Resistance reduction effect of potassium bismuth titanate doping in yttrium–manganese co-doped medium Curie temperature barium titanate lead free ceramics through improved synthesis process

Through improved synthesis process, resistance reduction effect of (K_0.5Bi_0.5)TiO₃ (KBT) doping in Y–Mn co-doped BaTiO₃ (BT) lead free ceramics was investigated. By different doping methods (doping K₂O, Bi₂O₃ and TiO₂ or synthesized KBT), medium Curie temperature (around 130 °C) lead free BT ceramics were obtained with ultra-low resistivity (13.84 Ωcm) with a temperature maintaining process at 700 °C. In this contribution, effect of sintering process and doping methods is discussed in detail.     

Understanding silica-supported metal catalysts: Pd/silica as a case study

Supported metal catalysts, particularly noble metals supported on SiO₂, have attracted considerable attention due to the importance of the silica–metal interface in heterogeneous catalysis and in electronic device fabrication. Several important issues, e.g., the stability of the metal–oxide interface at working temperatures and pressures, are not well-understood. In this review, the present status of our understanding of the metal–silica interface is reviewed. Recent results of model studies in our laboratories on Pd/SiO₂/Mo(1 1 2) using LEED, AES and STM are reported. In this work, epitaxial, ultrathin, well-ordered SiO₂ films were grown on a Mo(1 1 2) substrate to circumvent complications that frequently arise from the silica–silicon interface present in silica thin films grown on silicon.     

马钢二烧结配料计算机控制系统

阐明了马钢二烧结配科计算机控制系统的目的、控制形式、控制原理；根据烧结配料控制对象的特点对信号采样和控制算法进行了探讨；提供了系统的主要硬件结构，软件功能和程序框图。     

天然气空气绝热转化制合成气催化剂研究

制备了天然气空气绝热转化催化剂,采用固定床反应器进行稳定性评价试验,对反应前后的催化剂进行了分析表征。结果说明,天然气和空气绝热转化反应放热形成的高温对催化剂有烧结作用,使催化剂晶体结构发生了变化,起活性作用的金属镍和氧化铝载体转化为镍铝尖晶石结构的物质。进一步的试验表明,在1050～1300℃的温度可以把催化剂的晶体结构改变。     

Processing of Yttria-Alumina Coated Silicon Nitride Slips by Slip Casting

Si₃N₄powders coated with 6 wt% Y₂O₃and 4 wt% Al₂O₃were prepared by coprecipitation. The resulting powders were dispersed in water at different pH values and with addition of various amounts of ammonium polyacrylate (NH₄PA) to produce 32 vol% slips. The influence of the amount of NH₄PA solution added and pH on the rheological properties of 32 vol% coated Si₃N₄slips were studied. In addition, the sintered density of cast samples was determined and related to the degree of slip dispersion. The adsorption of the NH₄PA on the coated particle surface was rather high and the surface became saturated near 0.86 mg/m²at pH 9.2. High NH₄PA concentrations (1.7–3 wt%) were necessary to obtain well dispersed 32 vol% coated Si₃N₄slips at pH 9.2. The best stabilization was obtained with the addition of 2.3 wt% NH₄PA; in this condition, the viscosity reached a minimum value of 35 mPa.s at 100 s^–1. The slip viscosity increased with increasing pH from 9.2 to 10.2. Slips with low viscosities gave a more dense packing of cast samples and consequently higher sintered density values.     

气力输送在烧结电除尘输灰系统中的应用

针对烧结厂烧结电除尘灰的工况特性，介绍了输送烧结电除尘灰的正压气力输灰系统的特点、组成，还对在调试和试运行过程中遇到的故障进行了分析并制订了解决措施。     

烧结处理小矿山精矿的应用研究

研究小矿山精矿的性质，分析小矿山精矿对烧结过程的影响，提出了增加小矿山精矿配入量的途径及方法．     

降低烧结返矿率的途径与实践

通过对影响烧结返矿率的因素进行分析，从优化配料、强化制粒和造球、提高料层厚度、实现低碳低水均质烧结等几个方面着手，使烧结返矿率从1998年的23．6％降到了2003年的16．9％。     

Effect of Y2O3, CeO2 on Sintering Properties of Si3N4 Ceramics

The effect of rare earth oxides Y203 or Ce02 on sintering properties of Si3N4 ceramics was studied and the mechanism of assisting action during sintering was analyzed. The results in dicate that the best sintering properties appear in Si3N4 ceramics with 5% Y203 or 8% CeO2. Secondary crystallites are formed at grain boundaries after heat treatment,which decreases the amount of glass phase and contributes to the improvement of high-temperature mechanical properties of silicon nitride.