Low-temperature synthesis of SiC nanowires with Ni catalyst

SiC nano wires were fabricated on the silicon substrate dipped with a layer of Ni catalyst at 900 ℃ by gas pressure annealing processing. The morphologies and crystal structures were determined by scanning electron microscopy(SEM), transmission electron microscopy(TEM)and X-ray diffraction(XRD). The results show that the assynthesized nanowires are β-SiC single crystalline with diameter range of 50-100 nm, and length of tens of micron by directly annealing at 900 ℃. The SiC nano wires grow along the [111] direction with highly uniform morphology. And the possible growth mechanism of SiC nano wires is proposed.The present work provides an efficient strategy for the production of high-quality SiC nano wires.     

Fabrication and characterizations of Cr3+-doped ZnGa2O4 transparent ceramics with persistent luminescence

0.5 at.% Cr:ZnGa₂O₄ precursor was synthesized by the co-precipitation method with nitrates as raw materials, using ammonium carbonate as the precipitant. Low-agglomerated Cr:ZnGa₂O₄ powders with an average particle size of 43 nm were obtained by calcining the precursor at 900℃ for 4 h. Using the powders as starting materials, 0.5 at.% Cr:ZnGa₂O₄ ceramics with an average grain size of about 515 nm were prepared by presintering at 1150℃ for 5 h in air and HIP post-treatment at 1100℃ for 3 h under 200 MPa Ar. The in-line transmittance of 0.5 at.% Cr:ZnGa₂O₄ ceramics with a thickness of 1.3 mm reaches 59.5% at the wavelength of 700 nm. The Cr:ZnGa₂O₄ ceramics can be effectively excited by visible light and produce persistent luminescence at 700 nm. For Cr:ZnGa₂O₄ transparent ceramics, the brightness of afterglow was larger than 0.32 mcd/m² after 30 min, which is far superior to that of Cr:ZnGa₂O₄ persistent luminescence powders.     

气瓶内部淬火过程的流动换热特性

 大直径厚壁气瓶内部淬火时的流动换热过程极其复杂，受到多种因素的影响，而研究气瓶内部压强和温度的变化规律对改善流动换热效果、提高产品组织性能具有重要的理论指导意义。以914 mm厚壁气瓶和瓶内流体为研究对象，建立了二维等效流 固耦合模型；采用多喷嘴系统对气瓶内外进行喷水淬火，研究了气瓶总长、喷水流速及淬火时间对瓶内压强及内壁温度的影响，通过间歇淬火试验验证了数学模型的正确性。结果发现，气瓶长度对瓶内压强和瓶壁温度的影响显著，喷水流速次之，当喷水流速大于8 m/s后，水量对瓶壁的冷却效果大大降低；气瓶内壁长度方向的温度梯度分别随气瓶总长的增加和淬火时间的延长而减小，但基本不受喷水量的影响。     

Closure of Internal Porosity in Continuous Casting Bloom During Heavy Reduction Process

Metallurgical and Materials Transactions B - To investigate the closure behavior of internal porosity (also referred to as internal void) in continuous casting bloom during heavy reduction (HR) and...     

结合优化支持向量机与K-means++的工控系统入侵检测方法

针对工业控制系统传统单一检测算法模型对不同攻击类型检测率和检测速度不佳的问题，提出一种优化支持向量机和K-means++算法结合的入侵检测模型。首先利用主成分分析法（PCA）对原始数据集进行预处理，消除其相关性；其次在粒子群优化（PSO）算法的基础上加入自适应变异过程避免在训练的过程中陷入局部最优解；然后利用自适应变异粒子群优化（AMPSO）算法优化支持向量机的核函数和惩罚参数；最后利用密度中心法改进K-means算法与优化后的支持向量机组合成入侵检测模型，从而实现工业控制系统的异常检测。实验结果表明，所提方法在检测速度和对各类攻击的检测率上得到明显提升。     

醇盐水解法制备亚微米球形氧化铝粉体

以仲丁醇铝为铝源,以乙腈与正丁醇作溶剂,通过醇盐水解法制备了亚微米球形氧化铝粉体.研究了溶剂配比、水加入量及煅烧温度对产物相结构及微观形貌的影响.结果表明,乙腈与正丁醇的体积比及去离子水的加入量是影响产物的成球性以及粒径大小的关键因素,随着乙腈与正丁醇体积比增大,产物成球性变好;去离子水加入量的变化,影响了产物粒径的大小.经不同温度煅烧后,产物发生了由γ-Al2O3转化为α-Al2O3的相变,但仍保持着球形形貌.     

Improvement of polyamide/thermoplastic polyurethane blends with polyamide 6-polyurethane copolymer prepared via suspension polymerization as compatibilizer

The polyamide 6-polyurethane copolymer (PA6-b-PU-b-PA6) was synthesized through anionic suspension polymerization and then mixed with polyamide 6/thermoplastic polyurethane (PA6/TPU) and polyamide 6, 6/thermoplastic polyurethane (PA66/TPU) blends using as the compatibilizer. The results show that the PA6-b-PU-b-PA6 copolymers powders several can be obtained through suspension polymerization using dimethicone as disperse medium. The average diameter of PA6-b-PU-b-PA6 copolymer powders decreased with the increasing of PU content. With the addition of PA6-b-PU-b-PA6, the TPU phase dispersed more uniformly in PA6 or PA66 matrix, and the size of TPU dispersed phase decreased obviously. The PA6-b-PU-b-PA6 copolymer with higher PU content shows better compatibilizing effect. Addition of PA6-b-PU-b-PA6 can improve both strength and toughness of the PA/TPU blends. When the amount of PA6-PU25% copolymer was 5 phr, the tensile strength and notched impact strength of PA6/TPU/PA6-PU25% blends increased 29 and 159.4%, respectively, compared to the PA6/TPU blend without compatibilizer.