Sonoelectrochemical synthesis of a nanoscale complex of lead(II) and 2-methyl-8-hydroxyquinoline: spectroscopic, photoluminescence, thermal analysis studies and its application in an OLED

A new lead complex, [Pb(mq)₂], (mq = 2-methyl-8-hydroxyquinoline) was prepared via an electrochemical route from the oxidation of lead metal in the presence of 2-methyl-8-hydroxyquinoline in a fast and facile process. The complex was fully characterized by means of NMR and IR spectra and elemental analysis. The nanostructure of the prepared compound was obtained by sonoelectrochemical process and studied by scanning electron microscopy, atomic force microscopy, X-ray powder diffraction, IR spectroscopy and elemental analysis. Thermal stability of single crystalline and nanosize samples of the prepared compound was studied by thermal gravimetric and differential thermal analysis. The photoluminescence properties of the prepared compounds, as single crystals and as nanorods, have been investigated. The results showed a good correlation between the size and the shape of the complex particles and emission wavelength. The prepared complex was doped in PVK:PBD blend as guest and its application in the fabrication of OLED was studied. The ratio of lead complex was modified and was equal to 8 (w/w %) in PVK:PBD (100:40).     

Effect of metal loading on catalytic activity and selectivity of ZSM-5 zeolite catalyst in conversion of methanol to olefins and aromatics

Effect of ZSM-5 zeolite promotion using potassium, strontium, and cerium metals on conversion of methanol to light olefins and aromatics was investigated. ZSM-5 catalyst was promoted using wet impregnation of metal salts and its activity was tested in methanol to hydrocarbons process under optimum operational condition obtained in our group previously. Zeolite samples were characterized by X-ray powder diffraction, scanning electron microscopy, N₂ adsorption-desorption, acid sites distribution, and strength using temperature programmed desorption of NH₃. Results showed that presence of these metals could significantly affect acid site distribution and therefore influence the catalyst activity and selectivity to olefins and aromatics.     

Novel high strength Al-10.5Si-3.4Cu-0.2Mg alloy produced through two-stage solution heat treatment

Mechanical properties of aluminum-silicon-copper alloys are enhanced through precipitation hardening. The response of these alloys to age-hardening is very slow. To overcome this problem, 0.2, 0.4 and 0.7 wt.% magnesium were added to Al-10.5Si-3.4Cu alloy. The new alloys were subjected to two types of precipitation hardening processes different in the solutionizing stage. The results showed that the presence of various amounts of magnesium in the composition of this alloy accelerates the response to ageing treatments, increasing the hardness and strength. Higher mechanical properties can be achieved when the alloys were subjected to a two-stage solution heat treatment. It is found that Al-10.5Si-3.4Cu alloy containing 0.2 wt.% Mg treated through a two-stage solution process, has optimum properties with ultimate tensile strength of 383.9 MPa, yield strength of 289.7 MPa and elongation of 3.97%, and can be used as a substitute for a large number of aluminum castings which need high strength and excellent castability.     

Effect of various efficient vulcanization cure systems on the compression set of a nitrile rubber filled with different fillers

Effect of various efficient vulcanization (EV) sulfur cure systems on the compression set of a nitrile rubber filled with carbon black and silica/silane fillers was examined. The cure systems had different amounts of thiuram and sulfenamide accelerators and elemental sulfur, whilst the loading of zinc oxide and stearic acid activators was kept constant. The fillers had surface areas from 35 to 175 m²/g. In this study, the lowest compression set was measured for the rubber filled with carbon black with 78 m²/g surface area, which was cured with an EV cure system made of a small amount of elemental sulfur and large amounts of the two accelerators. Interestingly, a small change in the amount of elemental sulfur had a bigger effect on the compression set than did large changes in the loading of the accelerators in the cure system. Among the fillers, carbon black caused less compression set of the rubber vulcanizate than the silica/silane system did. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41512.     

Topology optimization of transient problem with maximum dynamic response constraint using SOAR scheme

Frontiers of Mechanical Engineering - This paper proposes a novel method for the continuum topology optimization of transient vibration problem with maximum dynamic response constraint. An...     

Synthesis of graphene-supported bimetallic nanoparticles for the sunlight photodegradation of Basic Green 5 dye in aqueous medium

Graphene nanosheets-supported Sn-Pt bimetallic nanoparticles (GNs/Sn-Pt) were prepared by precipitation method. The obtained GNs/Sn-Pt was used as a photocatalyst for photodegradation of Basic Green 5 (BG5) in aqueous solution under sunlight. The morphology and photodegradation study was performed by SEM and UV–VIS spectrophotometry, respectively. The SEM image showed the presence of Sn and Pt on GNs, being confirmed by energy dispersive X-ray (EDX) analysis. The photodegradation study of BG5 showed that the dye degradation increases as a function of irradiation time. The degradation of BG5 was found to be pH dependent and maximum degradation was found at higher pH.     

Influence of plasticizers and cryogenic grinding on the high‐cooling‐rate solidification behavior of PBT/PET blends

Two structurally different plasticizers (cyclic and linear) and the effect of cryogenic grinding on the solidification behavior at high cooling rates by a continuous cooling transformation approach of poly(butylene terephthalate)/poly(ethylene terephthalate), PBT/PET, blends are described. The solidification curve (density versus cooling rate) is confirmed as an effective tool to compare the differences in crystallization behavior under conditions mimicking processing. In comparison to the bulky cyclic plasticizer, the linear oligomeric one was found to have a more pronounced influence on the crystallization behavior. A 60/40 by weight PBT/PET blend shows a drop‐off of density at ～50 K/s. In the plasticized sample, the long‐range crystalline order appears up to a cooling rate of ～250K/s, making the blend comparable to pure PBT. Grinding the components before blending further improves crystallizability and synergy to the addition of the plasticizer. The results suggest the important role of local chain mobility in the solidification behavior at high cooling rates. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 43083.     

Investigation of structure and mechanical properties of toughened poly(l‐lactide)/thermoplastic poly(ester urethane) blends

In this study, poly(l ‐lactide) (PLA) is melt‐blended with thermoplastic polyurethane (TPU) to modify the brittleness of PLA. An aliphatic ester‐based TPU was selected in order to have an ester sensitivity for degradation and an inherent biocompatibility. Using this compatible TPU, there was no need to apply problematic compatibilizers, so the main positive properties of PLA such as biocompatibility and degradability were not challenged. The detected microstructure of PLA/TPU blends showed that when the TPU content was lower than 25 wt %, the structure appeared as sea‐islands, but when the TPU content was increased, the morphology was converted to a cocontinuous microstructure. A higher interfacial surface area in the blend with 25 wt % TPU (PLA25) resulted in a higher toughness and abrasion resistance. The various analyses confirmed interactions and successful coupling of two phases and confirmed that melt‐blending of PLA with the aliphatic ester‐based TPU is a convenient, cost‐effective, and efficient method to conquer the brittleness of PLA. The prepared blends are general‐purpose plastics, but PLA25 showed an optimum mechanical strength, toughness, and biocompatibility suitable for a wide range of applications. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 43104.