Cooling strategies for cryogenic machining from a materials viewpoint

This article discusses the cooling strategies for cryogenic machining from a materials viewpoint. It is argued that, because different materials respond to temperature and machining processes differently, different cooling strategies are needed to improve the machinabilities of materials by cryogenic machining. In this work, five workpiece materials such as AISI1010 low-carbon steel, AISI1070 high-carbon steel, AISIE52100 bearing steel, titanium alloy Ti-6Al-4V, and cast aluminum alloy A390 were studied experimentally at various temperatures. Based on the experimental results of the cryogenic properties of the materials and their known machining characteristics, the cooling strategies for cryogenic machining of these materials were analyzed.     

Q-52-51型摩托车车轮轮毂开裂原因分析

检测和分析了Q-52-51型摩托车车轮轮毂从材料成分，力学性能和金相组织。结果表明，轮毂在径向冲击检测时开裂的主要原因是镁含量偏高，以及热处理加热温度高造成组织过热所致。     

溶剂对溶剂热合成CdS纳米晶体的形貌控制

以溶剂热法在不同溶剂里的160℃下反应12 h制备不同形貌的CdS纳米晶粒,分别选用水(H2O)、二甲基甲酰胺(DMF)、乙醇胺(an)和乙二胺(en)为溶剂来控制纳米CdS的形貌和尺寸.对样品的结构和性能进行表征,重点分析了溶剂的物理性质和结构特征对CdS纳米粒子晶体结构、形貌和尺寸的影响,不同溶剂的作用机制不同,可通过选择合适的反应溶剂来控制纳米粒子的形貌和尺寸,以制备满足不同应用需要的纳米结构,尤其是性能独特的一维纳米结构.     

HPC修饰纳米二氧化钛薄膜的微观结构和光学性能

用羟基纤维素(HPC)作为添加剂,用溶胶-凝胶法制备了二氧化钛薄膜.用扫描电镜(SEM)和透射电镜(TEM)观察不同HPC含量的二氧化钛薄膜的微观结构,研究HPC对膜的微观结构的影响机理.用X射线衍射谱(XRD)分析不同薄膜样品的晶格常数.用吸收光谱观察薄膜光吸收端随HPC含量的变化.发现HPC的加入阻碍二氧化钛晶粒生长和减小膜厚两方面导致了二氧化钛晶格畸变,进而引起薄膜光吸收端的蓝移.     

高铬复合铸造轧辊综述

新材质高铬复合铸造轧辊是近三十年来继采用铸造适的高合金无限冷硬轧辊和合企半铜轧辊之后，轧辊制造技术的一大革新．综述了高铬的铁轧辊、高铬铜轧辊国内外制造工艺（化学成分的选择、热处理工艺等）及其应用效果。     

BREAKAGE MECHANISM OF TUNGSTEN BASED ALLOY BLOCK FOR ELECTRO-HEAT UPSETTING

The breakage mechanism of W-Ni-Fe alloy in the process of electro-heat upsetting studied both theoretically and experimetnally, and also the behaviors of crack formation and propagation were analysed. Alloy suffers from corrosion and thermal-mechanical fatigue mutual function. Simultaneously, the practical ways to improve the anvil life was discussed.     

基于计算机仿真分析的拉深工艺参数优化

汽车前照灯矩形反光镜是典型的非轴对称曲面深杯件，本文采用计算机仿真技术分析了其成形过程，并分别对毛坯形状，凹模圆角，压力力等工艺参数进行了优化设计，使成形质量大大提高。     

镁合金表面冷喷涂快凝Zn-Al合金粉末的研究

对镁合金表面冷喷涂快凝Zn-Al合金粉末工艺进行了研究，观察了涂层微观组织，并分析了涂层与基体之间的结合，测定了涂层的硬度和涂层与基体的结合强度。结果表明，采用冷喷涂技术制备的快凝Zn—Al合金粉末涂层组织致密，基体与涂层的结合处只产生塑性变形并且无熔化现象，涂层硬度比基体硬度显著提高。     

U型铸件内应力分析以及消除方法

我公司生产一种吊装用的卡头装置,见图1,需要承载一定的载荷.其材料为铁素体可锻铸铁,外表电镀锌.在对卡头本体做抗拉强度试验时发现,同一规格的卡头在毛坯和电镀锌后的拉力相差1～3 kN.例如最小的一种318型卡头,镀锌前平均拉力9 kN,镀锌后平均拉力7.5 kN.     

3Cr2W8V钢渗硼后热疲劳抗力的研究

３Ｃｒ２Ｗ８Ｖ钢渗硼后热疲劳抗力的研究于长山刘喜明赵宇邬占田（吉林工学院）本文收到日期：１９９７年３月１３日初稿，１９９７年６月１７日修改稿本文联系人：于长山，男，１９３８年３月生，副教授，吉林省长春市（１３００１１）吉林工学院热处理教研室吉林省科技...