Synergistic flame retardant effects of activated carbon and molybdenum oxide in poly(vinyl chloride)

The synergistic effects of activated carbon (AC) and molybdenum oxide (MoO₃) in improving the flame retardancy of poly(vinyl chloride) (PVC) were investigated. The effects of AC, MoO₃ and their mixture with a mass ratio of 1:1 on the flame retardancy and smoke suppression properties of PVC were studied using the limiting oxygen index and cone calorimeter tests. It was found that the flame retardancy of the relatively cheaper AC was slightly weaker than that of MoO₃. In addition, the incorporation of AC and MoO₃ greatly reduced the total heat release and improved smoke suppressant property of PVC composites. When the total content of AC and MoO₃ was 10 phr, PVC/AC/MoO₃ had the lowest peak heat release rate and peak smoke production rate values of 173.80 kW m^?2 and 0.1472 m² s^?1, which represented reductions of 47.3 and 59.9%, respectively, compared with those of PVC. Furthermore, thermogravimetric analysis and gel content tests were used to analyze the flame retardant mechanism of AC and MoO₃, with results showing that AC could promote early crosslinking in PVC. Char residue left after heating at 500 °C was analyzed using scanning electron microscopy and Raman spectroscopy, and the results showed that MoO₃ produced the most compact char, with the smallest and most organized carbonaceous microstructures. © 2017 Society of Chemical Industry     

-15℃下Na+， K+， Mg2+//Cl-， NO3-， SO42——H2O体系相平衡研究

新疆卤水硝酸盐矿主要含有Na⁺、K⁺、Mg²⁺、Cl^-、NO₃^-、SO₄^2-六种离子，属于高元复杂体系，其合理利用和开发需要不同温度下的相平衡研究作为理论支撑。采用等温溶解平衡法，对Na⁺， K⁺， Mg²⁺//Cl^-， NO₃^-， SO₄^2--H₂O体系在-15℃、NaCl·2H₂O饱和条件下的相平衡进行了研究，并构建了相图。相图中有六个零变量点和八个两盐结晶区，只存在一种复盐KCl·MgCl₂·6H₂O。八个两盐结晶区，分别对应于NaCl·2H₂O+Na₂SO₄·10H₂O、NaCl·2H₂O+NaNO₃、NaCl·2H₂O+KCl、NaCl·2H₂O+KNO₃、NaCl·2H₂O+MgSO₄·7H₂O、NaCl·2H₂O+MgCl₂·8H₂O、NaCl·2H₂O+Mg(NO₃)₂·6H₂O和NaCl·2H₂O+KCl·MgCl₂·6H₂O，其中NaCl·2H₂O+Na₂SO₄·10H₂O共晶区最大，在低温时，硫酸钠的溶解度最小，降温过程中较易结晶析出。与该体系在25℃下的相图相比，复盐种类减少5种，零变量点减少19个，相关系得以极大简化。     

15CrMoG钢棒材表面缺陷机理分析和工艺改进

分析得出,棒材表面细小纵裂纹和表面裂口缺陷产生于铸坯加热之前,且与结晶器弯月面保护渣有关。利用Thermo-Calc热力学软件计算15CrMoG钢凝固相变过程,结合亚包晶钢连铸凝固特点综合分析15CrMoG钢棒材表面缺陷的产生原因和产生机理。结果表明:15CrMoG钢在固相线温度附近发生包晶反应L+δ→γ和包晶转变δ→γ,不仅导致初生坯壳生长不均匀,而且加剧P、S元素在凝固前沿的偏析。而初生坯壳不均匀是导致棒材表面缺陷根本原因。棒材表面细小纵裂纹产生于结晶器内坯壳薄弱处,经过二冷和轧制工序在夹杂物和硫偏聚处扩展长大。棒材表面裂口缺陷是初生坯壳不均匀导致结晶器内液面波动大,造成铸坯夹渣所致。通过控制[C]0.16%～0.17%、[S]≤0.005%、保护渣碱度1.2、熔点≥1200℃、粘度≥1.0Pa·s,260 mm×30mm铸坯水量150 m³/h,拉速0.5 m/min等措施,裂纹合格探伤合格率由原45%提高至98%。     

矿用钻孔深度测量仪的设计

设计了一种以STM32F103微控制器为控制核心,基于24位高精度模数转换器的钻孔深度测量仪器。利用弹性波回波测距原理,通过测量出钻孔中钻杆的长度,实现钻孔深度的快速、无损、准确的测量,主要用于井下瓦斯抽放钻孔、探放水钻孔等煤矿通防工作的施工验收。仪器小巧轻便,操作简单,单人即可完成测量工作,节约下井的人力物力,提高生产效率,最长测量长度可达250米,误差不超过1米。     

