Bi3+对纳米MnO2水热合成的影响研究

在中性和酸性条件下，以MnO2作为锰源，通过水热合成了纳米MnO2，通过XRD和TEM对产物进行的观察表明，在酸性条件下，向溶液中添加一定量的Bi^3 ，产物的晶型由α型向γ型转化，产物形貌由针状、丝状向颗粒状转变。     

烃类在三甘醇和四甘醇中无限稀释活度系数的测定与关联

用气相色谱法分别测定了苯、甲苯、乙苯、正庚烷、正辛烷、正壬烷和正癸烷在三甘醇和四甘醇中的无限稀释活度系数 ,测定温度范围为 5 0～ 13 0℃。用修正的UNIFAC模型 (Dortmund)对上述不同温度下的无限稀释活度系数实验数据进行关联 ,得到了三甘醇和四甘醇与其它基团的相互作用参数 ,并将计算结果与实测值进行了比较。     

Microstructure of Pd_(77.5)Au_6Si_(16.5) Alloy Droplet Solidified in a Drop Tube Process

The microstructure development of Pd77.5Au6Si16.5 alloy droplet solidified in a drop tube process was studied. It was found that two distinct microstructures, i.e. (Pd,Au)3Si primary phase and Pd+(Pd,Au)3Si eutectic can be obtained when the droplet diameter is within the range between 2.3~0.4 mm. The morpologies of the (Pd,Au)3Si developed from dendrite trunk-like with single branching only into dendrite cluster-like with ternary branching with the decrease of the droplet diameter. When the droplet diameter is about 0.25 mm, the primary phase (Pd,Au)3Si almost disappears and the microstructure mainly shows Pd+(Pd,Au)3Si eutectic. The morphology of the eutectic transforms from fiber-like to plate-like with the decrease of the droplet diameter in the range between 2.3-0.25 mm. When the droplet diameter is about 0.19 mm, the microstructure is only the single phase of Pd solid solution     

被动锁模复合环形腔掺饵光纤激光器的自启动分析

本文对被动锁模复合环形腔掺饵光纤激光器的自启动工作特性进行了分析，指出谐振腔内残余反射面的存在是阻碍激光器实现自启动锁模的主要原因。利用半导体激光器有源区的折射率随注入电流的变化而改变的特性，在谐振腔中获得了一个可移动腔镜，克服了腔内残余反射面的影响，实现了锁模的自启动。     

新型缆用热熔胶的研制

分析了通信线缆用 YH- 4热熔胶组成原料的性能和作用 ,找出影响耐环境高温性能的主要原因 ,并对新研制出的耐环境高温性能 YH- 5热熔胶作了一些分析和探讨 .     

热力系统节能技术改造方案介绍

针对热电厂热力系统存在的浪费能源和设计不合理现象作了浅析 ,介绍了几种对热力系统进行改造的方案 ,并对取得的经济效益进行了计算。     

Continuous Separation of Inclusions from Aluminum Melt Flowing in a Circular Pipe using a High Frequency Magnetic Field

The continuous separation of inclusions from aluminum melt flowing in a circular pipe using a high frequency magneticfield was investigated both theoretically and experimentally The separation efficiency was calculated based on thetrajectory method and compared with experimental results. It is found that the separation efficiency is a functilnondimensional parameters t_i·d_p~2B_e~2/μ_fμ_eα~2 and α/δ.The effective way to improve the separation efficiency is to increasethe effective magnetic flux density and decrease the pipe radius. and the value of α/δ should be kept about 2 in orderto obtain the optimum separation efficiency.     

提高20t电弧炉炉衬寿命工艺实践

炉渣碱度、泡沫渣高度、吹氧角度、补炉方式等是影响20t电弧炉炉衬寿命的主要因素。为了提高炉衬寿命,莱钢炼钢厂采取了控制炉渣组成、泡沫渣全程埋弧操作、吹氧、喷补炉衬等多项措施,使炉衬寿命稳定在600炉次以上。     

石英晶体监控法镀制高精度光学薄膜

讨论了石英晶体监控法在光学薄膜镀制过程中的应用原理。通过与常规的光学监控法镀制的膜层相比较．证实了石英晶体监控法有助于提高光学薄膜的光学品质。试验表明所镀膜层的光学性能优异，在光通信和激光器等领域具有广阔的应用前景。     

镁合金表面喷铝防腐蚀层的微观组织分析

在AZ91D镁合金表面热喷铝，用以提高其表面的耐腐蚀性能。采用SEM，EPMA等方法对AZ91D表面喷铝扩散层的组织进行了仔细的观察与分析，发现在防腐蚀层上有大量的Mg17Al12相存在，且呈决状及非连续片状分布。经显微硬度测定，喷铝层硬度较镁合金基体高；腐蚀后这种相凸出于基体，比镁合金基体有较好的耐腐蚀性能。