materials by means of non-linear finite element analysis. External loads were catered for by producing influence coefficients from in-elastic analysis of the particular piping system and using them to calculate bending moments at critical positions on the pipework from load and displacement measurements made at the convenient points at the pipework. The thermal stress problem was solved by producing a completely new solution based on Green's Function and Fast Fourier transforms. This allowed the thermal stress in a complex component to be calculated from simple non-intrusive thermocouple measurements made on the outside of the component. The high-cycle fatigue problem was dealt with precalculating the fatigue damage associated with standard transients and adding this damage to cumulative total when a transient occurred.

The site testing provided good practical experience and showed up problems which would not otherwise have been detected.     

Materials modelling: A bridge from atoms to bulk properties

The use of molecular-level materials modelling techniques in the development of advanced performance polymers is discussed, with particular emphasis upon bridging the large difference in the scales of dimensions between atomic structure and fabricated parts. The advantages and disadvantages of bulk quantitative structure-property relations and atomistic modelling are assessed, and the method of group interaction modelling is suggested as a means of bridging the dimensional scales.After a brief introduction to the concept of group interaction modelling, examples of modelling the engineering properties of polymers are presented which are difficult to model quantitatively by any other means. The important phase transitions from the crystal and glassy states of matter to those of rubber- and liquidlike states are shown quantitatively to be due to the same isoenergetic condition. The viscoelastic properties of a polymer are critical for many applications and expressions are derived for the loss and storage components of the complex modulus, with reference to failure initiation conditions. The effect of crosslinking in thermosets upon the glass transition temperature and viscoelastic properties is outlined. Finally, the scaling of time from atomic vibrations to the years involved in creep and ageing effects are discussed.     

Incoloy 800H合金的应用和性能分析

通过对耐热耐蚀合金Incoloy 80 0H的性能分析 ,指出它与普通奥氏体不锈钢相比具有较优的抗氧化性能、耐蚀性和高温蠕变强度。针对催化裂化装置同轴式沉降再生器内部所用Incoloy 80 0H焊件易出现裂纹的问题进行分析 ,认为在施焊过程中由于合金凝固时有低熔点金属或化合物的液态膜残留在晶界区 ,该合金具有高的焊接热裂纹敏感性 ,若焊材选择不当 ,焊丝填充不充分、缺少保护气等将导致晶间裂纹产生。提出了该合金采用TIG焊接防止热裂纹产生的措施。     

锅炉对流管爆裂原因分析

采用化学分析、金相检验及力学性能测定等方法，对锅炉对流管爆裂原因进行了分析。结果表明，长期超温运行而引起的蠕变是导致爆裂的主要原因。     

Low-cycle fatigue properties of eutectic solders at high temperatures

This paper details the deformation mechanism and low‐cycle fatigue life of eutectic solder alloys at high temperature (around 0.8T_m). Grain boundary sliding generally nucleates a wedge‐type cavity that reduces the low‐cycle fatigue life of metals. In this study, grain boundary sliding has promoted intergranular failure contributing to the reduction in fatigue life of Sn–Ag–Cu alloy. However, grain boundary sliding has exerted no deleterious effects on fatigue resistance of eutectic Pb–Sn and Bi–Sn alloys. The phase boundary sliding with very fine microstructure induces exceptional ductility in these alloys leading to superior low‐cycle fatigue endurance for theses eutectic Pb–Sn and Bi–Sn alloys.     

混凝土多轴应力状态下的徐变研究

在搜集国内外有关资料的基础上,通过对混凝土在多轴应力作用下的徐变与强度关系分析,说明在多轴应力状态下不能简单地采用叠加原理。展示了新的三轴徐变量测仪器及其徐变试验成果以及2组多轴与单轴应力状态下的徐变恢复试验成果,并对试验数据进行比较分析,得到多轴应力状态下徐变恢复与应力大小以及持荷时间之间的规律,证实了多轴应力状态下的徐变恢复与已经产生的压缩徐变有密切的关系。