Recent progress of green sorbents-based technologies for low concentration CO2 capture

The increased concentration of CO₂ due to continuous breathing and no discharge of human beings in the manned closed space, like spacecraft and submarines, can be a threat to health and safety. Effective removal of low concentration CO₂ from the manned closed space is essential to meet the requirements of long-term space or deep-sea exploration, which is an international frontier and trend. Ionic liquids (ILs), as a widespread and green solvent, already showed its excellent performance on CO₂ capture and absorption, indicating its potential application in low concentration CO₂ capture. In this review, we first summarized the current methods and strategies for direct capture from low concentration CO₂ in both the atmosphere and manned closed spaces. Then, the multi-scale simulation methods of CO₂ capture by ionic liquids are described in detail, including screening ionic liquids by COSMO-RS methods, capture mechanism by density functional theory and molecular dynamics simulation, and absorption process by computational fluid dynamics simulation. Lastly, some typical IL-based green technologies for low concentration CO₂ capture, such as functionalized ILs, co-solvent systems with ILs, and supported materials based on ILs, are introduced, and analyzed the subtle possibility in manned closed spaces. Finally, we look forward to the technology and development of low concentration CO₂ capture, which can meet the needs of human survival in closed space and proposed that supported materials with ionic liquids have great advantages and infinite possibilities in the vital area.     

Effect of CuSO4 on the Hydromechanical Behavior of Compacted Tailings

Laboratory tests, including compressibility, permeability, and microstructure tests, were conducted on tailings samples using custom-designed test apparatus to investigate the effect of metal contamination (Cu²⁺) on the hydromechanical behavior of compacted tailings. Infiltrating samples with various dry densities with distilled water or CuSO₄ solution at various concentrations showed that the void ratio of compacted tailings decreased with increased dry density. An increase in the metal contaminant concentrations from 0 to 0.1 mol/L increased the compression coefficient of the tailings from 0.14 to 0.84 MPa^?1 under a vertical load of 0.01 to 2.0 MPa, while the yield stress of the tailings decreased from 204.3 to 98.7 kPa, respectively. The linear relationship between permeability coefficient (k) and void ratio (e) is described by k?=???6.48?+?17.17e. Microstructure test results showed that the diffusion double layer thinned, and the surface potential decreased, indicating that the contaminant of Cu²⁺ enhanced the compressibility and permeability of the tailings. The microstructure test results also showed that the amount of fine-grained soil in the copper tailings was significantly less after the hydromechanical test. Therefore, the permeability and compressibility of copper tailings increased. The experimental results are in good agreement with the estimated results.

     

Microstructures and mechanical properties of B4C-TiB2-SiC composites fabricated by ball milling and hot pressing

B₄C-TiB₂-SiC composites were fabricated via hot pressing using ball milled B₄C, TiB₂, and SiC powder mixtures as the starting materials. The impact of ball milling on the densification behaviors, mechanical properties, and microstructures of the ceramic composites were investigated. The results showed that the refinement of the powder mixtures and the removal of the oxide impurities played an important role in the improvement of densification and properties. Moreover, the formation of the liquid phases during the sintering was deemed beneficial for densification. The typical values of relative density, hardness, bending strength, and fracture toughness of the composites reached 99.20%, 32.84?GPa, 858?MPa and 8.21?MPa?m^1/2, respectively. Crack deflection, crack bridging, crack branching, and microcracking were considered to be the potential toughening mechanisms in the composites. Furthermore, numerous nano-sized intergranular/intragranular phases and twin structures were observed in the B₄C-TiB₂-SiC composite.     

A facile pathway to prepare molybdenum boride powder from molybdenum and boron carbide

Molybdenum boride is an ideal hard and wear-resistant material. In this study, a new method is proposed for preparing molybdenum boride, by which Mo first reacts with B₄C to generate the mixture of molybdenum boride and C, and then the product is decarburized by molten Ca to generate CaC₂. Pure molybdenum boride could be obtained after acid leaching to remove the by-product CaC₂. According to the experimental and thermodynamic calculation results, it is concluded that the single-phase MoB could be successfully prepared, while Mo₂B, Mo₂B₅, and MoB₄ could not be synthesized by this method. Moreover, it was found that the particle size of finally prepared MoB is determined by particle size of raw Mo powder. The residual carbon content of the product could be decreased to 0.10 wt% after first reaction at 1673 K for 6 hours and then decarburization reaction at 1673 K for 6 hours.