Research on microstructure and magnetostriction of Fe₈₃Ga₁₇Dy_x alloys

The crystal structure,microstructure and the magnetostriction of Fe83Ga17Dyx(x=0,0.2,0.4,0.6) series alloys were studied.The results showed that the influence of the Dy on the crystal structure of the alloy was very small but the effect on the microstructure was significant when different contents of Dy were added into the Fe83Ga17 alloy,respectively.Meanwhile,the magnetostriction of Fe83Ga17Dy0.2 alloy was greatly enhanced,the magnetostriction λ value reached 300×10-6 at 400(kA/m) magnetic field.     

Ni—Mn—Ga铁磁性形状记忆合金的最新研究进展

Ni—Mn—Ga合金是Heusler合金中唯一兼有铁磁性和形状记忆效应的材料,有望成为一种理想的智能驱动材料。本文系统阐述了近年来Ni—Mn—Ga磁性形状记忆合金的重要研究进展,着重介绍了目前研究的合金的成分、添加元素、外磁场、制备工艺、模型及其应用方面的一些最新的研究成果,并提出了磁性形状记忆合金目前存在的问题。     

Ni_（50）Mn_（25＋x）Ga_（25-x）Tb_（0.5）（x=0,1.5,3,4.5,6）合金马氏体相变与磁性能

研究了Ni50Mn25＋xGa25-xTb0.5（x=0,1.5,3,4.5,6）磁性记忆合金马氏体相变行为、饱和磁化强度和磁感生应变。结果表明,随着Mn含量的增加、Ga含量的降低,合金的马氏体相变温度从202 K升高到416 K,饱和磁化强度从700 mT降低到400 mT,最大磁感生应变达到1870ppm。     

稀土铽对Ni-Mn-Ga磁性记忆合金力学性能的影响

研究了稀土Tb对Ni50Mn29Ga21磁性记忆合金抗弯强度和断裂行为的影响。结果表明:稀土Tb可以显著提高材料的抗弯强度,改变断口形貌。不含稀土试样弯曲断裂后其断口主要是晶界断裂。添加稀土后,随着稀土加入量的增多,断裂方式由以晶界断裂为主转为以解理断裂为主。此外,Tb的加入,明显细化了晶粒,同时使材料的含氧量降低。     

预处理对Fe－15Cr－4Al合金475℃脆性的影响和钇的作用

１１００℃预处理的Ｆｅ－１５Ｃｒ－４Ａｌ合金在５００℃时效后迅速脆化，８００℃预处理的合金则无脆化倾向。高温处理的合金有明显的Ｓｎｏｅｋ内耗峰，α相中碳、氮的浓度较高。时效后Ｓｎｏｅｋ峰降低，在主峰的高温侧还分裂出一小峰。这表明４７５℃脆化包括碳、氮析出和α＇相析出两个过程。前者在时效初期有极强的脆化作用，后者在时效数百小时后才显示出微弱的影响。中温预处理的合金无Ｓｎｏｅｋ峰，碳、氮已充分析出，它们不再发生时效析出。含０．２和０．４ｗｔ％Ｙ的合金不出现４７５℃脆性。内耗无Ｓｎｏｅｋ峰，合金中碳化物、氮化物极少。Ｙ－Ｆｅ相俘获杂质原子，消除碳、氮的时效析出，是钇抑制４７５℃脆性的原因。     

Internal Friction in a Shape Memory Alloy Cu-Zn-Al under Equilibrium Condition

1. Introduction CuZnAl shape memory alloys have beenextensively studied as a new type of material.Dejonghe[1]et al. firstly reported theirresults on the internal friction (IF) of CuZnAlalloys in 1975. Later, some researchershave done much work on internal friction.But most of them were concerned withphase transformation internal frictionof martensite and reverse martensite andfew of them were about internal friction     

碳和钇对Fe－Cr－Al合金500℃时效脆化的影响

测定了Ｆｅ－１５Ｃｒ－４Ａｌ合金在５００℃的时效脆化动力学，利用内耗，ＴＥＭ，ＥＰＭＡ和ＳＥＭ等手段研究了合金在时效后的组织变化和断裂行为．结果表明，时效脆化第一阶段（０－１００ｈ）主要是碳化物在α相晶界析出的作用，它损害界面结合，降低断裂应力，使塑性在时效０．２５ｈ后消失；第二阶段（１００－１０００ｈ）主要是富Ｃｒ－α＇相均匀析出的作用，它通过强化基体引起二次脆化．含０．２和０．４％Ｙ的Ｆｅ－１５Ｃｒ－４Ａｌ－Ｙ合金在固溶态下无Ｓｎｏｅｋ内耗峰，碳在α相中的浓度低于０．０００７％，这是碳原子被Ｙ_２Ｆｅ_（１７）相俘获的结果．因此，含钇合金在５００℃时效时不发生晶界碳化物析出，时效１０００ｈ后塑性无明显变化．     

关于如何保护和利用好我国白云鄂博稀土矿资源的建议与思考

稀土作为我国优势战略资源,在新能源、新材料、航空航天、电子信息等领域有着广泛的应用。经过近60年的努力,我国已成为世界稀土生产、出口和消费的第一大国,在世界上具有举足轻重的地位。内蒙古包头白云鄂博矿的稀土资源储量位居全国和世界首位,     

元素替代、掺杂对Fe-Ga合金结构和磁致伸缩性能影响的研究进展

Fe-Ga合金是一种新型磁致伸缩材料,它的高强度、良好韧性、低场高磁致伸缩性能和低成本等优异特性使其具有广泛的商业应用。然而,实际制备的Fe-Ga合金的磁致伸缩数系数很小,提高Fe-Ga合金的磁致伸缩性能成为人们关注的课题。元素替代和掺杂是改善新型Fe-Ga磁致伸缩材料性能的一种有效方法。综述了近几十年来元素替代和掺杂对Fe-Ga磁致伸缩合金结构和性能的影响,并总结了各种元素替代和掺杂的研究进展。在此基础上,指出了元素替代和掺杂在改善Fe-Ga合金性能中存在的问题及今后的发展方向。     

磁性形状记忆合金Ni54Mn21Ga24.75Sm0.25的马氏体相变研究

本文通过内耗和交流磁化率,研究了多晶合金Ni54Mn21Ga25的马氏体相变特征,分析了稀土元素Sm对合金中间马氏体相变影响。研究结果表明,添加Sm使合金Ni54Mn21Ga24的马氏体相变温度提高到室温以上,并且降低了合金的温度滞后,在低磁场下Sm对合金磁感生应变影响不大。