不同矿区天然隐晶质石墨对天然橡胶性能的影响

选用两种不同矿区的天然隐晶质石墨材料,经过超细粉体制备研磨后用于天然橡胶,探究了不同矿区隐晶质石墨在天然橡胶中的溶解度和对性能的影响并研究了粒径和混合工艺对天然橡胶性能的影响规律。研究表明,不同矿区隐晶质石墨因集合体构成不同,在橡胶中的溶解度差异较大；粒径大小是影响橡胶性能的关键参数；混合工艺对橡胶性能的影响更为明显。     

Structural,morphological, dielectric and magnetic properties of Zn-Zr co-doping yttrium iron garnet

In this study, yttrium iron garnet co-doped with Zn and Zr atoms with a chemical formula Y₃Zn_xZr_xFe_(5−2x)O₁₂ (x = 0.0-0.3) has been successfully prepared by the solid-state reaction method. The effects of doping concentration on the microstructure, crystal structure, magnetic properties, and dielectric properties of Y₃Zn_xZr_xFe_(5−2x)O₁₂ were investigated. The microstructure analysis indicates that co-doping of YIG with Zn and Zr can effectively reduce the grain size of the ceramic. The crystal structure results reveal that the doping concentration of Zn–Zr has substantial influence on the lattice parameters of YIG, such as, increases the lattice constant, crystal cell size, and interplanar spacing. However, the second phase of ZrO₂ appears once x ≥ 0.15. Additionally, the dielectric properties of YIG ferrite can be regulated using this Zn–Zr co-doping method. Zn–Zr co-doping can improve the dielectric stability and reduce the dielectric loss at high temperature. The magnetization measurement shows that the saturation magnetization is stabilized at x < 0.15, and the magnetic loss is decreased with the increase in the doping concentration. Overall, the findings show that the ceramic with x = 0.1 exhibits better properties included high saturation magnetization (24.607 emu/g), low magnetic loss (0.0025 @ 1 MHz), and relatively low dielectric loss (496 @ 400°C).     

Discovery of Affinity-Based Probes for Btk Occupancy Assays

Bruton's tyrosine kinase (Btk) is an attractive target for the treatment of a wide array of B-cell malignancies and autoimmune diseases. Small-molecule covalent irreversible Btk inhibitors targeting Cys481 have been developed for the treatment of such diseases. In clinical trials, probe molecules are required in occupancy studies to measure the level of engagement of the protein by these covalent irreversible inhibitors. The result of this pharmacodynamic (PD) activity provides guidance for appropriate dosage selection to optimize inhibition of the drug target and correlation of target inhibition with disease treatment efficacy. This information is crucial for successful evaluation of drug candidates in clinical trials. Based on the pyridine carboxamide scaffold of a novel solvent-accessible pocket (SAP) series of covalent irreversible Btk inhibitors, we successfully developed a potent and selective affinity-based biotinylated probe 12 (2-[(4-{4-[5-(1-{5-[(3aS,4S,6aR)-2-oxo-hexahydro-1H-thieno[3,4-d]imidazol-4-yl]pentanamido}-3,6,9,12-tetraoxapentadecan-15-amido)pentanoyl]piperazine-1-carbonyl}phenyl)amino]-6-[1-(prop-2-enoyl)piperidin-4-yl]pyridine-3-carboxamide). Compound 12 has been used in Btk occupancy assays for preclinical studies to determine the therapeutic efficacy of Btk inhibition in two mouse lupus models driven by TLR7 activation and type I interferon.     

Computational Fluid Dynamics Study on a Top-Blown Smelting Process with Lance Failure in an Isa Furnace

JOM - The Isa/Ausmelt smelting technology with a top submerged lance (TSL) has been extensively used in copper smelting processes. However, the TSL is extremely vulnerable to damage and failure...     

In situ polymerization of flame retardant modification polyamide 6,6 with 2-carboxy ethyl (phenyl) phosphinic acid

A novel halogen-free flame retardant copolyamide 6,6 (FR-PA66) was prepared successfully by in situ polymerizing with adipic acid hexamethylene salt and 2-carboxy ethyl (phenyl) phosphinic acid (CEPPA). The elemental composition and chemical structure of FR-PA66 were characterized by energy dispersive X-ray spectroscopy, Fourier transform infrared spectrometer and ¹³C Nuclear magnetic resonance spectrometer. The flame retardancy, thermal stability, and morphology of char residues were also investigated by the limiting oxygen index (LOI), UL 94 test, thermogravimetric analysis, and scanning electron microscopy. The results showed that FR-PA66 samples had much better flame retardancy and char formation ability than pure PA66 after the flame retardant modification. The LOI values were increased from 24.0 to 28.0% by adding 6 wt % of CEPPA and all FR-PA66 samples were rated as V-0 rating in UL-94 test. Furthermore, the thermal stability analysis indicated that in situ polymerization with CEPPA effectively decreased the initial decomposition temperature and increased the amount of char residue. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 137, 48687.     

Operating Range Scheduled Robust Dahlin Algorithm to Typical Industrial Process with Input Constraint

International Journal of Control, Automation and Systems - There is a class of typical nonlinear industrial process, which can be characterized by a first-order inertia plus pure delay model in an...     

单相硼化物的制备及摩擦磨损性能研究

为了深入研究渗硼层中硼化物的性能，采用真空感应熔炼法制备单相硼化物材料。观察分析制备的硼化物微观组织，测试其力学性能。采用MMU-5G型销-盘式摩擦磨损试验机，在干摩擦条件下，研究了不同载荷下单相硼化物的摩擦学性能，观察其磨损表面形貌特征，探讨其磨损方式。结果表明：制备的硼化物为单一相，试样纯度高，试样的平均显微硬度为HV2065，平均断裂韧性值为1.68 MPa·m1/2；硼化物的断口处没有宏观的塑性变形，断口齐平光亮，表现为脆性断裂特征；干摩擦条件下随着载荷从10 N增加到30 N，硼化物的摩擦因数先降低后增加，20 N载荷时达到最小值，而其磨损量随着载荷的增加不断上升；随着载荷从10 N增加到30 N，磨损表面的粗糙度先逐渐上升后急剧上升； 10~20 N载荷下，硼化物的磨损以磨粒磨损为主，而25~30 N载荷下，硼化物的主要磨损方式从磨粒磨损转变为脆性破损。     

刘家山排土场滑坡治理措施

刘家山排土场为民采排弃形成，已经出现大规模滑坡。为了保证上下游生产生活设施的安全，依据现场实际情况，结合现场调查，提出了削坡处理的方案。经过治理后，刘家山排土场平稳地渡过了雨季，目前处于稳定状态，达到了治理目的。     

Unsteady free convection of second‐grade nanofluid with a new time‐space fractional heat conduction

The Caputo and Caputo–Fabrizio derivative are applied to study a second‐grade nanofluid over a vertical plate. A comparative analysis is presented to study the unsteady free convection of a second‐grade nanofluid with a new time–space fractional heat conduction. The governing equations with mixed time–space fractional derivatives are non‐dimensionalized and solved numerically, and a comparison between the Caputo and the Caputo–Fabrizio models is made. It is found that the temperature is higher for the Caputo–Fabrizio fractional model than the Caputo model, but the higher velocity only exists near the vertical plate for the Caputo–Fabrizio model than the Caputo model. Moreover, the velocity for the Caputo model will exceed the Caputo–Fabrizio model as y evolves.     

户内热转印粉末涂料用混合型聚酯树脂的合成研究

通过分析热转印性能的影响因素合成了不同结构的聚酯树脂，研究了树脂酸值对热转印性能的影响，同时研究了部分单体对聚酯树脂热转印性能的影响。采用 DSC热分析法研究了固化促进剂对粉末涂料固化行为的影响，结果表明：选择合适的固化促进剂对涂层转印性能的提高有至关重要的作用。